(Microsoft Word - \317 \332\341\355 \346\315\344\307\34422-29) Al-Khwarizmi Engineering Journal Al-Khwarizmi Engineering Journal,Vol. 13, No. 4, P.P. 22- 29 (2017) Optimization of Material Removal Rate and Temperature in Magnetic Abrasive Finishing Process for Stainless Steel 304 Ali H. Kadhum* Hanan H. Murad** *, ** Department of Automated Manufacturing Engineering / Al-Khwarizmi College of Engineering / Baghdad University *Email: kadhumali59@yahoo.com **Email: hananhasan729@yahoo.com (Received 3 January 2017; accepted 20 June 2017) https://doi.org/10.22153/kej.2017.06.001 Abstract The effect of the magnetic abrasive finishing (MAF) method on the temperature rise (TR), and material removal rate (MRR) has been investigated in this paper. Sixteen runs were to determine the optimum temperature in the contact area (between the abrasive powder and surface of workpiece) and the MRR according to Taguchi orthogonal array (OA). Four variable technological parameters (cutting speed, finishing time, working gap, and the current in the inductor) with four levels for each parameter were used, the matrix is known as a L16 (44) OA. The signal to noise ratio (S/N) ratio and analysis of the variance (ANOVA) were utilized to analyze the results using (MINITAB17) to find the optimum condition and identify the significant parameters affecting on the TR., and MRR of the steel 304. IR camera was used to measure the experimental temperature. The results showed that the optimum temperature in contact area of workpiece is 70.7 °C. Keyword: IR camera ,Magnetic abrasive finshing , Temprature rise. 1. Introduction Magnetic Abrasive Finishing (MAF) process is the one in which material is removed in such a way that the surface is finished. The most uses of MAF are manufacturing semiconductors, medical instruments, atomic energy parts and aerospace components that have a very precise surface roughness [1]. One of the main advantages of MAF operation as compared with traditional finishing operations is the minimizing of the possibility of micro cracks on the surface of the workpiece, because the cutting force is primarily controlled by the magnetic field [2]. The principle work of magnetic abrasive finishing involves filling the working gap between the workpiece and the pole with the magnetic abrasive powder, the current or the magnetic flux density is passed through the coil to produce the magnetic field, and the pole is rotating with the powder along the work piece. The magnetic field provides the abrasive powder with the energy, this energy makes the magnetic abrasive powder as a cutting tool for treating the surface, and the rotation of the pole makes the friction between the workpiece and the magnetic abrasive powder which the material can be removed from the workpiece [3-4]. MAF was inventoried by Harry P. Coat in 1938’s in U.S.A, the first patent was given in1940’s, the research began in the universities of Germany, and Soviet union in 1960’s and particularly appeared during 1980’s, 1990’s [5]. Many of the parameters, like number of the turns, and magnetic flux density affect on the materials removal rate [6]. Girma B. et al. [7] explored the MAF process by analyzing the materials removal rate and the surface roughness using response surface method in plane surfaces. It was concluded that the current, ratio size and the magnetic abrasive powder grain size are more Ali H. Kadhum Al-Khwarizmi Engineering Journal, Vol. 13, No. 4, P.P. 22- 29 (2017) 23 effective on the material removal rate. The MAF process, the thermal effect of electromagnetic flux in the coil produced from current and from the friction between the magnetic abrasive powders with workpiece. Vivek Mishra et al. [8] used the finite element method in the magnetic abrasive finishing process. The friction between the magnetic abrasive particles and the surface of the workpiece leads to frictional heating in the working zone of the surface, based on the ANSYS software to simulate the temperature and the magnetic field. The factors used were the magnetic flux density (0.233T) at (0.91A), it was found that the temperature was between (34– 51◦C). Chandan Gaur [9] applied the voltage and the working gap as parameters, and is