PEER-REVIEW ARTICLE REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2391 Biodegradability of Cellulose Fibers, Films, and Particles: A Review Martin A. Hubbe ,a,* Jesse S. Daystar ,b Richard A. Venditti ,a Joel J. Pawlak ,a Marielis C. Zambrano ,a Morton Barlaz ,c Mary Ankeny ,b and Steven Pires b Cellulose fibers are an abundant material that is well known for its biodegradability. Various forms of cellulose, such as cotton, paper pulp fibers, and microcrystalline cellulose can be regarded as benchmarks for biodegradability, when comparing other materials. However, as revealed by the literature, broad ranges of time and extent of biodegradation have been reported for cellulose. These large ranges can be attributed not only to environmental factors but also to the presence of lignin, the degree and perfection of crystallinity, the size and density of the physical specimens, and chemical modifications to the cellulose, if any. Studies also have shown differences in biodegradability associated with the selection of test methods. Although cellulose is subject to well-known enzyme-promoted mechanisms of biodegradation, the evolution of plant materials has favored development of some resistance to decay, i.e. recalcitrance. Cellulosic materials are clearly less biodegradable than starch. However, they are more biodegradable than various synthetic or bio-based plastics, as well as some cellulose derivatives, which persist in ocean water or soils for very long periods. This review indicates that cellulose biodegradability, while generally rapid and natural, has a rate and extent that depends on a complex and sometimes subtle set of environmental and chemical factors. DOI: 10.15376/biores.20.1.Hubbe Keywords: Cellulase; Recalcitrance; Seawater; Soil; Wastewater; Textiles; Environmental impacts Contact information: a: Department of Forest Biomaterials, North Carolina State University, Campus Box 8005, Raleigh, NC, 27695-8005 USA; b: Cotton Incorporated, 6300 Weston Parkway, Cary, NC 27516, USA; c: Dept. of Civil, Construction, and Environmental Engineering, North Carolina State University, Campus Box 7908, Raleigh, NC, 27695-7908 USA; *Corresponding author: hubbe@ncsu.edu Contents Introduction . . . . . . . . . . . . . . . . Scope of the problem . . . . . . Circular economy issues . . . . Cellulose biodegradation basics Cellulases . . . . . . . . . . . . . . . Hemicellulose biodegradation Lignin biodegradation . . . . . . Recalcitrance in general . . . . Environments . . . . . . . . . . . . . . Wastewater & its treatment Seawater . . . . . . . . . . . . . . . . Soil & Landfill . . . . . . . . . . . . Compost . . . . . . . . . . . . . . . . . Fiber-related factors . . . . . . . . . Type of cellulose entity . . . . . . Inherent differences in cellulose Size of cellulose entity . . . . . . . Effects of processing . . . . . . . . Chemical treatments . . . . . . . . Environment-related factors . . . . Moisture content . . . . . . . . . . . Temperature . . . . . . . . . . . . . . C:N ratio . . . . . . . . . . . . . . . . . Counter-ions . . . . . . . . . . . . . . Mechanistic issues . . . . . . . . . . Thermodynamics . . . . . . . . . . Kinetics . . . . . . . . . . . . . . . . . . Reaction product evidence . . . Life cycle issues . . . . . . . . . . . . Raised cellulose levels . . . . . . Filtering of cellulose fibers . . . Wastewater sludge options . . Seas, microplastics, cellulose Concluding statements . . . . . . . 2392 2396 2398 2398 2399 2403 2405 2406 2407 2407 2411 2412 2413 2414 2415 2416 2418 2420 2422 2425 2426 2426 2426 2427 2427 2428 2428 2433 2433 2433 2434 2435 2437 2438 https://orcid.org/0000-0002-2321-4218 https://orcid.org/0000-0002-4513-2803 https://orcid.org/0000-0002-7986-4092 https://orcid.org/0000-0002-9803-9004 https://orcid.org/0000-0002-6857-863X https://orcid.org/0000-0001-8028-3917 https://orcid.org/0000-0002-6375-9802 https://orcid.org/0000-0002-6558-0611 REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2392 INTRODUCTION This article reviews published findings related to the relative biodegradability of cellulose fibers, including factors affecting their accessibility to enzymatic attack. Interest in this topic has been spurred by reports of fibers and related materials remaining either after conventional wastewater treatment (López Alvarez et al. 2009; Ghasimi et al. 2016; Libardi et al. 2022), or when cellulosic matter is discharged to other environments as rinsewater after laundering (Ladewig et al. 2015; Zambrano et al. 2019). In addition, there have been concerns about slow biodegradation of cellulosic fibers that reach ocean environments (Zambrano et al. 2020; Nagamine et al. 2022; Royer et al. 2023). Issues to be reviewed include the rates and extent of cellulose fiber biodegradation under a variety of conditions, including fresh water, aerobic and anaerobic wastewater treatment environments, seawater, soil burial, and composting. Literature is examined to shed light on mechanisms of biodegradation, as well as factors that can promote or inhibit those natural processes. Common examples of cellulose fibers include sanitary tissue fibers, cotton and rayon textile fibers, and pulp fibers present in packaging, as well as in printing and writing papers. Biodegradability of cellulose fibers can be viewed as a continuum, in which specific materials exposed to defined environmental conditions can be compared to reference materials. Such a perspective is illustrated in Fig. 1. In this article the term environmental will be used broadly, including both natural conditions and those in wastewater treatment facilities, unless specified. Fig. 1. Relative biodegradability of various other polymers compared with that of some different forms of cellulose and wood As an example of a reference material, every year in temperate climates one can expect masses of leaves to fall from deciduous trees, such that they not only blanket the ground, but many of them pass into streams and eventually into oceans. The aquatic biodegradation of leaf litter has been studied (Sakamaki and Richardson 2008; Raposeiro et al. 2014). It was reported that half a year was sufficient for biological breakdown of Sugars Starch: Microcrystalline Cellulose (MCC) Cellulose fibers (lignin-free) Cellulose fibers (lignin-containing) Small biomass pieces, dead leaves: Blocks of wood Polyhydroxybutyrate (PHB) Poly(lactic acid) (PLA) Polyolefins, etc.: D e c re a s in g B io d e g ra d a b il it y n REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2393 leaves placed in tidal flat environments (Sakamaki and Richardson 2008). Raposeiro et al. (2014) reported between about 15% and 95% mass loss of leaves with no added nutrients or bacteria in 28 days in the North Atlantic island of São Miguel in the Azores, depending on the tree species in different fresh-water streams. In addition to such natural reference points, microcrystalline cellulose (MCC) is often used by researchers as a benchmark from which to judge the relative biodegradability of other cellulosic materials in selected environments. The fact that bioplastics, despite their plant-based origins, are not equally biodegradable was highlighted in recent work by Kwon et al. (2024), who compared biodegradation in aerobic water conditions. Pure poly(lactic acid) (PLA) was not degradable under the studied conditions, whereas poly(β-hydroxybutyrate) (PHB) readily degraded. Moreover, incorporation of just 25% of PLA into a mix of the two polymers, followed by melt-bending and extrusion, yielded fibers that showed only 11% degradation. The differences in biodegradability among bioplastics have been shown to be attributable to differences in crystallinity, hydrophobicity, and chemistry (Kwon et al. 2023b). Table 1. Highlights from Studies Considering the Biodegradability of Microcrystalline Cellulose (MCC) Highlights from Cited Studies % Degraded/ test period Citation MCC biodegradation was compared in shaken enzyme solutions with that of Douglas fir wood, with optional steam-explosion pretreatment. 70% / 2 days Esteghlalian et al. 2002 MCC biodegradation was compared to that of sugarcane bagasse in enzyme solutions. 53% / 2 days Wada et al. 2010 Factors affecting the biodegradation rate of MCC were studied in enzyme solutions, with discussion that the data can be used as a reference for other cellulosic materials. 40-80% / 2 days Yu et al. 2012b MCC biodegradation in enzyme solutions was compared with that of bleached softwood fibers and bacterial cellulose. 63% / 2 days Kafle et al. 2015 MCC was found to be more biodegradable than toilet paper and various other cellulosic fiber types under aqueous mesophilic and thermophilic anaerobic conditions of wastewater treatment. 86-91% / (tests stopped when no more methane was generated) Ghasimi et al. 2016 MCC biodegradation in aerated river water was used as a reference for cotton, rayon, and polyester fibers. 84% / 245 days Zambrano et al. 2019 MCC was used as a reference for studying biodegradation of fibers released during the laundering of cellulose and polyester-based textiles. 80% / 35 days (lakewater) 100% / 35 days (activ. sludge) 70% / 35 days (seawater) Zambrano et al. 2020 MCC was used as a biodegradability reference point when comparing three commercial plastics under aerobic composting conditions. 86% / 60 days Rossetti et al. 2021 MCC biodegradation was compared to that of various plastic and cellulosic fibers, including Lyocell. 100% / 30 days (marine) 50% / 30 days (fresh water) Royer et al. 2021 REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2394 Further work showed that mixtures of the more degradable PHB with less degradable polymers such as PLA and polypropylene gave rise to micro- or nanoplastic particles, which tend to build up in the tissues of marine organisms (Kwon et al. 2023a, 2024). Table 1 provides highlights from studies that have considered the biodegradation of MCC, often in comparison with cellulosic fibers of various types. Other studies have considered various less-biodegradable classes of material, such as bioplastics (Bhagwat et al. 2020; Royer et al. 2023) and synthetic plastic items, including fibers and fabrics (Cooke 1990; Li et al. 2010; Zambrano et al. 2020; Kwon et al. 2021; Royer et al. 2021, 2023). Another aspect to be considered in this article is the different environments in which biodegradation is important. As shown in Fig. 2, a rough division of categories can be drawn based on relatively dry to water-saturated environments (e.g. soils, composting, and landfilling) vs. aqueous environments (e.g. fresh water, seawater, wastewater treatment). Note that although the figure illustrates the possibility of collecting methane that forms within landfills, such collection is often incomplete or may be absent. Further information about composting (Hubbe et al. 2010; Reyes-Torres et al. 2018; Ruggero et al. 2019; Wu et al. 2022) and wastewater treatment technologies (Hubbe et al. 2016; Srivastava et al. 2022; Wang et al. 2022a) has been published. Fig. 2. Seven contrasting environments in which biodegradation of cellulose fibers can be expected to have different rates and controlling factors. The figure is arranged such that the gentler environments, with correspondingly slower biodegradation, are towards the top, whereas more biodegradative environments, often with higher temperatures, appear towards the bottom. Though broader ranges of cellulosic material are considered in this review, the primary focus will be on lignin-free fiber-based products, such as cotton and bleached kraft fibers, the latter of which is the main component of most flushable sanitary paper products. The distinction can be important, since, as will be described in more detail later, lignin can substantially slow down biodegradation (Reyes-Torres et al. 2018; Wu et al. 2022).  Dry Wet → Soil Composting Wind Fan Metabolic heating Landfill Anaerobic degradation CH4 collection Rotifer 100 m Protozoa Bacteria Fungus Fresh Water Sea Water Anaerobic digester CH4 collection Waste- water Treated water Returned sludge Air injection Agitated and aerated basin Clarifier Excess sludge Aeration with activated sludge Waste- water Agitation Clarifier Air Sludge H2O Sludge REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2395 Synthetic plastic materials generally were not considered in the literature covered in this article. A general finding is that many such plastics show much lower rates of biodegradation, or even no measurable biodegradation under conditions that lead to substantial degradation of MCC and other cellulosic materials. For instance, Zambrano et al. (2019) reported about 4% biodegradation of polyester after about 245 days in an aqueous aerated system. Under the matched conditions, the biodegradation of cotton was 76% and MCC was 83%. Royer et al. (2021) compared seawater biodegradation based on measurements of fiber diameter. Polyester fibers showed a 5% decrease after 7 months of exposure, whereas lyocell regenerated cellulose fibers showed a 20% decrease after about one month. Li et al. (2010) reported about 13% biodegradation of polyester fabric under conditions giving 23% biodegradation of cotton under large-scale compositing conditions (ASTM D 5988-03). Royer et al. (2023) reported essentially undetectable levels of marine biodegradation of polylactic acid (PLA), polyethylene terephthalate (PET), and polypropylene (PP), under various marine conditions and times that gave substantial biodegradation of cotton, rayon, lyocell, and modal cellulosic fibers (e.g. about 50% to 70% degradation in 7 days and about 80% in 28 days). In a review article, Cooke (1990) draws a distinction between so-called biodegradable synthetic plastics, such as aliphatic polyesters, polyurethanes, some polyamides, polyvinyl alcohol, polyvinyl acetate, polyacrylates, vs. non-biodegradable ones, including polyolefins, polystyrene, and aromatic polyesters. Even if a plastic material is prepared from plant materials, as in the case of PLA, one should not automatically assume that it is biodegradable (Royer et al. 2023). Thus, Bhaghwat et al. (2020) urge testing of each material under the environments of interest, following available standards when possible. Various plant-based materials, such as starch, chitin, proteins, hemicelluloses, lignin, lipids, and natural rubber, generally fall outside of the primary focus of this article. Attention has been paid to these substances in other reviews, some of which are listed in Table 2. A general rule, which is supported by entries in this table, is that specific enzymes are needed, often in combination, to achieve effective biodegradation of each unique natural polymer. Table 2. Natural Polymers and Enzymes Associated with their Biological Degradation Polymer Type - Natural Associated Enzymes Selected Citations Starch Amylases De Souza & Magalhaes 2010; Farooq et al. 2021 Chitin Chitinases, proteases, chitin deacetylase; chitosanases, lytic polysaccharide monooxygenases Younes & Rinaudo 2015; Kaczmarek et al. 2019 Proteins Proteases Tavano 2013; Kim et al. 2014 Cellulose Endoglucanase, cellobiohydrolase, -glucosidase Teeri 1997; Horn et al. 2012; Wang et al. 2013a Hemicelluloses Xylanases (endo & exo), -xylosidase, - arabinofuranosidase, esterases Saha 2003; Girio et al. 2010; Houfani et al. 2020 Lignin Laccase, peroxidases Datta et al. 2017; Chio et al. 2019; Khan & Ahring 2019 Lipids Lipases, lipoxygenase Shah 2005; Reis et al. 2009 Natural rubber Oygenase, lipoxygenase, peroxidase Rose & Steinbüchel 2005 REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2396 Scope of the Problem The term “cellulose fibers,” which defines the focus of this article, generally will follow the literal meaning of the words, thus excluding cellulose derivatives such as cellulose acetate. Cellulose derivatives will be considered only briefly, to show how they contrast with either natural cellulosic fibers or regenerated cellulose fibers, such as rayon. A reason to focus on biodegradability of cellulose fibers at this time is that large amounts are routinely discharged to natural environments. As illustrated in Fig. 3, two of the most prominent sources are from the flushing of toilets and the discharge or rinse water from laundering. An average US citizen, in 2018, used 12.7 kg of toilet paper, whereas lesser per capita amounts were used elsewhere (Armstrong 2018). Table 3 summarizes reported information of the total amounts of cellulosic fibers discharged to wastewater treatment systems, with emphasis on toilet paper as a major source. As reported by Gupta et al. (2018), the relative amounts of cellulose in various wastewater and sludge specimens can be determined with high accuracy. Table 3. Reports of Cellulosic Fibers, Mainly Toilet Paper, Routinely Discharged to Wastewater Treatment Facilities or the Natural Waterways Highlights from Cited Studies Citation To test the biodegradability of “very large quantities” of cellulose fibers discharged to wastewater, the authors used a bag method, allowing for long periods of degradation. Cotton strings required over 70 days to fully biodegrade in water. Edberg & Hofsten 1975 Amounts of cellulose present in municipal wastewater, mainly attributable to toilet paper, was estimated to be about 400 thousand tons per year in Japan. Sedimentation was suggested as a way to separate and recover the fibers. Honda et al. 2000, 2002 Between 12% and 27% of incoming solids to a wastewater treatment plant consisted of cellulose. López Alvarez et al. 2009 Between 38% and 43% of incoming cellulose fiber material in a wastewater treatment plant still remained after the typical aerobic biodegradation process, depending on the thermal conditions. Ghasimi et al. 2016 Toilet paper was found to be the main source of chemical oxygen demand in sewage. Chen et al. 2017 Cellulose constituted about 31% and 33% of the total suspended solids in wastewater treatment facilities in the Netherlands and Canada. Ahmed et al. 2019 Cellulose represents about 25% of the chemical oxygen demand of a typical municipal wastewater treatment system. Khan et al. 2022 The content of cellulosic material in municipal wastewater was about 21 to 28% by mass, depending on the measurement method. Libardi et al. 2022 Likewise, Table 4 highlights studies that have helped to quantify amounts of textile cellulose fibers discharged to wastewater. Two factors that tend to promote detachment of fine particles, including some of the fibers, in the course of laundering are the agitation and the usage of detergents (Zambrano et al. 2019). As described in a recent review article (Hubbe et al. 2022), laundry detergents are designed to promote separation between fibers such as cotton and other attached solids. REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2397 Fig. 3. Illustrate of two major sources of cellulosic fibers in municipal wastewaters. Part of figure (washing machine) previously published as an original drawing by the author (Hubbe et al. 2022) Table 4. Reports of Cellulosic Fibers Discharged to Wastewater Due to the Laundering of Textile Items Highlights from Cited Studies Citation Reported that washing of a single garment can release over 1900 fibers. Ladewig et al. 2015 An average of 0.3% of the mass of garments was discharged in rinsewater from laundering. Hartline et al. 2016 A cumulative amount of ca. 0.33% of the mass of cotton garments was released during five sequential washing cycles. The amount released per cycle decreased and then stabilized at less than half the amount of the first cycle. Sillanpää & Sainio 2017 Cotton clothing released 0.02 to 0.44% of the mass of the garment during accelerated washing. Zambrano et al. 2019 >80% of the microfibers released from the washing of 50/50 polyester/cotton blended fabrics are cotton. Haap et al. 2019; De Falco et al. 2020 The greatest proportion of shed cotton fibers were those below 0.2 mm in length. Frost et al. 2020 Commercial nonwoven wipes and meltblown textiles were found to release 1 to 65 mg of microfiber material per gram tested in a standardized laundering test. They released about 4 mg/g microfiber material in a dry shaking test. Kwon et al. 2022 Textile microfibers (i.e. fibers small enough to be released during laundering) have been detected in waterways. Published findings are summarized. Smith et al. 2024 Recent research indicates the pervasive presence of both synthetic and natural microfibers in natural environments. Suaria et al. (2020) discovered fibers in 99.7% of samples collected across six oceanic basins, with the majority being dyed. Polymers Toilet paper Wastewater treatment Laundering of textiles Bleached kraft fibers Lint released during washing REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2398 identified were typical of textiles, including 8.2% synthetic, 79.5% cellulosic, and 12.3% of animal origin. Athey et al. (2020) reported that microfibers constitute 87 to 90% of anthropogenic particles in lake sediments, with 41% identified as modified cellulose. Indigo-dyed cotton, common in denim jeans, accounted for 12 to 23% of microfibers analyzed. Similarly, Miller et al. (2017) estimated that 50% of fibers collected from the Hudson River, USA, were non-plastic, with cotton fibers identified via FTIR. Challenges associated with these studies include the fact that the amounts of various fibers initially entering the water were not known. As will be discussed in this review, there are several feasible paths by which cellulosic fibers may reach natural environments, including waterways and eventually the sea, though the relative amounts are difficult to quantify. Wastewater treatment operations can be expected to partly biodegrade cellulosic fibers, and most of the rest will end up in sludge, which is often landfilled, composted, or applied to land as a soil amendment, as will be discussed later. However, one can expect a wide variation in the operational efficiency of wastewater treatment, or even its absence, in different regions and situations, considering different parts of the world, seagoing ships, and overflow of combined wastewater and stormwater systems during high volume events. In addition, some cellulosic fibers may come from careless littering, from wind-blown lint, and illegal dumping, all of which will be hard to quantify. In addition, uncertainties persist regarding the origin of these cellulosic fibers. Current high throughput spectroscopic techniques face challenges in distinguishing between wood-based, cotton, and regenerated cellulose fibers. It is worth noting that these studies often lack morphological evaluations of the cellulosic fibers to confirm their origin, highlighting the need for comprehensive analyses to better understand their sources and pathways into natural environments. Issues related to contamination can interfere with many kinds of identification methods. For instance, some investigators may be assuming that any dyed fiber must be cotton; however, dyes and fluorescent whitening agents may be present in wood pulp fibers. Circular Economy Issues While the main focus of this review article is on biodegradability, it is important not to lose sight of an emerging imperative for industrial processes to move in the direction of circularity (Corona et al. 2019). In other words, rather than seeking the best ways to “throw away” materials after their single or multiple uses, society needs to find ways to employ such materials as building blocks for making other valued items. For instance, there is increased interest in the reuse of textile fibers at the end of a garment’s or bedsheet’s useful life (Jia et al. 2020). There also has been consideration of recovering used fibers from toilet paper and their beneficial use for other purposes (Honda et al. 2002; Ruiken et al. 2013; Ghasimi et al. 2016; Ahmed et al. 2019; Cipolletta et al. 2019; Li et al. 2019, 2020; Liu et al. 2022). Such issues will be considered further later in this article. CELLULOSE BIODEGRADATION BASICS In a broad sense, biodegradation is the natural process by which cellulosic materials, including cotton and paper pulp fibers, are decomposed in either natural environments or during wastewater treatment and composting. At the very end of biodegradation, the main product will be carbon dioxide. However, as discussed in this REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2399 section, other final products such as methane can result if the materials are subjected to anaerobic conditions. Fiber materials may accumulate in various environments in cases where biodegradation is sufficiently slow. As noted earlier, the fibers may enter various environments by such means as industrial discharges (e.g. insufficient wastewater treatment), flushing (e.g. insufficient treatment of municipal wastewater), and careless discharges, including littering. Enzymes, which are complex protein structures, are the main catalysts by which cellulosic materials break down in natural environments and in wastewater treatment plants. These catalysts are synthesized by various organisms, mainly bacteria and fungi (Bhat and Bhat 1997; Esteghlalian et al. 2002; dos Santos et al. 2023). For degradation of cellulose fibers, the most important category is the cellulases, which will be considered next. Other enzymes can be important when the fibers contain hemicellulose, lignin, or possibly additional functional groups as a result of some kind of chemical derivatization or sizing treatment of the fibers. In addition, many of the wood-derived fibers present in municipal solid waste will be highly lignified and rich in hemicellulose. In nature, and in most wastewater treatment operations, the enzymes are supplied directly by the bacteria and fungi that happen to be present. Because cellulosic material can be regarded as food for such organisms, the populations of bacteria and fungi may proliferate, depending on the amounts of such resources that are present. For some industrial purposes, and also as a means of studying the underlying mechanisms, it is also possible to isolate and use specific enzymes, such as the cellulase enzymes that catalyze the breakdown of cellulose. Teamwork is an important theme to bear in mind when aiming for highly effective biodegradation, either in a wastewater treatment plant or in a natural environment. As will be shown, different classes of cellulases work together in a cooperative manner to bring about suitably rapid and substantial biodegradation of the cellulose (Wang et al. 2013a). Likewise, biodegradation of the hemicellulose and lignin each require multiple enzyme types working together to achieve efficient and effective results. In many cases, an optimized community of bacterial and possibly fungal organisms will have become acclimated to the cellulosic material present, wherein different microbial members of the community are specialized in the production of different enzymes (Peng et al. 2016; Lillington et al. 2020). Libardi et al. (2022) proposed the optimization