Acta Polytechnica https://doi.org/10.14311/AP.2022.62.0248 Acta Polytechnica 62(2):248–261, 2022 © 2022 The Author(s). Licensed under a CC-BY 4.0 licence Published by the Czech Technical University in Prague EFFECT OF PIGMENTS ON BOND STRENGTH BETWEEN COLOURED CONCRETE AND STEEL REINFORCEMENT Joseph J. Assaad∗, Matthew Matta, Jad Saade University of Balamand, Department of Civil and Environmental Engineering, Balamand, PO Box 100, Al Kourah, Lebanon ∗ corresponding author: joseph.assaad@balamand.edu.lb Abstract. The effect of pigments on mechanical properties of coloured concrete intended for structural applications, including the bond stress-slip behaviour to embedded steel bars, is not well understood. Series of concrete mixtures containing different types and concentrations of iron oxide (red and grey colour), carbon black, and titanium dioxide (TiO2) pigments are investigated in this study. Regardless of the colour, mixtures incorporating increased pigment additions exhibited higher compressive and splitting tensile strengths. This was attributed to the micro-filler effect that enhances the packing density of the cementitious matrix and leads to a denser microstructure. Also, the bond to steel bars increased with the pigment additions, revealing their beneficial role for improving the development of bond stresses in reinforced concrete members. The highest increase in bond strength was recorded for mixtures containing TiO2, which was ascribed to formation of nucleus sites that promote hydration reactions and strengthen the interfacial concrete-steel transition zone. The experimental data were compared to design bond strengths proposed by ACI 318-19, European Code EC2, and CEB-FIP Model Code. Keywords: Coloured concrete, iron oxide pigment, carbon black, titanium dioxide, durability, bond strength. 1. Introduction Pigments including iron oxide (IO), carbon black (CB), and titanium dioxide (TiO2) are finely ground parti- cles for integral colouring of concrete and cementitious materials intended for architectural applications [1–3]. Often manufactured as per ASTM C979 [3] specifi- cation, the pigments are bound onto the surface of cement grains, thus altering the colour characteristics by absorbing certain wavelengths of the visible light and reflecting others. The IOs are synthetic colourants manufactured to display a variety of colours (i.e., red, grey, yellow, etc.), thus infusing the concrete with their shades [4, 5]. These pigments are stable in the high-alkaline Portland cement environment, confer- ring proper colour fastness to sunlight exposure and resistance to weathering effects. The CB is an eco- nomical black colourant with high tinting strength produced from petroleum and charring organic materi- als [1, 6]. Compared to IO, the CB generally disrupts the air-entrainment and increases the vulnerability of concrete to leaching when exposed to repeated wet/dry cycles [6]. The white-coloured TiO2 mostly occurs in the natural rutile and anatase crystal forms [7, 8]; it is normally used with white cement and other pozzolanic materials (metakaolin) to brighten the cementitious mixture. Earlier studies showed that the pigment character- istics (i.e., type, fineness, mineralogy, morphology, solubility, etc.), additions rates, and dispersion can drastically alter the fresh and hardened concrete prop- erties [9–11]. For instance, it is accepted that pig- ments absorb part of the free mixing water because of a significantly higher surface area (vs. cement), thus requiring increased water demand and/or high-range water reducer (HRWR) to achieve a given workabil- ity [12–14]. Meng et al. [15] reported that the drop in fluidity due to TiO2 can be controlled through HRWR and slag additions. If poorly dispersed, added pig- ments may agglomerate in the cement matrix, causing unreacted pockets or weak zones that decrease me- chanical properties [15, 16]. Lopez et al. [17] suggested using the mortar phase, while others recommended the use of extended mixing time [18] or water-based colourants [19] to improve pigment dispersibility. Despite their chemically inert nature, most stud- ies showed that synthetic IO and CB pigments lead to increased strength and durability of cementitious materials. This is generally associated to a micro- filler effect that blocks the capillary pores and leads to a denser microstructure [9, 20, 21]. Yildizel et al. [22] found that yellow and black IOs lead to in- creased strength and resistance to water permeabil- ity. Mortars produced using red pigments exhibited relatively higher pore ratios, which detrimentally af- fected freeze/thaw resistance and durability. Assaad et al. [11] reported that strength and bond to existing substrates increased when red or yellow pigments are incorporated by up to 6 % of cement mass. The cur- tail in strength at high pigment rates (above 6 %) was related to improper hydration reactions resulting from the excessive amount of powders that are adsorbed onto the cement grains. Masadeh [23] found that 248 https://doi.org/10.14311/AP.2022.62.0248 https://creativecommons.org/licenses/by/4.0/ https://www.cvut.cz/en vol. 62 no. 2/2022 Effect of pigments on bond strength between coloured . . . Physical properties Specificgravity Median particle size Soundness Blaine fineness Lightness (L-value) 3.15 26.5 µm 0.04 % 3150 cm2/g 88.5 Chemical properties CaO SiO2 Al2O3 Fe2O3 MgO 68.5 % 21.8 % 4.15 % 0.27 % 1.18 % Table 1. Physical and chemical properties of white cement. CB incorporated up to 0.5 % of cement mass reduces the concrete chloride permeability and corrosion rates of inserted steel bars. Inoue et al. [24] noted that the CB treatment using aqueous solution of humic acids helps improving the dispersibility together with a reduced interaction with air-entraining surfactants and superior adhesion to the cement matrix (i.e., less leaching). In addition to the micro-filler effect, numerous re- searchers found that TiO2 can participate in the ce- ment hydration process, at least as nucleation sites, to accelerate setting times and promote strength devel- opment [15, 16, 25, 26]. Chen et al. [27] showed that concrete durability and resistance to water infiltra- tion significantly improved with 3 % TiO2 additions, given the conversion of greater volume of calcium hydroxide (CH) crystals into C-S-H gels. Zhang et al. [28] reported that TiO2 acts as a filler in empty spaces and crystallization centre of CH to refine the concrete microstructure including its resistance to chloride ion penetration. Folli et al. [29] speculated that the strength improvement might be related to alteration in packing density and nucleus orientation around the interfacial transition zones, rather than increased amounts of hydration products. 