used MINITAB17 to obtain regression model to analyze the data, the result showed that the temperature increased with increasing the voltage and decreasing the machining gap. The maximum temperature during this process was 94.7 ◦C. It was concluded that the effect of the temperature during the MAF process is very small on the quality of the surface roughness, and there is no any conclusion on the various parameters. Singh et al. [10] according to the Taguchi’s design of experiments planned, used four parameters (working gap, voltage, and mesh number size of the abrasive and rotational speed). The result showed that the working gap and the voltage are more effective on the change in the surface roughness (ΔRa). The objective of this work is: 1-Optimization the MAF parameters through the materials removal rate, and determining the optimum temperature according to optimum MRR of stainless steel 304 2- Studying the influence of MAF parameters (cutting speed, finishing time, working gap, and current in the coil) on the MRR. 2. Experimental Work 2.1. Selection of MAF Process Parameters and Their Levels In this research, four parameters were considered to be effective on the temperature in the MAF process, these chosen parameters are (rotational speed, working time, current, and working gap) with four levels for each parameter. The selected parameters and their levels are listed in the Table 1; these parameters were selected based on the initial experiments. Table 1, The selected parameters and their levels. 2.2. Selection of the Orthogonal Array The experiments were designed based on the orthogonal array (OA) technique to reduce the number of the experiments. From the MINITAB17 software and by total degree of the freedom (DOF) needed to be computed, in order the select the appropriate OA for the experiments, each variable with four levels has two degrees of freedom. Based on Taguchi method, the total DOF of selecting OA must be greater than or equal to the total DOF required for the experiment; therefore, an orthogonal array L16 (4�) for the four factors with the four levels was used in the present investigation to perform the most effective experiments (16 experiments) from the overall experiments (256 experiments). 2.3. Experimental Procedure of MAF Process In this work, sixteen different tests are designed based on the Taguchi OA L16. Stainless steel 304 is used as flat workpiece with dimensions (100×50×3) mm. the chemical composition of stainless steel 304 is explained in the Table 2 No. Parameters Unit Code Levels 1 Rotational speed rpm A 250 500 750 1000 2 Working time min B 5 10 15 20 3 current Amp C 1.5 2 2.5 3 4 Working gap mm D 1 1.25 1.5 1.75 Ali H. Kadhum Al-Khwarizmi Engineering Journal, Vol. 13, No. 4, P.P. 22- 29 (2017) 24 Table2, The chemical composition of the stainless steel 304. The physical properties of stainless steel 304 are listed as in the Table 3. Table 3, The physical properties of stainless steel 304. Density (kg/m3) Elastic Modulus (GPa) Coefficient of Thermal Expansion (μm/m/°C) 0- 100°C Thermal Conductivity (W/m.K) at 100°C 8000 193 17.2 16.2 Specific Heat (J/kg.K) 0-100°C Electrical Resistivity (nΩ.m) 500 720 In the MAF process, an electromagnetic inductor was manufactured because it plays an important role in the finishing the surface layer. The inductor consists of the following: The core is from low carbon steel, the diameter of core is 22 mm, and the length of the core is 280 mm, while the diameter of the wire of coil is 0.9 mm, number of turns is 2400 for the primary coil and 1600 for the secondary coil, as shown in the Fig.1. A conventional “Turret vertical milling machine Model: MDM 4VS/4HS/4S’’ with its spindle was used to fix the magnetic inductor. This work is implemented on the workshop in the college. Fig. 1. The coil in the MAF process. Before MAF process, the weight of the stainless steel 304, was measured the work- piece was fixed by a special fixture to clamp the flat surface on the table, as shown in the Fig .2. Fig. 2. Fixing the workpiece in the MAF process. In the MAF process, the parameters for all 16 experimental tests were adjusted, the gap between the workpiece and the pole was first measured by the Verne instrument, and then filled with the MA powder, then the coil was provided with the current through the DC power supply. After that adjustment, the cutting speed was measured by the tachometer, and then the time was adjusted by using a timer. A properly calibrated Infrared camera was used measure the temperature in the contact region during finishing of workpiece at the last two second by. The fringe pattern readily changes with the change in any technological parameters, affecting the cutting temperature. The equation for measuring the MRR (g/min) is: MRR � � �� ����� ��� ���� ����� �� �.