Article AL-QADISIYAH JOURNAL FOR ENGINEERING SCIENCES 12 (2019) 056–060 Contents lists available at http://qu.edu.iq Al-Qadisiyah Journal for Engineering Sciences Journal homepage: http://qu.edu.iq/journaleng/index.php/JQES * Corresponding author. E-mail address: kaka2013331@gmail.com (Bariq A.H. Al-Qaisi) https://doi.org/10.30772/qjes.v12i1576 1998-4456/© 2019 University of Al-Qadisiyah. All rights reserved. Effect of pure Aluminum in Reduction of Silica from Sediments in Iraqi- Tigris Bariq A.H. Al-Qaisi a* and Sami. I.J. Al-Rubaiey a Dept. Production Eng. & Metallurgy, University of Technology , Baghdad, Iraq A R T I C L E I N F O Article history: Received 03 April 2019 Received in revised form 15 May 2019 Accepted 19 May 2019 Keywords: Tigris River Sediments Pyrometallurgy Hydrometallurgy Silic, and silicon A B S T R A C T This work was carried out on sediments in the Iraqi- Tigris river within the city of Baghdad. Three locations were taken from the Tigris river. The first is at the entrance to Baghdad City (Al-Muthanna Bridge), the second is in central Baghdad (Adhamiya) and the third is at the end of Baghdad (Diyala Jisr). The specimens were taken from the banks of the Tigris river at 1.5 meters from the edge of the water and a depth of 2 meters. Sediments formed mainly from silica, with concentrations between 59 - 66%. Therefore, the study focused on extracting the pure silicon element from these sediments. The extraction process of silicon from the sediments was performed in two stages. The first is pyrometallurgy stage, in which the reduction of silica was done by mixing pure aluminum powder with sediments at different mixing ratio (1:1, 1.5:1 and 2:1) sediments/aluminum and at temperatures (900, 950 and 1000)° C. The second stage was hydrometallurgy (leaching process), this process was carried out by using different concentrations (3,4 and 5)M of sulfuric acid to obtain silicon element with purity 98. 9%. The results show that the efficiency of extraction silicon from sediments of the Tigris river is greater than (88%). © 2019 University of Al-Qadisiyah. All rights reserved. 1. Introduction The sediments are formed on the banks of the rivers and at riverbed as a result of drift of the soil with the movement of water, in addition to the effect of streams and small rivers flowing into the main river [1]. The sediments are taken from the banks of Tigris river which contain various compounds such as (SiO2, CaO, MgO, Fe2O3, TiO2, Al2O3, P2O5, and K2O) at different concentrations. The source of sediments in Tigris River come from several areas, The most important one as Anatolia Plateau in Turkey: Also Tigris tributaries continue as the source of sediments in the Tigris river in Iraqi territory such Khabur, Great zab, Little zab ,Diyala river and Adhaim River [1]. The Sediments vary in Tigris river depending on the quality of the water and affected by different pollutants and type of soil and effect of Dayala river on these sediments [2, 3, 4]. The synthesis of high purity silicon from natural substances has been performed by several researchers, using metals like Mg, Ca, Al or C as reducing agents [5,6]. Sadique [7] extracted high purity silicon (99.1% purity) from the waste of silica fume (SF). He reached to 99.1% Si by using Pyrometallurgical process .The best temperature for reduction was (750- 850)°C at 2:1 mixing ratio of Mg/SF. Jehad & Jasim [8] studied the extraction of silicon with a high purity of 99% by using Iraqi starting http://qu.edu.iq/ mailto:kaka2013331@gmail.com https://doi.org/10.30772/qjes.v12i BARIQ A.H. AL-QAISI AND SAMI. I.J. AL-RUBAIEY /AL-QADISIYAH JOURNAL FOR ENGINEERING SCIENCES 12 (2019) 056–060 57 materials (quartzite rock, plant coal) via electric arc furnace at 1500 C̊ . Mishra et al. [9] produced Polycrystalline silicon from amorphous silica obtained from rice-husk white ash by using calcium at the reduction temperature equaled to 720 C̊ .The final purity of silicon was 99.9% after acid leaching with concentrated HNO3 and HF . Onojah, A. [10] studied the extraction of silicon from rice husk ash and natural quartz by using magnesium powder however the two sources of silica gave silicon purities in the range of 97-98%. This study focuses on extracting pure silicon element from Sediments in Iraqi-Tigris River which contain silica for percentage (59 – 66)% 2. Experimental work 2.1. Sampling preparations The specimens were taken from three locations at Tigris river in Baghdad City. The first is at the entrance to Baghdad City (Al-Muthanna Bridge), the second is in central Baghdad (Adhamiya) and the third is at the end of Baghdad (Diyala Jisr). The specimens were taken from the banks of the Tigris river at 1.5 m from the edge of the water and a depth of 2 m at three different locations along the Tigris River within Baghdad city. which are;  Al Muthanna Bridge  Al-Adhamiyah  Jisr Diyala The samples were taken by 10 kg from each mentioned location, in depth of 2 m. These samples were taken using steel- mold, The samples then dried at 100˚C for 4hrs. This process was achieved by using a bender oven. 2.2. Chemical analysis Chemical analysis of the river-sediments was carried out by using X-Ray Fluorescence (XRF) at the University of Baghdad / Iraqi- German laboratory as shown in Tables 1,2 and 3. Table 1. X-Ray Fluorescence (XRF) at the Al-Muthanna Bridge Compounds Concentration % SiO2 59.974 CaO 20.421 Al2O3 8.035 Fe2O3 4.94 K2O 1.447 P2O5 0.702 MgO 3.255 TiO2 0.739 Table 2. X-Ray Fluorescence (XRF) at Al-Adhamiya Location Compounds Concentration % SiO2 59.29 CaO 18.17 Al2O3 8.739 Fe2O3 5,848 K2O 1.523 P2O5 0.688 MgO 3.835 TiO2 0.752 Others 0.165 Table 3. X-Ray fluorescence (XRF) at Jisr Diyala Location Compounds Concentration% SiO2 66.007 CaO 16.26 Al2O3 7.70 Fe2O3 4.24 K2O 1.400 P2O5 0.702 MgO 2.54 TiO2 0.662 Other 0.078 2.3. Grinding and Sieving Processes These processes were accomplished to obtain particles with a size equal to 63 µm by using Ball mill machine for grinding time of 1hr.The speed of the ball milling was 300 rpm. Auto sieve shaker device at a specified range 53-710 µm was used for grinding process. 2.4. Washing process (primary leaching) The samples are washing by using hydrochloric acid at 10% concentration for removal some metal oxides such as (MgO, CaO ) and increases the silica ratio [11,12]. This process was done by a magnetic stirrer device for 80 ˚C at 2 hrs with a rotation speed of 500rpm and solid-liquid ratios (1- 4). After each experience, the sample was filtered and dried in an oven at 100 ̊ C for 2 hr. The following equations illustrate the process of dissolving some of the impurities [13,14]. 