2. Context and paper objectives The performance of coloured concrete in structural members, including the extent to which the use of pigments would alter the bond strengths to embedded steel bars, is not well understood. Generally, the trans- fer of stresses between the reinforcement and surround- ing concrete is attributed to chemical adhesion and mechanical bearing arising from the concrete surface around the steel ribs [30, 31]. The parameters affect- ing the bond are broadly related to the reinforcement characteristics (i.e., yield strength of bar, size, geom- etry, epoxy coating, cover, position in cast member, etc.) and concrete constituents and properties (i.e., density, strength, workability, presence of fibres, min- eral admixtures, etc.) [32]. The spliced or developed lengths are computed by relevant models proposed by various building codes; for example, ACI 318-19 [33] considers that the development length for deformed bars in tension members is inversely proportional to the square root of compressive strength, multiplied by specific factors to account for special considerations due to the reinforcement size, lightweight concrete, top bars, epoxy-coated bars, and contribution of confining transverse reinforcement. Yet, limited attempts have been made to assess the validity of existing models and design provisions in the case of coloured concrete. This paper is a part of a comprehensive research project undertaken to assess the effect of pigments on durability and mechanical properties of coloured concrete mixtures. Two concrete series made with 350 and 450 kg/m3 cement content and various con- centrations of IO (red or grey colour), CB, and TiO2 pigments are investigated. Tested properties included the compressive strength, splitting tensile strength, modulus of elasticity, and bond stress-slip behaviour to reinforcing steel bars. The experimental data were compared to design bond strengths proposed by rele- vant building codes including ACI 318-19 [33], Euro- pean Code EC2 [34], and CEB-FIP Model Code [35]. Data reported herein can be of interest to civil engi- neers and architects seeking the use of pigments in coloured concrete intended for structural applications. 3. Experimental program 3.1. Materials White-coloured Portland cement conforming to ASTM C150 Type I was used in this study. Its physical and chemical properties are listed in Table 1. The gradations of siliceous sand and crushed lime- stone aggregate were within the ASTM C33 specifica- tions. The specific gravity for the sand, fineness mod- ulus, and absorption rate were 2.65, 3.1, and 0.75 %, respectively. Those values were 2.72, 6.4, and 1 %, respectively, for the coarse aggregate, while the nomi- nal maximum particle size was 20 mm. Naphthalene- based HRWR was used; its specific gravity, solid con- tent, and maximum dosage rate were 1.2, 40.5 %, and 3.5 % of cement mass, respectively. Commercially available IO (i.e., red and grey colour), CB, and TiO2 pigments were used. As shown in Figure 1, the red and grey coloured IOs had almost spherical shapes; their specific gravities were 4.64 and 4.8, respectively, while their Fe2O3 contents were 97.5 % and 98.8 %, respectively. The white-coloured TiO2 is rutile-based manufactured by the chloride process; it also possesses round shape (Figure 1) with a specific gravity of 4.1. The CB is produced by combustion of aromatic petroleum oil feedstock and consists essentially of pure carbon (i.e., > 98 %); its specific gravity was 2.05. The particle size gradation curves obtained by laser diffraction for the various pigments are plotted in 249 J. J. Assaad, M. Matta, J. Saade Acta Polytechnica Red IO Grey IO TiO2 Carbon Black Figure 1. Morphology of various pigments used. 0 20 40 60 80 100 0.01 0.1 1 10 100 Pe rc en t p as si ng Particle diameter, 𝛍m Cement Red IO Grey IO TiO2 Carbon black Figure 2. Particle size distribution curves for the cement and various pigments. Figure 2. Generally speaking, the fineness of IO pig- ments is pretty close to each other; the median di- ameter (d50) computed as the size for which 50 % of the material is finer for the grey and red IO is 4.1 and 5.3 µm, respectively. The TiO2 and CB were re- markably finer, which shifted the gradation curves towards much smaller particle sizes. The resulting d50 dropped to 0.21 and 0.092 µm for the TiO2 and CB, respectively. Deformed steel bars complying to ASTM A615 No. 13 were used in this work to evaluate the effect of pigments on bond stress-slip properties of coloured concrete to embedded rebars. The bar nominal diam- eter (db), Young’s modulus, and yield strength (fy ) were 12 mm, 205 GPa, and 520 MPa, respectively. 