�.���� … (1) W: is the weight of the workpiece (g). Chemical analysis of stainless steel 304 C Si Mn Cr Ni Mo Cu 0.07 0.9 1.4 20.3 9.2 0.12 0.17 P S - - Chemical composition standard C Si Mn Cr Ni Mo Cu 0.08 max 1 max 2 max 18- 20 8- 10.5 - - P S 0.045 max 0.03 max Ali H. Kadhum Al-Khwarizmi Engineering Journal, Vol. 13, No. 4, P.P. 22- 29 (2017) 25 3. Results and Discussion 3.1. Signal to Noise Ratio (S/N) The S/N ratio is defined as a standard approach used for the average of the result in run with the main parameter. The optimum with S/N ratio is studying the main effect of the parameters and giving the best result which effect on the process [11]. In the MAF process, the S/N ratio is used to measure the MRR with the parameters, there are three categories of the quality characteristics: smaller is better, normal is better and bigger is better, in this case selecting the bigger is better which means the maximum response of the MRR. The mean squared deviation (MSD) and (S/N) ratio are determined by the equations: �� � !" ∑ $ ! %&'( )"*+! ...(2) �/- � −10123!4 5!" ∑ ! %&'( " *+! 6 ...(3) Where: n: number of trails 7*89 : the total result of the trails Table 4, Design of the experiments and result of the mean, S/N ratio for MRR the stainless steel 304. 3.1.1. Optimization of the MAF Process Parameters with MRR of Stainless Steel 304 In this study, the results of the MRR of the stainless steel 304 with factors are analyzed by S/N ratio, to obtain the influence of the levels of the parameters on the quality of the surface; the mean and the S/N ratio are given in Table 4. The main effect of each parameter with four levels on the mean and S/N ratio for MRR stainless steel 304 are calculated and listed in the Table 5. No. of EXP. A (rpm) B (min) C (amp) D (mm) MRR steel (g/min) S/N ratio Mean (g/min) TR. (°C) 1 250 5 1.5 1 0.0155 -36.1934 0.0155 28 2 250 10 2 1.25 0.0090 -40.9151 0.0090 24.1 3 250 15 2.5 1.5 0.0400 -27.9588 0.0400 49.6 4 250 20 3 1.75 0.0350 -29.1186 0.0350 68.5 5 500 5 2 1.5 0.0278 -31.1191 0.0278 35.9 6 500 10 1.5 1.75 0.0263 -31.6009 0.0263 32.8 7 500 15 3 1 0.0399 -27.9805 0.0399 54.9 8 500 20 2.5 1.25 0.0465 -26.6509 0.0465 70.3 9 750 5 2.5 1.75 0.0178 -34.9916 0.0178 22.3 10 750 10 3 1.5 0.0330 -29.6297 0.0330 41.5 11 750 15 1.5 1.25 0.0300 -30.4576 0.0300 34.1 12 750 20 2 1 0.0349 -29.1435 0.0349 39.9 13 1000 5 3 1.25 0.0480 -26.3752 0.0480 41.9 14 1000 10 2.5 1 0.0298 -30.5157 0.0298 40.3 15 1000 15 2 1.75 0.0350 -29.1186 0.0350 35.0 16 1000 20 1.5 1.5 0.0200 -33.9794 0.0200 29.2 Ali H. Kadhum Al-Khwarizmi Engineering Journal, Vol. 13, No. 4, P.P. 22- 29 (2017) 26 Table 5, The effect of the (S/N) ratio and mean of MRR stainless steel 304. S/N ratio optimization Mean optimization From the Table 5, the optimum parameters of the S/N ratio when (A2, B3, C4, and D3) (A= 500rpm, B= 15min, C= 3A, and D= 1.5mm) as shown in Fig. 3. and for mean effect in the (A2,B3,C4,andD2)(A=500rpm,B=15min,C=3A,an d D=1.25mm) as shown in Fig. 4. The values of the S/N ratio and mean in table (5) are calculated from Minitab software. The delta is a difference between maximum value and minimum value, for example (-29.34 +-33.55) = 4.21. Although the Rank of the S/N ratio and the means is the same, but this state need to make prediction, because the working gap value is different for two plots in Fig (3, 4). The prediction is used to determine the optimum value by choosing the large value of the S/N ratio in the prediction, as shown in the Table 6. Fig. 3. The S/N ratio effect on the parameters of stainless steel 304 on the MRR. Fig. 4. The mean effect on the parameters of stainless steel 304 on the MRR. :∆MRR < =�>� = � ?