1 Volume 22 2023 e238439 Original Article Braz J Oral Sci. 2023;22:e238439http://dx.doi.org/10.20396/bjos.v22i00.8668439 1 School of Dentistry, Federal University of Goiás, Goiânia, Goiás, Brazil. Corresponding author: Sicknan Soares da Rocha School of Dentistry, Federal University of Goias. 1ª Avenida esq. com Praça Universitária s/n, Setor Universitário, CEP 74605-220, Goiânia, GO, Brazil. Telephone/Fax: 55-62-3209-6325 E-mail address: sicknan@ufg.br Editor: Altair A. Del Bel Cury Received: Feb 16, 2022 Accepted: Aug 17, 2023 Flexural strength and Vickers hardness of milled and 3D-printed resins for provisional dental restorations Ana Luiza Caetano Souza1 , Jorge Luiz de Oliveira Cruvinel Filho1 , Sicknan Soares da Rocha1* Aim: Various forms of temporary resins are offered on the market; however, the properties of temporary resins obtained by milling and 3D printing have not been fully examined. This study aimed to compare the flexural strength and Vickers hardness of milled and 3D-printed resins. Methods: Three resins were tested: Evolux PMMA (milled resin), Cosmos Temp (3D-printed resin), and Structur 2 SC (bis-acrylic resin, group control). Specimens were prepared with rectangular shapes (n = 12) for flexural strength measurements and disc shapes (n = 9) for Vickers hardness tests. Flexural strength tests were performed at a crosshead speed of 0.75 mm/min, and the Vickers hardness was measured under a load of 20 N for 10 s. The obtained data were subjected to the Kruskal–Wallis test. Results: A significant difference (p < 0.05) in flexural strength was observed among the three sample groups: Evolux PMMA (111.76 MPa), Structur 2 SC (87.34 MPa), and Cosmos Temp (56.83 MPa). No significant difference (p < 0.05) was observed between the Vickers hardness values of Structur 2 SC (33.37 VHN) and Evolux PMMA (29.11 VHN); however, both materials were statistically superior to Cosmos Temp (10.90 VHN). Conclusion: While the mechanical properties of the milled resin were superior or similar to those of the bis- acrylic resin, the 3D-printed resin was statistically inferior to both the milled and bis-acrylic resins. Keywords: Dental restoration, temporary. Flexural strength. Hardness tests. Computer-aided design. https://orcid.org/0000-0003-1207-6929 https://orcid.org/0000-0002-7809-3994 https://orcid.org/0000-0002-3167-1048 2 Souza et al. Braz J Oral Sci. 2023;22:e238439 Introduction In recent years, bis-acrylic resins have attracted significant research interest among dental professionals. They comprise urethane dimethacrylate (UDMA), organic matrix components of composite resins, and microparticle fillers. These materials have important advantages for clinical applications include the ease of manipula- tion, high mechanical resistance, low polymerization shrinkage, less exothermic reaction, and low level of unpleasant odor1-3. Owing to these important characteris- tics, bis-acrylic resins are rapidly replacing polymethylmethacrylate (PMMA)-based resins in transitory restorations used by conventional techniques4. More recently, with the new advances in computer-aided design/computer-aided manufacturing (CAD/CAM) technology, other forms of temporary resins have become available. The CAD/CAM system has been widely utilized in the field of dentistry owing to its ability to manufacture high-quality prosthetic restorations5,6. Using this tech- nique, durable and esthetically pleasing parts are produced with high speed and effi- ciency while ensuring proper quality control7. The obtained CAD/CAM interim resins are highly resistant to hot, cold, and moist environments8. The CAD/CAM fabrication process of interim restorations can be implemented using subtractive manufacturing (SM) or additive manufacturing (AM) technology. The SM technique is based on removing material from a larger block to attain the shape of a virtually designed object9. AM technology, also known as 3D printing technology, is defined as the process of joining materials in a layer-by-layer manner to fabricate objects based on their 3D models10. Note that AM technology considerably differs from SM technology because it minimizes the material waste11-13. The literature on the physical and mechanical properties of PMMA-based temporary resins obtained by milling (SM) and 3D printing (AM) is very scarce. In this context, flexural strength and Vickers hardness tests represent important methods for evalu- ating the behavior of these materials and determining their limitations. This study aimed to evaluate the influence of the manufacturing method, such as SM and AM technologies, on the flexural strength and Vickers hardness of resins for transitory restorations using a bis-acrylic resin as a control, and two null hypotheses were formulated prior to the study: (H01) stating that there is no significant difference in flexural strength among the three resins and (H02) stating that there is no significant difference in Vickers hardness among the three resins. Materials and methods Flexural strength and Vickers hardness values were assessed for three different materials used in provisional restorations: bis-acrylic resin (BR), milled resin (MR), and 3D-printed resin (PR) (Table 1). 