3.2. Mixture proportions Two control concrete mixtures containing 350 (or, 450) kg/m3 cement with 0.5 (or, 0.42) water-to-cement ratio (w/c) were considered; the corresponding 28- days f ′c was 26.7 and 34.2 MPa, respectively. The fine and coarse aggregate contents in the lean concrete mixture were 830 and 1020 kg/m3, respectively; while these were 790 and 925 kg/m3 in the higher strength concrete mix. The resulting sand-to-total aggregate ratio was 0.45. The HRWR dosage was either 2.6 % or 2.35 % of cement mass, respectively, in order to secure a fixed workability corresponding to a slump of 210 ± 10 mm. The IO, CB, and TiO2 pigments were incorporated at three different concentrations varying from 1.5 % to 4.5 % of cement mass, at 1.5 % increment rates. The 250 vol. 62 no. 2/2022 Effect of pigments on bond strength between coloured . . . TiO2 Carbon black Control mix Red IO Grey IO 1.5% 3% 4.5% 1.5% 3% 4.5% 1.5% 3% 4.5% 1.5% 3% 4.5% Concrete with cement content = 350 kg/m3 Figure 3. Photo of coloured cylinders after the splitting tensile test. mixing sequence consisted on homogenizing the fine aggregate, coarse aggregate, and powder pigment for 3 minutes to ensure efficient dispersion of colourant materials. The cement, water, and HRWR were then sequentially introduced over 2 minutes. After 30 sec rest period, the mixing resumed for 2 more minutes. The ambient temperature and relative humidity (RH) remained within 23 ± 3 °C and 55 ± 5 %, respectively. 3.3. Testing procedures 3.3.1. Fresh and hardened properties Right after mixing, the workability and air content were determined as per ASTM C143 and C231, respec- tively. The concrete was cast in 100 × 200 mm cylin- ders to determine the density, compressive strength (f ′c), and splitting tensile strength (f t) as per ASTM C642, C39, and C496, respectively [36–38]. All speci- mens were demoulded after 24 hours, cured in water, and tested after 28 days. Averages of 3 values were considered. The modulus of elasticity (E) was de- termined through ultrasonic pulse velocity (U P V ) measurements using 100 × 200 mm concrete cylin- ders, as per ASTM C597 [39]. The pulse velocity was computed as the ratio between the 200 mm length of the concrete specimen to the measured transit time. The E was computed using the conventional wave propagation equation in solid rocks, expressed as: E, GP a = [(ρ × U P V 2)/g] 10−2, where g is gravity acceleration (9.81 m/s2) and ρ is the concrete density (kg/m3) [1, 31]. 3.3.2. Colourimetry The L, a, and b colour coordinates were determined following the Commission Internationale d’Eclairage (CIE) system using a portable colourimeter. The L-value reflects the colour lightness varying from 0 (black) to +100 (white), a-value represents the chro- matic intense of magenta/red (+127) and green (–128), and b-value the chromatic intense of yellow (+127) and blue (–128) [19, 40]. The specimens were oven-dried for one day at 50 ± 5 °C prior to testing. The measure- ments were realized using the broken cylinders after the tensile splitting test, as shown in Figure 3. Special care was taken to position the colourimeter sensor in the mortar phase (not the aggregate particle); while an average of 6 measurements was considered. The colour deviation (∆(E)) due to pigment additions from the control mix was determined as: ∆(E) = √ (LC − L)2 + (aC − a)2 + (bC − b)2, where LC = LControl, aC = aControl, bC = bControl. 3.3.3. Bond to steel reinforcement The direct bond method was used to determine the bond stress-slip properties of concrete mixtures, in accordance with RILEM/CEB/FIB specification [41]. The bars were vertically centred in the 150 mm cubic moulds (Figure 4); the embedded length was 60 mm (5 db) and PVC bond breaker was inserted around the bar at the concrete surface to reduce the concentration of stresses during loading. After 24 hours from casting, the specimens were demoulded and covered with plas- tic bags to cure at 23 ± 3°C for 28 days. The direct bond test was realized using a universal testing ma- chine, whereby the pullout load and slips of the steel bar relative to the concrete block are recorded [30, 42]. The tensile load was gradually applied until failure at a rate hovering 0.25 kN/sec. 4. Test results and discussion 4.1. HRWR demand Table 2 summarizes the HRWR demand and colour coordinates for mixtures prepared with various pig- ment types and concentrations. In line with current literature [1, 4, 8], the demand for HRWR increased with pigment additions, given their higher fineness 251 J. J. Assaad, M. Matta, J. Saade Acta Polytechnica 150 mm 150 mm 140 mm Steel bar Unbonded length (80 mm) Bonded length (5db = 60 mm) Top view: Bar placed centrally Side view: Figure 4. Photo of the experimental testing of bond stress-slip properties. Mixture codification HRWR [% of cement] Slump [mm] Air content [%] Density [kg/m]3 L a b ∆(E) 350-Control 2.6 205 2.8 2320 67.8 5.6 19.3 – 350-Red-1.5 % 2.6 205 n/a 2315 55.2 12.8 12.9 15.8 350-Red-3 % 2.9 200 2.7 2330 51.9 16.1 10.6 21.0 350-Red-4.5 % 3.2 200 2.9 2375 44.4 19.8 12 28.3 350-Grey-1.5 % 2.7 195 n/a 2330 61.9 2.2 12.4 9.6 350-Grey-3 % 2.9 205 3.1 2360 58.4 0.8 7.2 16.0 350-Grey-4.5 % 3.1 205 n/a 2350 49.4 -0.1 4.0 24.6 350-TiO2-1.5 % 2.7 210 n/a 2310 72.0 5.3 19.8 4.3 350-TiO2-3 % 3.0 210 3 2340 71.9 5.4 19.7 4.2 350-TiO2-4.5 % 3.1 195 2.9 2380 76.3 4.4 17.9 8.7 350-CBlack-1.5 % 2.9 190 n/a 2350 42.4 -0.2 -0.2 32.5 350-CBlack-3 % 3.5 195 3.2 2340 42.2 -0.5 -0.7 33.0 350-CBlack-4.5 % 3.6 205 3.4 2390 31.0 -0.05 -1.2 42.4 450-Control 2.4 205 3 2345 68.3 5.7 19.1 – 450-Red-3 % 2.5 210 3.1 2385 48.8 19.0 10.8 25.0 450-Grey-3 % 2.8 200 3 2385 56.2 0.58 6.9 17.9 450-TiO2-3 % 2.7 200 2.8 2405 77.1 5.1 19.1 8.9 450-CBlack-3 % 3.2 205 3.5 2415 41.9 -0.4 -0.8 33.6 The mix codification refers to cement content-Pigment type-Pigment dosage. n/a refers to not tested. Table 2. Effect of pigment types and concentrations on workability and colourimetry properties. 252 vol. 62 no. 2/2022 Effect of pigments on bond strength between coloured . . . 15.8 21.0 28.3 9.6 16.0 24.6 4.3 4.2 8.7 32.5 33.0 42.4 0 10 20 30 40 50 1. 5% 3% 4. 5% 1. 5% 3% 4. 5% 1. 5% 3% 4. 5% 1. 5% 3% 4. 