̅ABC + EFABC + G̅ABC + HABC − 3JFK ...(4) Where: JF � The overall mean of response MRR. ?̅ABC,EFABC, G̅ABC,MNO HABC = the average of response at the optimum level. From the Table 6, the optimum conditions of the MRR stainless steel 304 when (A= 500rpm, B=15min,C=3A, and D=1.5mm), and the temperature in the optimum experiment is 70.7°C 1 00 07505 00250 -2 8 -2 9 -3 0 -3 1 -3 2 -3 3 -3 4 201 51 05 3.02 .52.01 .5 1 .7 51 .501 .251 .00 Rotational Speed M e a n o f S N r a ti o s Working Time Current Working Gap Main Effects Plot for SN ratios Data Means Signal-to-noise: Larger is bet ter 1 0007 50500250 0.040 0.035 0.030 0.025 201 51 05 3.02.52.01 .5 1 .7 51 .501 .251 .00 Rotational Speed M e a n o f M e a n s Working Time Current Working Gap Main Effects Plot for Means Data Means The S/N ratio effect level A B C D 1 -33.55 -32.17 -33.06 -30.96 2 -29.34 -33.17 -32.57 -31.10 3 -31.06 -28.88 -30.03 -30.67 4 -30.00 -29.72 -28.28 -31.21 Delta 4.21 4.29 4.78 0.54 Rank 3 2 1 4 The means effect level A B C D 1 0.02488 0.02728 0.02295 0.03002 2 0.03513 0.02452 0.02668 0.03338 3 0.02892 0.03623 0.03352 0.03020 4 0.03320 0.03410 0.03897 0.02853 Delta 0.01025 0.01170 0.01602 0.00485 Rank 3 2 1 4 Ali H. Kadhum Al-Khwarizmi Engineering Journal, Vol. 13, No. 4, P.P. 22- 29 (2017) 27 Table 6, The prediction of the mean and S/N ratio. S/N ratio A B C D 2 3 4 3 mean S/N ratio 0.0489312 -24.2117 Mean A B C D 2 3 4 2 mean S/N ratio 0.0521062 -24.6396 3.2. The Analysis of Variance ANOVA of the MRR Stainless Steel 304 Anova was used to determine the effect of parameters with MRR and Ra, the results showed that the pole geometry and time are more effected on the MRR [12]. In order to obtain percentage of the effect of all parameters (A,B,C,D) on the materials removal rate of the stainless steel 304 surface, ANOVA was used to predict which parameter has a significant effect on the MRR, the contribution P% of each factors is explained in the Table 7. Table 7, ANOVA for MRR stainless steel 304. Source DOF Adj ss F P (%) A 3 0.0002512 0.49 14.022 B 3 0.0003673 0.72 20.503 C 3 0.0006104 1.19 34.073 D 3 0.0000499 0.10 2.785 Error 3 0.0005126 28.614 Total 15 0.0017914 Where: DOF: degree of freedom Adj ss: adjusted sum of squares F: F value or fisher factor, measurement of the significance of the factor P%: percentage contributed of each factor. The contribution of all factors is also manifested in Fig. 5. From this figure, it is noticed that the current (C) is more influence on the MRR, following by the working time (B), rotational speed (A) and then working gap (D), because the current and the working time lead to increase the heating in the MAF process, the heating effected on the surface layer of the workpiece and on the MRR. Fig. 5. Contribution of the parameters in the MRR stainless steel 304. 3.3. The Regression of the MRR of the Stainless Steel 304 with Temperature The regression is used to define the relationship between the temperatures with the MRR of the stainless steel 304, see Fig .6. The results of the MRR stainless steel 304 with temperature are listed in the Table 4; the temperature was measured during the experimental work for 16 experiments by infrared camera. Fig.6. The relationship between the temperature and MRR of steel. Where: x: temperature of the stainless steel 304. Fig.6. We shows the relationship between the temperature and the MRR of stainless steel 304. Is noticed that increasing the stainless steel 304 temperatures caused to increase MRR when the temperature is about (60°C) then after that decreases because the value of the temperature degree is obtained from the effect of the four 706050403020 0.05 0.04 0.03 0.02 0.01 S 0.0055352 R-Sq 7 7.8% R-Sq(adj) 7 4.3% X M R R ,S t Fitted Line Plot M RR = - 0.03897 + 0.002771 X - 0.000023 X^2 Ali H. Kadhum Al-Khwarizmi Engineering Journal, Vol. 13, No. 4, P.P. 22- 29 (2017) 28 parameters at each experiment. The optimum temperature is mean temperature which measured by the optimum conditions when (A= 500 rpm, B=15 min, C= 3A, and D=1.5 mm), Fig. 7. is explains the infrared camera at optimum conditions. Fig. 7. Infrared photography for optimum conditions. 