of a cellulase mixture, using municipal wastewater as a medium, for effective biodegradation. Though such a strategy is bound to be effective, the usual practice is just to let nature take its course in the competition and proliferation of microorganisms to achieve a suitable overall effect with less direct involvement of technologists or treatment plant operators. In very general terms, it is well known that the presence of lignin tends to block access of cellulase enzymes to the fibers surfaces and that enzymatic degradation can be accelerated by increasing the accessible surface area of the cellulosic materials. However, as noted by Esteghlalian et al. (2002), it is still not possible to make predictions of enzymatic hydrolysis rates based on information about lignin levels and the capacity of the surfaces to adsorb enzymes. Cellulases Endo attack Figure 4 provides an overall scheme of cellulose biodegradation, consistent with current literature (Teeri 1997; Horn et al. 2012). In this figure, sets of parallel, straight black lines represent crystalline cellulose domains, whereas non-parallel parts with curves REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2400 in the lines represent non-crystalline nano-scale regions. Little circles with light blue filling represent non-reducing ends of cellulose chains, whereas back-filled circles represent reducing ends. Short, barbell-like features with a glycosidic bond connecting a non- reducing end and a reducing end symbol represent cellobiose. As shown, the endoglucanases (shown as bright green features) have the job of random cleavage of cellulose chains in the non-crystalline zones (Wang et al. 2013b). Such cleavage involves hydrolysis, which entails the addition of a water molecule. Splitting of the glycosidic bond with a water molecule results in formation of an -OH group on each side of the broken bond. Thus, they are especially effective at reducing the chain lengths within cellulosic materials. However, since typical cellulosic materials such as cotton and wood pulps have quite high levels of crystallinity, e.g. 45 to 87% (Salem et al. 2023), one can expect there to be a plateau molecular mass remaining, even after extensive endoglucanase action (Chang et al. 2021). That is because the portions of cellulose chains that lie within the crystalline domains generally will not be susceptible to attack by endogluconase, which is represented by the bright green features in Fig. 4. Fig. 4. Schematic diagram showing the roles of three classes of cellulase enzyme relative to the biodegradation of cellulose (adapted from Teeri 1997) Exo attack The exoglucanases (shown as CBH2 and CBH1 in Fig. 4) have the function of un- zipping and cleaving off small pieces, mainly cellobiose, starting from the cellulose chain ends, mainly at the surfaces of crystals. They can be advancing from either reducing or non-reducing ends of the chains; thus, two different subclasses of such enzyme are needed (Teeri 1997; Horn et al. 2012; Wang et al. 2013b). Evidence to support the pictorial view shown in Fig. 4 was obtained by Lee et al. (2000). They showed atomic force images of “tracks” left by cellobiohydrolase enzymes in the course of traversing the surfaces of cel- lulose fibers. By contrast, endoglucanase had the effect of smoothing the surfaces and peel- ing away the loose debris. Oxidative cleavage-type cellulases In addition to the well-known endo- and exoglucanase categories, as just described, a specialized type of cellulase has been reported to have the ability to hydrolyze intermediate points within the exposed crystalline regions of cellulose, thus creating new reducing and non-reducing ends of chains that can then be attacked by exoglucanases (Horn Non- reducing ends Endo- glucan- ases Crystalline region Crystalline region Reducing ends Cellobio- hydrolase II (CBH2) Cellobiose CBH1 -glucosidase → glucose REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2401 et al. 2012; Wang et al. 2013b). A key difference is that these oxidative endoglucanases do not need to extract the cellulose chains from their associated crystal phases to do their work. The cited work does not give evidence as to whether or not such enzymes play a role when biodegradation occurs in natural environments. Solution-phase Cellulase enzyme systems appear to have evolved in such a way as to be inhibited by the presence of their reaction byproducts in solution, e.g. cellobiose (Zhao et al. 2004). Such a strategy makes sense in terms of the survival of specific cellulase-producing microorganisms. The produced cellobiose presumably can be used as food for the microorganism itself, after the final hydrolysis to glucose. Thus, the species may benefit by a mechanism that slows down the usage of the remnant of solid cellulose in the mixture. The breakdown of the small fragments, such as cellobiose, is catalyzed by another main category of cellulases, the -glucosidases (Teeri 1997), which are represented in Fig. 4 as a bright orange item. The tunnel-like features in these enzymes require the cellobiose or other small cellulose oligomers to diffuse into the tunnel, whereby the glycosidic bonds can be cleaved. Because this class of enzymes does not break cellulose chains, it has been found useful in some modifications of textile fibers (Teeri 1997). This issue merits further research attention, since textile cellulose fibers that had been treated in this way might be more susceptible to biodegradation by other cellulase enzymes when they enter the environment. Fragmentation effects In addition to the hydrolytic effects of cellulases, it has been proposed that certain of them play a role in fragmenting the cellulosic material (Saqib and Whitney 2006). This type of effect is illustrated schematically in Fig. 5. The large dark green arrow, pointing in the leftward direction of the figure, represents this type of enzymatic action, which does not need to involve cleavage of bonds. The cited authors proposed that such ability can explain some of the differences in biodegradative ability of different cellulases, especially when attacking different kinds of cellulosic materials. Such observations are consistent with the findings of Wang et al. (2012), who observed general swelling of cellulose material in response to cellulase action. Presumably, an enzyme acting in the manner depicted in Fig. 5 could, at least for a time, increase the thickness of a cellulose particle in the course of bringing about fragmentation. Fig. 5. Schematic diagram suggesting a proposed fragmentation-inducing effect of certain en- zymes, which would be expected to help open up lignocellulosic structures at the nano-scale, thus promoting hydrolysis reaction by the same of other enzymes Fragmentation enzyme Endo- glucan- ases Cellobio- hydrolases REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2402 Biodegradation of different parts of the cellulose Having considered the different cellulase components separately, it next makes sense to envision how the different types of enzymes tend to focus their activity on different parts of a cellulose particle or fiber. General attack on the amorphous regions (not within crystalline zones) of cellulose in the fibers is brought about by endoglucanases (Hosseini and Shah 2011), which break glycosidic bonds at random intermediate points in the chains. The next category is the exoglucanases (i.e. the cellobiohydrolases), which begin their degradative work at the ends of cellulose macromolecular chains, mainly focusing on the crystalline zones (Wang et al. 2013b). It appears that such work is direction-dependent; some of the exoglucanases have the ability to start at the reducing ends of cellulose chains, whereas others start at the non-reducing ends. As these enzymes do their work, they break off small groups, usually as cellobiose (Teeri 1997; Medve et al. 1998; Homma et al. 2013b) and likely also some cellotriose (Medve et al. 1998). Depending on the goals of the treatment, different recipes of cellulase enzyme can be selected. Esteghlalian et al. (2002) proposed that when one’s purpose is to modify the fiber surfaces for specialized applications, then treatment with single types of cellulase, e.g. endoglucanase, might be advantageous. However, for purposes of general and efficient biodegradation of the whole material, a complete “multicomponent” cellulase combination is preferred. In addition, higher enzyme concentrations and times of treatment are recommended to achieve complete breakdown. For polishing (depilling or aging) of textile fabrics, a multicomponent cellulase is also recommended, but with a relatively low dosage and an optimized exposure time (Esteghlalian et al. 2002). Enzyme immobilization It has been widely reported that the progress of a cellulase macromolecule, relative to its work of breaking down cellulose, can be greatly slowed down if it becomes immobilized at surfaces (Huang et al. 2022a; Zhao et al. 2023). The phenomenon is widely referred to as nonproductive binding. In particular, it has been shown that such binding onto lignin surfaces can impede the action of those enzymes (Berlin et al. 2005). The phenomenon is illustrated schematically in Fig. 6. The black feature in the figure represents lignin, and the several cellulase items resting on the lignin are envisioned as being attached with enough energy such that they spend much of their time immobilized on those surfaces. In such cases, the binding has been attributed to non-specific adsorption that is favored by the more hydrophobic nature of lignin (Huang et al. 2022b). Evidence in support of the binding mechanism is provided by studies in which increased activity of cellulase was achieved by the addition of surfactant (Lin et al. 2015). Presumably, the surfactant can enable the release of cellulase from lignin and thereby free it to do its work on nearby cellulose structures. A further possible strategy to promote more effective cellulose breakdown has been to select cellulase strains having lower affinity for lignin surfaces (Berlin et al. 2005). Yet another approach has been to apply a sulfonate treatment of the fiber material, which is akin to mild sulfite pulping (Lou et al. 2013; Wang et al. 2013c; Huang et al. 2022b). Such treatment tends to render the lignin surface more hydrophilic and thus less prone to bind cellulase. REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2403 Fig. 6. Schematic illustration of the non-productive binding of cellulase to the more hydrophobic surface of lignin, which has the potential to arrest its interactions with cellulose Enzyme denaturing All enzymes are subject to gradual loss of function, i.e. denaturation, over the course of time, depending on such conditions as increasing temperature. Efforts have been underway to identify or develop thermo-stable cellulases, with the goal of speeding up the transformation of underutilized cellulose to sugar, which can be fermented to produce ethanol and other valuable biofuels or monomers to be used in organic synthesis (Patel et al. 2019). Certain enzymes, called extremophiles, are able to perform well outside of the typical thermal ranges of enzymes, though even those enzymes have their limits of heating, beyond which they break down rapidly (Daniel et al. 2008). Tamo et al. (2020) showed that such decline could be reduced by encapsulation of cellulase in alginate, thus immobilizing it. In addition, the hydrolytic effect was enhanced when the cellulase was encapsulated. Hemicellulose Biodegradation Cellulose fibers derived from wood, as is common in toilet paper for instance, will contain substantial amounts of hemicellulose, often in the range 10 to 25% in the delignified material (Duchesne et al. 2001; Neto et al. 2004). Though cotton is mostly cellulose, it can contain about 2% of hemicellulose (Kim and Ralph 2014). Compared to cellulose, the hemicellulose is low in molecular mass, having a molecular mass in the range of 10,000 to 40,000 g/mole (Dahlman et al. 2003; Bai et al. 2012). Considering that anhydroglucose, a common repeat unit in some hemicellulose, has a mass of 162 g/mol, these values correspond to degrees of polymerization (DP) in a range from about 62 to 247. By contrast, the DP of cellulose has been reported to be in the range 300 to 1700 in wood pulps and in the range 800 to 10,000 in cotton and some other plants (Klemm et al. 2005). The amorphous nature of hemicelluloses and the presence of carboxylic acid functional groups cause them to swell in water, leading to hydrogel behavior (Gabrielii et al. 2000). The hemicellulose can be expected to be accessible to enzymes, which require water-filled passages in the size range of one or more nanometers, depending on the specific case (Mäki-Arvela et al. 2011). Whereas cellulose requires just three classes of enzymes, complete hemicellulose degradation can require more, due to a somewhat more complex chemical composition (Houfani et al. 2020). The complexity of hemicelluloses, leading to several different points of potential enzymatic attack, is illustrated in Fig. 7. The catalyzed Lignin Non-productively bound enzymes Cellulose Cellobio- hydrolases Endo- glucan- ases REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2404 chemical reaction, in those cases where a pointer is shown acting on an oxygen atom, generally can be described as the addition of water, i.e. hydrolysis. Fig. 7. Sketch of reported points of enzyme attack onto hemicellulose structures. The orange pointer suggests some main points of enzymatic attack, including various glycosidic bond types and deacetylation. The text labels in the figure refer to different sugar monomer units or functional groups present in natural hemicellulose structures. Aquatic biodegradation was carried out by Kwon et al. (2021), comparing three types of hemicellulose with two types of lignin and with MCC as the point of comparison. Results are provided in Fig. 8. Fig. 8. Aquatic biodegradation compared for three hemicellulose specimens, two lignin specimens, and MCC (Kwon et al. 2021). Permission to reuse figure was from the copyright owner, Springer. The inoculum was biosolids from a wastewater treatment plant. Hardwood hemicellulose example O O OO O O O O O O OHO HO HO HOOH OH OH O O OH OH OCH3 COOH (1-4) (1-2) 4-O-methyl--D-glocuronopyranose Acetyl -D-xylopyranose Softwood hemicellulose example O O O O O O O O O O O OH OH HO HO HO HO O O OHHO OH(1-6) OH OH OHOCCH3 O O O OHHO OH OH OH OH OH -D-glucopyranose -D-mannopyranose -D-galactopyranose (1-4) (1-6) Acetyl -D-galactopyranose Acetyl REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2405 As shown, all three of the hemicellulose specimens achieved somewhat higher bi- odegradation after 27 days (80 to 90%) in comparison to MCC (78%). These findings are consistent with the relatively hydrophilic and non-crystalline nature of hemicellulose, as described above. By contrast, conventional MCC has been reported to have a degree of crystallinity in the range of 48 to 96% (Ardizzone et al. 1999; Eichhorn and Young 2001; Ibrahim et al. 2013). Lignin Biodegradation As was shown in Fig. 8, there was a large contrast between the lignin specimens and both MCC and the hemicellulose specimens, relative to the observed extents of biodegradation in an aquatic environment. The two lignin specimens showed about zero to 4% biodegradation, in comparison to over 78% for the other specimens under the conditions of testing in that case. These differences can be tentatively attributed to the relatively dense and hydrophobic nature of lignin. It should be noted that there is no lignin at all in cotton, and the level is close to zero in common tissue paper products, for which the fibers are obtained from kraft pulping and bleaching to remove the lignin. However, there can be roughly 20 to 30% of lignin content in various species of wood and various non-wood biomass sources. Fungi are the main source of lignin-biodegrading enzymes in natural environments (Carvalho et al. 2009). When wood-based papermaking pulp is prepared by mechanical refining, the cellulose fibrils are often protected by a layer of lignin. This is especially the case for thermomechanical pulps, for which in ingoing wood chips are treated with steam under pressure ahead of the mechanical refining process. At the temperatures employed, above the ambient boiling point of water, the lignin becomes deformable, such that it becomes the point of separation when the fibers are mechanically pulled apart from each other (Irvine 1985; Mattsson et al. 2021). Such a manner of separation leaves the resulting fibers surrounded by a layer of lignin. In theory, treatment with lignin-degrading enzymes, such as manganese peroxidases and laccases (Bugg et al. 2011), can enable subsequent action by cellulases (Sun and Cheng 2002; Huang et al. 2022b). However, the hydrophobic nature and complex, random structure of lignin means that the enzymatic breakdown of lignin tends to be relatively slow (Datta et al. 2017; Janusz et al. 2017). Fig. 9. Representation of some major types of lignin-degrading enzymes Intact Lignin Laccase, a phenol oxidase Free radicals O2 2H2O Degraded Lignin Several heme peroxidases Lignin peroxidase Manganese peroxidase Versatile peroxidase H2O2 H2O2 Intermediate radicals Mediators Mn(II) → Mn(III) Chelated Mn(III) Second mediator Reactions with radicals REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2406 Figure 9 illustrates the way in which communities of different enzymes can participate in the biodegradation of lignin (Javaid et al. 2019). Of the major classes of ligninolytic enzymes, laccase serves the function of generating oxidative free radicals by the conversion of oxygen to water. Meanwhile, parts of lignin’s complex structure are subjected to three main groups of heme-type peroxidases, which employ hydrogen peroxide to oxidize Mn(II) to Mn(III), which is temporarily held in chelated form. The accumulated radical species undergo further reactions, with the help of mediators, leading to breakdown of connecting linkages within the lignin structure. In addition to blocking the access of cellulase enzymes to cellulose, the presence of lignin also can lead to non-productive binding of the cellulase, as noted already (Li et al. 2022). When a cellulase enzyme is essentially immobilized onto the relatively hydrophobic surface of lignin, it cannot contribute effectively to cellulose decomposition. Products that do not have lignin, such as cotton, will not have this issue affecting their biodegradation. Recalcitrance in General Natural wood-based fibers generally show a resistance to biodegradation, i.e. a recalcitrant nature, that goes beyond what can be attributed to each of its main components individually. Factors that can help explain this recalcitrance, in addition to the crystalline nature of the cellulose, will be considered in more detail later in this article. In general terms, the factors can be listed as hydrophobicity (mainly due to the lignin), density of the material (resulting from the details of biosynthesis), and the presence of covalent bonds between lignin and the polysaccharides, especially the hemicellulose (Tarasov et al. 2018). It should be noted that both cotton and bleached kraft pulp fibers are generally free of the concerns just mentioned, which is consistent with their only moderate resistance to biodegradation. By contrast, the complex, multicomponent nature of natural woody materials has been proposed as a main contribution to difficulty or slowness in biodegradation (Carvalho et al. 2009). Wood extractives, which include lipids, waxes, fats, phenolic compounds, and alkaloids, are quantified by extracting wood – often in the form of wood chips – by means of nonpolar solvents (N’Guessan et al. 2023). The levels of wood extractives in the wood chip types commonly used for production of papermaking pulps are generally rather low, e.g. about 1 to 4% for trees grown in temperate climates (Shebani et al. 2008). However, due to their hydrophobic nature, it might be expected that they could tend to either non- productively bind cellulase enzymes or to cover the fiber surface, thereby blocking the action of those enzymes. It has been argued, however, that by the time the wood has been chemically pulped and bleached, almost all of the extractives have been removed (Liu et al. 2012). In fact, it has been suggested that removal of the extractives may play a significant role in enabling the work of cellulase enzymes (Auxenfans et al. 2014). Likewise, Wang et al. (2018) concluded that structural features of the biomass are more important than factors such as extractives content in affecting rates of enzymatic hydrolysis. The waxes that are present on the outside of some cotton items, especially before scouring (Chung et al. 2004), are likewise hydrophobic, thus raising an expectation that they might tend to bind cellulase enzymes or block their access to the cellulose. REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2407 ENVIRONMENTS Rates and extents of biodegradation of cellulose fibers depend on many factors, and these can be grouped together using the labels environments, fiber-related factors, and conditions that can be adjusted by technologists. These will be considered in this and the following two main sections. Many studies have been conducted regarding the biodegradability of cellulosic fibers in wastewater, especially during processes of wastewater treatment. Other environments of concern include seawater, soil, landfill facilities, and composting systems. The form of cellulose input to each system will vary, with a high variety of lignocellulosic materials disposed of in landfills (chemical and mechanical pulps, wood) and treated in composting systems (i.e., yard waste). Wastewater and its Treatment Facilities Wastewater When cellulosic fibers are flushed or when they are discharged during the rinse cycle of a washing machine, they are essentially in a fresh-water environment. But as the suspended matter travels through a drainage system, the conditions may not be optimized to favor their biodegradation. Nagamine et al. (2022) considered the analogous environment of river water. The cited authors reported that such an environment was conducive to initial fragmentation of the cellulose, but complete biodegradation was not necessarily achieved. The degree of biodegradation in river water increased with the passage of time, though the rate of biodegradation gradually decreased over the course of 30 days, which was the study period. Based on the results of biological oxygen demand tests, the river water environment was much more conducive to biodegradation than either brackish water or seawater, in decreasing order. When the results were analyzed based on weight loss, there was less difference. The study compared ramie, mercerized ramie, and fully regenerated cellulose fibers. Wastewater treatment in general The first step in a typical wastewater treatment operation involves settling by gravity, i.e. primary clarification. It can be expected that a majority of the cellulosic fibers present in the incoming effluent will have been removed from the water already in such an operation prior to any aerobic or anaerobic stage of treatment. Thus, Ahmed et al. (2019) found that about 80% of cellulose present in the influent to a typical aerobic wastewater treatment plant was physically removed by a primary clarifier operation, upstream of the activated sludge operation. The initial separation from the water phase is settling, by gravity. This usually happens within a wide, circular tank of wastewater (the clarifier), in which the incoming flow enters at the center, and the clarified water is collected as it overflows at the outside edges of the tank. The primary sludge, after it has settled to the floor of the clarifier, is thickened first by raking and then by pressing. The common fate of such primary sludge is landfilling, though land application is also used (Chynoweth et al. 1992; Wang et al. 2008). For example, it has been reported that about half of the wastewater sludge residuals from kraft pulping are placed in landfills, with land application making up much of the remainder (Meyer 2022). Because primary clarification operations depend on such fiber attributes as density and size, one can expect roughly equal efficiency of clarification for various cellulose fibers originating from sanitary tissues, textiles, or other sources. REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2408 Relative to the potential biodegradation of cellulose fibers, an important aspect of a wastewater treatment facility is whether the biological treatment stage employs an aerobic or an anaerobic treatment stage (Hubbe et al. 2016). Each of these options can allow for at least some cellulose biodegradation, but the operations are quite different, as described next. Aerobic activated sludge wastewater treatment For both municipal and industrial wastewaters in the US, activated sludge systems, using aeration, are commonly used to reduce the biological demand (BOD) before discharge of the treated water (Hubbe et al. 2016; Liu et al. 2022). Since cellulosic matter in wastewater contributes to the BOD, there has been an expectation that such treatment ought to biodegrade cellulosic materials. A standard BOD test measures the consumption of oxygen during the microbial metabolism of an aqueous sample (sometimes with suspended plant materials) over a period of five days. As shown by the examples highlighted in Table 5, it has been found that such biodegradation is usually only partial in the case of cellulose fibers. Thus, results of standardized BOD tests generally cannot be assumed to include more than a fraction of the cellulose that is present in a specimen. As noted in 1975 by Edberg and Hofsten, full decomposition of cellulose fibers may require several weeks of retention time before the remaining secondary sludge from the biodegradation process is settled, thickened, and sent to a landfill (Hubbe et al. 2016). In practice, wastewater treatment facilities are run in such a way as to emphasize the quality of outgoing water rather than minimizing the quantity of sludge, which would include cellulose. Thus, the undegraded portion of cellulose, following a cycle of aerobic wastewater treatment, is likely to be included within thickened sludge that is hauled to a landfill or land applied. Based on most of the data in Table 5, activated sludge treatment can be expected to decompose and remove 60 to 90% of the cellulose remaining after the primary (settling) stage. Table 5. Highlights from Studies on the Extent of Cellulose Fiber Biodegradation in Aerated (Activated Sludge) Wastewater Treatment Facilities Highlights from the Study Percent Degraded Citation 96 h at ~ 54 degrees F in aerobic sludge: 96 h at ~ 74 degrees F in aerobic sludge: 19.9% 87.7% Hurwitz et al. 1961 Aerobic treatment for 70 days or more 100% Edberg & Hofsten 1975 Activated sludge