5% ∆( E) Red Grey TiO2 C. Black Cement content = 350 kg/m3 Figure 5. Effect of pigment type and concentration on ∆(E) variations for concrete prepared with 350 kg/m3 cement. that absorbs part of the mixing water and results in requirement of additional superplasticizing molecules to ensure the targeted slump of 210 ± 10 mm. For example, at a 3 % pigment rate, the HRWR dosage varied from 2.6 % for the 350-Control mix to 2.9 % and 2.85 % for the 350-Red-3 % and 350-Grey-3 % mixtures, respectively. The increase in HRWR was particularly pronounced for the CB pigment, given its extremely fine particles [13]. Hence, the HRWR reached 3.45 % and 3.6 % for the concrete containing 3 % or 4.5 % CB, respectively. 4.2. Colourimetry As can be noticed in Table 2, the lightness of colour (L- value) increased from 67.75 for the 350-Control mix to 72 and 76.3 with the addition of 1.5 % and 4.5 % TiO2, respectively, which can be attributed to the intrinsic white-coloured nature of this pigment [26, 29]. Yet, as expected, the L-value followed a decreasing trend when darker pigments were used; it dropped to 49.35, 44.35, and 31 for mixtures containing 4.5 % grey, red, and CB pigments, respectively. To the other end, the magenta chromatic intense (i.e., a-value) varied from 5.55 to 16.1 for the 350-Control and 350-Red-3 % mixtures, respectively, while in contrast, the highest b-value of 19.75 corresponded to the 350-TiO2-1.5 % mix. Concrete mixtures prepared with CB exhibited negative a and b values, reflecting the black colouring effects of such powders. As shown in Figure 5, the mixtures containing the white-coloured TiO2 pigments exhibited the lowest ∆(E) values, reflecting relatively limited variations with respect to the control mix. The incorporation of red or grey IO pigments gradually increased the ∆(E) values that varied from 9.6 to 28.3, while the CB- modified mixtures exhibited the highest ∆(E) that varied from 32.5 to 42.4. It should be noted that ∆(E) steadily increased with pigment additions (Figure 5), without showing a clear stabilization tendency that reflects colour saturation [11, 17]. This can be at- tributed to the relatively reduced cement volume (i.e., about 11 % of the overall concrete mix), thus requiring additional pigment powders to achieve colour satu- ration. Additionally, the beige-like colour of natural sand could have affected the pigment tinting strength, which reduced the tendency towards the colour satu- ration [10, 11]. 4.3. Hardened properties The effect of pigment type and concentration on the 28-days f ′c for concrete prepared with 350 kg/m3 cement are summarized in Table 3, and plotted in Fig- ure 6. Regardless of the colour, mixtures incorporating increased pigment additions exhibited higher strength values. For example, compared to the 26.7 MPa value obtained for the control mix, the f ′c increased to 29.7 and 34.9 MPa for the mixtures containing 1.5 % and 4.5 % red IO, respectively. Such values reached 30 and 34.2 MPa for the mixtures containing 1.5 % and 4.5 % grey IO, respectively. This could be associated to the micro-filler effect and enhanced packing density that lead to a denser microstructure capable of supporting higher loads. Yildizel et al. [22] reported that IO pigments are inert materials (i.e., do not react with water) that fill the interspaces and capillary pores in cementitious systems, leading to an improved resis- tance against permeability and attack of aggressive ions. For the given concentration, the effect of CB on strength development is pretty similar or slightly higher than the IO pigments. Hence, the f ′c reached 35.1 MPa for the 350-CBlack-4.5 % mixture. Know- ing the inert nature of such powders, the increase in strength can be physically related to the micro-filler ef- fect that enhances packing density of the cementitious matrix. The highest increase in f ′c was recorded for con- crete mixtures prepared with TiO2 additions; this 253 J. J. Assaad, M. Matta, J. Saade Acta Polytechnica 26.7 29.7 34 34.9 30 29.8 34.2 33.5 36 37.7 30.2 34 35.1 25 30 35 40 Co nt ro l 1. 5% 3% 4. 5% 1. 5% 3% 4. 5% 1. 5% 3% 4. 5% 1. 5% 3% 4. 5% f'c , M Pa Red Grey TiO2 C. Black Cement content = 350 kg/m3 Figure 6. Effect of pigment types and concentrations on hardened properties and bond to steel bars. Mixture codification 7-d f ′c [MPa] 28-d f ′c [MPa] f t [MPa] UPV [km/s] E [GPa] τu [MPa] δu [mm] 350-Control 14.8 26.7 2.16 3.55 29.8 11.36 4.1 350-Red-1.5 % 17 29.7 2.28 3.58 30.2 11.94 5.3 350-Red-3 % 20.1 34 2.41 3.6 30.8 18.00 10.3 350-Red-4.5 % 19.8 34.9 3.06 3.62 31.7 17.78 10.5 350-Grey-1.5 % 17.2 30 n/a 3.5 29.1 n/a n/a 350-Grey-3 % 20.2 29.8 2.86 3.62 31.5 12.74 4.9 350-Grey-4.5 % 20.6 34.2 3.36 3.58 30.7 14.05 6.1 350-TiO2-1.5 % 19.7 33.5 2.62 3.57 30.0 17.25 6.2 350-TiO2-3 % 19.6 36 2.7 3.66 32.0 n/a n/a 350-TiO2-4.5 % 20.6 37.7 3.22 3.62 31.8 20.70 7.8 350-CBlack-1.5 % 19 30.2 2.87 3.6 31.0 15.34 4.4 350-CBlack-3 % 18.8 34 n/a 3.72 33.0 n/a n/a 350-CBlack-4.5 % 20.5 35.1 3.28 3.8 35.2 17.89 5 450-Control 23.4 34.2 2.56 3.7 32.7 18.90 5.8 450-Red-3 % 27.3 38.9 3.76 3.8 35.1 23.41 11.5 450-Grey-3 % 25.8 42.3 n/a 3.83 35.7 19.78 6.3 450-TiO2-3 % 28.6 44.5 3.94 3.7 33.6 24.85 9.2 450-CBlack-3 % 27.6 41.6 3.85 3.9 37.4 21.96 7.2 n/a refers to not tested. Table 3. Effect of pigment types and concentrations on workability and colourimetry properties. 254 vol. 62 no. 2/2022 Effect of pigments on bond strength between coloured . . . y = 6.962x + 13.87 R² = 0.7 y = 2.976x + 23.32 R² = 0.58 25 29 33 37 41 45 2.0 2.4 2.8 3.2 3.6 4.0 f'c , M Pa o r E, G Pa ft, MPa f'c E Figure 7. Relationships between f t with respect to f ′c and E responses for all tested concrete mixtures. 