3 Souza et al. Braz J Oral Sci. 2023;22:e238439 Table 1. Type, code, resin, and manufacturer of tested resin materials for provisional restorations Type Code Resin Manufacturer Bis-acrylic BR Structur 2 SC Voco, Porto Alegre, Brasil Milled MR Evolux PMMA Blue Dent, Pirassununga, Brasil 3D-printed PR Cosmos Temp Yller, Pelotas, Brasil For flexural strength measurements, specimen standards (25 x 2 x 2 mm, n = 12) were fabricated according to ADA–ANSI specification #2714. BR was mixed accord- ing to manufacturer’s instructions using a self-mixing gun and then injected into custom-fabricated silicone rubber molds with dimensions of 25 × 2 × 2 mm (Zeta- labor, Zhermack, BadiaPolesine, Italy). After 5 min, the blocks were retrieved from the molds. MR specimens with dimensions of 25 × 2 × 2 mm were virtually designed using the CAD software Ceramill Mind (Amann Girrbach, Koblach, Austria) and milled from a Evolux PMMA block (101 x 101 x 20 mm) using a milling machine Ceramill Motion 2 (Amann Girrbach, Koblach, Austria). PR specimens were also virtually designed using the Ceramill Mind software and then printed on a stereolithography (SLA) printer (D30, Rapid Shape, Heimsheim, Germany). After printing, the specimens were cleaned with 90% isopropyl alcohol for 5 min according to manufacturer’s specifications and post-polymerized with 3000 flashes of ultraviolet light (385 nm) in a UV-A type 3 post-polymerization light- box (Flashlight plus, Shera Material Technology, Lemforde, Germany). The sizes of the three resin specimens were measured with a digital caliper (Fowler/Sylvac Ultra- Cal Mark IV Electronic Caliper, Crissier, Switzerland) for the standard quality assess- ment. Subsequently, the specimens were polished by grinding on wet silicon carbide papers (200, 400, and 800 grit). For the Vickers hardness test, specimens (n = 9) with disk shapes (diameter: 8 mm, thickness: 2 mm) were fabricated according to ADA–ANSI specification #2711 follow- ing the manufacturing procedure established for flexural strength test samples. All specimens were stored in a water bath at 37 ± 1 ºC for 24 h. A three-point bending test was performed using an Instron 4411 universal test- ing machine (Instron Testing Instruments, Canton, MA, USA) with a crosshead speed of 0.75 mm/min (n = 12). The Vickers hardness test was conducted using a micro-Vickers hardness tester (HMV-G20, Shimadzu, Tokyo, Japan) with a 20-N load applied for 10 s. Five readings were obtained for the top and bottom parts of the test specimens, and their values were averaged for each sample. The obtained data were checked for normal distribution using que Shapiro-Wilk test. As the data were not normally distributed, statistical significance among the differ- ent specimen group was tested with the non-parametric Kruskal–Wallis test, using the SPSS software (Version 25.0, Chicago, IL, USA). The level of significance was set to 0.05. 4 Souza et al. Braz J Oral Sci. 2023;22:e238439 Results The obtained flexural strength and Vickers hardness values are listed in Table 2. Table 2. Mean flexural strength (MPa) and Vickers hardness of three resins. Structur 2 SC (BR) Evolux PMMA (MR) Cosmos Temp (PR) Flexural Strength (MPa) 87.34 111.76 56.83 Vickers Hardness (VHN) 33.37 29.11 10.90 The results of the Kruskal–Wallis tests revealed the existence of a significant dif- ference among the flexural strengths of the BR, MR, and PR groups (p < 0.05). The MR group exhibited the highest flexural strength (111.76 MPa) followed by the BR (87.34 MPa) and PR (56.83 MPa) groups. Meanwhile, no significant difference in Vick- ers hardness was observed between the BR (33.17 VHN) and MR (29.11 VHN) groups (p > 0.05). In contrast, the PR group (10.90 VHN) was statistically inferior to the other two groups (p < 0.05) (Table 3). Table 3. Kruskal-Wallis test Compared factors Post hoc Post Dif. Calculated Z Critical Z Flexural Strength BR-MR 18.5 2.7899 2.394 p<.05BR-PR 30.5 2.7899 MR-PR 6.5 5.5799 Vickers Hardness BR-MR 21.4 1.5739 2.394 ns BR-PR 15.5 4.3950 p<.05 MR-PR 5.0 2.8211 Discussion Considering the significance level of 5% (α = 0.05), the null hypothesis (H01) stating that there is no significant difference in flexural strength among the three resins was rejected, opting for the alternative hypothesis (H1). For the Vickers hardness tests, the null hypothesis (H02) was rejected, despite no statistical difference between the bis- acrylic and milled resins was observed. Bis-acrylic resins based on multifunctional methacrylic acid esters have emerged as the materials of choice for provisional restorations because of their easy intra- oral manipulation and mechanical properties comparable to those of conventional materials available in the powder/liquid form4. However, mixing and filling the over-impression may lead to the incorporation of voids, compromising the mechan- ical strength of these materials, which significantly limited their application in multi- ple extensive prostheses15,16. 