treatment for 4 to 5 weeks 60% Verachtert et al. 1982 90 days, for cotton, ramie, and rayon fibers 30 to 60% Niu et al. 2012 Conventional 6 to 7 day activated sludge treatment 70 to 90% Ahmed et al. 2019 Cotton & rayon yarns, evaluated after 15 to 30 days >70% Zambrano et al. 2020 Various kinds of cellulosic fibers, 27 days 46 to 90% Kwon et al. 2021 Aerobic wastewater treatment for 3 or 15 days 78 to 90% Kim et al. 2022 Cotton microfibers, tissue, flushable wipes, MCC 60 to 86% Smith et al. 2024 Smith et al. (2024) compared the aerobic environments associated with wastewater treatment plants, lakewater, and seawater. Their results corresponding to the freshwater environments (wastewater treatment and freshwater conditions) are given in Figs. 10 and 11, respectively. As shown, the cotton microfibers (those likely to be released from textiles) achieved the highest levels of biodegradation under each of the conditions of testing, reaching about 85% and about 96%, respectively. Under the aerobic wastewater treatment REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2409 conditions, the MCC relatively quickly (over about 20 days) reached about 60% biodegradation, and then it remained at that level until the end of testing (105 days). By contrast, the tissue paper and the flushable (cellulose) wipes exhibited an initially slower but more persistent biodegradation, eventually surpassing that of the MCC under the wastewater treatment conditions. A likely explanation for the different rate behavior of the MCC is that though it has a smaller particle size, which can favor its biodegradation, it also typically has a higher degree of crystallinity, which will tend to slow down the process. Under lakewater conditions, the tissue paper, flushable wipes, and MCC had generally similar trends. The apparent negative values for biodegradation of the non-flushable wipes under lakewater conditions may be tentatively attributed to algal growth. Such growth might account for an increase, rather than a decrease in mass during exposure to lakewater. Fig. 10. Biodegradation results for various commonly flushed items under conditions of wastewater treatment (Smith et al. 2024). Permission to reuse figure obtained from R. A. Venditti, copyright holder. The PP wipes were mainly comprised of polypropylene but also contained 28% of cellulosic fibers. Fig. 11. Biodegradation results for various commonly flushed items under lakewater conditions (Smith et al. 2024). Permission to reuse figure obtained from R. A. Venditti, copyright holder. The PP wipes were mainly comprised of polypropylene but also contained 28% of cellulosic fibers. REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2410 Anaerobic wastewater treatment Though it requires a higher capital investment, there is interest in anaerobic wastewater treatment systems due to their tendency to yield less sludge that needs to be hauled away (Chan et al. 2009), and also the fact that such systems produce methane or hydrogen (Shen et al. 2015), which can be captured and burned as fuel. The mechanisms involved in anaerobic biodegradation of cellulose and other components of biomass have been reported (Li et al. 2018; Peces et al. 2018). Peces et al. (2018) showed that regardless of the composition of inoculants at the start of anaerobic digestion, over time the microbial community within bioreactors tended to converge in a predictable, repeatable way. In other words, the evolution of community composition can be viewed as deterministic rather than resulting from differences in starting inoculum conditions. On the other hand, anaerobic biodegradation of cellulose has been shown for specific populations of microbes, such as those in the rumens of cattle (Zhang et al. 2017). Li et al. (2018) showed that the relative order of biodegradation, under anaerobic conditions, was hemicellulose > cellulose > lignin, except that cellulose was the most favorable source when the goal is to produce methane. A study by Yu et al. (2012a) showed that the anaerobic biodegradation of microcrystalline cellulose (MCC) proceeds by development of channels in the size range of 400 to 500 nm within the MCC. Table 6 summarizes some findings from such systems. Although some of the numbers shown in Table 6 may appear favorable relative to aerobic systems, Edberg and Hofsten (1975) pointed out that long treatment times are more commonly employed in anaerobic treatment systems. Thus, the size of the equipment may have to be suitably scaled up relative to aerobic treatment to accommodate given amounts of flows and amounts of incoming solids to be treated. However, operating costs may be lower than in aerobic systems, since it is not necessary to pump air or to use fountains or sprays. Toilet paper typically exhibits a lower biochemical methane potential compared to mixed food waste (Cho et al. 1995; Naroznova et al. 2016), which can be attributed to its high cellulose content. Despite this, toilet paper can be effectively co-digested alongside food waste and human feces without diminishing the overall methane yield. Such methane is regarded as beneficial, since it can be fully captured and used as fuel or in other applications. This approach has been shown to be feasible for valorizing the primary organic wastes generated in households (Kim et al. 2019). Table 6. Highlights from Studies on the Extent of Cellulose Fiber Biodegradation in Anaerobic Treatment Facilities Highlights from the Study Percent Degraded Citation Sulfite pulps in various anaerobic sludge systems for 50 to 125 days 70 to 95% Edberg & Hofsten 1975 Cotton anaerobically digested as sludge for up to 35 days 55 to 75% Verachtert et al. 1982 Different materials from a pulp & paper mill compared from various literature sources and time periods 30 to 90% Meyer & Edwards 2014 Various papermaking pulps, based on CH4 production within about 400 days 90 to 95% Wang et al. 2015 Toilet paper ~ 7.5 days in a bioreactor making CH4 100% Chen et al. 2017 REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2411 Seawater Biodegradation of Cellulose Although the world’s seas represent a huge area, and a huge volume, there are some common features, such as salinity and pH, which remain relatively constant. On the other hand, the sea contains varying temperatures. In particular, the cold temperature and absence of light deep in the sea can be expected to slow down biological processes. Table 7 lists highlights from studies dealing with cellulose biodegradation in real or simulated seawater. As shown in the table, wide ranges of biodegradability have been reported for cellulose fibers in seawater. Studies involving matched tests in both fresh water and seawater have indicated substantially lower biodegradation in the seawater (Zambrano et al. 2020; Nagamine et al. 2020; Miyaji et al. 2023). Possible reasons for the difference include possible inhibition of enzymatic actions due to salinity (Miyaji et al. 2023), or maybe a lower availability and concentration of cellulase enzymes in ocean environments. Table 7. Highlights from Studies on Cellulose Fiber Biodegradation in Seawater Highlights from the Study Percent Degraded Citation Cotton, rayon, & MCC for 35 days 46 to 71% Zambrano et al. 2020 MCC in seawater, 30 days 85% Royer et al. 2021 Cellulose “readily degradable” in seawater No report Wang et al. 2021 Ramie, mercerized ramie, and rayon 30 days, BOD 3 to 14% Nagamine et al. 2022 Emphasis on comparing lab vs. field data 30 to 100% 5 Gyres Inst. 2023 Cellulose powder (presumably MCC) for 30 days 12% Miyaji et al. 2023 Bioreactor for 28 days; cotton & regenerated cellulose 76 to 82% Royer et al. 2023 Cotton microfibers, tissue, flushable wipes, MCC 70 to 78% Smith et al. 2024 Tests by the 5 Gyres Institute (2023) showed essentially complete biodegradation of paper straws after about 16 weeks in a marine environment. However, tests of bamboo utensils (forks) showed only about 30% biodegradation in 64 weeks. It is not reported, but it is possible that the commercial tableware listed above may have contained substances in addition to cellulose or bamboo. It follows that these cited results will need confirmation. Fig. 12. Biodegradation results for various commonly flushed items under seawater conditions (Smith et al. 2024). Permission to reuse figure obtained from R. A. Venditti, copyright holder. The polypropylene (PP) non-woven wipes had a main component of polypropylene but also contained 28% cellulose. REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2412 Figure 12, which features biodegradation results from seawater exposure of various materials, shows a strong contrast between those products that were cellulose based, in comparison to the non-woven wipes, for which the main component was polypropylene fibers (Smith et al. 2024). The cellulosic products, which included cotton microfibers, tissue paper, microcrystalline cellulose, and flushable wipes made from cellulose fibers, all were between 30 and 50% degraded after five days, followed by more gradual degradation up to about 30 days, and then a stagnation in the degradation process. Soil Biodegradation of Cellulose Due to the possibilities of littering and airborne transportation of dryer lint, etc., substantial quantities of cellulose can become subject to degradation in natural soils. Standard evaluation protocols are available (Tyagi et al. 2022). Table 8 features highlights from studies dealing with biodegradation in soil. Table 8. Highlights from Studies on the Extent of Cellulose Fiber Biodegradation in Soil Specimens and Key Aspects of the Study Percent Degraded Citation Films of regenerated cellulose; weight loss 30 days; kraft paper 70% 55% Zhang et al. 1996a Cotton and rayon textiles evaluated after 14 days soil burial, based on tensile strength ~ 100% Salerno-Kochan et al. 2001 Cotton evaluated as a control relative to Ag-treated cotton specimens; 12 days soil burial; loss of DP 10% Klemencic et al. 2010 Textile fabrics, 90 days soil burial 23 to 28% Li et al. 2010 Cotton evaluated after 12 days soil burial based on DP loss 20% Simoncic et al. 2010a Softwood mechanical pulp, 14 days; Other wood pulp 20% 57% Dobrin et al. 2012 TEMPO-oxidized NFC (an experimental material) with different counter-ions for 12 days 2 to 100% Homma 2013a All-cellulose composites formed from rayon after 70 days of soil burial 38 to 73% Kalka et al. 2014 Analytical grade cellulose after 29 days in soil 84 to 88% Mistriotis et al. 2019 Cellulose film regenerated in ionic liquid with most of degradation within three weeks ~100% Zhao et al. 2019 Cellulose film regenerated from an ionic liquid completely biodegraded in soil. Evaluations done after 7 and 14 days 100% Ai et al. 2020 Bacterial cellulose film after 3 and 7 days of burial 50 to 100% Zahan et al. 2020 Numerous natural cellulosic fibers, with cotton showing the highest soil biodegradation in 32 days 60 to 100% Margariti 2021 Cellulose hydrogel nanocomposites were judged to be fully biodegradable in soil. ~ 100% Das et al. 2023 Tests by the 5 Gyres Institute (2023) showed that test conditions affect the results of biodegradability testing. The study considered six types of natural environment, to which the specimens were exposed. The test locations were Maine, Florida, and California, and in each case Coastal marine environments were compared with terrestrial environments relative to their effects on biodegradation. Weight loss, after exposure, gentle cleaning, and drying, was used as the measure of biodegradation. Fragmentation of the specimens was REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2413 judged visually. Key factors were found to be soil type, temperature, and moisture content. The synthetic plastics polystyrene and polyethylene showed essentially no biodegradation over 32 weeks, whereas paper straws were in a similar category to biodegradable bioplastics. Landfill Substantial quantities of cellulosic materials are sent to landfills. Milbrandt et al. (2024) estimated that in 2019, 110 million tons of used paper and cardboard were managed domestically in the US, and that approximately 56% was landfilled, 38% was recycled, and 6% was combusted. The authors noted that the landfilled waste represents a loss of value, and that recycling and energy production (by combustion) can be much better options. Johnson et al. (2022) estimated that 11.6 million metric tons of cotton waste are generated annually during production activities in the cotton mill. The authors advocated non- traditional end uses, including biofuels and composites, as alternatives to landfilling. Problems inherent in landfill operations include a slow rate of biodegradation (De La Cruz and Barlaz 2010). Biodegradation rates for all materials including cotton textiles increase with moisture content. Decay rate constants for municipal solid waste were estimated to be 0.02, 0.04, 0.08, and 0.12 yr-1 (proportional amount per year) for dry, average, wet, and bioreactor conditions, as defined in De La Cruz and Barlaz (2010). In addition, different portions of the cellulose-based content of a landfill may remain undecomposed, depending on the material (Barlaz 1998). Undecomposed fractions of cellulosic materials, based on kg C per dry kg of waste, rose in the order of office paper (0.05), food waste (0.08), old corrugated containers (0.26), coated paper (0.34), and old newspapers (0.42), among others. Though methane is evolved from landfills, the process occurs over years to decades, and not all of the generated methane will be collected. Methane collection efficiencies, over a 100-year period, have been estimated to range between about 64% to 88%, when assuming various scenarios corresponding to practices in the US (Barlaz 2009). Collection efficiency may be lower, depending on the age of the facility, its location in the world, and local regulations. Compost Composting can be a practical way to stabilize various biodegradable wastes to a form that can be added to soil with beneficial effects, such as moisture retention (Briassoulis et al. 2010; Hubbe et al. 2010). Composting can be defined as the aerobic biodegradation of organic materials under engineered conditions. Heat generated by metabolism during the aerobic degradation typically results in increased temperature within the pile. Though such heating often accelerates the process, temperatures above about 60 C can lead to self-sterilization (MacGregor et al. 1981). A distinction can be made between industrial composting conditions, in which the interior of the pile rises in temperature to about 60 C, compared to home composting, in which such temperature rises may be lower or in doubt. Table 9 lists highlights from studies in which cellulose fibers and related materials were subjected to industrial composting. With the exception of a few studies showing very high degradation levels of nanocellulose films and certain regenerated cellulose films, the extents of cellulose degradation generally fell within a range of about 30 to 80%. Within such ranges, some of the highest levels were obtained in systems that had been inoculated with bacteria, and sometimes also with fungal treatment. In general, the rates of degradation have been reported to decline with the passage of time. REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2414 Table 9. Highlights from Studies Dealing with the Extent of Cellulose Fiber Biodegradation under Industrial Composting Conditions Specimens and Key Aspects of the Study Percent Degraded Citation Diverse types of paper in 45 days 36 to 79% López Alvarez et al. 2009 Cotton t-shirts treated with a fabric softener degraded faster than untreated cotton after 90 days of composting. 50 to 77% Li et al. 2010 Filter paper, MCC, biofilms, nanocellulose, etc., were evaluated over 66 days, with most of the degradation occurring during the first 30 days. 70 to 100% Vickman et al. 2015 Bacterial inoculation increased the breakdown of cellulose in compost. Most biodegradation took place during the first 20 days, with slower degradation continuing to the end of the study at 36 days. 30 to 70% Zhao et al. 2016 Inoculation increased cellulose breakdown during composting. Higher rates of cellulose breakdown were observed up to 18 days of composting, followed by slower rates. 30 to 63% Zang et al. 2018 Cellulose films prepared from ionic liquid had been fully degraded after 2 days of composting. Cellophane was 90% hydrolyzed, and wet-strength paper was 80% hydrolyzed within the same period. 100% Leppanen et al. 2020 Bacterial community enhancement promoted cellulose degradation and humus formation. 75 to 80% Wang et al. 2022b Bacteria and fungi worked synergistically; however lower biodegradation was observed for hemicellulose (50%) and lignin (21%) than cellulose. 70% Han et al. 2023 Cotton fabric specimens composted for 77 days under laboratory conditions were biodegraded by 18% to 62% and showed no effect related to various indigo dyes. 18 to 62% Alwaya et al. 2024 Addition of denim to the compost mixture did not have a notable effect on the rate of composting over the course of 77 days; however, those specimens containing non-cellulose fibers left contaminants at the end of composting. Close to 100% Schwarz et al. 2024 A delay in cellulose biodegradation can result when other more degradable substrates (e.g., starch) are present (López Alvarez et al. 2009). The progress of composting can be expected to be most favorable when the C:N ratio is in the range 25:1 to 50:1 and when there is also a sufficient amount of phosphorus and moisture (Hubbe et al. 2010). When the mixture is too rich in cellulosic materials, the C/N ratio will be too high for optimum composting. FIBER-RELATED FACTORS The subsections below will consider classes of factors that have been reported to affect the rate and extent of the biodegradation of cellulose fibers under a variety of conditions. Factors related to the fibers will be considered here, namely the fiber type, the REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2415 sizes of the cellulosic entities, effects of processing of the fibers, the degree of crystallinity, and various treatments of the fiber surfaces. Type of Cellulose Fiber or Particle Relatively few researchers have attempted to answer questions such as “how does the biodegradability of one kind of fiber compare to that of another kind of fiber?” The work of Kwon et al. (2021) carried out such comparisons in aquatic environments. Results in Fig. 13 show that beached hardwood kraft achieved the highest extent of biodegradation, about 90%, which was even higher than that of MCC (78%) in the course of 27 days in fresh water. It is worth noting that not only does the chemical pulping process remove the hard-to-biodegrade lignin component, but it also renders the fibers porous in the range 2 to 50 nm (mesoporous) (Stone and Scallan 1968), thus allowing better access of enzymes to the cellulose. Next came bleached softwood fibers (74%), which also have a mesoporous nature. The slower biodegradation of the softwood fibers compared to hardwood fibers, is consistent with a larger fiber size. Unbleached fibers from linerboard took longer to start the biodegradation process, which might be attributed to the presence of considerable lignin content in the unbleached pulp used to make such products. Mechanical pulp and material from newsprint were found to have the slowest rates of biodegradation, which might be attributed to the fact that such pulps have the highest lignin content. Fig. 13. Extent of biodegradation of different types of wood-derived pulp fibers (bleached kraft pulps from hardwood and softwood (SBSK = southern bleached softwood kraft), unbleached kraft pulp from linerboard, mechanical pulp and such pulp obtained from newsprint paper, all compared relative to MCC (Kwon et al. (2021). Permission to reuse figure was from the copyright owner, Springer. Mizutani et al. (2002) compared the extent of enzymatic degradation of cotton fibers to that of MCC. The extent of biodegradation of the MCC was higher by a factor of 1.7 in the absence of surfactant and by a factor of 2.1 in the presence of the surfactant. The type of MCC particles used in the studies had a nominal size of 50 µm. Smith et al. (2024) compared the biodegradability of cotton microfibers, tissue paper, flushable wipes, polypropylene-based wipes, and MCC under the conditions REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2416 associated with aerobic wastewater treatment, lakewater exposure, and seawater exposure. Their results for these three environments are summarized in Table 10. As shown, the cotton microfibers typically showed the greatest degradation, except that in seawater the MCC was slightly higher. High, but intermediate biodegradability was observed for the tissue paper and the flushable (cellulose) wipes, except that the flushable wipes were superior to the tissue paper and MCC in the lakewater conditions. The polypropylene-based wipes consistently achieved the lowest biodegradation, even achieving negative numbers as a result of tests done in lakewater. Positive numbers can be regarded as evidence of attachment of organic matter, such as algae. Table 10. Comparative Extents of Biodegradation of Commonly Flushed Materials after Exposure to Conditions of a Wastewater Treatment Plant, Lakewater, and Seawater (Smith et al. 2024). Samples Wastewater Treatment (110 days) Seawater (38 days) Lakewater (50 days) Mean bio- degradation Statistical groups Mean bio- degradation Statistical groups Mean bio- degradation Statistical groups Cotton microfibers 88.2% b 75.8% a, b 96.8% a Tissue paper 78.6% c 72.7% b, c 58.2% c Flushable wipes 75.8% a, b, c 75.1% c 75.3% b PP-based wipes 18.2% d 22.7% d -14.0% d MCC 94.3% a 79.0% a 61.7% c Note: Materials with different letters for statistical groups were statistically different. The statistical groups were relabeled to match the order of biodegradability. Inherent Differences in the Cellulosic Material To begin to explain the observed differences in the extents of biodegradation of different types of cellulosic entities, as shown in the previous subsection, it can be hypothesized, first of all, that the observed differences in biodegradation are due to some inherent differences in the materials. In particular, it can be proposed that the degree of crystallinity in the cellulose can be a contributing factor. Likewise, it might be proposed that biodegradation will be affected by the proportion of lignin or the proportion of hemicellulose in the specimen. Crystallinity The research question to be considered here is whether the literature supports the idea that the crystalline nature or the degree of crystallinity play a governing role relative to rates or extents of biodegradation of cellulose. Strikingly high resistance to enzymatic breakdown was reported in a study of tunicate cellulose (Cheng et al. 2020). As reported by these authors, tunicate cellulose has an especially high degree of crystallinity (circa 94%). They observed only 7.8% hydrolysis after 96 hours of biodegradation. By contrast, 83% of high-purity cellulose obtained from kraft pulping (i.e. alpha-cellulose) was degraded over 72 hours under similar conditions. Amorphous cellulose exhibited even faster and more complete hydrolysis, approaching 100% hydrolysis in just 10 hours. Such findings can be rationalized based on the explanations given earlier for the functioning of REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2417 the main categories of cellulase. Thus, if it is assumed that endoglucanases are ineffective in the crystalline regions and that exoglucanases begin their work only from the ends of cellulose chains, then cellulose having a high crystallinity would be expected to reduce the extent of biodegradation. Earlier work by Sazaki et al. (1979) showed that the biodegradability of cellulose could be greatly facilitated by its dissolution and regeneration, using various chemical systems. The regenerated cellulose specimens, some of which were textile fiber material, all were completely hydrolyzed within 48 hours by a fungal cellulase mixture. By contrast, cryo-milling of the native cellulose yielded only a modest increase in biodegradation (increasing the hydrolysis extent from 26% to 36%) within that time period. Though such results show clear differences, three things need to be considered. First, the final crystal form of the regenerated cellulose will have been changed from the native cellulose I to cellulose II in the regenerated cellulose specimens. In the native crystalline form, all of the chains within cellulose are facing the same direction, whereas in cellulose II, each adjacent chain faces in the opposite direction from end to end. Second, the degree of crystallinity of regenerated cellulose is often lower than it had been in the native form (Armir et al. 2021). Third, some decrease in degree of polymerization can be expected to result from the dissolution and regeneration processes (Liu et al. 2011; Dong et al. 2020). Zhu et al. (2008) compared cellulose specimens that had been decrystallized by ball milling to different extents. Large and distinct increases in biodegradation rates were found with decreasing crystallinity. However, once again, it is to be expected that decreased crystallinity was not the only change induced in the cellulose. A ball-milling process, with its intensive damage to the cellulose crystals, can be expected to decrease the molecular mass as well (Ling et al. 2019). A consequence of a lower molecular mass is a higher number of ends of chains, which presumably will provide more starting points for exoglucanase. In summary, although several studies have shown strong correlations between decreasing cellulose crystallinity and accelerated biodegradation, other factors such as molecular mass and the type of the cellulose crystals may also contribute to the increased biodegradability. Lignification Compared to the other main components of woody material, lignin has a more hydrophobic nature, a more complex assortment of links between the subunits, and a high proportion of aromatic groups (Li et al. 2016). It has been found that plant materials having higher content of lignin tend to be slower to biodegrade (Huang et al. 2022b). For instance, Renouard et al. (2017) reported that coconut coir fibers, which have a high lignin content, are less easily biodegraded in soil in comparison the flax fibers, which have a higher proportion of cellulose. In the work of Nagamine et al. (2022), the initial ramie fibers, which may be assumed to have lignin content, were over 8% degraded in 24 days, whereas the mercerized ramie and regenerated cellulose from ramie, which were free of lignin, were degraded by about 15% and 52%, respectively, in the same period. Kwon et al. (2021) compared the biodegradability of the main components of woody materials in aquatic media. Under matched conditions of 27 days of wastewater biodegradation, specimens of hardwood