Acta Polytechnica CTU Proceedings https://doi.org/10.14311/APP.2024.47.0058 Acta Polytechnica CTU Proceedings 47:58–62, 2024 © 2024 The Author(s). Licensed under a CC-BY 4.0 licence Published by the Czech Technical University in Prague PROCESSING AND RECYCLING OF AGGREGATE RESIDUES AFTER ORE EXTRACTION FOR STABILIZATION OF MINED AREAS Andrea Jančíková∗, Karel Dvořák, Simona Ravaszová Brno University of Technology, Faculty of Civil Engineering, Veveří 331/95, 602 00 Brno, Czech Republic ∗ corresponding author: andrea.jencikova@vut.cz Abstract. The article focuses on the treatment and recycling of aggregate. It also addresses the issue of treatments effects on mine tailings, fly ash and acid mine water on the measured parameters of concrete with load-bearing and backfilling paste with non-load-bearing function. Four different mixes were developed, and standard tests were performed on them. These mixtures were made with different types of mine tailing’s fillers with varying degrees of treatment. Mineralogical and chemical tests were carried out on the treated aggregates, with sieve analysis and their subsequent adjustment for suitable aggregate gradation curve in concrete. Strength and volumetric weight tests were carried out on hardened samples at 28, 56 and 90 days. The results of the determined functional specimens showed that it is possible to develop an almost completely waste-free technology using recycled aggregate and fly ash from the ore mining and energy industries and its subsequent processing and use for backfilling of mine deposits with load bearing and non-load bearing function concrete. Keywords: Mined residues, mine tailings, mechanical properties, filling and static requirements. 1. Introduction The mining industry is divided into two major cat- egories, metallic and non-metallic, based on the ore extracted. Both industries lead to the generation of large quantities of solid industrial wastes from mine expansions [1]. A large amount of sub waste gen- erated from the processing of metallic ores in the separation of valuable minerals, this waste is called tailings [2, 3]. The generation of large quantities of tailings adversely affects the environment, including air, water, and soil [4, 5]. Consequently, a large area of surface land is required for the appropriate storage and management of this waste. An effective solu- tion is the underground disposal of these industrial wastes (tailings, fly ash, mud, etc.) generated from mining and related activities in the form of mine back- fill [6–8]. The spaces created after ore extraction in underground mines can be filled with a specific waste material referred to as backfill mix of cement and mined aggregate, fly ash, in a consistency that can be well pumped and transported. Backfill material can be divided into two major cat- egories, the first being unconsolidated backfill without static function and the second being backfill with cement and static function [4–6]. Unconsolidated backfill, waste is added without any binder. While in cemented backfill, a hydraulic binder is added, usually this binder is Portland cemen, which is added to the solid waste material to provide a background for the mechanical properties of the paste or concrete [7, 8]. One form of cemented backfill used in underground mines is a paste with well-defined mechanical proper- ties [3–7]. Mine fill mixtures should be homogeneous, mobile, suitable for transport by pumping over distances of hundreds of meters, and workable for a minimum of 120 minutes. After curing, they should ideally reach a strength of at least 4 MPa after 90 days; however, a strength of about half 0.1 MPa may be acceptable in conditions without static function. The aim is to completely minimize the binder component, which should only have the function of ensuring the cohesion of the cured composite. One way to achieve this is use of fluidized power plant fly ash, which is not used at all to produce conventional concretes. In this case, even total replacements of conventional cements as binders are realistic options. Fluidized fly ash from “Ledvice” was used as a binder for number of samples in this article. Backfill mixture for stabilization of old mining sites. The important requirement here is not ulti- mate strength but low hydration heat development and workability. The residue after separation of heavy and light recoverable components from the “Zlaté Hory” landfill was used to create the mixture without static function. The residue after separation of heavy and light recoverable components from the “Cínovec” deposit was used to form the second mixture with static function. An important requirement is ultimate strength and low hydration heat development. The implementation of the achieved theoretical ba- sis will be carried out according to the developed complex design of the treatment plant technology for the “Zlaté Hory” underground mine with obtaining the residual material from the treatment in a fur- ther usable form. The results are summarized in the TREND FW project report 01010061-1-2022. 