𝐶𝑎𝑂 + 2𝐻𝐶𝑙 = 𝐶𝑎𝐶𝑙2 + 𝐻2𝑂 (1) 𝑀𝑔𝑂 + 2𝐻𝐶𝑙 = 𝑀𝑔𝐶𝑙2 + 𝐻2𝑂 (2) 2.5. Mixing and Pressing Processes Different ratio of Al/Sediments were used. These ratios are (1:1, 1.5:1 , 2:1) the specimens were compressed using compression a die with a diameter of 3 cm, the applied load was 20 ton for 1 min. 2.6. Reduction Process The reduction process was carried out in carbolite furnace (type cwf12/13, England) at temperatures 900, 950 ,1000 °C for 2 hrs, The specimens were tightly covered in steel crucible for dimensions (11 cm diameter, and 15 cm length ) to full the crucible. The cover was supplied with value allow for following for argon gas flow. All specimens were tested by atomic absorption spectrometry, X-ray Diffraction Analysis test was done onetime for each reduction temperature. 2.7. Leaching process The leaching process was done to remove impurities in the reduction process by using sulfuric acid at 3, 4 and 5 M and leaching temperature 100 °C for 4 hrs and solid to liquid ratio of 1:6 via using Heating mantle device. The insoluble residue was separated from the solution by vacuum pump using filtration paper. Then the filtered cake was washed with distilled water several times and then dried in an oven at 100 °C for 1hr. 2.8. X-ray Diffraction Analysis To identify the formed compounds after reduction X-ray test was done on machine BRUKER. The test was accomplished under the following parameters: voltage 40 kV , current 30 mA ,1.540 A˚ and scan rate 5-10 ˚deg/min. The test was done at geological department , college of sciences, University of Baghdad. 58 BARIQ A.H. AL-QAISI AND SAMI. I.J. AL-RUBAIEY /AL-QADISIYAH JOURNAL FOR ENGINEERING SCIENCES 12 (2019) 056–060 2.9. X-ray fluorescence analysis The purity of extracted silicon powder was tested by using X-ray fluorescence-XRF a type (AMETEK 2010 Germany). The analysis was conducted at the place mentioned above. 3. Results and discussion 3.1. Washing process (Primary leaching) Tables 4, 5 and 6 show the increase of silica percentage in samples and decrease the percentage of other compounds after Primary leaching process according to X-ray fluorescence analysis compared with Tables 1, 2 and 3. Table 4. X-Ray Fluorescence (XRF) at the Al-Muthanna Bridge location Compounds Concentration % SiO2 70.132 CaO 13.251 Al2O3 9.522 Fe2O3 2.651 K2O 0.923 P2O5 0.632 MgO 1.554 TiO2 0.519 Other 0.816 Table 5. X-Ray Fluorescence (XRF) at the Al-Adhamiyah Location Compounds Concentration % SiO2 68.241 CaO 11.216 Al2O3 11.631 Fe2O3 3.642 K2O 0.989 P2O5 0.423 MgO 2.415 TiO2 0.514 Others 0.929 Table 6. X-Ray Fluorescence (XRF) at the Jisr Diyala Location Compounds Concentration % SiO2 76.500 CaO 8.800 Al2O3 10.415 Fe2O3 2.145 K2O 0.478 P2O5 0.315 MgO 0.918 TiO2 0.211 Other 0.218 3.2. Reduction Process The reduction process by mixing aluminum powder with sediments was carried out to obtain the silicon element from sediments in the Tigris river. The compounds present in the products at different temperature were Si and some traces like Al2O3, and Al non-react. In addition to the small amount of non-reacted silica as shown in Tables 7, 8 and 9.The mixing aluminum powder with silica in the reduction process, Al reacts with silica to produce directly Si element and alumina (Al2O3),because the aluminum element is more active metal than silicon, according to the following reaction(3)[12,13]. The corresponding X-Ray diffraction analysis (XRD) was shown in Fig. 1. 