and softwood lignin showed less than 3% biodegradation, based on oxygen consumed, whereas specimens of cellulose and hemicellulose showed 75 to 87% degradation. The strong contrast in these numbers suggests that lignin is more difficult to REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2418 degrade. Another factor to consider is the concentrations and activities of lignin-degrading enzymes present in aqueous systems. Some exceptions to the rule have been reported, in which lignin levels were not a good predictor of slower biodegradation. For instance, in anaerobic systems, hardwoods have been reported to degrade faster than softwoods, despite similar lignin levels (Wang et al. 2011). Grass is high in lignin, but it degrades faster than wood (Eleazer et al. 1997). The latter finding is likely explainable by the much smaller particle size, which implies greater accessibility. Here the word “size” refers especially to the thickness of a blade of grass, which will determine the approximate surface area that will be immediately accessible to enzymes, especially in the early stages of biodegradation. Mansfield et al. (1999) suggested that in addition to the chemical composition, the inherent complexity of the intertwined cellulose, hemicellulose, and lignin components in plant-based materials is responsible for higher resistance to biological breakdown, in comparison to the individual parts. Thus, the biodegradation process can be expected to depend on a gradual loosening of the material’s structure, eventually enabling different enzymes to access and cleave different kinds of bonds holding the material together. In principle, the overall progress could be blocked at various points due to the need for a specific enzyme capable of breaking a certain kind of linkage. Hemicellulose Tests by Kwon et al. (2020) showed that three types of hemicellulose (switchgrass, hardwood, and softwood) reached 82 to 90% biodegradation in 27 days of aquatic exposure. These values were slightly higher than the results obtained for MCC (about 77% and much higher than for lignin (3% or less). Such results are consistent with the hydrophilic and non-crystalline nature of hemicellulose. Size of Cellulosic Entity If one assumes that cellulolytic enzymes will mainly or initially operate at the outside surfaces of cellulosic material, then it follows that there should be a correlation between size of the cellulosic particle and the rate of biodegradation. Here, “size” refers to the external dimensions. In cases where the material is dense and non-porous, the square of the smallest main dimension would be expected to be roughly proportional to the accessible surface area, depending on such factors as roughness. However, whether or not such a relationship is observed can help to shed light on whether any pores in the material are sufficiently large to allow access to the enzymes. Kraft pulp fibers are known to be mesoporous, due at least in part to the spaces left behind when removing lignin; therefore, it makes sense to consider them separately from other kinds of cellulosic fibers. Published findings related to such questions will be considered here, starting with lignin-containing natural fibers. As illustrated in Fig. 14, a relatively dense piece of lignocellulosic materials would be expected to begin to biodegrade at its outer surface, and progress into the interior might then depend on a gradual process of degradation of successive layers. In general, thinner fibers or fibrils will be expected to expose greater surface area. Likewise, any fragmentation of fibers that results in thin sheets or fibrils can be expected to greatly increase the accessible surface area. REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2419 Fig. 14. Sketch of expected layer-wise degradation of dense lignocellulosic materials, depending on their dimensions A practical way to decrease the effective size of wood-based fibers, whether they still contain lignin or not, is by mechanically refining them, i.e. subjecting them to repeated shearing and compression in the wet state (Gharehkhani et al. 2015). Chen et al. (2015) carried out such an enzymatic procedure with recovered newspaper fibers. Since newspapers are commonly made by mechanical separation of softwood fibers, without removing the lignin, the cell walls are expected to be relatively dense and inaccessible to enzyme access, in the natural state. Refining of the recovered fibers was found to increase the amount of sugar produced during subsequent enzymatic saccharification. Such results are consistent with the idea that refining will increase the effective surface area of the material, just as if the material had been broken into smaller pieces. Likewise, Sinitsyn et al. (1991) found a proportionality between the rates of enzymatic hydrolysis and the surface area accessible to enzymes following dry milling of either cellulose or lignocellulose specimens. Steam explosion is another way that researchers have attempted to increase the areas of cellulosic materials that are accessible to enzymes (Muzamal and Rasmuson 2017). Esteghlalian et al. (2002) carried out such treatment on Douglas fir wood. Consistent with the goal of increasing the surface area, it was observed that the adsorption capacity of the woody material for cellulase enzymes was increased by the treatment. However, they did not observe a proportionality between enzyme adsorption and the enzymatic hydrolysis of the cellulose. A broad range of sizes of cellulose have been evaluated for biodegradability, but in many cases the results cannot be directly compared due to chemical derivatization or other factors. For instance, Homma et al. (2013a,b) showed 96% degradation of TEMPO- oxidized nanofibrillated cellulose (NFC) after 12 days, but only if the counter-ion was sodium. The term “TEMPO” refers to the radical species 2,2,6,6-tetramethylpiperidin-1- yl)oxyl, which catalyzes oxidation of the C6 -OH group of cellulose to form the corresponding carboxylic acid. Since chemical derivatization often interrupts the action of enzymes (Glasser et al. 1994; Yadav and Hakkarainen 2021), such results may provide general support to the hypothesis that developing a small size and higher surface area of cellulosic will promote biodegradation. However, as will be argued later, those results might also be attributed mainly to a swelling effect coming from the charged nature of the material and colloidal effects. Extent of decay (time = 1) Extent of decay (time = 2) Extent of decay (time = 3) REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2420 Miyaji et al. (2023) directly compared cellulose powder, microcrystalline cellulose (MCC), and cellulose gel in three media, namely fresh water, brackish water, and sea water. Though the size distributions of each cellulose type were not specified, the degrees of biodegradation in all three media followed the order of microcrystals, gel, powder. This is notable, since the crystallinity of the MCC is expected to be higher than that of the gel, and its typical geometric width is typically larger. In addition, the gel would consist of a porous assembly of elongated cellulosic entities, whereas the MCC and powder would typically be dispersed as individual particles. Thus, the comparison among the three specimens does not provide clear support for the hypothesis about size and surface area relative to biodegradation. In summary, there appears to be a need for studies in which particle sizes are changed, in a controlled manner, while keeping other variables constant. For example, as a means to avoid other changes in the course or reducing the particle size, one possibility would be to cool the selected cellulosic material in liquid nitrogen, followed by cryo- crushing to different extents. Steam explosion represents another option, though the high temperature can cause chemical changes, in addition to disruption of the material. In either case, parallel measurements of surface area and biodegradation outcomes are recommended. Though such tests have been carried out in the case of various lignified materials, such as wood chips (Reyes et al. 2016), there is a need for such work to settle theoretical questions related to the biodegradation of kraft pulps and cotton. To place such issues in context, it is well known that a typical cotton textile fiber can be 20 µm in diameter, whereas kraft pulp fibers are typically from about 20 to 30 µm in diameter. If one makes the rough estimate of about 1 nm per molecular layer and ignores the presence of a lumen space in the middle of a fiber, an enzymatic process would need to chew through 10,000 such layers to completely degrade the material. Caution is needed in drawing conclusions about enzyme accessibility based on outer dimensions of cellulose fibers. Natural cotton is known to be porous (Mao et al. 2014). Especially before drying, the cited study showed that cotton fibers have a mean pore size of about 50 nm, which can be regarded as large enough to accommodate cellulase enzymes. Though the average pore size was decreased dramatically by drying, it was shown that the pores were able to open up again to approximately their original condition upon rewetting by water. On the other hand, the drying of kraft pulp fibers, as happens during the production of paper products, has been shown to permanently reduce the initially high porosity of freshly pulped kraft or sulfite fibers (Stone and Scallan 1968; Hubbe et al. 2007). Effects of Processing The term processing is used here to denote common treatments of cellulosic materials either to make them available as fibers or to modify their properties. Subsections that follow will consider delignification, mechanical refining, and chemical treatments. In principle, any process that breaks down the structure of the initial cellulosic material is of interest, since it could potentially promote further accessibility of the cellulose to enzymes. Of particular interest are chemical processes that remove lignin (i.e. pulping), mechanical processes that internally delaminate the cellulosic fibers (i.e. refining), and processes that dissolve and then reconstitute cellulose and the form of filaments of films (regeneration). REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2421 Delignification Kwon et al. (2020) correlated the extent of biodegradation for a series of ten plant- based cellulosic specimens, some of which had been subjected to delignification. A strong quasi-linear trend was observed with strongly decreasing biodegradation with increasing lignin content in the range of zero to about 32%, which is the native lignin content of certain wood species. These results are consistent with the findings of Wang et al. (2015), who reported a higher biodegradation rate of delignified wood fibers in comparison to mechanical pulp fibers from the same wood source. Zhu et al. (2008) likewise reported a much higher rate of biodegradation of wood pulp fibers that had been delignified. Such results can be rationalized by the removal of microdomains of lignin from woody material in the course of kraft pulping. Figure 15 envisions such a selective removal process involving a small section (e.g. 100 to 500 nm) within the cell wall of a pulped chip of wood. The cellulose is depicted in the figure as being grouped together as fibrils, which are surrounded first by a layer rich in hemicellulose, and then by lignin, which essentially surrounds the cellulose within the nanostructure of wood. As shown, full delignification of the cell wall can be expected to open up pores, thus rendering the carbohydrate portion of the material susceptible to chemical or enzymatic influences. Fig. 15. Concept of removal of nanodomains of lignin, inspired by an early description by Kerr and Goring (1976); A: Small fragment of native wood, showing parts of about 10 cellulosic fibers bound together by lignin; B: Sketch of the same structure after chemical breakdown and removal of most of the lignin and some of the hemicellulose by chemical pulping, e.g. by the kraft process Regeneration The regeneration of cellulose is carried out by dissolving it and then exposing it to anti-solvent conditions. Important classes of regenerated cellulose include textile fibers such as viscose (rayon) and lyocell. As has already been mentioned in this article, regeneration changes the crystal type from cellulose I to cellulose II, so it is reasonable to expect that it might affect the material’s biodegradability as well. Table 11 shows a compilation of studies that have considered the biodegradation of regenerated cellulose specimens. The seven listed studies give a consistent message: Regeneration has been found to enhance biodegradability relative to the fibers before regeneration. Lignin domains Cellulose fibrillar clusters Hemicellulose predomiantly as mediator between lignin and cellulse A. Wood Cell Wall B. Lignin byproducts: dissolved & fragments Part of the hemicellulose may remain; part may dissolve. Pores open up, exposing cellulose Cellulose resists NaOH & Na2S. REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2422 Table 11. Highlights from Studies Considering Biodegradability of Regenerated Cellulose Study Highlights Citation The dimethylsulfoxide-paraformaldehyde solvent system was used to prepare regenerated cellulose (lyocell type), which was much more biodegradable than the starting material. Sasaki et al. 1979 Regenerated cellulose showed more rapid biodegradation in soil. Zhang et al. 1996a Mercerization of MCC with NaOH, with rinsing but not drying, resulted in the most rapid biodegradation (cellulose II hydrate), followed by the dried are rewetted cellulose II. Wada et al. 2010 The biodegradation rate of viscose (rayon) fibers exceeded that of cotton and ramie. Niu et al. 2012 Cellulose obtained from Whatman filter paper became much more biodegradable after regeneration from an ionic liquid solution. Li et al. 2017 Rayon fibers were compared with other fibers when exposed for up to 35 days in lakewater, seawater, and activated sludge. Their biodegradation extents (about 70%, 42%, and 90% in the three listed media) were generally similar to those of cotton. Zambrano et al. 2020 Fully regenerated cellulose from ramie fibers was much more biodegradable than mercerized (i.e. partly regenerated) ramie cellulose, and even more so than the original ramie fibers. Nagamine et al. 2022 Partial dissolution of cellulose, similar to mercerization, resulted in much higher rates of soil biodegradation. Biodegradation was essentially complete in 19 days. Tian et al. 2022 Chemical Treatments For different current and potential uses, there are a broad range of chemical treatments of cellulose fibers. This subsection will consider published information related to their effects on biodegradability. Types of treatment to be considered include antimicrobial, hydrophobic, ultraviolet (UV)-blocking, and creation of cellulose derivatives. Table 12. Highlights from Studies Considering Effects of Various Antimicrobial Treatments Study Highlights Citation The effectiveness of different silver-containing treatments of cotton specimens were compared in soil biodegradation. Agglomeration of the negatively charged Al species resulted in lower effectiveness, which was attributed to less Al+ ions released. Klemencic et al. 2010 A multi-component treatment that included AgCl as a textile finish was more effective than single-component treatment relative to soil burial tests. The other components included a binder and hydrophobic silane-type monomers. Simoncic et al. 2010b Treatment of flax fibers with polyquanternium-10 at a concentration of 0.5% was sufficient to completely suppress soil biodegradation. Renouard et al. 2017 Lauric acid treated bacterial cellulose was used as a coating film for antimicrobial food packaging. Zahan et al. 2020 REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2423 Antimicrobial treatments Various studies involving treatment of cellulose fibers to achieve antimicrobial effects have also involved evaluation of biodegradation. Table 12 lists some highlights from such studies. Review articles on antimicrobial treatments for wood have been published (Schultz and Nicholas 2003; Freeman and McIntyre 2008; Rajput et al. 2023). In general, given their detrimental action towards the microbial populations, the antimicrobial treatments generally reduced the degradation rates. Hydrophobizing treatments It can be hypothesized that hydrophobic treatments of cellulose fibers could suppress biodegradation (Park et al. 2004). Studies that help to test that hypothesis are listed in Table 13. The work of Zahan et al. (2020) is listed again in this table because lauric acid can be used as a hydrophobic agent (Yin et al. 2020). The general principle of hydrophobicity contributing to resistance to biodegradation has been reviewed with respect to bioplastics and synthetic plastic materials (Hubbe et al. 2021). As shown in the table, the hypothesized negative effect of hydrophobic treatment on rates of biodegradation was generally supported by the experiments. Table 13. Highlights from Studies Considering Effects of Hydrophobic Surface Treatments Study Highlights Citation Slow biodegradability of cellulose acetate was attributed to its hydrophobic nature. Rayon and cotton were found to be more biodegradable in soil burial tests. Park et al. 2004 A multi-component treatment that included AgCl as a textile finish was more effective in resisting biodegradation than single-component treatment relative to soil burial tests. The other components included a binder and hydrophobic silane- type monomers. Simoncic et al. 2010b Oleic acid treatment contributed to biodegradation resistance of mulch prepared by delignification of cornhusk. Hernawan et al. 2020 Lauric acid treated bacterial cellulose was used as a coating film for antimicrobial food packaging. Zahan et al. 2020 The onset of biodegradation was delayed by about 3 days by high hydrophobic treatment relative to unfinished cotton. Nevertheless, all cotton fabrics degraded significantly (50 to 70% by 100 days) under the conditions of this study. Zambrano et al. 2021 UV-blocking treatments Treatment with the anti-UV agent Tinuvin P helped to suppress soil biodegradation, especially during the first couple weeks of soil exposure, in comparison to oleic acid treatment alone of the delignified corn husk fiber (Hernawan et al. 2020). In other words, there was a lag period before substantial biodegradation. Chemical treatments to derivatize the cellulose surface Because microbes and their cellulolytic enzymes mainly have been evolved to deal with natural cellulosic materials, it makes sense that chemical derivatization treatments would tend to interfere with such action. Related studies are highlighted in Table 14. REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2424 Table 14. Highlights from Studies Considering Effects of Chemical Derivatization of Cellulose on Biodegradability Study Highlights Citation Unmodified cotton showed about five times the biodegradation of cellulose acetate during the period of 20 to 115 days of aqueous biodegradation. However, the blend between the two showed enhanced biodegradability. Suh et al. 1996 A cellulose ether phthalate was found to be slower to biodegrade than MCC in a composting test; however, a related sodium salt was more biodegradable than MCC. Simon et al. 1997 Slow biodegradability of cellulose acetate was attributed to its hydrophobic nature. Rayon and cotton were found to be more biodegradable in soil burial tests. Park et al. 2004 Increased acetylation decreased total sugar conversion consistently with various cellulase dosages and times. Zhu et al. 2008 The presence of oxidized functional groups on TEMPO- oxidized nanocellulose inhibited their biodegradation. Removal of those groups allowed subsequent layers of cellulose chains to be biodegraded rapidly. Homma et al. 2013b A broad range of cellulosic materials were subjected to pilot- scale composting. Biodegradation was strongly repressed with an increasing degree of substitution (DS). Complete inhibition was achieved at a DS level of 1 in some cases. Leppanen et al. 2020 Other treatments of fibers for textiles and papermaking Textile fibers are often subjected to finishing treatments to aid either in their processing or in the final attributes of fabrics. Li et al. (2010) showed that treatment with a softener tended to enhance the biodegradation of cotton and polyester in soil, whereas treatment with a resin had the opposite effect. Likewise, Zambrano et al. (2021) observed the greatest degree of cotton fiber degradation in the case of fibers treated with a softener; these were about 89.6% degraded in comparison to 72.2% for the corresponding untreated cotton and 63.0% for durable press cotton fibers. Notably, cellulosic textiles can be processed with cellulase and other enzymes, aiming to achieve desired surface properties in an eco-friendly manner (Stanescu 2023). Thus, in at least some cases, the finishing treatment might already be counted as a start in the direction of full biodegradation. In aquatic environments, this phenomenon tends to be less pronounced, although the biodegradation rate can still be influenced by finishes commonly applied to cotton fabrics. Fabrics treated with crosslinking chemicals such as durable press and water repellents may exhibit initial resistance to biodegradation, particularly on the surface. However, it is noteworthy that even these treated cotton fabrics degrade noticeably under freshwater conditions, exceeding 60% within 102 days of testing (Zambrano et al. 2021). Kraft fibers that are used in preparation of printing and writing papers, as well as some packaging grades, are often treated to increase the hydrophobic nature of the product (Hubbe 2007). Xerographic copy papers additionally are likely to contain fluorescent whitening agents (Hubbe et al. 2008). Though colorants are widely used to fine-tune the color of white papers, there are also some strongly colored paper products. Because none of these paper products is likely to be flushed, the most likely fates of printing paper, after it has been used, will be either recycling or landfill. Dyed fibers that are lost from the papermaking process in the course of recycling operations are expected to mostly end up in the thickened sludge from wastewater treatment, which most often becomes another REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2425 contribution to landfills (Hubbe et al. 2016). Though it is reasonable to expect that strongly dyed papermaking fibers would be more difficult to biodegrade, there is a need for studies to quantify such expected effects. ENVIRONMENT-RELATED FACTORS The environmental conditions present during biodegradation are often specified in standard tests. However, in many cases it may be important to know how different conditions affect cellulose fiber degradation. Conditions to be considered in this section include the microbial community or the presence of enzymes, moisture, temperature, C:N ratio, counter-ions (including salinity), and products of decomposition. Another general issue to address is the environmental relevance of various test protocols. Ideally, research can be carried out under conditions that will lead to valid predictions of what will happen either in typical wastewater treatment plants, composting systems, or natural water environments. On the other hand, future studies will also need to consider what happens at the sea floor, for instance, where the cold temperatures and lack of light would tend to slow down various routes to biodegradation of cellulose fibers that settle into such environments. Fig. 16. Illustration of some key attributes of environments that can be expected to affect rates of biodegradation of cellulose fibers The presence of enzymes The essential nature of enzymes in the biodegradation of cellulose fibers and plant- based materials has been shown clearly in studies involving inoculation (Greff et al. 2022). Thus, Zainudin et al. (2022) reviewed studies in which substantial increases in the rates and extents of cellulose degradation during composting were observed after adding cellulase-producing microbes. Related work involving anaerobic conditions was reviewed by Leschine (1995). Here, emphasis was placed on the importance of microbial communities present in different environments. As noted by Meyer and Edwards (2014), during continued or repeated exposure to certain environmental conditions, even including toxins, the microbial groups can become acclimated and thereby better able to break down the cellulose and other plant materials. Cellulose Crystallinity Lignin (hydrophobicity, blocking & non-productive binding) C H CH3 C H CH3 Size of the object Chemical derivatization or complexity Porosity REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2426 In such communities, different microbes specialize in the production of different enzymes. Rabelo et al. (2018) found that such optimized communities were present during anaerobic biological treatment of wastewater from pulp and papermaking. Suh et al. (1996) emphasized the synergistic effects of different enzymes working together in cellulose biodegradation of cotton and cellulose acetate. Zambrano et al. (2020) documented the microbiological communities that were present in lakewater, activated sludge, and seawater in the presence of cellulose fibers. Though the present review is mainly concerned with degradation of individualized cellulose fibers that are released by means of wastewater systems, it is worth noting that biodegradation of cellulose-containing plant materials also takes place in such environments as rice paddies and wetlands. Moisture Content The presence of moisture is an essential requirement for biodegradation. Park et al. (2004) found a correlation between the moisture regain of dry fibers and their subsequent rate of biodegradation. Biological processes require moisture, which may differ in terms of optimum levels. Another concern is that moisture levels may be unevenly distributed, e.g. in an anaerobic digester or landfill. Due to the importance of this issue, especially during soil degradation and composting, there is a need for more research related to effects of limiting moisture content on cellulose biodegradation. Such studies are inherently difficult to carry out in field conditions due to uneven mixing and distribution of water. Temperature Though temperature is expected to have profound effects on biodegradation, it is important to bear in mind that different microbial communities and different enzymes will be favored by different temperature ranges. Thus, as noted by Ahmed et al. (2019), cellulose biodegradation can take place effectively over a wide temperature range, e.g. 14 to 25 C in the cited work. Ghasimi et al. (2016) found higher rates of biodegradation under thermophilic (55 C) conditions compared to mesophilic (35 