0 4 8 12 16 20 24 0 2 4 6 8 10 12 14 Bo nd s tr es s, M Pa Displacement, mm Mixtures with 350 kg/m3 cement Control mix Grey-4.5% TiO2-4.5% Red-4.5% Figure 8. Typical bond stress vs. displacement curves for mixtures prepared with 350 kg/m3 cement. reached 33.5 and 37.7 MPa at 1.5 % and 4.5 % rates, respectively. Besides the micro-filler effect, the in- crease in strength may be ascribed to the formation of nucleation sites that promote hydration reactions and precipitate additional gels in the hardened ma- trix [16, 29]. The hydration products grow around the TiO2 particles, causing the formation of secondary C- S-H in the capillary pores that reduces the porosity of the matrix. As shown in Table 3, the f ′c significantly increased from 34.2 MPa for the 450-Control mix to 44.5 MPa for the 450-TiO2-3 % concrete, which can be associated to the micro-filler effect prompted with additional C-S-H hydrating compounds that could refine the concrete microstructure [27, 28]. The effect of pigment type and concentration on f t and E properties is quite similar to the one observed on f ′c responses. Hence, the strength increased with IO and CB pigments, while being particularly pro- nounced with the use of TiO2 (Table 3). Moderate relationships with correlation coefficients (R2) larger than 0.58 are obtained between the hardened prop- erties for all tested concrete mixtures prepared with 350 and 450 kg/m3 cement, as shown in Figure 7. 4.4. Bond stress-slip behavior Table 3 summarizes the ultimate bond strength (τu) at failure and corresponding slip (δu) for all tested concrete mixtures. It is worth noting that the coeffi- cient of variation (COV) for τu responses determined for selected mixtures varied from 9.6 % to 14.7 %, rep- resenting an acceptable repeatability. The steel bars did not reach their yielding state during pullout test- ing (i.e., the yielding load is 58.8 kN). A pullout mode of failure occurred for all tests, whereby the concrete crushed and sheared along the embedded steel re- gion with no visible cracks on the external concrete specimens [30, 31]. Typical bond stress-slip (τ vs. δ) curves determined for the 350-Control mix and those incorporating dif- ferent pigment types and concentrations are plotted in Figure 8. All curves are initially linear, which can be ascribed to the adhesive component of the bond and mechanical interlock that takes place between the 255 J. J. Assaad, M. Matta, J. Saade Acta Polytechnica 11.36 11.94 18.00 17.78 12.74 14.05 17.25 20.70 15.34 17.89 10 13 16 19 22 Co nt ro l 1. 5% 3% 4. 5% 3% 4. 5% 1. 5% 4. 5% 1. 5% 4. 5% U lti m at e bo nd s tr en gt h, M Pa Red Grey TiO2 C. Black Cement content = 350 kg/m3 Figure 9. Effect of pigment type and concentration on τu for mixtures prepared with 350 kg/m3 cement. y = 1.129x + 15.12 R² = 0.83 y = 0.104x + 1.17 R² = 0.57 2.0 2.5 3.0 3.5 4.0 4.5 25 29 33 37 41 45 10 13 16 19 22 25 28 ft , M Pa f'c , M Pa Ultimate bond strength, MPa f'c ft Figure 10. Relationships between τu with respect to f ′c and f t for all tested concrete mixtures. embedded steel ribs and the surrounding concrete [32]. The 350-TiO2-4.5 % mixture exhibited the highest τ vs. δ responses, given the micro-filler effect and formation of secondary C-S-H hydrating compounds that strengthen the interfacial concrete-steel transition zone [26, 29]. Hence, compared to the 11.36 MPa value obtained from the control mix, τu reached 20.7 MPa for the 350-TiO2-4.5 % concrete. The increase in τu was also noticeable for mixtures prepared with IO pig- ments, albeit this remained comparatively lower than what was achieved with TiO2 additions. Hence, τu reached 14.05 and 17.78 MPa for the 350-Grey-4.5 % and 350-Red-4.5 %, respectively. When the adhesive and interlock components fail, the concrete between the steel ribs breaks, causing excessive local slips at reduced bond stresses [42, 43]. Only the frictional bond component remains in the post-peak region of τ vs. δ curves, whereby the steel bars are dynamically pulled out from the concrete specimens. Figure 9 summarizes the effect of the pigment type and concentration on τu responses determined for mixtures prepared with a 350 kg/m3 cement content. Regardless of the pigment type, τu gradually increased with such additions, which practically reveals their beneficial role for improving the development and transfer of bond stresses in reinforced concrete mem- bers. The highest value of 20.7 MPa was recorded for the concrete containing the highest TiO2 concen- tration of 4.5 %. This was followed by mixtures in- corporating 3 % and 4.5 % red IO as well as those made using 4.5 % CB; the resulting τu hovered around 18 MPa. Just like the mechanical properties, the in- crease in τu due to inert IO or CB pigments can be attributed to the micro-filler effect that densifies the cementitious microstructure around the steel ribs, leading to an improved bond behaviour. Moderate relationships with R2 of 0.57 and 0.83 are established between τu with respect to f ′c and f t for all tested concrete mixtures (Figure 10). As shown in Figure 8, the increase in τu due to pigment additions is accompanied by an increase in the maximum slip that occurs at failure. For example, δu of 4.1 mm was registered for the 350-Control mix, while it reached 6.1 and 7.8 mm for the 350-Grey- 256 vol. 62 no. 2/2022 Effect of pigments on bond strength between coloured . . . y = 0.838x + 10.28 R² = 0.41 y = 0.86x + 14.89 R² = 0.67 10 14 18 22 26 3 4 5 6 7 8 9 10 11 12 U lt im at e bo nd s tr en gt h, M Pa Displacement at failure, mm Cement = 350 kg/m3 Cement = 450 kg/m3 Figure 11. Relationships between τu and δu for mixtures prepared with 350 or 450 kg/m3 cement. 4.5 % and 350-TiO2-4.5 %, respectively. In addition to the improved bond strength, this reflects that pig- ments confer higher ductility, which can be partic- ularly relevant in high-strength concrete reinforced members [33, 43, 44]. Figure 11 plots the relationships between τ and δ for concrete mixtures prepared with 350 or 450 kg/m3 cement. Clearly, mixtures exhibiting higher τu are characterized by increased displacements at failure. 