3𝑆𝑖𝑂2 + 4𝐴𝑙 = 2𝐴𝑙2𝑂3 + 3𝑆𝑖 (3) Figure 1. XRD pattern of reduction products at 1000˚C and ratio of Al/sediments 1:1 Table 7. Effect of Al/sediments ratio in reduction process at different temperature at the Al Muthanna Bridge location Others % CaO % Al2O3 % Al % SiO 2% Si % Temperature C˚ Al/Sediments 0.9 5.3 42.2 32.5 0.9 18.2 900 1:1 0.6 6.1 40.2 31.5 0.7 20.9 950 1:1 0.7 3.1 32.9 38.1 0.4 24.8 1000 1:1 0.9 7.3 43.5 32.05 2.7 13.5 900 1.5:1 1.1 7.1 44.1 35.9 1.5 14.9 950 1.5:1 2.2 6.8 43.1 30.6 1.2 16.1 1000 1.5:1 1.8 9.2 40.2 34.4 3.2 11.2 900 2:1 1.2 7.8 41.8 33.1 2.7 13.4 950 2:1 0.6 5.4 38.1 40.5 1.7 13.7 1000 2:1 Table 8. Effect of Al/sediments ratio in reduction process at different temperature at the Al-Adhamiyah Location Other% CaO % Al2O3 % Al % SiO % Si % Temperatue C˚ Al/Sediments 0.9 4.1 41.9 31.2 1.2 20.7 900 1:1 0.6 2.4 38.5 35.6 0.8 22.1 950 1:1 1 3.8 38.9 29.1 1.9 25.3 1000 1:1 0.9 3.2 39.6 38.3 1.6 16.4 900 1.5:1 1.6 2.7 46.8 32.6 1.5 14.8 950 1.5:1 1.4 4.1 40.3 35.1 0.9 18.2 1000 1.5:1 2.4 7.9 37.6 35.3 2.7 14.1 900 2:1 0.5 3.1 40.1 38.1 2.9 15.3 950 2:1 1.5 4.9 38.2 37.4 2.4 15.6 1000 2:1 Table 9. Effect of Al/sediments ratio in reduction process at different temperature at the Jisr Diyala Location Other % CaO % 3O2Al % Al % 2SiO % Si % Temperature C˚ Al/Sediment 1.9 5.5 36.1 35.3 1.6 19.6 900 1:1 2.6 6.8 32.6 33.4 1.2 23.4 950 1:1 1.7 6.1 36.8 26.9 2.4 26.1 1000 1:1 2.9 8.2 40.6 31.2 2.1 15.1 900 1.5:1 1.7 6.5 37.8 35.7 1.5 16.8 950 1.5:1 1.3 6.4 43.7 30.3 1.1 17.2 1000 1.5:1 2.8 8.3 43.5 31.1 1.8 12.5 900 2:1 1.8 9.2 46.9 35.9 0.8 13.7 950 2:1 1.4 7.9 39.5 36.4 1.3 13.5 1000 2:1 BARIQ A.H. AL-QAISI AND SAMI. I.J. AL-RUBAIEY /AL-QADISIYAH JOURNAL FOR ENGINEERING SCIENCES 12 (2019) 056–060 59 A. Effect of Al/sediments ratio in the reduction process at different temperature: Tables 7 , 8 and 9 show the amount of Al powder added to sediments at referent mixing ratio 2:1 , 1.5:1 and 1:1 and different temperature 900, 950, 1000 ˚C. The Tables show that the amount of Al addition have a large effect on the reduction of silica Located in sediments. It had been shown that at 1000 ˚C using ratio 1:1 Al/Sediments, Si appears very high amount in three locations (24.8, 25.3, and 26.1) %, whereas at 1000 ˚C ratio with a 2:1 appears small amount in three locations (13.7, 15.6, and 13.5)%. As a result of atomic absorption spectrometry and XRD analysis the percentage of extracted Silicon increase when mixing ratio decrease into 1:1 at constant temperature 1000 ˚C [7, 15]. Sadique[7]:explain when mixing aluminum or magnesium powder with silica in the reduction process , Al or Mg can react with Silica to produce Si element and alumina compound (Al2O3), because these elements are more active metal than silicon in ellingham diagram (∆G of aluminum or magnesium ≥ ∆G of silicon). Sadique extracted high purity silicon (99.1% purity) from the waste of silica fume (SF) by using magnesium element to reduction of silica (SiO2). Figure (2) shows Si content as a function of Al/sediments. The maximum amount of Si is achieved at mixing ratio1:1. While the Si yield decreases at mixing ratio 2:1 because of non-reaction all silica (SiO2) with Al powder. Figure 2. Shows the effect of Al/sediments ratio on the silicon yield at three different locations. B. Effect of temperature in the reduction process: As shown in Tables 7, 8, and 9 that the effect of the temperature on the reduction process of SiO2 at a constant ratio of Al/SiO2 (1:1). According to atomic absorption spectrometry and XRD