C) conditions. The thermophilic conditions generally shortened the time required for cellulose breakdown, though the final state after more than about 6 days of treatment was not very sensitive to temperature. These results are in agreement with those of Kim et al. (2022). These results also were consistent with earlier work that showed an increase in the first-order rate coefficient for anaerobic cellulose hydrolysis with increasing temperature (Ge et al. 2011). Chen et al. (2015) found that increased temperature of an autohydrolysis pretreatment of wood material adversely affected subsequent biological degradation. The effect was attributed to closure of mesopores in the cell walls of the fibers, i.e. hornification. C:N ratio The progress of composting has been shown to be dependent on having a suitable ratio between the hydrosoluble forms of carbon and nitrogen present (Hubbe et al. 2010; Yu et al. 2020). Thus, López Alvarez et al. (2009) kept a range of C:N between 32:1 and 57:1 for their studies. When the goal is to degrade cellulose, the danger is likely to be too high a proportion of carbon. Though the effect of C:N ratio has been widely considered in systems that contain cellulose in some form (Greff et al. 2022), there has been a lack of such studies dealing with cellulose fibers as a component of compost. When considering future studies, a likely hypothesis to guide that work is that a certain range of C:N ratios may be favorable to the biodegradation of cotton or wood-derived fibers. Notably, most REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2427 standard tests to assess compostability specify C:N ratios in the range of 10 to 40, or more ideally 15 (Wyman and Salmon 2024). The level of phosphorus compared to carbon may also be considered in such future studies (Chen et al. 2022). Counter-ions Some remarkable effects related to counter-ions were shown in a series of work by Homma et al. (2013a,b). To begin, they showed that TEMPO-mediated oxidation (Saito and Isogai 2004) moderately decreased the biodegradability of bleached softwood kraft cellulosic fibers (Homma et al. 2013a). However, there were huge differences depending on the type of counter-ion associated with the carboxyl groups created by the oxidative treatment. Highest biodegradation (about 45% weight recovery after 12 days) was observed for the ammonium form and the sodium form. Essentially no biodegradation was noted with the copper counter-ion form. Only 5% loss in weight recovery was observed when the proton was the counter-ion, i.e. the protonated form of TEMPO-oxidized cellulose. However, tests by Homma et al. (2013b) showed that the protonated and deprotonated forms of TEMPO-oxidized nanofibrillated cellulose exhibited equally high rates of biodegradation in water in the presence of a crude cellulase. These results suggest that the effects reported in the first article (Homma et al. 2013a) were attributable to the growth and viability of the microbes and their production of enzymes in the presence of different counter-ions. Levels of salinity can be expected to affect the types of microbes that are able to thrive in different situations. For example, it has been proposed that the brackish conditions of the Baltic Sea allowed the warship Wasa, which sank in Stockholm harbor, to remain intact for 333 years until it was recovered and preserved (Sandström et al. 2002). On the other hand, it has been shown that biodegradation in natural waters follows the order of fresh water > brackish water > seawater (Miyaji et al. 2023). In addition, the studies already cited in this work clearly show that the level of salinity present in the ocean is not a barrier to biodegradation of cellulose (Zambrano et al. 2020; Royer et al. 2021; Royer et al. 2023; Smith et al. 2024). MECHANISTIC ISSUES This section considers some fundamental mechanistic explanations that have been published relative to cellulose biodegradability and factors affecting it. Given the complexity of the processes considered in this article, involving biological organisms, numerous enzymes, contrasting environments, and effects of numerous controllable variables, it might be regarded as unrealistic to be able to predict rates and extents of biodegradation based on thermodynamics. Rather, one needs to look at published data to find out whether the effects predicted from thermodynamics can be regarded as rate- governing factors. Thus, after thermodynamics, the next topic to consider will be kinetics. The ways in which reaction rates and extents are affected by such variables as concentrations, temperature, and time can help support or rule out various hypotheses about mechanisms. A third category to be considered in this section is analysis of reaction byproducts. Again, such evidence can help explain some of the theoretical predictions and show whether they adequately explain what is happening in practice. REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2428 Thermodynamics and its Limitations Inherent stability of cellulose in its crystalline form A greater difficulty in breaking down crystalline cellulose, by various means, in comparison to non-crystalline zones, has been proposed based on thermodynamic principles (Beckham et al. 2011). It is possible to calculate the amount of energy that must be contributed to decrystallize different crystalline forms of cellulose. Though the cited work provides detailed analysis of cellulose crystalline states, less attention is paid to the amount of bonding energy embodied within amorphous cellulose zones. This may be a key issue to address in future work. As noted earlier, endoglucanases are expected to mainly cleave random glycosidic bonds in non-crystalline zones, whereas exoglucanases are expected to proceed from the ends of cellulose chains, proceeding along the surfaces of crystalline zones (Horn et al. 2012; Wang et al. 2013b). Beckham et al. (2011) reported that the native cellulose I-beta crystalline form represents a lower energy state in comparison to other crystalline forms of cellulose, e.g. cellulose II, which is the common form resulting from industrially important regeneration methods, such as the viscose and lyocell processes. Based on that information, more energy is required to separate a cellulose chain from an edge of the cellulose I crystal, compared to the other crystalline forms. Stability of cellulose associated with its contrasting crystal planes Another reason to suspect a high degree of stability of cellulose crystalline zones is their incorporation of two contrasting bonding mechanisms in different crystal planes (Liu et al. 2022). Thus, relative to the plane of the anhydroglucose rings, the hydrophilic –OH groups are projected mainly equatorially, thereby contributing to hydrogen bonding within that plane (Yamane et al. 2006). By contrast, at 90 degrees to that plane, the chains are held together primarily by van der Waals forces. The idea is that it will be inherently difficult to break both types of bonds simultaneously. Though this concept appears to account for difficulties in dissolving cellulose by means of various solvents, it is unclear whether the same arguments can be applied to cases of enzymatic breakdown. Inability of thermodynamic factors to account for rates of degradation Although thermodynamic factors can explain the direction of likely changes in chemical systems, they cannot reliably predict the rates, which will be the next topic to consider. In particular, it is reasonable to expect that such modifications as coatings and chemical derivatization will slow down or block the reaction paths associated with biodegradation. For example, Zambrano et al. (2021) observed a small but statistically significant decrease in the rate of cotton biodegradation when comparing dyed cotton specimens to undyed cotton. Kinetics Important evidence to the mechanisms of rate-limiting steps in biodegradation can be obtained by examining the rates, including studies of how those rates depend on factors such as concentrations and time. Figure 17 illustrates some key factors that are likely to affect the kinetics of cellulose fiber biodegradation in different cases. As will be discussed below, this includes both the forward and reverse rates of binding of enzymes such as cellulases both to the lignin (non-productive) and to the cellulose itself (which is often productive). A mechanistic, kinetic study (Wang et al. 2004) showed that the biodegradation of cotton by different cellulose enzymes can be modeled based on REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2429 sequential and parallel actions of cellobiohydrolase and endoglucanase enzymes. In addition, note that when the endoglucanase (pacman item) adsorbs onto lignin, it is shown as having become immobilized. Note that the exoglucanase (shown as a claw-like shape) is shown as being possibly blocked by either lignin by itself of by the density of the cellulose structure, when approached from the polymer ends. Other important aspects impacting the kinetics are the buildup of inhibitors (such as cellobiose) and their enzymatic breakdown, blockage of enzyme progress by lignin or other debris, such as denatured enzymes, and the status of growth, starvation, or demise of the bacterial or fungal sources of enzymes. These processes can be expected to be affected by rates of diffusion and convection, the latter of which will be affected by agitation of the mixture. There is a need for more study of kinetic aspects, especially under conditions that mimic natural environments and wastewater treatment. In addition, there is evidence that some non-enzymatic mechanisms are involved in fungal breakdown of lignocellulosic materials (Aguiar and Ferraz 2011). Fig. 17. Factors that can be expected to affect the kinetics of biodegradation of cellulose fibers Results falling short of 100% degradation One of the most striking findings, relative to the kinetics of cellulose biodegradation, has been a plateau effect in plots of cellulose hydrolysis vs. time. In other words, the rates of hydrolysis tend to decrease with time, and the endpoint falls well short of complete breakdown. Highlights from studies exhibiting such behavior are listed in Table 15. Table 15. Highlights from Studies Showing Evidence Relative to the Existence of a Plateau of Incomplete Cellulose Biodegradation vs. Time Study Highlights Citation Activated sludge degradation of cellulosic fibers was limited to about 20% in 96 hours of mesophilic treatment and 88% in the same time of thermophilic treatment. Hurwitz et al. 1961 Unlike many other examples in this list, these authors showed no plateau in anaerobic digestion of cellulose, though times of greater than 100 days were required for full hydrolysis. Edberg & Hofsten 1975 Blockage in path of an exoglucanase Nonpoductive binding adsorption & desorption rates Cellulose binding adsorption & desorption rates Inhibitors -glucosidase → glucose Lignin Inactive debris buildup Growth, starvation of the source bacteria REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2430 Soil burial studies over 20 to 45 days showed a maximum biodegradation of about 73% for regenerated cellulose films and perhaps lower in the case of kraft paper. Zhang et al. 1996a According to this review article, whereas theory would lead these authors to expect 100% biodegradation of cellulose, plateau levels of about 80 to 90% are typically reported. Mansfield et al. 1999 Biodegradation extents in the range of about 30 to 60% were achieved in 45 days of industrial composting. López Alvarez et al. 2009 Biodegradation rates of cellulose fibers and fabrics decreased with time in aerobic activated sludge treatment. Niu et al. 2012 Cotton fabrics with various finishes biodegraded in soil for 154 days began a plateau in CO2 production after 140 days but no plateau in weight loss through the end of the study. Smith et al. 2012 Observations of single crystalline cellulose fibers showed marked decreases in hydrolysis rate with time. Wang et al. 2012 MCC appeared to become increasingly recalcitrant to further biodegradation with the passage of time during single- and multi-stage cellulase treatment. Yu et al. 2012b All-cellulose composites prepared from rayon by means of ionic liquid treatments showed soil biodegradation levels in the range of 38 to 73%. Kalka et al. 2014 Aqueous biodegradation over 96 hours showed plateau levels for MCC (70%), bacterial cellulose (about 80%), and bleached softwood kraft fibers (about 90%). Kafle et al. 2015 Biodegradation levels in the range of 38 to 62% were observed for a range of cellulose types exposed to aerobic wastewater treatment under mesophilic and thermophilic conditions. Ghasimi et al. 2016 Biodegradation of toilet paper fibers during wastewater treatment was generally in the range of 80 to 90% in two aerobic systems for municipal wastewater. Ahmed et al. 2019 Soil biodegradation levels of about 84 and 88% were achieved after soil exposure for 209 days. Mistriotis et al. 2019 A declining rate of cotton and rayon biodegradation was observed over 240 days in natural water. The plot suggests a plateau level of about 65% in the case of rayon. Zambrano et al. 2019 Plots of biodegradation vs. time showed clear plateau features for cellulose biodegradation in fresh water, brackish water, and sea water. In lakewater, MCC showed an ultimate biodegradation of about 85%, whereas cotton showed 80%. Zambrano et al. 2020 Microcrystalline cellulose (MCC) reached a plateau of 82% biodegradation within about 7 days of aqueous biodegradation and remained at that level to 27 days. Kwon et al. 2021 Thin-layer chromatography-grade cellulose, presumably MCC, degraded in a quasi-linear manner to about 80% in 20 days and thereafter the rate became very slow. Rossetti et al. 2021 Marine biodegradation of MCC reached about 85% in 28 days, in contrast to a theory-based curve projecting 100%. Royer et al. 2021 A review of the literature estimated that about 30% of cellulose from toilet paper becomes biodegraded in typical aerobic, activated sludge wastewater treatment cycles. Liu et al. 2022 Biodegradation rates in natural water were found to decline with time. The authors reported that after fragmentation, the fine fragments were resistant to further hydrolysis. Nagamine et al. 2022 Marine water biodegradation levels after 28 days were generally in the range 76 to 83%. Royer et al. 2023 REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2431 When considering the results shown in Table 15, it is important to bear in mind some studies in which contrasting results were obtained, i.e. showing essentially 100% biodegradation. For instance, this is what Edberg and Hofsten (1975) observed in the case of very long anaerobic treatment cycles. Leppanen et al. (2020) reported essentially 100% biodegradation of many cellulose fiber types under industrial composting conditions. Various theories have been advanced to explain the tendency of cellulose biodegradation to slow down and even to reach a plateau of stable resistance. Some of these are described below. Production of inhibitors Enzymatic cellulose biodegradation can be inhibited due to the buildup of decomposition products, including cellobiose (Yu et al. 2012b; Teugjas and Väljamäe 2013; Olsen et al. 2016). Thus, Van Wyk and Mohulatsi (2003) observed that cellulose biodegradation by cellulase was inhibited by the buildup of sugars. Meyer and Edwards (2014) described the buildup of inhibitors during the anaerobic treatment of wastewater from pulp and paper manufacturing. Though such effects can be expected, they do not seem to account for the full range of reported findings. In addition to the production of inhibitors to biodegradation, the hydrolysis of polysaccharides also can lead to decreases in pH (Liu et al. 2006), which can be expected to affect further biodegradation in various ways. However, a product inhibition effect would not account for the instances biodegradation essentially stopping at certain levels, as shown in many of the examples that were listed in Table 15. It is worth stating that the results of small batch biodegradation reactors are expected to be much more sensitive to inhibitor formation than for biodegradation in large water bodies that have a significant convective flow and thus a strong dilution and diffusion that minimizes inhibitor concentrations near the substrate. Non-productive adsorption onto lignin and surfactant effects Another type of inhibition of the action of cellulases can occur due to strong adsorption and apparent immobilization onto the relatively hydrophobic surface of lignin (Huang et al. 2022b). Such non-productive binding of the enzymes prevents them from hydrolyzing cellulose. Another way that lignin could explain some of the slow-down and plateauing of cellulose biodegradation is if some of the cellulose is encased in a contiguous layer of lignin (Huang et al. 2022b). However, such an explanation would not account for the many published examples in which lignin-free cellulose samples have shown plateau- type biodegradation behavior. It has been shown in some cases that non-productive binding of cellulase to lignin can be overcome by the use of surfactants. Mizutani et al. (2002) showed that the nonionic surfactant polysorbate 20 enhanced the rates of cellulase-induced breakdown of microcrystalline cellulose as well as several regenerated cellulose types. The effect was attributed to overcoming a form of non-productive binding of the enzymes to the cellulose itself. Chen et al. (2015) found that increased levels of lignin generally inhibited cellulose biodegradation. A combination of mechanical refining and surfactant addition was found to be especially effective in facilitating cellulose hydrolysis. The refining action would be expected to render more of the cellulose accessible to the enzyme (de Assis et al. 2018), whereas the surfactant would be expected to facilitate reversible release of the enzyme from the lignin surfaces (Seo et al. 2011). Although surfactants can be expected to help to disperse enzymes from surfaces, the opposite might be expected when treating a mixture of enzymes and cellulosic fibers with a cationic copolymer of polyacrylamide, i.e. a REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2432 flocculant. Notably, such treatment has been shown to enhance the activity of cellulase (Reye et al. 2011). Presumably, the cationic polymer serves as a tether, keeping the enzyme in the neighborhood of the cellulose to be degraded without fully immobilizing it. Starvation in confined reactors Plateau effects observed within isolated bioreactors have been attributed to a starvation effect (Mistriotis et al. 2019). Thus, it was proposed that biodegradation can be expected to proceed readily during an initial period during which cellulose is abundant in the mixture. But it is reasonable to expect that microorganisms could have a feedback system that slows down the consumption of any remaining cellulose during periods of developing scarcity. The starving microorganisms were proposed to excrete inhibitory chemical agents. It is worth noting here that, whether or not the starvation hypothesis is valid, there might be other unknown contributions to plateau effects, such as depletion of essential nutrients (e.g. N, P) or in some cases the recalcitrant nature of lignin, if and when it is present. A search of the literature showed a need for studies addressing the question of whether the biodegradation of cellulose may be sometimes slowed down by insufficient concentrations of nutrients, including trace nutrients. Deposition of non-hydrolysable substances Another hypothesis is that non-hydrolysable substances may increasingly coat the surfaces of a remnant of cellulose remaining in a mixture (Kafle et al. 2015). These substances might even include denatured or otherwise immobilized cellulase (Yu et al. 2012b; Kafle et al. 2015). The effect has been called “enzyme blockage” (Yu et al. 2012b). Since there have been relatively few definitive studies related to these issues, future research is recommended. For example, tests could be carried out using optional treatments with isolated cellulose binding domains and/or denatured cellulases. The research question is whether or not such pretreatments would inhibit subsequent hydrolysis by active cellulase treatment. Table 16. Studies that Analyzed the Presence and Concentration of Byproducts of Cellulose Biodegradation Study Highlights Citation Biodegradation products of regenerated cellulose films included oligosaccharides, various sugars, organic acids, glycerol, ethanol, and formaldehyde. Zhang et al. 1996b Headspace analysis of atmosphere associated with stored books provides clues to mechanisms contributing to their degradation. Lattuati-Derieux et al. 2006 Certain degradation products associated with the aging of books appeared to be decomposition products from lignin. Dupont et al. 2007 Furfural and the breakdown products of fatty acids were associated with the degradation of books during storage. Clark et al. 2011 Headspace analysis was used to detect breakdown products of cellulose decomposition in electrical transformers. Bruzzoniti et al. 2014 Wood decay fungi, during their breakdown of alfalfa stems, produced a range of byproducts, including furfural. Girometta et al. 2017 Products from anaerobic decomposition of pulp and paper mill wastewater included butyric acid along with hydrogen, methane, acetic acid, and hydrogen sulfide. Rabelo et al. 2018 REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2433 Reaction Product Evidence Another approach to verifying hypotheses related to the mechanisms of biodegradation is to examine the byproducts that accumulate during cellulose biodegradation. Evidence of this type is highlighted in Table 16. In principle, the reaction products that are found in such studies can be compared to those that would be expected based on specific hypothetical reaction paths. LIFE CYCLE ISSUES Raised Cellulose Levels in Environments The biodegradation of cellulose fibers can be regarded as an essential link in a potentially sustainable cycle. Human-contributed effects can be judged relative to whether they significantly affect natural cycles. Based on literature reviewed in this work, it is not so much the biodegradability, but rather the amounts of cellulose fibers introduced to wastewater that are likely to have adverse environmental effects. Published information of the amounts of such cellulose released to wastewater or released to the environment were summarized earlier in Tables 3 and 4. As has been reviewed, the rates of biodegradability of human-discharged cellulose fibers to the environment is in an intermediate range, often requiring weeks to a few months to be mostly assimilated back into the natural cycle. However, the amounts of cellulose fibers, especially the contribution of sanitary tissue, has a demonstratable effect on the capacity and energy consumption of municipal wastewater treatment plants (Wang et al. 2023). It is worth noting that the contribution of cellulose fibers from laundering will be a small fraction of the amount that a typical person will discharge to wastewater as sanitary tissue. The combination of relatively large amounts of discharged fibers and moderate rates of biodegradation have some practical consequences relative to future priorities: • To the degree that some of the discharged cellulose fibers pass through or around wastewater treatment operations, one needs to be concerned about their effects on eutrophication (Razza et al. 2015). In other words, they can be expected to use up available oxygen in the water as they biodegrade. This concern supports policies to promote efficient wastewater treatment technologies. Ideally, the goal should be to completely remove cellulose before discharge of treated water to waterways. • Conventional wastewater treatment operations that are optimized for the production of purified water, rather than the full digestion of organic sludge, can be expected to result in 10 to 60% of the incoming cellulose becoming part of the sludge that requires management. The most widely used disposal alternatives for biosolids are landfills and land application. Cellulose that is buried in a landfill, when sufficient moisture is present, is expected to degrade anaerobically, with the generation of methane. The global warming potential (GWP) of CH4 has been estimated to be about 37 times that of CO2 (Derwent 2020). It has been estimated that 20 to 30% of the methane fails to be collected, even in modern landfill facilities (work of Levis and Barlaz 2014, listed in the Environmental Protection Agency website, EPA 2023; and Barlaz, EPA 2014). Here there appear to be opportunities for optimized composting. In ideal cases, the resulting compost might have sufficient value as a soil amendment to be sold. A concern is whether the sludge contains excessive levels of contaminants, including organic compounds, that might harm crops. In REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2434 addition, any petroleum-based fibers and microplastics present in sludge may adversely affect natural processes due to their tendency to accumulate. Filtering to Selectively Remove Cellulose from Wastewater As mentioned earlier in this article, the limited rate of degradation of cellulose fibers, especially toilet tissue fibers, has been found to limit the capacity and completeness of municipal wastewater treatment operations. Several authors have proposed efforts to achieve beneficial usage of such fibers by filtering the incoming water to such facilities. Highlights from related articles are listed in Table 17. The general finding from studies of this type is that the separation of cellulosic fibers from municipal wastewater is feasible. Table 17. Studies Considering the Filtering, Recovery, and Various Alternative Beneficial Uses of Cellulose Fibers Entering Municipal Wastewater Treatment Facilities Study highlights Citation Recovery of cellulose fibers from incoming municipal wastewater to a treatment plant was demonstrated. Honda et al. 2002 Screens of 0.35 mm mesh size were effective in recovery of cellulose fibers from untreated municipal wastewater. Ruiken et al. 2013 Fine screening was shown to be effective for the collection of cellulose fibers before municipal wastewater treatment. Those materials were shown to be 57 to 62% biodegradable under anaerobic conditions. Ghasimi et al. 2016 Both gravity settling and microsieving were able to remove cellulose fibers from incoming municipal wastewater at >80% efficiency, but the microsieving was able to do so selectively. Ahmed et al. 2019 The cellulose fibers recovered by filtering the intake from municipal wastewater treatment can be used in materials for construction. Cipolletta et al. 2019 These authors studied the biodegradation of cellulose fibers that had not been removed from municipal wastewater, but their article discusses