5. Comparison with international bond models In order to ensure compliance of bond properties of the coloured concrete to international design code models, the τu values determined experimentally are compared with the design bond strengths (τmax) specified in CEB-FIP [35], ACI 318-19 [33], and European Code EC2 [34] models. The CEB-FIP (2010) considers that the stiffness of ascending τ vs. δ curves follows an exponential trend raised to a power of 0.4, until reaching τmax equal to 2 or 2.5 √ f ′c, depending on whether the concrete is confined or not. This can be expressed in Eqs. 1 and 2 as follows. CEB-FIP for unconfined concrete: τmax = 2 √ f ′c (1) CEB-FIP for confined concrete: τmax = 2.5 √ f ′c (2) In ultimate state conditions, the ACI 318-19 [33] considers that τmax can be calculated as: τmax = 10 √ f ′c ( Cb+Ktr db ) 4 × 9 Ψt Ψe Ψs λ (3) where Cb is the concrete cover and Ktr the transverse reinforcement index (note that the (Cb + Ktr )/db ratio is limited to 2.5). The Ψs, Ψe, Ψt, and λ factors refer to the bar-size, epoxy coated bars, bar location with respect to the upper surface, and lightweight concrete, respectively. In this study, Ψs is taken as 0.8 for bars No. 13, while Ψt, Ψe, and λ equal to 1. The τmax expression proposed by EC2 [34] for de- termining the ultimate bond stress is given as: τmax = 2.25 η1 η2 fctd (4) where η1 is a coefficient reflecting the bond quality to the embedded steel (taken as 1.0) and η2 is related to the bar diameter (taken as 1, given that db is less than 32 mm). The fctd = αct fctk,0.05/γc refers to concrete design tensile strength, where αct and γc refer to the long-term effects on tensile strength and partial safety factor, respectively (both taken as 1). The fctk,0.05 refers to the concrete characteristic axial tensile strength computed as 0.7 × 0.3 × f (2/3)ck , where fck is the 28-days compressive strength concrete cylinder. Table 4 summarizes the τmax values computed using the different codes as well as the resulting experimental-to-design bond strength ratios (i.e., τu/τmax). As shown in Figure 12, the τmax values fol- lowed an increasing trend with pigment additions. On average, the experimental τu values are 3.35- and 4.85- times higher than the ACI 318-19 and EC2 equations (Table 4), respectively; this reveals the conservative nature of such models for predicting the bond strength between steel bars and coloured concrete structures. Yet, the τu/τmax becomes pretty close or even lower than 1.0 when the CEB-FIP equations are used (i.e., Eqs. 1 and 2), reflecting the unconservative nature of such equations for assessing the bond strengths of coloured concrete. 6. Conclusions This paper is part of an investigation that aims at investigating the impact of pigments on the structural properties of reinforced coloured concrete members. The findings of this paper reveal that such additions have a rather beneficial effect on the concrete bond 257 J. J. Assaad, M. Matta, J. Saade Acta Polytechnica y = 0.375x + 13.18 R² = 0.71 y = 0.13x + 4.57 R² = 0.71 y = 0.117x + 3.03 R² = 0.71 2.5 3.5 4.5 5.5 12 13 14 15 16 0 1 2 3 4 5 𝜏m ax , M Pa (A CI a nd E C2 ) 𝜏m ax , M Pa (C EB -F IP ) Pigment concentration, % of cement CEB-FIP ACI EC2 Cement = 350 kg/m3 Figure 12. Relationships between pigment concentration and τmax computed by different codes for mixtures prepared with 350 kg/m3 cement. Mixture codification τmax computed by different codes Experimental-to-design bond ratio MPa (τu/τmax) 2 √ f ′c 2.5 √ f ′c ACI 318 EC2 2 √ f ′c 2.5 √ f ′c ACI 318 EC2 350-Control 10.3 12.9 4.5 3 1.1 0.88 2.53 3.84 350-Red-1.5 % 10.9 13.6 4.7 3.2 1.1 0.88 2.52 3.76 350-Red-3 % 11.7 14.6 5.1 3.5 1.54 1.23 3.56 5.19 350-Red-4.5 % 11.8 14.8 5.1 3.5 1.5 1.2 3.47 5.03 350-Grey-3 % 10.9 13.6 4.7 3.2 1.17 0.93 2.69 4.01 350-Grey-4.5 % 11.7 14.6 5.1 3.5 1.2 0.96 2.77 4.03 350-TiO2-1.5 % 11.6 14.5 5 3.4 1.49 1.19 3.43 5.02 350-TiO2-4.5 % 12.3 15.4 5.3 3.7 1.69 1.35 3.88 5.57 350-CBlack-1.5 % 11 13.7 4.8 3.2 1.4 1.12 3.22 4.78 350-CBlack-4.5 % 11.8 14.8 5.1 3.5 1.51 1.21 3.48 5.04 450-Control 11.7 14.6 5.1 3.5 1.62 1.29 3.72 5.42 450-Red-3 % 12.5 15.6 5.4 3.8 1.88 1.5 4.32 6.16 450-Grey-3 % 13 16.3 5.6 4 1.52 1.22 3.5 4.93 450-TiO2-3 % 13.3 16.7 5.8 4.2 1.86 1.49 4.29 5.98 450-CBlack-3 % 12.9 16.1 5.6 4 1.7 1.36 3.92 5.53 Average = 1.45 1.16 3.35 4.85 St. Deviation = 0.26 0.2 0.59 0.77 Table 4. Experimental-to-design bond strengths computed by different codes. 258 vol. 62 no. 2/2022 Effect of pigments on bond strength between coloured . . . properties to embedded steel bars, which could practi- cally be assuring to consultants and architects in the concrete building industry. Based on the foregoing, the following conclusions can be warranted: • Mixtures containing TiO2 exhibited the lowest ∆(E) values, reflecting relatively limited variations with respect to the control mix. The incorporation of gradually increased red or grey IO pigments led to an increased ∆(E), while the CB-modified mixtures exhibited the highest ∆(E) values. • The steady ∆(E) increase with pigment additions was attributed to the relatively reduced cement volume and beige-like colour of natural sand, thus affecting the pigment tinting strength and reducing the tendency towards colour saturation. • Regardless of the colour, mixtures incorporating increased pigment additions exhibited higher f ′c and f t responses. This was directly associated to the micro-filler effect and enhanced packing density that lead to denser microstructure. The IO and CB pigments are inert materials (i.e., do not react with water) that fill the interspaces and capillary pores in cementitious systems, leading to improved strength properties. • The highest increase in strength was recorded for mixtures prepared with TiO2 additions. Besides the micro-filler effect, the increase in strength was ascribed to the formation of nucleation sites that promote hydration reactions and reduce the porosity of the hardened matrix. • Just like the f ′c and f t responses, τu gradually increased with such additions, which practically reveals their beneficial role for improving the devel- opment and transfer of bond stresses in reinforced