58 https://doi.org/10.14311/APP.2024.47.0058 https://creativecommons.org/licenses/by/4.0/ https://www.cvut.cz/en vol. 47/2024 Processing of aggregate residues for stabilization of mined areas Label CEM I 42,5 R Fluidized Fly Aggregates Water Plasticizing additive Ash Ash “Cínovec” [l] [l] 1 “Cínovec” C 25/30 300 100 200 1 260 400 10 2 “Cínovec” filling 50 33 66 1 720 480 3 Table 1. The main concrete and filling recipe in [kg]. Label CEM I 42,5 R Fluidized Fly Aggregates Water Plasticizing additive Ash Ash “Cínovec” [l] [l] 3 ZH CEM 50 33 66 1 720 460 3 Table 2. Composition of mixtures with “Zlaté Hory” aggregate without static function in [kg]. Label Modified fluidized ash Aggregates Water Plasticizing additive (SOR) “Zlaté Hory” [l] [l] 4 ZH SOR 150 1 720 460 3 Table 3. Composition of mixtures with modified fluidized ash without static function in [kg]. 2. Material and methods Based on the results of the laboratory tests, a for- mulation for a foundation with a static function that uses aggregate from mine “Cínovec” was selected for validation in a mining environment. A mixture of fluidized and conventional fly ash supplemented with Portland cement was selected as the binder. At the same time, a mixture based on aggregate from mine “Zlaté Hory” with a filling function without static requirements was also proposed. The main concrete recipe in [kg] is given in Table 1 and the recipes of the base mortar cast mixes in Tables 2 and 3. For each sample, four samples of 20 liters of mixture were produced. At the same time. control cubes were formed for storage under laboratory conditions. The sample storage conditions were set to a stable tem- perature of 7 °C ± 1 °C. Strength checking and mine water sampling for pH measurements were carried out 90 and 180 days after mixing also with Schmidt reflec- tion hardness test. The resulting pH of the sampled mine water, as determined by a digital pH meter, was 4.8. The water was therefore slightly acidic. In the case of structural concrete, the following laboratory tests were carried out: • concrete mix design, • determination of basic technological tests on fresh and hardened mixes (water coefficient, settlement, fresh concrete temperature, bulk density, flexural and compressive tensile strength. In the case of the development of aggregate mixture cement cemented, the following tests were carried out: • Design of the gradation curve of the resulting ag- gregate mixture, • design of the composition of the mixture, • Proctor test, • determination of basic technological tests – bulk density, compressive strength. The following laboratory tests were carried out for the aggregates from “Cínovec” within this sub-stage: • sieve analysis of aggregate with percentage of fine particles, • design of the composition of cast mixtures, subse- quent testing of the resulting recipes, • determination of basic technological tests on fresh and hardened mixtures (water coefficient, spillage, bulk density, flexural and compressive tensile strength) The XRD analysis on samples was performed using a Panalytical Empyrean diffractometer. The reflec- tion Bragg-Brentano para focusing geometry device is equipped with a Cu anode (λ = 1.54184 Å) and pro- gramable divergence slits a PIXcel3D detector with 255 active channels. The X-ray generator settings were 45 kV and 40 mA. The measured range was 5– 80° with a step size of 0.013° and 38 s per step. Each sample was measured four times, and the scans were next simply summed. The total measurement time for each sample was 60 min. The Panalytical HighScore 3 plus software was used to identify the individual phases. 3. Results and discussion There is no relevant standard available for foundation materials, however, the concrete standard ČSN EN 206 can be used and to verify the parameters of the sam- ples, the following tests were carried out: To perform the strength tests, the recipes of mortar mixes for individual types of fillers and mining wastewater from the extraction of tailings were designed and compared with a reference recipe prepared in proportions cor- responding to the standard mortar according to the 59 A. Jančíková, K. Dvořák, S. Ravaszová Acta Polytechnica CTU Proceedings Label 1. “Cínovec” C 25/30 2. “Cínovec” filling 3. ZH CEM 4. ZH SOR Consistency by spilling [cm] [days] 24.5 25.4 26 26 Volumetric mass [kg m−3] 1 830 1 360 11 390 11 390 Compressive cubic strength [MPa] 28 18.7 0.3 0.1 0.1 Schmidt reflection [-]/ strength [MPa] Not determined