such filtering as an option. Li et al. 2019 Screening, specialized sieving, and settling were compared for the recovery of cellulose fibers from untreated municipal wastewater. Sieves with 0.1 to 1 mm openings were found to be the most effective, allowing up to 94.5% recovery. Li et al. 2020 Cellulose fiber recovery options are reviewed, with an emphasis on rotating filter belt dewatering. About 30% of the recovered cellulose in the filter sludge can be degraded biologically during reported conventional processing under aerobic or anaerobic conditions. Liu et al. 2022 A life cycle assessment (LCA) showed that recovery of cellulose fibers by filtering before municipal wastewater treatment can save 8.6% of the energy needed to run the operations. Wang et al. 2023 Djordjevicová and co-authors (2023) carried out work to determine whether or not the presence of cellulosic fibers would affect the operation of a typical septic tank system, which can be regarded as a type of anaerobic treatment. A matched pair of reactors was set up to mimic septic tank conditions. The process that included cellulose fibers showed similar behavior or a cellulose-free process with respect to most of the measured variables, including temperature, pH, electrical conductivity, turbidity, color, chemical oxygen REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2435 demand, and ammonia nitrogen content. Only the level of nitrate nitrogen content was higher for the system to which cellulose fibers had been added. The cited authors concluded that the presence of cellulose fibers had no important effects on the operation of the septic tank processing. The study did not include any analysis of the extent of biodegradation of the cellulose with respect to time. Though it is clear from the studies listed in Table 17 that cellulose fibers can be effectively collected by filtering untreated wastewater at the intake of a municipal wastewater treatment plant, there has been much less attention regarding ways to achieve value from such wet and contaminated fibers. Options for the recovered fibers can include composting (with production of a stable soil component), anaerobic digestion (with the production of methane or hydrogen fuels), and possible recovery and sanitation to allow use in paper products. Regarding this last option, developmental engineers can rise to the challenge, perhaps by application of bleaching strategies (Dence and Reeve 1996; Bajpai 2012), novel cleaning and sanitation technologies (Henriksson et al. 2017), and other unit operations of paper recycling (Doshi and Dyer 1997), to render those fibers free of any smells or perceived contamination issues. In addition, potential uses of such fibers in construction (Cipolletta et al. 2019) may avoid the kind of consumer attitude problems of some other potential applications. Henriksson et al. (2017) pioneered a method for recovering paper pulp, along with recyclable plastics and metals, from municipal solid waste. This process could be applied to cellulose-rich fractions obtained from wastewater processes, such as screened materials and waste sludge. By subjecting the waste material, including wastepaper, to a combination of heat and mechanical energy, it undergoes efficient repulping and unintentional sterilization. The effectiveness of repulping fibrous materials within the waste mixture crucially depends on the addition of dilution water and the application of rotational energy. Notably, this patented process, now operational at Toledo, Oregon, is owned by Georgia Pacific. The recovered and sterilized paper fiber, known as Juno™ Fiber, is transformed into new paper products. Another option that avoids problems of consumer attitude is to convert the recovered cellulose fibers to biofuels. In principle, lignin-free cellulose fibers recovered from wastewater treatment plants have some inherent advantages. The absence of lignin makes such fibers more suitable for saccharification and fermentation to produce bioethanol and related liquid fuel products (Wang et al. 2013c; Taha et al. 2016). The downside is that such technology has yet to demonstrate large-scale economic viability (Devi et al. 2022). Even if economic success is achieved in the future with cellulose-to- bioethanol factories, an individual wastewater treatment plant will likely have too little recovered cellulose fiber to achieve the needed economies of scale. The wet and contaminated nature of the recovered fibers may discourage their transportation to the site of an efficient cellulose-to-ethanol facility. Wastewater Sludge Options Landfilling of wastewater sludge The sludge produced during conventional treatment of municipal wastewater, with its expected content of cellulose fibers, is often landfilled (Barlaz 2006). As was noted earlier, although modern landfill facilities are set up to collect methane that is generated by anaerobic breakdown of cellulose and other biomaterials in the mixture (Kumar et al. 2004; Barlaz 2006; Pearse et al. 2018), the recovery of methane is not likely to be complete (Huber-Humer et al. 2008; Mønster et al. 2019; Huang et al. 2021), leading to an REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2436 environmental impact. Methane has a greenhouse gas equivalency about 37 times greater than that of carbon dioxide (Derwent 2020), noting that its ultimate impact is reduced somewhat due to a much shorter presence in the environment relative to carbon dioxide (Smith et al. 2012). Other processing of wastewater sludge More environmentally and economically advantageous options can be sought. Some possible options are illustrated in Fig. 18. Due to its content of biodegradable organic materials and moisture, the latter of which can be adjusted by use of a belt press or other thickening technology (Hubbe et al. 2010), municipal sludge is a good candidate for composting. The substantial carbon content due to the presence of the cellulosic fibers will be at least partly balanced by the nitrogen content from solid human waste and food waste in the mixture. As noted earlier, a delay of the composting process has been observed, depending on the addition of cellulose fibers in a compost mixture (López Alvarez et al. 2009). Such delays are likely attributable to the time required for completion of multiple steps in enzymatic breakage of glycosidic bonds, in combination with the relatively dense, layered structure of cellulose fibers. Fig. 18. Possible alternatives to the landfilling of cellulose-rich sludge from wastewater treatment Life cycle assessment has shown that composting reduces greenhouse gas emissions in comparison to landfilling (Lou and Nair 2009). However, such predictions will depend on details, such as whether it is food waste, yard waste, a windrow composting system, or an engineered composting system (Hodge et al. 2016). When a mixture of biomaterials to be composted contains more readily decomposable sugar sources, such as starch, those will tend to be utilized first by microorganisms in preference to cellulose (López Alvarez et al. 2009). The progress of composting can be expected to be most favorable when the C:N elemental ratio is about 25:1 to 50:1 (Hubbe et al. 2010). When one focuses on treating waste cellulose only, there is a danger of having too high a C:N ratio. Fortunately, the composition of such compost mixtures can be optimized by adding such components as manure (Hubbe et al. 2010). By that means, the relative amount of available nitrogen can be adjusted to a favorable range. In addition, industrial composting can achieve sufficiently high temperatures to effectively break down the cellulose Composting Wind Fan Metabolic heating Landfill Anaerobic degradation CH4 collection Anaerobic digester Waste- water Treated water Returned sludge Air injection Agitated and aerated basin Clarifier Excess sludge Aeration with activated sludge Waste- water Agitation Clarifier Air Sludge H2O Sludge Common practice Low-tech, make soil CH4 Water in Water out Sludge Make fuel REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2437 (Leppanen et al. 2020). The goal in composting often is to achieve a mature compost, meaning that its organic content has been largely converted into humus-like compounds. These are mainly byproducts of lignin decomposition (Hubbe et al. 2010). Their slow rate of further biodegradation allows them to contribute to soil quality by holding water and binding various metal ions (Dinu and Shkinev 2020). Biofuel production When wastewater is treated using anaerobic conditions, valuable products can be collected, including methane and/or hydrogen (Hubbe et al. 2016; Nguyen et al. 2021), which can be used as fuels. The technology is relatively mature. However, it is important to keep one’s sense of proportions. The amounts of methane or hydrogen that can be produced in a wastewater treatment operation are often about in the same order of magnitude as the amounts of heat energy and mechanical energy to run the treatment plant itself (Nguyen et al. 2021). Most of the methane or hydrogen collected at US wastewater treatment plants is merely flamed off (Shen et al. 2015). From a life cycle perspective, the bigger benefits include a net reduction in greenhouse gas emissions and a relatively low discharge of final sludge needing to be landfilled (Bagi et al. 2017; Zhen et al. 2017). In addition to methane production, extensive research has been devoted to the conversion of cellulosic resources to liquid fuels, such as ethanol. This can be done either through enzymatic saccharification (Ceaser et al. 2024; Joyia et al. 2024) or by thermal processing (Hoang et al. 2021; Qiu et al. 2022). Of these two main approaches, the enzymatic route is generally better suited for cellulosic materials recovered from wastewater, since it does not require evaporation of the water, which has a high demand for energy. However, as noted in the review articles cited above, though both enzymatic and thermal approaches have been shown to be technically feasible, there is a challenge to compete with the current costs of fossil fuels. Seawater, Microplastics, and Cellulose Fibers As has been noted, the laundering of textile articles can be a source of small fibrous material, including microplastics (Ladewig et al. 2015; Hartline et al. 2016; Sillanpää and Sainio 2017; Zambrano et al. 2019). These will enter municipal wastewater, and presumably some of it may remain in the treated water, thereby passing into streams leading to the ocean (Ladewig et al. 2015). Studies have shown that it is possible to use fine filters to intercept such fibers at the household washing machine or laundromat (De Falco et al. 2018, 2019; McIlwraith et al. 2019; Erdle et al. 2021). However, the noted success reported in such studies suggests that filtering also could take place during wastewater treatment. Two options can be considered. As described above, there already has been work related to collecting fibrous content from incoming wastewater by filtration (see Table 17). A third option, which is likely to be the simplest and cheapest, would be to install and operate suitably fine filters at the discharge point of the wastewater treatment plant. This is where the water would be the cleanest, and thus the demands placed on such filters would be the lowest. As another version of the filtering option, cellulosic fibers and other fibers also would be fully retained on membrane filters, e.g. nanofiltration or ultrafiltration (Mohammad et al. 2015; Hubbe et al. 2016; Al Aani et al. 2020), which are sometimes employed as a polishing step when needed at the end of a wastewater treatment operation. REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2438 CONCLUDING STATEMENTS This review has considered the biodegradability of cellulose fibers. Published studies were considered to shed light not only on the rates and extents of biodegradation, but also to understand various factors that affect biodegradation. Important factors include the presence and activity of enzymes, the type of cellulose fibers and their lignin content, and environmental conditions, which can include moisture content, temperature, C:N ratio, and the presence of counter-ions. In general, cellulose fibers, including cotton and wood- based fibers, can be regarded as a natural part of the environment, with potential to fit in well with natural cycles of biodegradation and regrowth of plants. Rates of cellulose fiber biodegradability are generally fast enough to alleviate concerns about long-term buildup of cellulose fibers in waterways. As shown in Table 5, for example, cotton typically biodegraded in the range 30% to 90% over the course of 15 to 90 days. Reported rates of cellulose biodegradation are slower than highly degradable natural polymers, such as starch, but much faster than hard-to-biodegrade synthetic polymers such as polyesters and polyolefins. Though the rates and extents of cellulose fiber biodegradation are different for soils, fresh water, seawater, and various sludge treatment operations, such as anaerobic digestion, most cellulosic material will degrade within several weeks, according to most of the studies cited in this work. An exception to this is the high solids/low liquids environment of a landfill, where biodegradation occurs over decades. ACKNOWLEDGEMENTS The authors are grateful to two experts in the field who studied an earlier version of this article and suggested ways to improve it. These experts were Margaret W. Frey of Cornell University, Vincent V. C. Woo Professor in Fiber Science & Apparel Design, College of Human Ecology, and Carmen-Alice Teacă of Petru Poni Institute of Macromolecular Chemistry, Center of Advanced Research for Bionanoconjugates and Biopolymers, 41A Gr Gh Voda Alley, Iasi 700487, Romania. The preparation of the review article was funded by Cotton Incorporated, located in Cary, North Carolina, USA. REFERENCES CITED 5 Gyres Institute (2023). “Better alternatives 3.0, a case study on bioplastic products and packaging,” Nov. 2023, https://static1.squarespace.com/static/6537fd1a80e60f606d49 aaff/t/65a823cae7f9fc3a3973bd73/1705825414688/Better+Alternatives+3.pdf Aguiar, A., and Ferraz, A. (2011). “Mechanisms involved in the biodegradation of lignocellulosic materials and related technological applications,” Quimica Nova 34(10), 1729-1738. DOI: 10.1590/S0100-40422011001000006 Ahmed, A. S., Bahreini, G., Ho, D., Sridhar, G., Gupta, M., Wessels, C., Marcelis, P., Elbeshbishy, E., Rosso, D., Santoro, D., and Nakhla, G. (2019). “Fate of cellulose in primary and secondary treatment at municipal water resource recovery facilities,” Water Environ. Res. 91, 1479-1489. DOI: 10.1002/wer.1145. Ai, B. L., Zheng, L. L., Li, W. Q., Zheng, X. Y., Yang, Y., Xiao, D., Shi, J., Sheng, Z. W. (2021). “Biodegradable cellulose film prepared from banana pseudo-stem using an REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2439 ionic liquid for mango preservation,” Front. Plant Sci. 12, article 625878. DOI: 10.3389/fpls.2021.625878 Al Aani, S., Mustafa, T. N., and Hilal, N. (2020). “Ultrafiltration membranes for wastewater and water process engineering: A comprehensive statistical review over the past decade,” J. Water Proc. Eng. 35, article 101241. DOI: 10.1016/j.jwpe.2020.101241 Alwaya, W., Perju, A., Schwarz, M., Bonhotal, J., Pires, S., Ankeny, M., Daystar, J., and Frey, M. (2024). “The compostability of denim fabrics dyed with various indigos,” BioResources 19(2), 2685-2700. DOI: 10.15376/biores.19.2.2685-2700 Ardizzone, S., Dioguardi, F. S., Mussini, T., Mussini, P. R., Rondinini, S., Verceli, B., and Vertova, A. (1999). “Microcrystalline cellulose powders: Structure, surface features and water sorption capability,” Cellulose 6, 57-69. DOI: 10.1023/A:1009204309120 Armir, N. A. Z., Zulkifli, A., Gunaseelan, S., Palanivelu, S. D., Salleh, K. M., Othman, M. H. C., and Zakaria, S. (2021). “Regenerated cellulose products for agricultural and their potential: A review,” Polymers 13(20), article 3586. DOI: 10.3390/polym13203586 Armstrong, M. (2018). “The U.S. leads the world in toilet paper consumption,” [WWW Document]. Statista. URL https://www.statista.com/chart/15676/cmo-toilet-paper- consumption/ Athey, S. N., Adams, J. K., Erdle, L. M., Jantunen, L. M., Helm, P. A., Finkelstein, S. A., and Diamond, M. L. (2020). “The widespread environmental footprint of indigo denim microfibers from blue jeans,” Environ. Sci. Tech. Lett. 7(11), 840-847. DOI: 10.1021/acs.estlett.0c00498 Auxenfans, T., Buchoux, S., Larcher, D., Husson, G., Husson, E., and Sarazin, C. (2014). “Enzymatic saccharification and structural properties of industrial wood sawdust: Recycled ionic liquids pretreatments,” Energy Convers. Manag. 88, 1094-1103. DOI: 10.1016/j.enconman.2014.04.027 Bagi, Z., Acs, N., Böjti, T., Kakuk, B., Rákhely, G., Strang, O., Szuhaj, M., Wirth, R., and Kovács, K. L. (2017). “Biomethane: The energy storage, platform chemical and greenhouse gas mitigation target,” Anaerobe 46, 13-22. DOI: 10.1016/j.anaerobe.2017.03.001 Bai, L. K., Hu, H. R., and Xu, J. F. (2012). “Influences of configuration and molecular weight of hemicelluloses on their paper-strengthening effects,” Carbohyd. Polym. 88(4), 1258-1263. DOI: 10.1016/j.carbpol.2012.02.002 Bajpai, P. (2012). Environmentally Benign Approaches for Pulp Bleaching, 2nd Ed., Elsevier, Boston. Barlaz, M. A. (1998). “Carbon storage during biodegradation of municipal solid waste components in laboratory-scale landfills,” Global Biogeochemical Cycles 12(2), 373- 380. DOI: 10.1029/98GB00350 Barlaz, M. A. (2006). “Forest products decomposition in municipal solid waste landfills,” Waste Manag. 26(4), 321-333. DOI: 10.1016/j.wasman.2005.11.002 Barlaz, M. A. (2009). “WARM component-specific decay rate method,” Memo sent to the Office of Resource Conservation and Recovery, EPA, https://www.epa.gov/sites/default/files/2016- 03/documents/warm_decay_rate_structure_10_30_2009.pdf Beckham, G. T., Matthews, J. F., Peters, B., Bombie, Y. J., Himmel, M. E., and Crowley, M. F. (2011). “Molecular-level origins of biomass recalcitrance: Decrystallization REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2440 free energies for four common cellulose polymorphs,” J. Phys. Chem. B 115, 4118- 4127. DOI: 10.1021/jp1106394 Berlin, A., Gilkes, N., Kurabi, A., Bura, R., Tu, M. B., Kilburn, D., and Saddler, J. (2005). “Weak lignin-binding enzymes – A novel approach to improve activity of cellulases for hydrolysis of lignocellulosics,” Appl. Biochem. Biotechnol. 121, 163- 170. DOI: 10.1385/ABAB:121:1-3:0163 Bhagwat, G., Gray, K., Wilson, S. P., Muniyasamy, S., Vincent, S. G. T., Bush, R., and Palanisami, T. (2020). “Benchmarking bioplastics: A natural step towards a sustainable future,” J. Polym. Environ. 28(12), 3055-3075. DOI: 10.1007/s10924- 020-01830-8 Bhat, M. K., and Bhat, S. (1997). “Cellulose degrading enzymes and their potential industrial applications,” Biotech. Advan. 15(3-4), 583-620. DOI: 10.1016/S0734- 9750(97)00006-2 Briassoulis, D., Dejean, C., and Picuno, P. (2010). “Critical review of norms and standards for biodegradable agricultural plastics. Part II: Composting,” J. Polym. Environ. 18(3), 364-383. DOI: 10.1007/s10924-010-0222-z Bruzzoniti, M. C., Maina, R., De Carlo, R. M., Sarzanini, C., and Tumiatti, V. (2014). “GC methods for the determination of methanol and ethanol in insulating mineral oils as markers of cellulose degradation in power transformers,” Chromatographia 77(15- 16), 1081-1089. DOI: 10.1007/s10337-014-2650-8 Bugg, T. D. H., Ahmad, M., Hardiman, E. M., and Rahmanpour, R. (2011). “Pathways for degradation of lignin in bacteria and fungi,” Natur. Prod. Rep. 28(12), 1883-1896. DOI: 10.1039/c1np00042j Carvalho, W., Canilha, L., Ferraz, A., and Milagres, A. M. F. (2009). “A vision of wood structure, composition and biodegradation,” Quimica Nova 12(8), 2191-2195. DOI: 10.1590/S0100-40422009000800033 Ceaser, R., Montané, D., Constanti, M., and Medina, F. (2024). “Current progress on lignocellulosic bioethanol including a technological and economical perspective,” Environ. Devel. Sustain, early access. DOI: 10.1007/s10668-024-04792-2 Chan, Y. J., Chong, M. F., Law, C. L., and Hassell, D. G. (2009). “A review on anaerobic-aerobic treatment of industrial and municipal wastewater,” Chem. Eng. J. 155(102), 1-18. DOI: 10.1016/j.cej.2009.06.041 Chang, Y. H., Lin, C. L., Hsu, Y. H., and Lin, J. H. (2021). “Medium effect on acid degradation of cotton and wood celluloses,” Indust. Crops Prod. 167, article 113540. DOI: 10.1016/j.indcrop.2021.113540 Chen, H., Han, Q., Venditti, R. A., and Jameel, H. (2015). “Enzymatic hydrolysis of pretreated newspaper having high lignin content for bioethanol production,” BioResources 10(3), 4077-4098. DOI: 10.15376/biores.10.3.4077-4098 Chen, R., Nie, Y. L., Kato, H., Wu, J., Utashiro, T., Ju, J. B., Yue, S. C., Jiang, H. Y., Zhang, L., and Li, Y. Y. (2017). “Methanogenic degradation of toilet-paper cellulose upon sewage treatment in an anaerobic membrane bioreactor at room temperature,” Bioresour. Technol. 228, 69-76. DOI: 10.1016/j.biortech.2016.12.089 Chen, W. J., Zhan, Y. B., Zhang, X. J., Shi, X., Wang, Z. G., Xu, S. Q., Chang, Y., Ding, G. C., Li, J., and Wei, Y. Q. (2022). “Influence of carbon-to-phosphorus ratios on phosphorus fractions transformation and bacterial community succession in phosphorus-enriched composting,” Bioresour. Technol. 362, article 127786. DOI: 10.1016/j.biortech.2022.127786 REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2441 Cheng, Y. A., Mondal, A. K., Wu, S., Xu, D. Z., Ning, D. W., Ni, Y. H., and Huang, F. (2020). “Study on the anti-biodegradation property of tunicate cellulose,” Polymers 12(12), article 3071. DOI: 10.3390/polym12123071 Chung, C., Lee, M., and Choe, E. K. (2004). “Characterization of cotton fabric scouring by FT-IR ATR spectroscopy,” Carbohyd. Polym. 58(4), 417-420. DOI: 10.1016/j.carbpol.2004.08.005 Chynoweth, D. P., Owens, J., Okeefe, D., Earle, J. F. K., Bosch, G., and Legrand, R. (1992). “Sequential batch anaerobic composting of the organic fraction of municipal solid-waste,” Water Sci. Technol. 25(7), 327-339. DOI: 10.2166/wst.1992.0165 Chio, C. L., Sain, M., and Qin, W. S. (2019). “Lignin utilization: A review of lignin depolymerization from various aspects,” Renew Sustain Energy Rev. 107, 232-249. DOI: 10.1016/j.rser.2019.03.008 Cho, J. K., Park, S. C., and Chang, H. N. (1995). “Biochemical methane potential and solid-state anaerobic-digestion of Korean food wastes,” BioResour. Technol. 52(3), 245-253. DOI: 10.1016/0960-8524(95)00031-9 Cipolletta, G., Eusebi, A. L., Palmieri, S., Giosuè, C., Tittarelli, F., Frison, N., Pastore, C., Foglia, A., and Fatone, F. (2019). “Toilet paper recovery from municipal wastewater and application in building sector,” Earth Environ. Sci. 296, article 012024. DOI: 10.1088/1755-1315/296/1/012024. Clark, A. J., Calvillo, J. L., Roosa, M. S., Green, D. B., and Ganske, J. A. (2011). “Degradation product emission from historic and modern books by headspace SPME/GC-MS: Evaluation of lipid oxidation and cellulose hydrolysis,” Anal. Bioanal. Chem. 399(10), 3589-3600. DOI: 10.1007/s00216-011-4680-5 Cooke, T. F. (1990). “Biodegradability of polymers and fibers – A review of the literature,” J. Polym. Eng. 9(3), 171-211. DOI: 10.1515/POLYENG.1990.9.3.171 Corona, B., Shen, L., Reike, D., Carreón, J. R., and Worrell, E. (2019). “Towards sustainable development through the circular economy – A review and critical assessment on current circularity metrics,” Resour. Concerv. Recyc. 151, article 104498. DOI: 10.1016/j.resconrec.2019.104498 Dahlman, O., Jacobs, A., and Sjöberg, J. (2003). “Molecular properties of hemicelluloses located in the surface and inner layers of hardwood and softwood pulps,” Cellulose 10(4), 325-334. DOI: 10.1023/A:1027316926308 Das, D., Bhattacharjee, S., and Bhaladhare, S. (2023). “Preparation of cellulose hydrogels and hydrogel nanocomposites reinforced by crystalline cellulose nanofibers (CNFs) as a water reservoir for agriculture use,” ACS Appl. Polym. Mater. 5(4), 2895-2904. DOI: 10.1021/acsapm.3c00109 Daniel, R. M., Danson, M. J., Eisenthal, R., Lee, C. K., and Peterson, M. E. (2008). “The effect of temperature on enzyme activity: New insights and their implications,” Extremophiles 12(1), 51-59. DOI: 10.1007/s00792-007-0089-7 Datta, R., Kelkar, A., Baraniya, D., Molaei, A., Moulick, A., Meena, R. S., and Formanek, P. (2017). “Enzymatic degradation of lignin in soil: A review,” Sustainability 9(7), article 1163. DOI: 10.3390/su9071163 de Assis, T., Huang, S. X., Driemeier, C. E., Donohoe, B. S., Kim, C., Kim, S. H., Gonzalez, R., Jameel, H., and Park, S. (2018). “Toward an understanding of the increase in enzymatic hydrolysis by mechanical refining,” Biotechnol. Biofuels 11, article 289. DOI: 10.1186/s13068-018-1289-3 De Falco, F., Cocca, M., Avella, M., and Thompson, R. C. (2020). “Microfiber release to water, via laundering, and to air, via everyday use: A comparison between polyester REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2442 clothing with differing textile parameters,” Environ. Sci. Technol. 54(6), 3288-3296. DOI: 10.1021/acs.est.9b06892 De Falco, F., Di Pace, E., Cocca, M., and Avella, M. (2019). “The contribution of washing processes of synthetic clothes to microplastic pollution,” Sci. Rep. 9, article 6633. DOI: 10.1038/s41598-019-43023-x De Falco, F., Gullo, M. P., Gentile, G., Di Pace, E., Cocca, M., Gelabert, L., Brouta- Agnésa, M., Rovira, A., Escudero, R., Villalba, R., Mossotti, R., Montarsolo, A., Gavignano, S., Tonin, C., and Avella, M. (2018). “Evaluation of microplastic release caused by textile washing processes of synthetic fabrics,” Environ. Pollut. 236, 916- 925. DOI: 10.1016/j.envpol.2017.10.057 De La Cruz, F. B, and Barlaz, M. (2010). “Estimation of waste component-specific landfill decay rates using laboratory-scale decomposition data,” Environ. Sci. Technol. 44(12), 4722-4728. DOI: 10.1021/es100240r Dence, C. W., and Reeve, D. W. (1996). Pulp Bleaching: Principles and Practice, TAPPI Press, Atlanta. Derwent, R. G. (2020). “Global warming potential (GWP) for methane: Monte Carlo analysis of the uncertainties in global tropospheric model predictions,” Atmos. 11(5), article 486. DOI: 10.3390/atmos11050486 de Souza, P. M., and Magalhaes, P. D. E. (2010). “Application of microbial α-amylase in industry – A review,” Brazil. J. Microbiol. 41(4), 850-861. DOI: 10.1590/S1517- 83822010000400004 Devi, A., Bajar, S., Kour, H., Kothari, R., Pant, D., and Singh, A. (2022). “Lignocellu- losic biomass valorization for bioethanol production: A circular bioeconomy approach,” Bioenergy Res. 15(4), 1820-1841. DOI: 10.1007/s12155-022-10401-9 Dinu, M. I., and Shkinev, V. M. (2020). “Complexation of metal ions with organic substances of humus nature: Methods of study and structural features of ligands, and distribution of elements between species,” Geochem. Internat. 