analysis at 900˚C appears silicon amount in three locations (19.6, 20.7, and 19.6). Whereas at high temperature of 1000˚C the silicon amount increases (24.8, 25.3, and 26.1). As a result of atomic absorption spectrometer, the amount of Si increases when the temperature increases into 1000˚C at constant mixing ratio (1:1)[7]. Figure 3. shows Si content as a function of temperature. The maximum amount of Si is achieved 1000 ˚C .While the Si yield decrease at 900 ˚C Figure 3. Shows the effect of temperature on silicon percentage at three different locations. 3.3. Evaluation of silicon amount production The extraction of silicon process was evaluated since the main purpose of the reduction experiments is to achieve the highest amount of Si with high purity. The best condition for this process to obtain the maximum amount of Si 26.1 % with high purity 98.9% is achieved at the Al/sediments ratio of 1:1 at 1000 C̊. 3.4. Hydrometallurgical Process Hydrometallurgy (leaching process) is a method for obtaining metals from their ores via using different solutions. the Pyrometallurgical process for extraction of silicon which was made at different conditions led to the production of various compounds in the reduction process such Al2O3. For the purification of the Produced silicon, the leaching processes were used. Table (10) shows the purification of silicon produced an effect of sulfuric acid on dissolving impurities in the samples and figure (4) shows the EDX spectra of the silicon powder. Angus L. Daniels [16] and Paween Numluk [17] explained that the aluminum oxide (alumina) react with sulfuric acid at different concentration (3–5)M and forming aluminum sulfate according to following equation(5) at 100 ˚C for 4 hrs, The efficiency of silicon extracted from sediments of Tigris river is greater than (88%). 𝐴𝑙2 𝑂3𝐻2𝑂 + 3𝐻2𝑆𝑂4 = 𝐴𝑙2(𝑆𝑂4)3 + 6𝐻2𝑂 (4) Table 10. XRF analysis of purification of silicon when temperature =100°C, and time=4hHr Samples Concentration M Si% SiO2% Al2O3% Al-Muthanna Bridge 3 95.98 0.3 3.72 4 98.9 0.3 0.8 5 93.24 0.4 6.36 Adhamiyah 3 96.43 1.4 2.17 4 98.4 1.5 0.1 5 92.76 1.8 5.44 Jisr Diyala 3 96.92 2 1.08 4 97.3 1.9 0.8 5 93.65 2.1 4.25 12 17 22 27 0.5 1.5 2.5 S i ra ti o Al/ Sediments Jisr Diyala Location Al Muthanna Bridge location Al-Adhamiyah Location 17 19 21 23 25 27 880 930 980 S i ra ti o temperature ⁰C Al- Adhamiyah Location Al Muthanna Bridge location Jisr Diyala Location 60 BARIQ A.H. AL-QAISI AND SAMI. I.J. AL-RUBAIEY /AL-QADISIYAH JOURNAL FOR ENGINEERING SCIENCES 12 (2019) 056–060 Figure 4. EDX spectra of the as-produced silicon The SEM micrograph of the silicon powder as shown in Fig. 5. and it can be seen that the shape of particles is random and different size for 4 hrs of leaching time, 100 °C of temperature and (4M) concentration of sulfuric acid. Figure 5. The SEM micrograph of as-produced silicon The particle size distributions of silicon powder can be seen in Fig. 6. shows that approximately 90 %volume of the produced silicon is ≤ 66 µm, 50% of the produced silicon volume ≤ 22µm and 10% volume of the produced silicon is ≤ 5µm. Figure 6. The particle size distribution of as-produced silicon 4. Conclusions  Pure silicon (98,9%) has been successfully produced from sediments of Tigris river by pyrometallurgy and hydrometallurgy processes  The reduction process was carried out with attrition of aluminum powder (63 µm particle size) at different ratio ( 2;1, 1.5;1 and 1;1) the best results obtained at ratio 1;1. The effect of Al powder is to decrease the reduction temperature of silica  The leaching process carried out by using 4M H2SO4 to remove impurities such (Al2O3).  