Study the effect of corrosion on fatigue strength of alloy steel (CK45) 
using in crank shaft under shot peening processes 

 
Dr.Abdulhussain H.rafesh 

Lecturer 
Institute of technology –Baghdad 

ABSTRACT 
In this study fulfilled, prediction of fatigue life for alloy steel (CK45) at the several cases: 
As received after shot peening after immersed in 36% Mgcl2, 30 day shot peening for 
specimens after corrosion. 
All tests carried out under constant amplitude load, rotating bending at stress ratio    (R = -1) 
and room temperature.  
The following conclusions are obtained: 
The fatigue strength increased 11% with shot penning process The fatigue strength decreased 
18% after corrosion in corrosive medium The fatigue strength increased 14% with shot 
penning process after immersed in corrosive medium. 



 

 2012 لسنة  114-106 ،رابعال العدد الخامس، المجلد الھندسیھ، للعلوم القادسیھ مجلة               107
 



بعد قذفھ قالب  المستخدم في صناعة المحور ال (CK45) دراسة تأثیر التآكل على مقاومة التعب للفوالذ ألسبائكي
 لمعدنیةا تبالكرا

108 2012 لسنة  114-106 ،رابعال العدد الخامس، المجلد الھندسیھ، للعلوم القادسیھ مجلة

(Shot Tumblast control panel model STB-OB),   



 

 2012 لسنة  114-106 ،رابعال العدد الخامس، المجلد الھندسیھ، للعلوم القادسیھ مجلة               109
 



بعد قذفھ قالب  المستخدم في صناعة المحور ال (CK45) دراسة تأثیر التآكل على مقاومة التعب للفوالذ ألسبائكي
 لمعدنیةا تبالكرا

110 2012 لسنة  114-106 ،رابعال العدد الخامس، المجلد الھندسیھ، للعلوم القادسیھ مجلة



 

 2012 لسنة  114-106 ،رابعال العدد الخامس، المجلد الھندسیھ، للعلوم القادسیھ مجلة               111
 

1- Jaske .C ,Broek "Corrosion fatigue of cathodically protected welded carbon steel in cold sea 
water” , Final report to American petroleum institute , Committee on off shore  safety and 
antipollution research , Dallas , Feb. 11 , 1977. 
 

2- Dugdale , D. S ,Corrosion fatigue of sharply notched steel specimens”                     , 
Metallurgica ,pp, 27-28 , Jan , 1972.  
 

3- F .Abadie , L .Barrlier “Ceramic shot enhancement of high strength steel endurance 
application to springs and gears”, Icspa shot peening , 2005. 
 

4- Ahmed ali hussain “Corrosion – fatigue under combined loading and different conditions” , 
p.H.D thesis , , university of technology , Baghdad 1997. 
 

5-   “Optimization of the shot peening process in terms of  fatigue resistance” S .Romero, E 
.Rios, presented at seventh international conference on shot peening , ICSP-7 warsaw, 
Poland, 1999. 
 

6-  “Effect of shot peening on the fatigue strength of spring steel after exposure to corrosion” 
Aleksander, Grzegorz, waraw, Poland, 2005. 
 

7-  “Shot peening as an alternative to fatigue life improvement of ck45 steel coated with an 
electro less Ni-Cu-P” T .Saeid , S .yazdani , International journal of ISSI, vol2 , 2005. 

≤≤

σσ



بعد قذفھ قالب  المستخدم في صناعة المحور ال (CK45) دراسة تأثیر التآكل على مقاومة التعب للفوالذ ألسبائكي
 لمعدنیةا تبالكرا

112 2012 لسنة  114-106 ،رابعال العدد الخامس، المجلد الھندسیھ، للعلوم القادسیھ مجلة

σ

σ

σ

σ



 

 2012 لسنة  114-106 ،رابعال العدد الخامس، المجلد الھندسیھ، للعلوم القادسیھ مجلة               113
 



بعد قذفھ قالب  المستخدم في صناعة المحور ال (CK45) دراسة تأثیر التآكل على مقاومة التعب للفوالذ ألسبائكي
 لمعدنیةا تبالكرا

114 2012 لسنة  114-106 ،رابعال العدد الخامس، المجلد الھندسیھ، للعلوم القادسیھ مجلة