58(2), 200-211. DOI: 10.1134/S0016702920020032 Djordjevicová, D., Miino, M. C., Racek, J., Hlavínek, P., Chorazy, T., Rajakovic- Ognjanovic, V., and Cvijetic, N. (2023). “Influence of cellulose on the anoxic treatment of domestic wastewater in septic tanks: Statistical analysis of the chemical and physico-chemical parameters,” Sustainability 15(10), article 7990. DOI: 10.3390/su15107990 Dobrin, E., Rosu, M., Draghici, E., and Nechita, P. (2012). “Evaluation of potential biodegradation of materials based on peat and waste of cellulose fibres for use in seedling production,” Sci. Papers – Ser. B – Hort. 56, 89-91. Dong, C. H., Meng, Y. H., Wang, B. S., Zhu, W. Y., and Pang, Z. Q. (2020). “Effect of antisolvents on the structure of regenerated cellulose: Development of an efficient regeneration process,” Holzforschung 74(9), 881-890. DOI: 10.1515/hf-2019-0100 Doshi, M. R., and Dyer, J. M. (1997). Paper Recycling Challenge, Doshi & Associates, Appleton, WI. dos Santos, J. R., Moreira, L. R. D., and Ferreira, E. X. (2023). “Cellulose-degrading enzymes: Key players in biorefinery development,” Biologia 78(7), 1759-1772. DOI: 10.1007/s11756-022-01274-6 Duchesne, I., Hult, E., Molin, U., Daniel, G., Iversen, T., and Lennholm, H. (2001). “The influence of hemicellulose on fibril aggregation of kraft pulp fibres as revealed by FE-SEM and CP/MAS 13C-NMR,” Cellulose 8(2), 103-111. DOI: 10.1023/A:1016645809958 REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2443 Dupont, A.-L., Egasse, C., Morin, A., and Vasseur, F. (2007). “Comprehensive characterisation of cellulose- and lignocelluloses- degradation products in aged papers: Capillary zone electrophoresis of low-molar mass organic acids, carbohydrates, and aromatic lignin derivatives,” Carbohydrate Polymers 68, 1-16. DOI: 10.1016/j.carbpol.2006.07.005 Edberg, N., and Hofsten, B. V. (1975). “Cellulose degradation in wastewater treatment,” J. Water Pollut. Control Fed. 47(5), 1012-1020. Eichhorn, S. J., and Young, R. J. (2001). “The Young’s modulus of a microcrystalline cellulose,” Cellulose 8(3), 197-207. DOI: 10.1023/A:1013181804540 Eleazer, W. E, Odle, W. S., Wang, Y.-S., and Barlaz, M. A. (1997). “Biodegradability of municipal solid waste components in laboratory-scale landfills,” Env. Sci. Technol. 31(3), 911-917. DOI: 10.1021/es9606788 EPA (2023). Environmental Protection Agency, “Landfill gas Monte Carlo model documentation and results,” in: Waste Reduction Model (WARM) Data Quality Assessment Report, https://www.epa.gov/warm Erdle, L. M., Parto, D. N., Sweetnam, D., and Rochman, C. M. (2021). “Washing machine filters reduce microfiber emissions: Evidence from a community-scale pilot in Parry Sound, Ontario,” Front. Marine Sci. 8, article 777865. DOI: 10.3389/fmars.2021.777865 Esteghlalian, A. R., Mansfield, S. D., and Saddler, J. N. (2002). “Cellulases: Agents for fiber modification or bioconversion? The effect of substrate accessibility on cellulose enzymatic hydrolyzability,” in: Biotechnology in the Pulp and Paper Industry: 8th ICBPPI, L. Viikari and R. Lantto (eds.), book series Progress in Biotechnology 21, 21-36. DOI: 10.1016/S0921-0423(02)80005-3 Farooq, M. A., Ali, S., Hassan, A., Tahir, H. M., Mumtaz, S., and Mumtaz, S. (2021). “Biosynthesis and industrial applications of α-amylase: A review,” Archives Microbiol. 203(4), 1281-1292. DOI: 10.1007/s00203-020-02128-y Freeman, M. H., and McIntyre, C. R. (2008). “A comprehensive review of copper-based wood preservatives,” Forest Prod. J. 58(11), 6-27. Frost, H., Zambrano, M. C., Leonas, K., Pawlak, J. J., and Venditti, R. A. (2020). “Do recycled cotton or polyester fibers influence the shedding propensity of fabrics during laundering?,” AATCC Journal of Research 7(1 suppl), 32-41. DOI: 10.14504/ajr.7.S1.4 Gabrielii, I., Gatenholm, P., Glasser, W. G., Jain, R. K., and Kenne, L. (2000). “Separation, characterization and hydrogel-formation of hemicellulose from aspen wood,” Carbohyd. Polym. 43(4), 367-374. DOI: 10.1016/S0144-8617(00)00181-8 Ge, H., Jensen, P., and Batstone, D. (2011). “Relative kinetics of anaerobic digestion under thermophilic and mesophilic conditions,” Water Sci. Technol. 64, 848-853. DOI10.2166/wst.2011.571 Gharehkhani, S., Sadeghinezhad, E., Kazi, S. N., Yarmand, H., Badarudin, A., Safaei, M. R., and Zubir, M. N. M. (2015). “Basic effects of pulp refining on fiber properties – A review,” Carbohyd. Polym. 115, 785-803. DOI: 10.1016/j.carbpol.2014.08.047 Ghasimi, D. S. M., Zandvoort, M. H., Adriaanse, M., van Lier, J. B., and de Kreuk, M. (2016). “Comparative analysis of the digestibility of sewage fine sieved fraction and hygiene paper produced from virgin fibers and recycled fibers,” Waste Management 53, 156-164. DOI: 10.1016/j.wasman.2016.04.034 REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2444 Gírio, F. M., Fonseca, C., Carvalheiro, F., Duarte, L. C., Marques, S., and Bogel-Lukasik, R. (2010). “Hemicelluloses for fuel ethanol: A review,” Bioresour. Technol. 101(13), 4775-4800. DOI: 10.1016/j.biortech.2010.01.088 Girometta, C., Zeffiro, A., Malagodi, M., Savino, E., Doria, E., Nielsen, E., Buttafava, A., and Dondi, D. (2017). “Pretreatment of alfalfa stems by wood decay fungus Perenniporia meridionalis improves cellulose degradation and minimizes the use of chemicals,” Cellulose 24(9), 3803-3813. DOI: 10.1007/s10570-017-1395-6 Glasser, W. G., McCartney, B. K., and Samaranayake, G. (1994). “Cellulose derivatives with low degree of substitution. 3. The biodegradability of cellulose esters using a simple enzyme assay,” Biotech. Prog. 10(2), 214-219. DOI: 10.1021/bp00026a011 Greff, B., Szigeti, J., Nagy, A., Lakatos, E., and Varga, L. (2022). “Influence of microbial inoculants on co-composting of lignocellulosic crop residues with farm animal manure: A review,” J. Environ. Manag. 302B, article 114088. DOI: 10.1016/j.jenvman.2021.114088 Gupta, M., Ho, D., Santoro, D., Torfs, E., Doucet, J., Vanrolleghem, P. A., and Nakhla, G. (2018). “Experimental assessment and validation of quantification methods for cellulose content in municipal wastewater and sludge,” Environ. Sci. Technol. 25(17), 16743-16753. DOI: 10.1007/s11356-018-1807-7 Haap, J., Classen, E., Beringer, J., Mecheels, S., and Gutmann, J. S. (2019). “Microplastic fibers released by textile laundry: A new analytical approach for the determination of fibers in effluents,” Water (Switzerland) 11(10). DOI: 10.3390/w11102088. Han, Y., Liu, W. Y., Chang, N., Sun, L., Bello, A., Deng, L. T., Zhao, L. Y., Egbeagu, U. U., Wang, B., and Zhao, Y. (2023). “Exploration of β-glucosidase-producing microorganisms community structure and key communities driving cellulose degradation during composting of pure corn straw by multi-interaction analysis,” J. Environ. Manag. 325(B), article 116694. DOI: 10.1016/j.jenvman.2022.116694 Hartline, N. L., Bruce, N. J., Karba, S. N., Ruff, E. O., Sonar, S. U., and Holden, P. A. (2016). “Microfiber masses recovered from conventional machine washing of new or aged garments,” Environ. Sci. Technol. 50, 11532-11538. DOI: 10.1021/acs.est.6b03045. Henriksson, D. C., Winkler, W. F., Lucas, B. E., and Topping, P. (2017). “Integrated method and system for recycling waste material,” US Patent 9,752,279 B2. Hernawan, F. A., Syamani, F. A., and Kurniati, M. (2020). “Biodegradable mulch based on cellulose of cornhusk with addition anti UV-tinuvin,” Seminar Nasional Fisika (SNF) Unesa 2019 1491, article 012051. DOI: 10.1088/1742-6596/1491/1/012051 Hoang, A. T., Ong, H. C., Fattah, I. M. R., Chong, C. T., Cheng, C. K., Sakthivel, R., and Ok, Y. S. (2021). “Progress on the lignocellulosic biomass pyrolysis for biofuel production toward environmental sustainability,” Fuel Proc. Technol. 223, article 106997. DOI: 10.1016/j.fuproc.2021.106997 Hodge, K. L., Levis, J. W., DeCarolis, J. F., and Barlaz, M. A. (2016). “Systematic evaluation of industrial, commercial, and institutional food waste management strategies in the United States,” Environ. Sci. Technol. 50, 8444-8452. DOI: 10.1021/acs.est.6b00893 Homma, I., Fukuzumi, H., Saito, T., and Isogai, A. (2013a). “Effects of carboxyl-group counter-ions on biodegradation behaviors of TEMPO-oxidized cellulose fibers and nanofibril films,” Cellulose 20(5), 2505-2515. DOI: 10.1007/s10570-013-0020-6 REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2445 Homma, I., Isogai, T., Saito, T., and Isogai, A. (2013b). “Degradation of TEMPO- oxidized cellulose fibers and nanofibrils by crude cellulase,” Cellulose 20(2), 795- 805. DOI: 10.1007/s10570-013-9872-z Honda, S., Miyata, N., and Iwahori, K. (2000). “A survey of cellulose profiles in actual wastewater treatment plants,” Japanese Journal of Water Treatment Biology 36(1), 9- 14. DOI: 10.2521/jswtb.36.9 Honda, S., Miyata, N., and Iwahori, K. (2002). “Recovery of biomass cellulose from waste sewage sludge,” Journal of Material Cycles and Waste Management 4(1), 46- 50. Horn, S. J., Vaaje-Kolstad, G., Westereng, B., and Eijsink, V. G. H. (2012). “Novel enzymes for the degradation of cellulose,” Biotechnol. Biofuels 5. DOI: 10.1186/1754-6834-5-45. Hosseini, S. A., and Shah, N. (2011). “Modelling enzymatic hydrolysis of cellulose part I: Population balance modelling of hydrolysis by endoglucanase,” Biomass Bioenergy 35(9), 3841-3848. DOI: 10.1016/j.biombioe.2011.04.026 Houfani, A. A., Anders, N., Spiess, A. C., Baldrian, P., and Benallaoua, S. (2020). “Insights from enzymatic degradation of cellulose and hemicellulose to fermentable sugars – A review,” Biomass Bioenergy 134, article 105481. DOI: 10.1016/j.biombioe.2020.105481 Huang, D. D., Du, Y., Xu, Q. Y., and Ko, J. H. (2021). “Quantification and control of gaseous emissions from solid waste landfill surfaces,” J. Environ. Manag. 302, article 114001. DOI: 10.1016/j.jenvman.2021.114001 Huang, C. X., Jiang, X., Shen, X. J., Hu, J. G., Tang, W., Wu, X. X., Ragauskas, A., Jameel, H., Meng, X. Z., and Yong, Q. (2022a). “Lignin-enzyme interaction: A roadblock for efficient enzymatic hydrolysis of lignocellulosics,” Renew. Sustain. Energy Rev. 154, article 111822. DOI: 10.1016/j.rser.2021.111822 Huang, C. X., Li, R. L., Tang, W., Zheng, Y. Y., and Meng, X. Z. (2022b). “Improve enzymatic hydrolysis of lignocellulosic biomass by modifying lignin structure via sulfite pretreatment and using lignin blockers,” Fermentation – Basel 8(10), article 558. DOI: 10.3390/fermentation8100558 Hubbe, M. A. (2007). “Paper’s resistance to wetting – A review of internal sizing chemicals and their effects,” BioResources 2(1), 106-145. DOI: 10.15376/biores.2.1.106-145 Hubbe, M. A., Venditti, R. A., and Rojas, O. J. (2007). “What happens to cellulosic fibers during papermaking and recycling? A review,” BioResources 2(4), 739-788. DOI: 10.15376/biores.2.4.739-788 Hubbe, M. A., Pawlak, J. J., and Koukoulas, A. A. (2008). “Paper’s appearance: A review,” BioResources 3(2), 627-665. DOI: 10.15376/biores.3.2.627-665 Hubbe, M. A., Nazhad, M., and Sánchez, C. (2010). “Composting as a way to convert cellulosic biomass and organic waste into high-value soil amendments: A review,” BioResources 5(4), 2808-2854. DOI: 10.15376/biores.5.4.2808-2854 Hubbe, M. A., Metts, J. R., Hermosilla, D., Blanco, M. A., Yerushalmi, L., Haghighat, F., Lindholm-Lehto, P., Khodaparast, Z., Kamali, M., and Elliott, A. (2016). “Wastewater treatment and reclamation: A review of pulp and paper industry practices and opportunities,” BioResources 11(3), 7953-8091. DOI: 10.15376/biores.11.3.Hubbe REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2446 Hubbe, M. A., Lavoine, N., Lucia, L. A., and Dou, C. (2021). “Formulating bioplastic composites for biodegradability, recycling, and performance: A review,” BioResources 16(1), 2021-2083. DOI: 10.15376/biores.16.1.Hubbe Hubbe, M. A., Szlek, D. B., and Vera, R. E. (2022). “Detergency mechanisms and cellulosic surfaces: A review,” BioResources 17(4), 7167-7249. DOI: 10.15376/biores.17.4.Hubbe Huber-Humer, M., Gebert, J., and Hilger, H. (2008). “Biotic systems to mitigate landfill methane emissions,” Waste Manag. Res. 26(1), 33-46. DOI: 10.1177/0734242X07087977 Hurwitz, E., Beck, A. J., Sakellariou, E., and Krup, M. (1961). “Degradation of cellulose by activated sludge treatment,” J. Water Pollut. Control Fed. 33, 1070-1075. Ibrahim, M. M., El-Zawawy, W. K., Jüttke, Y., Koschella, A., and Heinze, T. (2013). “Cellulose and microcrystalline cellulose from rice straw and banana plant waste: Preparation and characterization,” Cellulose 20(5), 2403-2416. DOI: 10.1007/s10570- 013-9992-5 Irvine, G. M. (1985). “The significance of the glass-transition of lignin in thermomechan- ical pulping,” Wood Sci. Technol. 19(2), 139-149. DOI: 10.1007/BF00353074 Janusz, G., Pawlik, A., Sulej, J., Swiderska-Burek, U., Jarosz-Wilkolazka, A., and Paszczynski, A. (2017). “Lignin degradation: Microorganisms, enzymes involved, genomes analysis and evolution,” FEMS Microbiol. Rev. 41(6), 941-962. DOI: 10.1093/femsre/fux049 Javaid, R., Sabir, A., Sheikh, N., and Ferhan, M. (2019). “Recent advances in applications of acidophilic fungi to produce chemicals,” Molecules 24(4), article 786. DOI: 10.3390/molecules24040786 Jia, F., Yin, S. Y., Chen, L. J., and Chen, X. W. (2020). “The circular economy in the textile and apparel industry: A systematic literature review,” J. Cleaner Prod. 259, article 120728. DOI: 10.1016/j.jclepro.2020.120728 Johnson, S., Echeverria, D., Venditti, R., Jameel, H, and Yao, Y. (2022). “Supply chain of waste cotton recycling and reuse: A review,” AATCC J. Res. 7(1). DOI: 10.14504/ajr.7.S Joyia, M. A. K., Ahmad, M., Chen, Y. F., Mustaqeem, M., Ali, A., Abbas, A., and Gondal, M. A. (2024). “Trends and advances in sustainable bioethanol production technologies from first to fourth generation: A critical review,” Energy Conver. Manag. 321, article 119037. DOI: 10.1016/j.enconman.2024.119037 Kaczmarek, M. B., Struszczyk-Swita, K., Li, X. K., Szczesna-Antczak, M., and Daroch, M. (2019). “Enzymatic modifications of chitin, chitosan, and chitooligosaccharides,” Front. Bioeng. Biotech. 7, article 243. DOI: 10.3389/fbioe.2019.00243 Kafle, K., Shin, H., Lee, C. M., Park, S., and Kim, S. H. (2015). “Progressive structural changes of Avicel, bleached softwood and bacterial cellulose during enzymatic hydrolysis,” Sci. Rep. 5, 1-10. DOI: 10.1038/srep15102 Kalka, S., Huber, T., Steinberg, J., Baronian, K., Mussig, J., and Staiger, M. P. (2014). “Biodegradability of all-cellulose composite laminates,” Composites: Part A – Appl. Sci. Manufac. 59, 37-44. DOI: 10.1016/j.compositesa.2013.12.012 Kerr, A. J., and Goring, D. A. I. (1976). “Distribution of lignin in thermomechanical fibers,” TAPPI 59(10), 116-117. Khan, M. N., Lacroix, M., Wessels, C., and Van Dael, M. (2022). “Converting wastewater cellulose to valuable products: A techno-economic assessment,” J. Cleaner Prod. 365, article 132812. DOI: 10.1016/j.jclepro.2022.132812 REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2447 Khan, M. U., and Ahring, B. K. (2019). “Lignin degradation under anaerobic digestion: Influence of lignin modifications – A review,” Biomass Bioenergy 128, article 105325. DOI: 10.1016/j.biombioe.2019.105325 Kim, H., and Ralph, J. (2014). “A gel-state 2D-NMR method for plant cell wall profiling and analysis: A model study with the amorphous cellulose and xylan from ball-milled cotton linters,” RSC Adv. 4(15), 7549-7560. DOI: 10.1039/c3ra46338a Kim, J., Kim, J., and Lee, C. (2019). “Anaerobic co-digestion of food waste, human feces, and toilet paper: Methane potential and synergistic effect,” Fuel 248, 189-195. DOI: 10.1016/j.fuel.2019.03.081 Kim, I. J., Lee, H. J., Choi, I. G., and Kim, K. H. (2014). “Synergistic proteins for the enhanced enzymatic hydrolysis of cellulose by cellulase,” Appl. Microbiol. Biotech. 98(20), 8469-8480. DOI: 10.1007/s00253-014-6001-3 Kim, M., Elbahrawi, M., Aryaei, A., Nakhla, G., Santoro, D., and Batstone, D. J. (2022). “Kinetics of aerobic cellulose degradation in raw municipal wastewater,” Sci. Total Environ. 802, article 149852. DOI: 10.1016/j.scitotenv.2021.149852. Klemencic, D., Simoncic, B., Tomsic, B., and Orel, B. (2010). “Biodegradation of silver functionalised cellulose fibres,” Carbohydr. Polym. 80(2), 426-435. DOI: 10.1016/j.carbpol.2009.11.049 Klemm, D., Heublein, B., Fink, H. P., and Bohn, A. (2005). “Cellulose: Fascinating biopolymer and sustainable raw material,” Angew. Chemie – Int. Ed. 44(22), 3358- 3393. DOI: 10.1002/anie.200460587 Kumar, S., Gaikwad, S. A., Shekdar, A. V., Kshirsagar, P. S., and Singh, R. N. (2004). “Estimation method for national methane emission from solid waste landfills,” Atmos. Environ. 38(21), 3481-3487. DOI: 10.1016/j.atmosenv.2004.02.057 Kwon, S., Zambrano, M. C., Pawlak, J. J., Ford, E., and Venditti, R. A. (2023a). “Aquatic biodegradation of poly(β-hydroxybutyrate) and polypropylene blends with compatibilizer and the generation of micro- and nano-plastics on biodegradation,” J. Polym. Environ. 31(8), 3619-3631. DOI: 10.1007/s10924-023-02832-y Kwon, S., Zambrano, M. C., Pawlak, J. J., Ford, E., and Venditti, R. A. (2024). “Aquatic biodegradation of poly(β-hydroxybutyrate) in polylactic acid and maleic anhydride blended fibers,” J. Poly. Res. 31(4), article 100. DOI: 10.1007/s10965-024-03930-8 Kwon, S., Zambrano, M. C., Pawlak, J. J., and Venditti, R. A. (2021). “Effect of lignocellulosic fiber composition on the aquatic biodegradation of wood pulps and the isolated cellulose, hemicellulose and lignin components: Kinetic modelling of the biodegradation process,” Cellulose 28(5), 2863-2877. DOI: 10.1007/s10570-021- 03680-6 Kwon, S., Zambrano, M. C., Venditti, R. A., Frazier, R., Zambrano, F., Gonzalez, R. W., and Pawlak, J. J. (2022). “Microfiber shedding from nonwoven materials including wipes and meltblown nonwovens in air and water environments,” Environ. Sci. Pollut. Res. 29(40), 60584-60599. DOI: 10.1007/s11356-022-20053-z Kwon, S., Zambrano, M. C., Venditti, R. A., and Pawlak, J. J. (2023b). “Aerobic aquatic biodegradation of bio-based and biodegradable polymers: Kinetic modeling and key factors for biodegradability,” Int. Biodeter. Biodegrad. 185, article 105671. DOI: 10.1016/j.ibiod.2023.105671 Ladewig, S. M., Bao, S., and Chow, A.T. (2015). “Natural fibers: A missing link to chemical pollution dispersion in aquatic environments,” Environ. Sci. Technol. 49, 12609-12610. DOI: 10.1021/acs.est.5b04754. REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2448 Lattuati-Derieux, A., Bonnassies-Termes, S., and Lavédrine, B. (2006). “Characterisation of compounds emitted during natural and artificial ageing of a book. Use of headspace-solid-phase microextraction/gas chromatography/mass spectrometry,” J. Cultural Heritage 7(2), 123-133. DOI: 10.1016/j.culher.2006.02.004 Lee, I., Evans, B. R., and Woodward, J. (2000). “The mechanism of cellulase action on cotton fibers: Evidence from atomic force microscopy,” Ultramicroscopy 82, 213- 221. DOI: 10.1016/S0304-3991(99)00158-8 Leppanen, I., Vikman, M., Harlin, A., and Orelma, H. (2020). “Enzymatic degradation and pilot-scale composting of cellulose-based films with different chemical structures,” J. Polym. Environ. 28(2), 458-470. DOI: 10.1007/s10924-019-01621-w Leschine, S. B. (1995). “Cellulose degradation in anaerobic environments,” Annu. Rev. Microbiol. 49, 399-426. DOI: 10.1146/annurev.mi.49.100195.002151. Levis, J., and Barlaz, M. A. (2014). “Landfill gas Monte Carlo model documentation and results,” report to the EPA, https://www.epa.gov/sites/default/files/2016- 03/documents/lanfl_gas_mont_carlo_modl.pdf Li, L., Frey, M., and Browning, K. J. (2010). “Biodegradability study on cotton and polyester fabrics,” J. Eng. Fibers Fabr. 5, 42-53. DOI: 10.1177/155892501000500406 Li, M., Pu, Y. Q., and Ragauskas, A. J. (2016). “Current understanding of the correlation of lignin structure with biomass recalcitrance,” Front. Chem. 4, article 45. DOI: 10.3389/fchem.2016.00045 Li, Q., Qi, W., Su, R., and He, Z. (2017). “Enhanced enzymatic hydrolysis and changes in structure of cellulose regenerated with ionic liquids,” Cellul. Chem. Technol. 51, 593-600. Li, W. W., Khalid, H., Zhu, Z., Zhang, R. H., Liu, G. Q., Chen, C., and Thorin, E. (2018). “Methane production through anaerobic digestion: Participation and digestion characteristics of cellulose, hemicellulose and lignin,” Appl. Energy 226, 1219-1228. DOI: 10.1016/j.apenergy.2018.05.055 Li, S., Wu, Z., and Liu, G. (2019). “Degradation kinetics of toilet paper fiber during wastewater treatment: Effects of solid retention time and microbial community,” Chemosphere 225, 915-926. DOI: 10.1016/j.chemosphere.2019.03.097. Li, S. M., Wu, Z. Z., Wu, Z. X., and Liu, G. Q. (2020). “Enhancing fiber recovery from wastewater may require toilet paper redesign,” J. Cleaner Prod. 261, article 121138. DOI: 10.1016/j.jclepro.2020.121138 Li, M., Jiang, B., Wu, W. J., Wu, S. F., Yang, Y. Q., Song, J. L., Ahmad, M., and Jin, Y. C. (2022a). “Current understanding and optimization strategies for efficient lignin- enzyme interaction: A review,” Int. J. Biol. Macromol. 195, 274-286. DOI: 10.1016/j.ijbiomac.2021.11.188 Li, M. H., Yuan, Y. F., Zhu, Y. S., Jiang, B., Wu, W. J., Wu, S. F., and Jin, Y. C. (2022b). “Comparison of sulfomethylated lignin from poplar and masson pine on cellulase adsorption and the enzymatic hydrolysis of wheat straw,” Bioresour. Technol. 343, article 126142. DOI: 10.1016/j.biortech.2021.126142 Libardi, N., Vandenberghe, L. P. D, Vasquez, Z. S., Tanobe, V., de Carvalho, J. C., and Soccol, C. R. (2022). “A non-waste strategy for enzymatic hydrolysis of cellulose recovered from domestic wastewater,” Environ. Technol. 43(10), 1503-1512. DOI: 10.1080/09593330.2020.1840635 REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2449 Lillington, S. P., Leggieri, P. A., Heom, K. A., and O'Malley, M. A. (2020). “Nature’s recyclers: Anaerobic microbial communities drive crude biomass deconstruction,” Curr. Opin. Biotech. 62, 38-47. DOI: 10.1016/j.copbio.2019.08.015 Lin, X. L., Qiu, X. Q., Yuan, L., Li, Z. H., Lou, H. M., Zhou, M. S., and Yang, D. J. (2015). “Lignin-based polyoxyethylene ether enhanced enzymatic hydrolysis of lignocelluloses by dispersing cellulase aggregates,” Bioresour. Technol. 185, 165- 170. DOI: 10.1016/j.biortech.2015.02.067 Ling, Z., Wang, T., Makarem, M., Cintron, M. S., Cheng, H. N., Kang, X., Bacher, M., Potthast, A., Rosenau, T., and King, H. (2019). “Effects of ball milling on the structure of cotton cellulose,” Cellulose 26(1), 305-328. DOI: 10.1007/s10570-018- 02230-x Liu, J. B., Wang, W. D., Yang, H. Y., Wang, X. F., Gao, L. J., and Cui, Z. J. (2006). “Process of rice straw degradation and dynamic trend of pH by the microbial community MC1,” J. Environ. Sci. 18(6), 1142-1146. DOI: 10.1016/S1001- 0742(06)60052-1 Liu, R. B., Li, Y. X., Zhang, M. B., Hao, X. D., and Liu, J. (2022). “Review on the fate and recovery of cellulose in wastewater treatment,” Resour. Conserv. Recyc. 184, article 106354. DOI: 10.1016/j.resconrec.2022.106354 Liu, S. J., Lu, H. F., Hu, R. F., Shupe, A., Lin, L., and Liang, B. (2012). “A sustainable woody biomass biorefinery,” Biotechnol. Advan. 30(4), 785-810. DOI: 10.1016/j.biotechadv.2012.01.013 Liu, Z., Wang, H., Li, Z. X., Lu, X. M., Zhang, X. P., Zhang, S. J., and Zhou, K. B. (2011). “Characterization of the regenerated cellulose films in ionic liquids and rheological properties of the solutions,” Mater. Chem. Phys. 128(1-2), 220-227. DOI: 10.1016/j.matchemphys.2011.02.062 López Alvarez, J. V., Aguilar Larrucea, M., Arraiza Bermúdez, P., and León Chicote, B. (2009). “Biodegradation of paper waste under controlled composting conditions,” Waste Manag. 29, 1514-1519. DOI: 10.1016/j.wasman.2008.11.025 Lou, H. M., Wang, M. X., Lai, H. R., Lin, X. L., Zhou, M. S., Yang, D. J., and Qiu, X. Q. (2013). “Reducing non-productive adsorption of cellulase and enhancing enzymatic hydrolysis of lignocelluloses by noncovalent modification of lignin with lignosulfonate,” Bioresour. Technol. 146, 478-484. DOI: 10.1016/j.biortech.2013.07.115 Lou, X. F., and Nair, J. (2009). “The impact of landfilling and composting on greenhouse gas emissions – A review,” Bioresour. Technol. 100(16), 3792-3798. DOI: 10.1016/j.biortech.2008.12.006 MacGregor, S. T., Miller, F. C., Psarianos, K. M., and Finstein, M. S. (1981). “Composting process-control based on interaction between microbial heat output and temperature,” Appl. Environ. Microbiol. 41(6), 1321-1330. DOI: 10.1128/AEM.41.6.1321-1330.1981 Mäki-Arvela, P., Salmi, T., Holmbom, B., Willför, S., and Murzin, D. Y. (2011). “Synthesis of sugars by hydrolysis of hemicelluloses – A review,” Chem. Rev. 111(9), 5638-5666. DOI: 10.1021/cr2000042 Mao, Z. P., Yu, H., Wang, Y. F., Zhang, L. P., Zhong, Y., and Xu, H. (2014). “States of water and pore size distribution of cotton fibers with different moisture ratios,” Indust. Eng. Chem.Res. 53(21), 8927-8934. DOI: 10.1021/ie501071h REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2450 Mansfield, S. D., Mooney, C., and Saddler, J. N. (1999). “Substrate and enzyme characteristics that limit cellulose hydrolysis,” Biotech. Prog. 15(5), 804-816. DOI: 10.1021/bp9900864 Margariti, C. (2021). “The effects of micro-organisms in simulated soil burial on cellulosic and proteinaceous textiles and the morphology of the fibres,” Studies Conservation 66(5), 282-297. DOI: 10.1080/00393630.2020.1812245 Mattsson, A., Joelsson, T., Miettinen, A., Ketoja, J. A., Pettersson, G., and Engstrand, P. (2021). “Lignin inter-diffusion underlying improved mechanical performance of hot- pressed paper webs,” Polymers 13(15), article 2485. DOI: 10.3390/polym13152485 McIlwraith, H. K., Lin, J., Erdle, L. M., Mallos, N., Diamond, M. L., and Rochman, C. M. (2019). “Capturing microfibers – Marketed technologies reduce microfiber emissions from washing machines,” Marine Pollution Bull. 139, 40-45. DOI: 10.1016/j.marpolbul.2018.12.012 Medve, J., Karlsson, J., Lee, D., and Tjerneld, F. (1998). “Hydrolysis of microcrystalline cellulose by cellobiohydrolase I and endoglucanase II from Trichoderma reesei: Adsorption, sugar production pattern, and synergism of the enzymes,” Biotech. Bioeng. 59(5), 621-634. DOI: 10.1002/(SICI)1097-0290(19980905)59:5<621::AID- BIT13>3.0.CO;2-C Meyer, T. (2022). “Utilization of kraft pulp mill residuals,” TAPPI J. 21(2), 83-92. DOI: 10.32964/TJ21.2.83 Meyer, T., and Edwards, E. A. (2014). “Anaerobic digestion of pulp and paper mill wastewater and sludge,” Water Res. 65, 321-349. DOI: 10.1016/j.watres.2014.07.022 Milbrandt, A., Zuboy, J., Doney, K., and Badgett, A. (2024). “Paper and cardboard waste in the United States: Geographic, market, and energy assessment,” Waste Manag. Bull. 2(1), 21-28. DOI: 10.1016/j.wmb.2023.12.002 Miller, R. Z., Watts, A. J. R., Winslow, B. O., Galloway, T. S., Barrows, A. P. W. (2017). “Mountains to the sea: River study of plastic and non-plastic microfiber pollution in the northeast USA,” Marine Pollution Bull. 124(1), 245-251. DOI: 10.1016/j.marpolbul.2017.07.028 Mistriotis, A., Papardaki, N. G., and Provata, A. (2019). “Biodegradation of cellulose in laboratory-scale bioreactors: Experimental and numerical studies,” J. Polym. Environ. 