The best reduction temperature was found at (1:1) mixing ratio of Al/Sediments was 1000˚C .  The efficiency of silicon extracted from sediments of Tigris river is greater than (88%) REFERENCES [1] Al-Bassam, K.S. and Al-Mukhtar, L.E.,. Heavy minerals in sediments of the Euphrates River. Iraqi Bulletin of geology and mining, 4(1) (2008) p. 29 – 41. [2] Abdul-Hameed M. J. Al-Obaidy, Zahraa Zahraw Al-Janabi, Abdul-Rahman Al- Kubaisi, Distribution of Some Heavy Metals in Tigris River middle of Iraq, 11(2) (2014). [3] Luma abdalalah skben Al-abadi, The relative distribution of mica minerals in sand fractions and different soil depths, Al- Qadisiyah Journal for Engineering Sciences, 14(4) (2008) p1- 9. [4] Philip, G., Mineralogy of Recent sediments of Tigris and Euphrates River and some older detrital deposits Jour. Sed. Pet. 38 (1968) p. 35 – 44. [5] Nazma and M. Akhter, X–Ray diffraction analysis of silicon prepared from rice husk ash, J. Mater. Sci. 23, 23792381 (1998). [6] L. P. Hunt, J. P. Dismukes, J. A. Amick, A. Schei and K. Larsen, Rice hulls as a raw material for producing silicon, Journal of the Electrochemical Society, 131 (1984) P.1683- 1686. [7] S. Elius Sadique , Production and Purification of Silicon by Magnesiothermic Reduction of Silica Fume, Copyright by Sarder Elius Sadique, (2010). [8] Jehad. Abed Taies & Jasim H. Hassen, Production of Silicon Metal From Iraqi Sand ,journal of Baghdad for science , 11(1) (2014). [9] Mishra P., Chakraverty A. and Banerjee H.D. Production and purification of silicon by calcium reduction of rice-husk white ash. Journal of Materials Science, 20 (1985) P.4387-4391. [10] Onojah, A., Amah, A. N. and Ayomanor, B. O, Comparative studies of silicon from rice husk ash and natural quartz, American Journal of Scientific and Industrial Research, 3(3) (2012) p.146 -149. [11] Daroon H. Khorsheed , Abbas R. Ali , Heavy Minerals Distribution in the Recent Stream Sediments of Diyala River Basin/ Northeastern IRAQ, Kirkuk University Journal /Scientific Studies, 10(4) (2015) p.415-438 [12] Abdul Salam Mehdi Salih, Study of morphological aspects and variation of clay minerals in the recent alluvial sediments of Tigres River in Sharqat area, Tikrit Journal of Pure Science, 15(1) (2009). [13] Lide ،David. CRC Handbook of Chemistry and Physics, (2000). [14] Perry ،R.؛ Green D.؛ Maloney J. Perry's Chemical Engineers' Handbook, (1984). [15] Takeshi Okutami., Utilization of Silica in Rice Hulls as Raw Materials for Silicon Semiconductors , Journal of Metals, Materials and Minerals, 19 (2) (2009) pp.51-59. [16] Angus L. Daniels, Edison Muzenda, Recovery of Aluminium Oxide from Flint Clay through H2SO4 Leaching, Proceedings of the World Congress on Engineering, 3 (2012) p1-3, 3p. [17] Paweena Numluk and Aphiruk Chaisena, Sulfuric Acid and Ammonium Sulfate Leaching of Alumina from Lampang Clay, E-Journal of Chemistry, 9(3) (2012) p. 1364-1372 c p s/e v kev https://www.iasj.net/iasj?func=issues&jId=131&uiLanguage=ar https://www.iasj.net/iasj?func=issues&jId=131&uiLanguage=ar https://www.iasj.net/iasj?func=issues&jId=131&uiLanguage=ar https://www.iasj.net/iasj?func=issues&jId=131&uiLanguage=ar