biotropia-1169	Howpinjai, Itsaree; Laemsak, Nikhom; Hengniran, Pongsak	DEVELOPMENT OF WOODCERAMICS FROM TROPICAL FLORA	2020	7	.pdf	application/pdf	3328	133	48	The SSA of woodceramics made from Bamboo, Pine, Eucalyptus, Rubberwood and Oil Palm shell particleboard was determined using the Brunauer-Emmett-Teller (BET) method, after being carbonized at 800 °C at a heating rate of 5 °C/min. Table 1 Specific Surface Area, pore volume and average pore diameter of woodceramics derived from various raw materials Raw material SSA area (m2/g) Pore volume (cm3/g) Table 1 also shows that the SSA of woodceramics derived from Bamboo is 4 m2/g and Oil Palm shell particleboards is 65 m2/g. The range of woodceramics pore volume made from Bamboo, Pine, Eucalyptus, Rubberwood and Oil Palm shell particleboard was 0.012-0.048 cm3/g, which is low when compared with other materials.	cache/biotropia-1169.pdf	txt/biotropia-1169.txt