27(12), 2793-2803. DOI: 10.1007/s10924-019-01560-6 Miyaji, K., Zhou, C., Maeda, A., Kobayashi, K., Kusumi, R., and Wada, M. (2023). “Biodegradation of various forms of cellulose and chitin in natural waters with different salinity,” Polym. Degrad. Stabil. 215, article 110423. DOI: 10.1016/j.polymdegradstab.2023.110423 Mizutani, C., Sethumadhavan, K., Howley, P., and Bertoniere, N. (2002). “Effect of a nonionic surfactant on Trichoderma cellulase treatments of regenerated cellulose and cotton yarns,” Cellulose 9(1), 83-89. DOI: 10.1023/A:1015821815568 Mohammad, A. W., Teow, Y. H., Ang, W. L., Chung, Y. T., Oatley-Radcliffe, D. L., and Hilal, N. (2015). “Nanofiltration membranes review: Recent advances and future prospects,” Desalination 356, 226-254. DOI: 10.1016/j.desal.2014.10.043 Mønster, J., Kjeldsen, P., and Scheutz, C. (2019). “Methodologies for measuring fugitive methane emissions from landfills – A review,” Waste Manag. 87, 835-857. DOI: 10.1016/j.wasman.2018.12.047 Muzamal, M., and Rasmuson, A. (2017). “Dynamic simulation of disintegration of wood chips caused by impact and collisions during the steam explosion pretreatment,” Wood Sci. Technol. 51(1), 115-131. DOI: 10.1007/s00226-016-0840-2 REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2451 Nagamine, R., Kobayashi, K., Kusumi, R., and Wada, M. (2022). “Cellulose fiber biodegradation in natural waters: River water, brackish water, and seawater,” Cellulose 29(5), 2917-2929. DOI: 10.1007/s10570-021-04349-w Naroznova, I., Moller, J., and Scheutz, C. (2016). “Characterisation of the biochemical methane potential (BMP) of individual material fractions in Danish source-separated organic household waste,” Waste Manag. 50, 39-48. DOI: 10.1016/j.wasman.2016.02.008 Neto, C. P., Silvestre, A. J. D., Evtuguin, D. V., Freire, C. S. R., Pinto, P. C. R., Santiago, A. S., Fardim, P., and Holmbom, B. (2004). “Bulk and surface composition of ECF bleached hardwood kraft pulp fibres,” Nordic Pulp Paper Res. J. 19(4), 513-520. DOI: 10.3183/npprj-2004-19-04-p513-520 N’Guessan, J. L. L., Niamke, B. F., Yao, N. J. C., and Amusant, N. (2023). “Wood extractives: Main families, functional properties, fields of application and interest of wood waste,” Forest Prod. J. 73(3), 194-208. DOI: 10.13073/FPJ-D-23-00015 Nguyen, L. N., Kumar, J., Vu, M. T., Mohammed, J. A. H., Pathak, N., Commault, A. S., Sutherland, D., Zdarta, J., Tyagi, V. K., and Nghiem, L. D. (2021). “Biomethane production from anaerobic co-digestion at wastewater treatment plants: A critical review on development and innovations in biogas upgrading techniques,” Sci. Total Environ. 765, article 142753. DOI: 10.1016/j.scitotenv.2020.142753 Niu, J. T., Zhang, X. Y., Pei, N., and Tian, Q. L. (2012). “Biodegradability of cellulose fibers and the fabrics in activated sludge,” in: Advanced Materials and Process Technology, X. H. Liu, Z. H. Bai, Y. H. Shauang, C. L. Zhou, and J. Shao (eds.), Vol. 217-219, pp. 918-922. DOI: 10.4028/www.scientific.net/AMM.217-219.918 NREL (2023). “News release: NREL research quantifies losses from cardboard, paper waste,” https://www.nrel.gov/news/press/2023/news-release-nrel-research-quantifies- losses-from-cardboard-paper-waste.html Olsen, J. P., Alasepp, K., Kari, J., Cruys-Bagger, N., Borch, K., and Westh, P. (2016). “Mechanism of product inhibition for cellobiohydrolase Cel7A during hydrolysis of insoluble cellulose,” Biotech. Bioeng. 113(6), 1178-1186. DOI: 10.1002/bit.25900 Park, C. H., Kang, Y. K., and Im, S. S. (2004). “Biodegradability of cellulose fabrics,” J. Appl. Polym. Sci. 94, 248-254. DOI: 10.1002/app.20879 Patel, A. K., Singhania, R. R., Sim, S. J., and Pandey, A. (2019). “Thermostable cellulases: Current status and perspectives,” Bioresour. Technol. 279, 385-392. DOI: 10.1016/j.biortech.2019.01.049 Pearse, L. F., Hettiaratchi, J. P., and Kumar, S. (2018). “Towards developing a representative biochemical methane potential (BMP) assay for landfilled municipal solid waste – A review,” Bioresour. Technol. 254, 312-324. DOI: 10.1016/j.biortech.2018.01.069 Peces, M., Astals, S., Jensen, P. D., and Clarke, W. P. (2018). “Deterministic mechanisms define the long-term anaerobic digestion microbiome and its functionality regardless of the initial microbial community,” Water Res. 141, 366- 376. DOI: 10.1016/j.watres.2018.05.028 Peng, X. F., Gilmore, S. P., and O'Malley, M. A. (2016). “Microbial communities for bioprocessing: Lessons learned from nature,” Current Opin. Chem. Eng. 14, 103-109. DOI: 10.1016/j.coche.2016.09.003 Qiu, B. B., Tao, X. D., Wang, J. H., Liu, Y., Li, S. T., and Chu, H. Q. (2022). “Research progress in the preparation of high-quality liquid fuels and chemicals by catalytic REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2452 pyrolysis of biomass: A review,” Energy Conver. Manag. 261, article 115647. DOI: 10.1016/j.enconman.2022.115647 Rabelo, C. A. B. S., Soares, L. A., Sakamoto, I. K., and Varesche, M. B. A. (2018). “Bioconversion of cellulose into hydrogen, biogas and organic acids using microbial consortium from a pulp and paper mill wastewater treatment plant,” Quimica Nova 41(2), 169-175. DOI: 10.21577/0100-4042.20170157 Rajput, H., Rajan, P., Li, S. J., Stratton, G. W., Murray, G., and He, Q. (2023). “Development of wood preservatives to prevent biodeterioration,” J. Wood Chem. Technol. 43(6), 371-389. DOI: 10.1080/02773813.2023.2284161 Raposeiro, P. M., Martins, G. M., Moniz, I., Cunha, A., Costa, A. C., and Gonçalves, V. (2014). “Leaf litter decomposition in remote oceanic islands: The role of macroinvertebrates vs. microbial decomposition of native vs. exotic plant species,” Limnologica 45, 80-87. DOI: 10.1016/j.limno.2013.10.006 Razza, F., Degli Innocenti, F., Dobon, A., Aliaga, C., Sanchez, C., and Hortal, M. (2015). “Environmental profile of a bio-based and biodegradable foamed packaging prototype in comparison with the current benchmark,” J. Cleaner Prod. 102, 493-500. DOI: 10.1016/j.jclepro.2015.04.033 Reis, P., Holmberg, K., Watzke, H., Leser, M. E., and Miller, R. (2009). “Lipases at interfaces: A review,” Adv. Colloid Interface Sci. 147-148, 237-250. DOI: 10.1016/j.cis.2008.06.001 Renouard, S., Hano, C., Ouagne, P., Doussot, J., Blondeau, J. P., and Laine, E. (2017). “Cellulose coating and chelation of antibacterial compounds for the protection of flax yarns against natural soil degradation,” Polym. Degrad. Stabil. 138, 12-17. DOI: 10.1016/j.polymdegradstab.2017.02.006 Reye, J. T., Lu, J., Maxwell, K. E., and Banerjee, S. (2011). “Enhancement of cellulase catalysis of wood pulp fiber by cationic polyelectrolytes,” Biomass Bioenergy 35(12), 4887-4891. DOI: 10.1016/j.biombioe.2011.10.011 Reyes, P., Márquez, N., Troncoso, E., Parra, C., Mendonça, R. T., and Rodríguez, J. (2016). “Evaluation of combined dilute acid-kraft and steam explosion-kraft processes as pretreatment for enzymatic hydrolysis of Pinus radiata wood chips,” BioResources 11(1), 612-625. DOI: 10.15376/biores.11.1.612-625 Reyes-Torres, M., Oviedo-Ocaña, E. R., Dominguez, I., Komilis, D., and Sánchez, A. (2018). “A systematic review on the composting of green waste: Feedstock quality and optimization strategies,” Waste Manag. 77, 486-499. DOI: 10.1016/j.wasman.2018.04.037 Rose, K., and Steinbüchel, A. (2005). “Biodegradation of natural rubber and related compounds: Recent insights into a hardly understood catabolic capability of microorganisms,” Appl. Environ. Microbiol. 71(6), 2803-2812. DOI: 10.1128/AEM.71.6.2803-2812.2005 Rossetti, I., Conte, F., and Ramis, G. (2021). “Kinetic modelling of biodegradability data of commercial polymers obtained under aerobic composting conditions,” Eng. 2, 54- 68. DOI: 10.3390/eng2010005. Royer, S. J., Greco, F., Kogler, M., and Deheyn, D. D. (2023). “Not so biodegradable: Polylactic acid and cellulose/plastic blend textiles lack fast biodegradation in marine waters,” PLOS One 18(5). DOI: 10.1371/journal.pone.0284681 Royer, S. J., Wiggin, K., Kogler, M., and Deheyn, D. D. (2021). “Degradation of synthetic and wood-based cellulose fabrics in the marine environment: Comparative REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2453 assessment of field, aquarium, and bioreactor experiments,” Sci. Total Environ. 791, article 148060. DOI: 10.1016/j.scitotenv.2021.148060 Ruggero, F., Gori, R., and Lubello, C. (2019). “Methodologies to assess biodegradation of bioplastics during aerobic composting and anaerobic digestion: A review,” Waste Manag. Res. 37(10), 959-975. DOI: 10.1177/0734242X19854127 Ruiken, C. J., Breuer, G., Klaversma, E., Santiago, T., and van Loosdrecht, M. C. M. (2013). “Sieving wastewater – Cellulose recovery, economic and energy evaluations,” Water Res. 47, 43-48. DOI: 10.1016/j.watres.2012.08.023 Saha, B. C. (2003). “Hemicellulose bioconversion,” J. Indust. Microbiol. Biotechnol. 30(5), 279-291. DOI: 10.1007/s10295-003-0049-x Saito, T., and Isogai, A. (2004). “TEMPO-mediated oxidation of native cellulose. The effect of oxidation conditions on chemical and crystal structures of the water- insoluble fractions,” Biomacromol. 5(5), 1983-1989. DOI: 10.1021/bm0497769 Sakamaki, T., and Richardson, J. S. (2008). “Retention, breakdown, and biological utilisation of deciduous tree leaves in an estuarine tidal flat of southwestern British Columbia, Canada,” Can. J. Fisheries Aquat. Sci. 65(1), 38-46. DOI: 10.1139/F07- 151 Salem, K. S., Kasera, N. K., Rahman, M. A., Jameel, H., Habibi, Y., Eichhorn, S. J., French, A. D., Pal, L., and Lucia, L. A. (2023). “Comparison and assessment of methods for cellulose crystallinity determination,” Chem. Soc. Rev. 52(18), 6418- 6446. DOI: 10.1039/d2cs00569g Salerno-Kochan, R., and Szostak-Kotowa, J. (2001). “Biodegradation of cellulose textiles,” Fibres Textiles East. Europe 9(3), 69-72. Sandström, M., Jalilehvand, F., Persson, I., Gelius, U., Frank, P., and Hall-Roth, I. (2002). “Deterioration of the seventeenth-century warship Vasa by internal formation of sulphuric acid,” Nature 415(6874), 893-897. DOI: 10.1038/415893a Saqib, A. A. N., and Whitney, P. J. (2006). “Role of fragmentation activity in cellulose hydrolysis,” Int. Biodeter. Biodegr. 581(3-4), 180-185. DOI: 10.1016/j.ibiod.2006.06.007 Sasaki, T., Tanaka, T., Nanbu, N., Sato, Y., and Kainuma, K. (1979). “Correlation between X-ray diffraction measurements of cellulose crystalline structure and the susceptibility to microbial cellulase,” Biotechnol. Bioeng. 21, 1031-1042. DOI: 10.1002/bit.260210608 Schultz, T. P., and Nicholas, D. D. (2003). “A brief overview of non-arsenical wood preservative systems,” Wood Deter. Preserv. 845, 420-432. DOI: 10.1021/bk-2003- 0845.ch026 Schwarz, M., Alawa, W., Perju, A., Bonhotal, J., Frey, M., Pires, S., Ankeny, M., and Daystar, J. (2024). “The effect of denim fabric as a feedstock in large scale composting of manure/bedding and food scraps,” Compost. Sci. Util. 31(1-2), 61-73. DOI: 10.1080/1065657X.2024.2349081 Seo, D. J., Fujita, H., and Sakoda, A. (2011). “Effects of a non-ionic surfactant, Tween 20, on adsorption/desorption of saccharification enzymes onto/from lignocelluloses and saccharification rate,” Adsorption – J. Int. Adsorp. Soc. 17(5), 813-822. DOI: 10.1007/s10450-011-9340-8 Shah, J. (2005). “Lipids, lipases, and lipid-modifying enzymes in plant disease resistance,” Ann. Rev. Phytopathol. 43, 229-260. DOI: 10.1146/annurev.phyto.43.040204.135951 REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2454 Shebani, A. N., van Reenen, A. J., and Meincken, M. (2008). “The effect of wood extractives on the thermal stability of different wood species,” Thermochimica Acta 471(1-2), 43-50. DOI: 10.1016/j.tca.2008.02.020 Shen, Y. W., Linville, J. L., Urgun-Demirtas, M., Mintz, M. M., and Snyder, S. W. (2015). “An overview of biogas production and utilization at full-scale wastewater treatment plants (WWTPs) in the United States: Challenges and opportunities towards energy-neutral WWTPs,” Renew. Sustain. Energy Rev. 50, 346-362. DOI: 10.1016/j.rser.2015.04.129 Sillanpää, M., and Sainio, P. (2017). “Release of polyester and cotton fibers from textiles in machine washings,” Environ. Sci. Pollut. Res. 24, 19313-19321. DOI: 10.1007/s11356-017-9621-1 Simon, J., Muller, H. P., Koch, R., and Muller, V. (1997). “Thermoplastic and biodegradable polymers of cellulose,” Polym. Degrad. Stabil. 59, 107-115. DOI: 10.1016/S0141-3910(97)00151-1 Simoncic, B., Tomsic, B., Orel, B., and Jerman, I. (2010a). “Biodegradation of untreated cellulose fibers,” in: Biodegradation of Cellulose Fibers, book series Bacterial Research Developments, Ch. 4, pp. 17-21. Simoncic, B., Tomsic, B., Orel, B., and Jerman, I. (2010b). “Biodegradation of cellulose fibers and its inhibition by chemical modification,” Handbook of Carbohydrate Polymers: Development, Properties and Application, R. Ito and Y. Matsuo (eds.), Polymer Science and Technology Series, pp. 237-277. Sinitsyn, A., Gusakov, A., and Vlasenko, E. Y. (1991). “Effect of structural and physico- chemical features of cellulosic substrates on the efficiency of enzymatic hydrolysis,” Appl. Biochem. Biotechnol. 30, 43-59. DOI: 10.1007/BF02922023 Smith, S. M., Lowe, J. A., Bowerman, N. H. A., Gohar, L. K., Huntingford, C., and Allen, M. R. (2012). “Equivalence of greenhouse-gas emissions for peak temperature limits,” Nature Climate Change 2(7), 535-538. DOI: 10.1038/NCLIMATE1496 Smith, M. M., Zambrano, M., Ankeny, M., Daystar, J., Pires, S., Pawlak, J., and Venditti, R. A. (2024). “Aquatic aerobic biodegradation of commonly flushed materials in aerobic wastewater treatment plant solids, seawater, and lakewater,” BioResources 19(1), 1150-1164. DOI: 10.15376/biores.19.1.1150-1164 Srivastava, A., Rani, R. M., Patle, D. S., and Kumar, S. (2022). “Emerging bioremediation technologies for the treatment of textile wastewater containing synthetic dyes: A comprehensive review,” J. Chem. Technol. Biotech. 97(1), 26-41. DOI: 10.1002/jctb.6891 Stanescu, M. D. (2023). “Applications of enzymes in processing cellulosic textiles – A review of the latest developments,” Cellulose Chem. Technol. 57(1-2), 1-15. DOI: 10.35812/CelluloseChemTechnol.2023.57.01 Stone, J. E., and Scallan, A. M. (1968). “A structural model of the cell wall of water- swollen wood pulp fibres based on their accessibility to macromolecules,” Cellulose Chem. Technol. 2(3), 343-358. Suaria, G., Achtypi, A., Perold, V., Lee, J. R., Pierucci, A., Bornman, T. G., Aliani, S., and Ryan, P. G. (2020). “Microfibers in oceanic surface waters: A global characterization,” Sci. Advan. 6(23), article eaay8493. DOI: 10.1126/sciadv.aay8493 Suh, H., Duckett, K., and Bhat, G. (1996). “Biodegradable and tensile properties of cotton cellulose acetate nonwovens,” Textile Res. J. 66(4), 230-237. DOI: 10.1177/004051759606600408 REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2455 Sun, Y., and Cheng, J. Y. (2002). “Hydrolysis of lignocellulosic materials for ethanol production: A review,” Bioresour. Technol. 83(1), article PII S0960-8524(01)00212- 7. DOI: 10.1016/S0960-8524(01)00212-7 Taha, M., Foda, M., Shahsavari, E., Aburto-Medina, A., Adetutu, E., and Ball, A. (2016). “Commercial feasibility of lignocellulose biodegradation: Possibilities and challenges,” Curr. Opin. Biotech. 38, 190-197. DOI: 10.1016/j.copbio.2016.02.012 Tamo, A. K., Doench, I., Helguera, A. M., Hoenders, D., Walther, A., and Madrazo, A. O. (2020). “Biodegradation of crystalline cellulose nanofibers by means of enzyme immobilized-alginate beads and microparticles,” Polymers 12(7), article 1522. DOI: 10.3390/polym12071522 Tarasov, D., Leitch, M., and Fatehi, P. (2018). “Lignin-carbohydrate complexes: Properties, applications, analyses, and methods of extraction: A review,” Biotech. Biofuels 11, article 269. DOI: 10.1186/s13068-018-1262-1 Tavano, O. L. (2013). “Protein hydrolysis using proteases: An important tool for food biotechnology,” J. Molec. Catal. B – Enzymatic 90, 1-11. DOI: 10.1016/j.molcatb.2013.01.011 Teeri, T. T. (1997). “Crystalline cellulose degradation: New insight into the function of cellobiohydrolases,” Trends Biotech. 15(5), 160-167. DOI: 10.1016/S0167- 7799(97)01032-9 Teugjas, H., and Väljamäe, P. (2013). “Product inhibition of cellulases studied with 14C- labeled cellulose substrates,” Biotech. Biofuels 6, article 104. DOI: 10.1186/1754- 6834-6-104 Tian, S. B., Jiang, J. A., Zhu, P. G., Yu, Z. Y., Oguzlu, H., Balldelli, A., Wu, J., Zhu, J. Y., Sun, X., and Saddler, J. (2022). “Fabrication of a transparent and biodegradable cellulose film from kraft pulp via cold alkaline swelling and mechanical blending,” ACS Sustain. Chem. Eng. 10(32), 10560-10569. DOI: 10.1021/acssuschemeng.2c01937 Tyagi, P., Agate, S., Velev, O. D., Lucia, L., and Pal, L. (2022). “A critical review of the performance and soil biodegradability profiles of biobased natural and chemically synthesized polymers in industrial applications,” Environ. Sci. Technol. 56(4), 2071- 2095. DOI: 10.1021/acs.est.1c04710 Van Wyk, J. P. H., and Mohulatsi, M. (2003). “Biodegradation of wastepaper by cellulase from Trichoderma viride,” Bioresour. Technol. 86, 21-23. DOI: 10.1016/S0960-8524(02)00130-X Verachtert, H., Ramasamy, K., Meyers, M., and Bevers, J. (1982). “Investigations on cellulose biodegradation in activated sludge plants,” Journal of Applied Microbiology 52(2), 185-190. DOI: 10.1111/j.1365-2672.1982.tb04839.x Wada, M., Ike, M., and Tokuyasu, K. (2010). “Enzymatic hydrolysis of cellulose I is greatly accelerated via its conversion to the cellulose II hydrate form,” Polym. Degrad. Stab. 95, 543-548. DOI: 10.1016/j.polymdegradstab.2009.12.014 Wang, L.-S., Zhang, Y.-Z., Yang, H., and Gao, P.-J. (2004). “Quantitative estimate of the effect of cellulose components during degradation of cotton fibers,” Carbohydr. Res. 339, 819-824. DOI: 10.1016/j.carres.2004.01.004 Wang, H. L., Brown, S. L., Magesan, G. N., Slade, A. H., Quintern, M., Clinton, P. W., and Payn, T. W. (2008). “Technological options for the management of biosolids,” Environ. Sci. Pollut. Res. 15(4), 308-317. DOI: 10.1007/s11356-008-0012-5 REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2456 Wang, X., Padgett, J. M., De la Cruz, F. B., and Barlaz, M. A. (2011). “Wood biodegradation in laboratory-scale landfills,” Environ. Sci. and Tech. 45(16), 6864- 6871. DOI: 10.1021/es201241g Wang, J. P., Quirk, A., Lipkowski, J., Dutcher, J. R., Hill, C., Mark, A., and Clarke, A. J. (2012). “Real-time observation of the swelling and hydrolysis of a single crystalline cellulose fiber catalyzed by cellulase 7B from Trichoderma reesei,” Langmuir 28(25), 9664-9672. DOI: 10.1021/la301030f Wang, J. P., Quirk, A., Lipkowski, J., Dutcher, J. R., and Clarke, A. J. (2013a). “Direct in situ observation of synergism between cellulolytic enzymes during the biodegradation of crystalline cellulose fibers,” Langmuir 29(48), 14997-15005. DOI: 10.1021/la403401c Wang, M. Y., Liu, K., Dai, L., Zhang, J., and Fang, X. (2013b). “The structural and biochemical basis for cellulose biodegradation,” J. Chem. Technol. Biotech. 88(4), 491-500. DOI: 10.1002/jctb.3987 Wang, Z. J., Zhu, J. Y., Fu, Y. J., Qin, M. H., Shao, Z. Y., Jiang, J. G., and Yang, F. (2013c). “Lignosulfonate-mediated cellulase adsorption: Enhanced enzymatic saccharification of lignocellulose through weakening nonproductive binding to lignin,” Biotechnol. Biofuels 6, article 156. DOI: 10.1186/1754-6834-6-156 Wang, X., De la Cruz, F. B., Ximenes, F., and Barlaz, M. A. (2015). “Decomposition and carbon storage of selected paper products in laboratory-scale landfills,” Sci. Total Environ. 532, 70-79. DOI: 10.1016/j.scitotenv.2015.05.132 Wang, Z., Winestrand, S., Gillgren, T., and Jönsson, L. J. (2018). “Chemical and structural factors influencing enzymatic saccharification of wood from aspen, birch and spruce,” Biomass Bioenergy 109, 125-134. DOI: 10.1016/j.biombioe.2017.12.020 Wang, G. X., Huang, D., Ji, J. H., Völker, C., Wurm, F. R. (2021). “Seawater-degradable polymers – Fighting the marine plastic pollution,” Adv. Sci. 8(1), 1-26. DOI: 10.1002/advs.202001121 Wang, W., Chang, J. S., Show, K. Y., and Lee, D. J. (2022a). “Anaerobic recalcitrance in wastewater treatment: A review,” Bioresour. Technol. 363, article 127920. DOI: 10.1016/j.biortech.2022.127920 Wang, X. G., Tian, L., Li, Y. X., Zhong, C., and Tian, C. J. (2022b). “Effects of exogenous cellulose-degrading bacteria on humus formation and bacterial community stability during composting,” Bioresour. Technol. 359, article 127458. DOI: 10.1016/j.biortech.2022.127458 Wang, X. Y., Liu, G. Q., Sun, W. M., Cao, Z. G., Liu, H. Q., Xiong, Y. Q., Li, B. Q., Sun, X. X., Li, Y. B., and Xu, R. (2023). “Removal of toilet paper fibers from residential wastewater: A life cycle assessment,” Environ. Sci. Pollution Res. 30, 84254-84266. DOI: 10.1007/s11356-023-28291-5 Wu, D., Wei, Z. M., Mohamed, T. A., Zheng, G. R., Qu, F. T., Wang, F., Zhao, Y., Song, C. H. (2022). “Lignocellulose biomass bioconversion during composting: Mechanism of action of lignocellulase, pretreatment methods and future perspectives,” Chemosphere 286(1), article 131635. DOI: 10.1016/j.chemosphere.2021.131635 Wyman, D. A., and Salmon, S. (2024). “Critical factors in lab-scale compostability testing,” J. Polym. Environ 32, 6182-6210. DOI: 10.1007/s10924-024-03311-8 Yadav, N., and Hakkarainen, M. (2021). “Degradable or not? Cellulose acetate as a model for complicated interplay between structure, environment and degradation,” Chemosphere 265, article 128731. DOI: 10.1016/j.chemosphere.2020.128731 REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2457 Yamane, C., Aoyagi, T., Ago, M., Sato, K., Okajima, K., and Takahashi, T. (2006). “Two different surface properties of regenerated cellulose due to structural anisotropy,” Polymer J. 38(8), 819-826. DOI: 10.1295/polymj.PJ2005187 Yin, Y.-Y., Lucia, L. A., Pal, L., Jiang, X., and Hubbe, M. A. (2020). “Lipase-catalyzed laurate esterification of cellulose nanocrystals and their use in reinforcement in PLA composites,” Cellulose 27, 6263-6273. DOI: 10.1007/s10570-020-03225-3 Younes, I., and Rinaudo, M. (2015). “Chitin and chitosan preparation from marine sources. Structure, properties and applications,” Marine Drugs 13(3), 1133-1174. DOI: 10.3390/md13031133 Yu, K. F., Li, S. Y., Sun, X. Y., and Kang, Y. (2020). “Maintaining the ratio of hydrosoluble carbon and hydrosoluble nitrogen within the optimal range to accelerate green waste composting,” Waste Manag. 105, 405-413. DOI: 10.1016/j.wasman.2020.02.023 Yu, L., Chen, Z. X., Tong, X., Li, K., and Li, W. W. (2012a). “Anaerobic degradation of microcrystalline cellulose: Kinetics and micro-scale structure evolution,” Chemosphere 86(4), 348-353. DOI: 10.1016/j.chemosphere.2011.09.049 Yu, Z., Jameel, H., Chang, H. M., Philips, R., and Park, S. (2012b). “Evaluation of the factors affecting Avicel reactivity using multi-stage enzymatic hydrolysis,” Biotechnol. Bioeng. 109, 1131-1139. DOI: 10.1002/bit.24386. Zahan, K. A., Azizul, N. M., Mustapha, M., Tong, W. Y., Rahman, M. S. A., and Sahuri, I. S. (2020). “Application of bacterial cellulose film as a biodegradable and antimicrobial packaging material,” Mater. Today – Proc. 31, 83-88. DOI: 10.1016/j.matpr.2020.01.201 Zainudin, M. H. M., Zulkarnain, A., Azmi, A. S., Muniandy, S., Sakai, K., Shirai, Y., and Hassan, M. A. (2022). “Enhancement of agro-industrial waste composting process via the microbial inoculation: A brief review,” Agronomy 12(1), article 198. DOI: 10.3390/agronomy12010198 Zambrano, M. C., Pawlak, J. J., Daystar, J., Ankeny, M., Cheng, J. J., and Venditti, R. A. (2019). “Microfibers generated from the laundering of cotton, rayon and polyester based fabrics and their aquatic biodegradation,” Mar. Pollut. Bull. 142, 394-407. DOI: 10.1016/J.MARPOLBUL.2019.02.062. Zambrano, M. C., Pawlak, J. J., Daystar, J., Ankeny, M., Goller, C. C., and Venditti, R. A. (2020). “Aerobic biodegradation in freshwater and marine environments of textile microfibers generated in clothes laundering: Effects of cellulose and for polyester- based microfibers on the microbiome,” Marine Pollution Bull. 151, article 110826. DOI: 10.1016/j.marpolbul.2019.110826 Zambrano, M. C., Pawlak, J. J., Daystar, J., Ankeny, M., and Venditti, R. A. (2021). “Impact of dyes and finishes on the aquatic biodegradability of cotton textile fibers and microfibers released on laundering clothes: Correlations between enzyme adsorption and activity and biodegradation rates,” Marine Pollution Bull. 165, article 112030. DOI: 10.1016/j.marpolbul.2021.112030 Zang, X. Y, Liu, M. T., Fan, Y. H., Xu, J., Xu, X. H., and Li, H. T. (2018). “The structural and functional contributions of β-glucosidase-producing microbial communities to cellulose degradation in composting,” Biotech. Biofuels 11, article 51. DOI: 10.1186/s13068-018-1045-8 Zhang, L., Chung, J. S., Jiang, Q. Q., Sun, R., Zhang, J., Zhong, Y. J., and Ren, N. Q. (2017). “Characteristics of rumen microorganisms involved in anaerobic degradation REVIEW ARTICLE bioresources.cnr.ncsu.edu Hubbe et al. (2025). “Cellulose fiber biodegradability,” BioResources 20(1), 2391-2458. 2458 of cellulose at various pH values,” RSC Advan. 7(64), 40303-40310. DOI: 10.1039/c7ra06588d Zhang, L., Liu, H., Zheng, L., Zhang, J., Du, Y., and Feng, H. (1996a). “Biodegradability of regenerated cellulose films in soil,” Ind. Eng. Chem. Res. 35(12), 4682-4685. DOI: 10.1021/ie950624r Zhang, L. N., Liu, H. Q., Zheng, L. S., Zhang, J. Y., Du, Y. M., and Liu, W. L. (1996b). “Biodegradation of regenerated cellulose films by fungi,” Chinese J. Polym. Sci. 14(4), 338-345. Zhao, G. L., Lyu, X. M., Lee, J., Cui, X., and Chen, W. N. (2019). “Biodegradable and transparent cellulose film prepared eco-friendly from durian rind for packaging application,” Food Packag. Shelf Life 21, article 100345. DOI: 10.1016/j.fpsl.2019.100345 Zhao, X. X., Bian, B., Huang, C. X., Lai, C. H., Song, J. L., Jin, Y. C., Meng, X. Z., Ragauskas, A., and Yong, Q. (2023). “Elucidating the nonproductive adsorption mechanism of cellulase with lignin fractions from hydrothermally pretreated poplar using multi-dimensional spectroscopic technologies,” Green Chem. 25(16), 6383- 6397. DOI: 10.1039/d3gc00907f Zhao, Y., Lu, Q., Wei, Y. Q., Cui, H. Y., Zhang, X., Wang, X., Shan, S., and Wei, Z. M. (2016). “Effect of actinobacteria agent inoculation methods on cellulose degradation during composting based on redundancy analysis,” Bioresour. Technol. 219, 196-203. DOI: 10.1016/j.biortech.2016.07.117 Zhao, Y., Wu, B., Yan, B. X., and Gao, P. J (2004). “Mechanism of cellobiose inhibition in cellulose hydrolysis by cellobiohydrolase,” Sci. China Ser. C – Life Sci. 47(1), 18- 24. DOI: 10.1360/02yc0163 Zhen, G. Y., Lu, X. Q., Kato, H., Zhao, Y. C., and Li, Y. Y. (2017). “Overview of pretreatment strategies for enhancing sewage sludge disintegration and subsequent anaerobic digestion: Current advances, full-scale application and future perspectives,” Renew. Sustain. Energy Rev. 69, 559-577. DOI: 10.1016/j.rser.2016.11.187 Zhu, L., O’Dwyer, J. P., Chang, V. S., Granda, C. B., and Holtzapple, M. T. (2008). “Structural features affecting biomass enzymatic digestibility,” Bioresour. Technol. 99, 3817-3828. DOI: 10.1016/j.biortech.2007.07.033