Not determined Not determined Not determined Volumetric mass [kg m−3] 1 800 1 350 1 380 1 380 Compressive cubic strength [MPa] 90 21.1 0.4 0.1 0.1 Schmidt reflection [-]/ strength [MPa] 22/ 15 ± 4 Indefinable Indefinable Indefinable Volumetric mass [kg m−3] 1 780 1 330 1 360 1 360 Compressive cubic strength [MPa] 180 21.9 0.7 0.3 0.3 Schmidt reflection [-]/ strength [MPa] 26 / 19 ± 4 17 / <10 MPa 16 / <10 MPa 16 / <10 MPa Table 4. Properties of concrete and mortar cast mixes. Label Properties Unit Measured Value Aggregate “Cínovec” 0/2 mm Volume weight of aggregate grains [Mg m−3] 2.69 Volumetric weight of grains after drying in the oven [Mg m−3] 2.65 Volumetric weight of water-saturated and surface-dried grains [Mg m−3] 2.66 Absorption after immersion in water for 24 hours WA24 [%] 0.47 Table 5. Determination of bulk density and water absorption of aggregates “Cínovec”. fresh mortar consistency test using a shaking table ac- cording to ČSN EN 1015-3. Volumetric weight of fresh mortar according to ČSN EN 1015-10 (722400), and Flexural tensile strength and compressive strength at curing times of 28, 90 and 180 days according to ČSN EN 1015-11 (722400), determination of flexural and compressive strength of hardened mortars. Prop- erties of concrete and mortar cast mixes made of aggregates from “Cínovec” and “Zlaté Hory” are in the Table 4. Due to the requirement for flowability of the mixes, the consistency of fresh mortar was chosen to have more than 240 mm spillage. To achieve a 240 mm spillage, more water and had to be added to the mixes due to wetting of the separated aggregate and more fine filler to ensure the correct consistency of the mixture. A sieve analysis was carried out on the tin aggregate with results at Figure 1. To de- termine the volumetric weights and absorption rates according to the relevant standard. ČSN EN 933-1: Testing of geometric properties of aggregates – Part 1: Determination of grain size – Sieve analysis. And ČSN EN 1097-6: Testing of mechanical and physical properties of aggregates – Part 6: Determination of bulk density of grains and water absorption, Chapter 9 with results in the Table 5. Mineralogical analysis shown in Figure 2 shows that the proportion of heavy components (pyrite and chalcopyrite) after separation is low. The gravity separation of the heavy component was quite effective. The light component: concentrate separation ratio was determined after processing of 1 000 kg. The deposit was composed of 56 % quartz, 16.5 % muscovite, 14.6 % albite and 12.6 % chamosite. A chemical analysis was also performed on the sample, which can be found in Table 6. Figure 1. Result of sieve analysis of aggregate from mine “Cínovec” fraction 0/2 mm. Loss on drying (105 °C) % 0.27 Sulphides mg/kg dry 23.3 Calcium oxide % dry 3.53 Magnesium oxide % dry 2.26 Potassium oxide % dry 2.13 Aluminium oxide % dry 10.5 Silicon dioxide % dry 67.8 Iron oxide % dry 7.03 Sodium oxide % dry 0.937 Zinc % dry 0.206 Zinc oxide % dry 0.257 Table 6. Results of the chemical analysis of the “Zlaté Hory” landfill. Despite the low strength in backfill mixes without static function, the amount and type of binder was chosen in both cases to be sufficient to ensure the 60 vol. 47/2024 Processing of aggregate residues for stabilization of mined areas Figure 2. Mineralogical analysis from mine “Zlaté Hory”. Properties ZH SOR Declared property of the backfill mixture “Cínovec” C 25/30 Declared property of the concrete mix Spillage ČSN EN 1015-3 250/255 mm > 240 mm 240/245 mm > 230 mm Bulk mass ČSN EN 12390-7 - 28 days 1 390 kg m−3 1 390 ± 100 kg m−3 1 840 kg m−3 1 850 ± 100 kg m−3 - 60 days 1 380 kg m−3 1 380 ± 100 kg m−3 1 800 kg m−3 1 800 ± 100 kg m−3 - 90 days 1 360 kg m−3 1 360 ± 100 kg m−3 1 780 kg m−3 1 800 ± 100 kg m−3 Compressive strength ac- cording to ČSN EN 12390-3 - 28 days 0.1 MPa ≥ 0.1 MPa 19.2 MPa ≥ 15 MPa - 60 days 0.1 MPa ≥ 0.1 MPa 20.9 MPa ≥ 18 MPa - 90 days 0.3 MPa ≥ 0.3 MPa 21.4 MPa ≥ 20 MPa Hydration temperature ac- cording to ČSN EN 196-9 Max 21.8 ° C at 152 minutes ≤ 25 ° C untill 250 min- utes Max 22.3 ° C at 44 hours 49 minutes ≤ 25 ° C until 50 hours Table 7. Results of monitoring, development of the strengths and condition of the samples. compactness of the samples. Both binders, due to their chemical and mineralogical nature, should not suffer chemical damage from the acid mine water which was used for the samples. Monitoring of the development of the strengths and condition of the samples with test results with comparing to the declared properties of backfilling mixtures with and without static function are shown in the Table 7. All tests and trials were carried out according to the following list of technical regulations and standards. • ČSN EN 206+A2 