concrete members. The highest increase was noticed for the concrete mixture containing TiO2 additions, given the micro-filler effect and formation of addi- tional hydrating gels that strengthen the interfacial concrete-steel transition zone. • The increase in τu due to pigment additions was accompanied with an increase in the maximum slip that occurs at failure. This reflects that pigments confer higher ductility, which can be particularly relevant in high-strength concrete reinforced mem- bers. • On average, the experimental τu values are 3.35- and 4.85-times higher than the ACI 318-19 and EC2 equations, respectively. Yet, the τu becomes pretty close to τmax computed by the CEB-FIP equations, reflecting the unconservative nature of such equa- tions to predict the bond strengths of coloured con- crete mixtures. Acknowledgements The authors wish to acknowledge the support provided by Sodamco-Weber, Lebanon. References [1] P. Bartos. Fresh concrete properties and test. Elsevier, Amsterdam, 1992. [2] L. Popelová. The symbolic-aesthetic dimension of industrial architecture as a method of classification and evaluation: the example of bridge structures in the Czech republic. Acta Polytechnica 47(1):23–31, 2007. https://doi.org/10.14311/912. [3] ASTM C979. Standard specification for pigments for integrally colored concrete. Annual book of ASTM standards. Farmington Hills, USA, 4(2), 2007. [4] V. Hospodarova, J. Junak, N. Stevulova. Color pigments in concrete and their properties. Pollack Periodica 10(3):143–151, 2015. https://doi.org/10.1556/606.2015.10.3.15. [5] S. R. Naganna, H. A. Ibrahim, S. P. Yap, et al. Insights into the multifaceted applications of architectural concrete: A state-of-the-art review. Arabian Journal for Science and Engineering 46:4213–4223, 2021. https://doi.org/10.1007/s13369-020-05033-0. [6] Y.-M. Gao, H.-S. Shim, R. H. Hurt, et al. Effects of carbon on air entrainment in fly ash concrete: The role of soot and carbon black. Energy Fuels 11(2):457–462, 1997. https://doi.org/10.1021/ef960113x. [7] K. Loh, C. C. Gaylarde, M. A. Shirakawa. Photocatalytic activity of ZnO and TiO2 ‘nanoparticles’ for use in cement mixes. Construction and Building Materials 167:853–859, 2018. https: //doi.org/10.1016/j.conbuildmat.2018.02.103. [8] S. S. Lucas, V. M. Ferreira, J. L. Barroso de Aguiar. Incorporation of titanium dioxide nanoparticles in mortars – Influence of microstructure in the hardened state properties and photocatalytic activity. Cement and Concrete Research 43:112–120, 2013. https://doi.org/10.1016/j.cemconres.2012.09.007. [9] H.-S. Jang, H.-S. Kang, S.-Y. So. Color expression characteristics and physical properties of colored mortar using ground granulated blast furnace slag and White Portland cement. KSCE Journal of Civil Engineering 18(4):1125–1132, 2014. https://doi.org/10.1007/s12205-014-0452-z. [10] R. Alves, P. Faria, A. Brás. Brita Lavada – An eco-efficient decorative mortar from Madeira Island. Journal of Building Engineering 24:100756, 2019. https://doi.org/10.1016/j.jobe.2019.100756. [11] J. J. Assaad, D. Nasr, S. Chwaifaty, T. Tawk. Parametric study on polymer-modified pigmented cementitious overlays for colored applications. Journal of Building Engineering 27:101009, 2020. https://doi.org/10.1016/j.jobe.2019.101009. [12] J. J. Assaad. Disposing waste latex paints in cement- based materials – effect on flow and rheological properties. Journal of Building Engineering 6:75–85, 2016. https://doi.org/10.1016/j.jobe.2016.02.009. [13] H.-S. Lee, J.-Y. Lee, M.-Y. Yu. Influence of inorganic pigments on the fluidity of cement mortars. Cement and Concrete Research 35(4):703–710, 2005. https://doi.org/10.1016/j.cemconres.2004.06.010. 259 https://doi.org/10.14311/912 https://doi.org/10.1556/606.2015.10.3.15 https://doi.org/10.1007/s13369-020-05033-0 https://doi.org/10.1021/ef960113x https://doi.org/10.1016/j.conbuildmat.2018.02.103 https://doi.org/10.1016/j.conbuildmat.2018.02.103 https://doi.org/10.1016/j.cemconres.2012.09.007 https://doi.org/10.1007/s12205-014-0452-z https://doi.org/10.1016/j.jobe.2019.100756 https://doi.org/10.1016/j.jobe.2019.101009 https://doi.org/10.1016/j.jobe.2016.02.009 https://doi.org/10.1016/j.cemconres.2004.06.010 J. J. Assaad, M. Matta, J. Saade Acta Polytechnica [14] A. Woods, J. Y. Lee, L. J. Struble. Effect of material parameters on color of cementitious pastes. Journal of ASTM International 4(8):1–18, 2007. https://doi.org/10.1520/JAI100783. [15] T. Meng, Y. Yu, X. Qian, et al. Effect of nano-TiO2 on the mechanical properties of cement mortar. Construction and Building Materials 29:241–245, 2012. https: //doi.org/10.1016/j.conbuildmat.2011.10.047. [16] A. Mohammed, N. T. K. Al-Saadi, J. Sanjayan. Inclusion of graphene oxide in cementitious composites: state-of-the-art review. Australian Journal of Civil Engineering 16(2):81–95, 2018. https://doi.org/10.1080/14488353.2018.1450699. [17] A. López, J. M. Tobes, G. Giaccio, R. Zerbino. Advantages of mortar-based design for coloured self-compacting concrete. Cement and Concrete Composites 31(10):754–761, 2009. https: //doi.org/10.1016/j.cemconcomp.2009.07.005. [18] L. Hatami, M. Jamshidi. Application of SBR- included pre-milled colored paste as a new approach for coloring self-consolidating mortars (SCMs). Cement and Concrete Composites 65:110–117, 2016. https: //doi.org/10.1016/j.cemconcomp.2015.10.015. [19] P. Weber, E. Imhof, B. Olhaut. Coloring pigments in concrete: Remedies for fluctuations in raw materials and concrete recipes. Tech. Report, Harold Scholz & Co GmbH, 2009. [20] J. J. Assaad, M. Vachon. Valorizing the use of recycled fine aggregates in masonry cement production. Construction and Building Materials 310:125263, 2021. https: //doi.org/10.1016/j.conbuildmat.2021.125263. [21] M. J. Positieri, P. Helene. Physicomechanical properties and durability of structural colored concrete. In ACI Symposium Publication, vol. 253, pp. 183–200. 