4. Conclusions From the previous results, the followings can be concluded: 1- The optimum temperature rise is obtained according to optimum MRR (maximum) ,for the steel 304 the optimum levels are (A2, B3, C4, and D3) when rotational speed is (500 rpm), working time is (15 min),current is (3A) and working gap is (1.5mm) ,and then the optimum temperature at these levels is TR=70.7°C. 2- The analysis of the variance for the materials removal rate, it is noticed that the current (C) is more influential on the MRR, followed by the working time (B), rotational speed (A) and then working gap (D). 3- MRR of the steel 304 is increasing when the temperature increase up to 60 °C. 5. References [1] Mithlesh Sharma,and Devinder Pal Singh” ,To Study the Effect of Various Parameters on Magnetic Abrasive Finishing”, international Journal of Research In Mechanical Engineering & Technology Vol. 3, Issue 2, May - Oct 2013. [2] S. Jayswal, V. Jain, and P. Dixit, “Modeling and simulation of magnetic abrasive finishing process”, International Journal of Advanced Manufacturing Technology, Vol.26, pp. 477– 490, 2005. [3] Tae-Wan Kim” Application of Magnetic Abrasive Polishing to Composite Materials”, Journal of Mechanical Science and Technology, Vol 5, PP 1029-1034, 2010. [4] Japman singh, and radhey sham “Experimental Investigation of Process Parameter of MAF on Surface Roughness, “International Journal of the Science, Technology and Management,‘SGI Reflection ‘ may 2013. [5] Yamaguchi H, and Sato T, “Polishing and Magnetic Field-Assisted Finishing“, intelligent energy Field Manufacturing Interdisciplinary Process Innovations, 2012. [6] Rishi Devi Joshi,.Gursewak Singh Brar, and Mithlesh Sharma.”Effect on Magnetic Abrasive Machining with Different Range of the Electrical Parameters “,International Journal of Emerging Technology and Advanced Engineering , Vol.4,Issue 9,Sep 2014. [7] Girma B., Joshi S.S., Raghuram M. V. G. S., and Balasubramaniam R., “An Experimental Analysis of Magnetic Abrasive Finishing of Plane Surfaces”, Machining Science and Technology, Vol. 10, Issue 3, pp 323–340, 2006. [8] Vivek Mishra, Harsha Goel, Rahul S. Mulik, and P.M.Pandey, “Determining work-brush interface temperature in magnetic abrasive finishing process’ Journal of Manufacturing process,Vol.16,Issue 2,PP.248-256,2014. [9] Chandan Gaur “The analysis of the temperature during magnetic abrasive finishing of the plane plate “International Journal for Scientific Research & Development” Vol. 3, issue 4, PP. 1835-1841, 2015. [10] Dhirendra K. Singh, V.K. Jain, and V. Raghuram, “Parametric study of magnetic abrasive finishing process”, Journal of Materials Processing Technology, Vol.149, Issue 1-3, pp.22-29, 2003. [11] Ranjit K. Roy,”Aprimer on the Taguchi method,1ST Edition ,New York: Van Nostrand Reinhold ,1990. [12] M. K. Qate’a , A. .H. Kadhum, F. F. Mustafa ,”The influence of the magnetic abrasive finishing system for cylinder surface on the surface roughness and MRR” AL- Khwarizmi engineering journal ,Vol. 11,No.3, pp. 1-10,2015. )2017(22-29 ، صفحة 4، العدد13دجلة الخوارزمي الهندسية المجلم علي حسين كاظم 29 معدن ل المغناطيسي الحكب التشغيل عملية خالل وللحرارة المزال للمعدن المثلى القيم ايجاد ٣٠٤ الفوالذ علي حسين كاظم* حنان حسن مراد** جامعة بغداد كلية الهندسة الخوارزمي / /قسم هندسة التصنيع المؤتمت ،*** kadhumali59@yahoo.com :البريد االلكتروني * hananhasan729@yahoo.com :البريد االلكتروني ** ةالخالص اجريت ست المواد من المعدن وكذلك على ارتفاع درجات الحرارة. الجلغ المغناطيسي على عملية ازالةفي هذا البحث سوف يدرس تأثير التشغيل ب زال هذه للمعدن المالمثلى غولة وكذلك اليجاد القيمةشالمثلى للحرارة فى منطقه االتصال بين مسحوق المعدن والقطعة الم عشرة تجربة اليجاد القيمة ارتفاع القطب هي ( سرعة القطب المغناطيسي وزمن التشغيل والتياروالعالم الياباني تاجوشي وذلك باستخدام اربعة مدخالت التجارب تتم وفقا لمصفوفة ) وتقنية (S/N ratioمستويات لكل مدخل. في هذا العمل سوف يطبق (نسبة األشارة الى الضوضاء) ةالمغناطيسي عن سطح المشغولة) مع وجود أربع أليجاد الشروط المثلى مع تعريف المدخالت المهمة التي تؤثر على (MINITAB17)وذلك باستخام البرنامج االحصائي ANOVA) تحليل التباين ( عدن المذكور.أرتفاع درجات الحرارة ومعدل أزالة المادة للم 70.7 °C لى الحرارة المث العملية ان النتائج اظهرت ان درجةخالل التجارب ميرا الحرارية سوف تستخدم لقياس درجة الحرارةالكا .لمعدن الفوالذ