Concrete-Specifications, proper- ties, production, and compliance • ČSN EN 12390-3: Testing of hardened concrete – Part 3: Compressive strength of test bodies • ČSN EN 12390-7: Testing of hardened concrete – Part 7: Bulk density • ČSN EN 933-1: Testing of geometric properties of aggregates - Part 1: Determination of gradation – Sieve analysis • ČSN EN 1097-6: Testing of mechanical and physical properties of aggregates – Part 6: Determination of bulk density of grains and water absorption, Chap- ter 9 • ČSN EN 1015-3: Test methods for mortars for ma- sonry – Part 3: Determination of consistency of fresh mortar (using a shaking table) • ČSN EN 196-9: Test methods for cement – Part 9: Determination of heat of hydration – Semi adiabatic method 4. Conclusion Aggregate samples were taken and analysed from exist- ing deposits and stockpiles at the “Cínovec and Zlaté Hory” locations. Samples simulating cleaned mining residues were prepared by gravity separation methods. Samples of stockpile mixtures for the foundation of areas with requirements for static and non-static func- tion during active mining were developed, prepared, and tested. In doing so, a nearly waste-free technol- ogy was developed to produce stockpile mixes while maximizing the use of existing tailings. Simulations of tailings purification and tailings preparation with the constituents of interest removed were performed. It was demonstrated for the windrowed samples of land- fill mixtures for the foundation of areas with static 61 A. Jančíková, K. Dvořák, S. Ravaszová Acta Polytechnica CTU Proceedings and non-static function requirements that: • According to the measured results, it can be con- cluded that it is possible to prepare relatively well- flowing mixtures with very high-water coefficients. • It is possible to achieve good strength results with extremely low dosage of binder based on fly ash mixtures under placement conditions without static function. • Modified and recycled aggregates free of heavy pyrite components after ore extraction are very suitable for use in ash fly ash mixtures. Acknowledgements We acknowledge the financial support to project (FW01010061) TACR, “Comprehensive technology of ore residue processing for the stabilization of mined out areas and for the underlying layers of linear structures” and project (FAST-S-23-8246) “Study of the formation and stability of various tricalcium aluminate polymorphs”. References [1] S. Lamani, M. Aruna, H. Vardhan. Utilisation of mine waste in the construction industry - a critical review. International journal of Earth sciences and engineering 9:182–195, 2016. ISSN 0974-5904. [2] H. E. Jamieson, S. R. Walker, M. B. Parsons. Mineralogical characterization of mine waste. Applied Geochemistry 57:85–105, 2015. https://doi.org/10.1016/j.apgeochem.2014.12.014 [3] M. B. J. Lindsay, M. C. Moncur, J. G. Bain, et al. Geochemical and mineralogical aspects of sulfide mine tailings. Applied Geochemistry 57:157–177, 2015. https://doi.org/10.1016/j.apgeochem.2015.01.009 [4] N. Sivakugan, K. J. Rankine, K. S. Rankine. Study of drainage through hydraulic fill stopes using method of fragments. Geotechnical & Geological Engineering 24(1):79–89, 2006. https://doi.org/10.1007/s10706-004-1949-x [5] T. Belem, M. Benzaazoua. Design and application of underground mine paste backfill technology. Geotechnical & Geological Engineering 26(2):147–174, 2008. https://doi.org/10.1007/s10706-007-9154-3 [6] B. Ercikdi, F. Cihangir, A. Kesimal, et al. Utilization of industrial waste products as pozzolanic material in cemented paste backfill of high sulphide mill tailings. Journal of Hazardous Materials 168(2-3):848–856, 2009. https://doi.org/10.1016/j.jhazmat.2009.02.100 [7] K. Pal, H. Vardhan, M. Aruna. Investigation of contaminant transport in groundwater from the tailings pond of uranium mine: a case study. International Journal of Mining and Mineral Engineering (IJMME) 2(4):290–309, 2010. https://doi.org/10.1504/IJMME.2010.039039 [8] M. Keppert, V. Davidová, B. Doušová, et al. Recycling of fresh concrete slurry waste as supplementary cementing material: Characterization, application and leaching of selected elements. Construction and Building Materials 300:124061, 2021. https: //doi.org/10.1016/j.conbuildmat.2021.124061 62 https://doi.org/10.1016/j.apgeochem.2014.12.014 https://doi.org/10.1016/j.apgeochem.2015.01.009 https://doi.org/10.1007/s10706-004-1949-x https://doi.org/10.1007/s10706-007-9154-3 https://doi.org/10.1016/j.jhazmat.2009.02.100 https://doi.org/10.1504/IJMME.2010.039039 https://doi.org/10.1016/j.conbuildmat.2021.124061 https://doi.org/10.1016/j.conbuildmat.2021.124061 Acta Polytechnica CTU Proceedings 47:58–62, 2024 1 Introduction 2 Material and methods 3 Results and discussion 4 Conclusion Acknowledgements References