2013. https://doi.org/10.14359/20175. [22] S. A. Yıldızel, G. Kaplan, A. U. Öztürk. Cost optimization of mortars containing different pigments and their freeze-thaw resistance properties. Advances in Materials Science and Engineering 2016:5346213, 2016. https://doi.org/10.1155/2016/5346213. [23] S. Masadeh. The effect of added carbon black to concrete mix on corrosion of steel in concrete. Journal of Minerals and Materials Characterization and Engineering 3(4):271–276, 2015. https://doi.org/10.4236/jmmce.2015.34029. [24] D. Inoue, H. Sakurai, M. Wake, T. Ikeshima. Carbon black for coloring cement and method for coloring molded cement article. European patent, WO 01/046322, 10 p, 1999. [25] J. Topič, Z. Prošek, K. Indrová, et al. Effect of pva modification on properties of cement composites. Acta Polytechnica 55(1):64–75, 2015. https://doi.org/10.14311/AP.2015.55.0064. [26] A. Nazari, S. Riahi. The effect of TiO2 nanoparticles on water permeability and thermal and mechanical properties of high strength self-compacting concrete. Materials Science and Engineering: A 528(2):756–763, 2010. https://doi.org/10.1016/j.msea.2010.09.074. [27] J. Chen, S.-C. Kou, C.-S. Poon. Hydration and properties of nano-TiO2 blended cement composites. Cement and Concrete Composites 34(5):642–649, 2012. https: //doi.org/10.1016/j.cemconcomp.2012.02.009. [28] R. Zhang, X. Cheng, P. Hou, Z. Ye. Influences of nano-TiO2 on the properties of cement-based materials: Hydration and drying shrinkage. Construction and Building Materials 81:35–41, 2015. https: //doi.org/10.1016/j.conbuildmat.2015.02.003. [29] A. Folli, C. Pade, T. B. Hansen, et al. TiO2 photocatalysis in cementitious systems: Insights into self-cleaning and depollution chemistry. Cement and Concrete Research 42(3):539–548, 2012. https://doi.org/10.1016/j.cemconres.2011.12.001. [30] M. Konrad, R. Chudoba. The influence of disorder in multifilament yarns on the bond performance in textile reinforced concrete. Acta Polytechnica 44(5-6):186–193, 2004. https://doi.org/10.14311/654. [31] J. J. Assaad, P. Matar, A. Gergess. Effect of quality of recycled aggregates on bond strength between concrete and embedded steel reinforcement. Journal of Sustainable Cement-Based Materials 9(2):94–111, 2020. https://doi.org/10.1080/21650373.2019.1692315. [32] ACI 408R-03. Bond and development of straight reinforcing bars in tension, 2003. [33] ACI 318-19. Building code requirements for reinforced concrete, 2019. [34] EN 1992-1-1. Eurocode 2: design of concrete structures – part 1-1: general rules and rules for buildings, 2004. [35] FIB (International Federation for Structural Concrete). Model Code for Concrete Structures. Ernst & Sohn, Berlin, 2013. [36] ASTM C642-13. Standard test method for density, absorption, and voids in hardened concrete. Annual book of ASTM standards. West Conshohocken, PA, 2013, USA. [37] ASTM C39/C39 M-05. Standard test method for compressive strength of cylindrical concrete specimens. Annual book of ASTM standards. West Conshohocken, PA, 2005, USA. [38] ASTM C496/C496 M-04. Standard test method for splitting tensile strength of cylindrical concrete specimens. Annual book of ASTM standards. West Conshohocken, PA, 2004, USA. [39] ASTM C 597-16. Standard test method for pulse velocity through concrete. Annual book of ASTM standards. West Conshohocken, PA, 2016, USA. [40] G. Teichmann. The use of colorimetric methods in the concrete industry. Betonwerk Fertigteil-Technik 11:58–73, 1990. [41] RILEM/CEB/FIB. Bond test for reinforcing steel: 2, pullout test. Materials and Structures 3:175–178, 1970. [42] J. Němeček, P. Padevět, Z. Bittnar. Effect of stirrups on behavior of normal and high strength concrete columns. Acta Polytechnica 44(5-6):158–164, 2004. https://doi.org/10.14311/648. 260 https://doi.org/10.1520/JAI100783 https://doi.org/10.1016/j.conbuildmat.2011.10.047 https://doi.org/10.1016/j.conbuildmat.2011.10.047 https://doi.org/10.1080/14488353.2018.1450699 https://doi.org/10.1016/j.cemconcomp.2009.07.005 https://doi.org/10.1016/j.cemconcomp.2009.07.005 https://doi.org/10.1016/j.cemconcomp.2015.10.015 https://doi.org/10.1016/j.cemconcomp.2015.10.015 https://doi.org/10.1016/j.conbuildmat.2021.125263 https://doi.org/10.1016/j.conbuildmat.2021.125263 https://doi.org/10.14359/20175 https://doi.org/10.1155/2016/5346213 https://doi.org/10.4236/jmmce.2015.34029 https://doi.org/10.14311/AP.2015.55.0064 https://doi.org/10.1016/j.msea.2010.09.074 https://doi.org/10.1016/j.cemconcomp.2012.02.009 https://doi.org/10.1016/j.cemconcomp.2012.02.009 https://doi.org/10.1016/j.conbuildmat.2015.02.003 https://doi.org/10.1016/j.conbuildmat.2015.02.003 https://doi.org/10.1016/j.cemconres.2011.12.001 https://doi.org/10.14311/654 https://doi.org/10.1080/21650373.2019.1692315 https://doi.org/10.14311/648 vol. 62 no. 2/2022 Effect of pigments on bond strength between coloured . . . [43] A. AlArab, B. Hamad, J. J. Assaad. Strength and durability of concrete containing ceramic waste powder and blast furnace slag. Journal of Materials in Civil Engineering 34(1):04021392, 2022. https: //doi.org/10.1061/(ASCE)MT.1943-5533.0004031. [44] J. Machovec, P. Reiterman. Influence of aggressive environment on the tensile properties of textile reinforced concrete. Acta Polytechnica 58(4):245–252, 2018. https://doi.org/10.14311/AP.2018.58.0245. 261 https://doi.org/10.1061/(ASCE)MT.1943-5533.0004031 https://doi.org/10.1061/(ASCE)MT.1943-5533.0004031 https://doi.org/10.14311/AP.2018.58.0245 Acta Polytechnica 62(2):248–261, 2022 1 Introduction 2 Context and paper objectives 3 Experimental program 3.1 Materials 3.2 Mixture proportions 3.3 Testing procedures 3.3.1 Fresh and hardened properties 3.3.2 Colourimetry 3.3.3 Bond to steel reinforcement 4 Test results and discussion 4.1 HRWR demand 4.2 Colourimetry 4.3 Hardened properties 4.4 Bond stress-slip behavior 5 Comparison with international bond models 6 Conclusions Acknowledgements References