5 Souza et al. Braz J Oral Sci. 2023;22:e238439 The restorations fabricated using the CAD/CAM system are more accurate and easier to manipulate than bis-acrylic resins. In addition, they are predicted to possess good mechanical properties and thus represent a viable solution for long-term/long-span interim restorations, which require high strength and color stability8,17. The results obtained for the Evolux PMMA milled resin group were in agreement with the findings of previous studies. Dureja et al.4 reported the highest flexural strengths for CAD/CAM resin blocks. The same results were obtained in a study that evaluated the flexural strength and microhardness of three transitory resins fabricated by printing, milling, and conventional methods. The highest and lowest flexural strength means were obtained for the milled and printed resins, respec- tively18. In an evaluation of various resins for occlusal devices, 3D-printed resins also demonstrated lower wear and fracture resistances than those of the milled and conventionally fabricated resins13. After examining the flexural strengths and marginal accuracies of conventional and CAD/CAM transitory resins under the influence of thermal cycling, Yao et al.8, found that the CAD/CAM resins exhibited the best behavior even after 5000 thermal cycles. This improved stability resulted from the high polymerization efficiency during the fabrication of resin blocks. Hardness can be used as an indicator of density, and it was hypothesized that a denser material would be more resistant to wear and surface deterioration18. How- ever, surface hardness alone is not an indicator of the overall rigidity and strength and cannot be used to predict the clinical behavior of long-span prostheses19. This limita- tion shows the need for conducting other mechanical tests such as measurements of flexural strength, which is generally considered the main indicator of the mechanical response of a restorative material20. With the results similar to those obtained in the present study, Perea-Lowery et al.17 demonstrated that during the evaluation of mechanical properties, including flexural strength, Martens hardness, Vickers hardness, and elastic modulus, the 3D-printed resin materials were not as resistant to stress and aging as the pressed or milled resin materials. All tests revealed that the pressed and milled resins exhibited higher mean values than those of the 3D-printed resins. This inferior behavior of 3D-printed resins is a result of the high residual monomer content21 and greater porosity, which is minimized through the industrial manufactur- ing of PMMA blocks for milled resins22. This process allows the production of poly- mers with high density, which increases the strength of restorations18,23. Conventional resins based on PMMA are mono-functional resins with linear mole- cules, low molecular weight, and low strength. In addition to the intrinsic characteris- tics of these resins, they cannot be polymerized under pressure, and the high content of residual monomers contributes to their inferior mechanical behavior2. Additionally, the blocks for the milling process prevent heating and polymerization shrinkage24. These properties of PMMA resins are preserved by CAD/CAM technology and have enabled their application in transitory dental restorations. 6 Souza et al. Braz J Oral Sci. 2023;22:e238439 In addition to the superior mechanical properties of the produced resins, the CAD/ CAM process based on the milling method is more accurate in terms of anatomical shape, marginal adaptation, and occlusal/interproximal contacts. The milling process can be performed using a simplified procedure with a significantly reduced operating time18. However, despite the increasing availability and ease of operating the software and milling equipment (subtractive process), they require considerable investments for their acquisition. Concomitantly, the increasing application of the 3D printing process has pro- moted a substantial expansion of digital flow in dentistry10, allowing the produc- tion of objects with different degrees of complexity and limited material waste11,13. 3D printing requires less expensive equipment as compared with milling machines in addition to the low fabrication time. Within the timeframe of approximately 20 min, which is required for milling a single block, it is possible to simultaneously print several objects positioned on the same tray21. Therefore, 3D printing is becom- ing increasingly popular in dentistry. 3D-printed resins are widely used in the pro- duction of cast models, surgical templates for guiding implant surgeries, maxillo- facial prostheses, and orthodontic appliances and have been recently applied for provisional restorations21. The inferior mechanical behavior of 3D-printed resins is related to several factors, includ- ing printing technology, light intensity and wavelength, CAD design, printing orientation, layer thickness, post-processing procedures, and material characteristics20,21,25-28. Previous studies have shown that the orientation angle during printing (0º, 45º, or 90º) strongly influences the printing accuracy and mechanical properties (such as flex- ural strength) of 3D-printed resins20,21,29,30. This phenomenon is likely correlated with the thicknesses and union of various resin layers; however, no consensus has been reached regarding this issue in the literature. Furthermore, various resin properties (such as viscosity, critical energy for polymerization, and photon penetration depth) and printing hardware capabilities (such as photon length and power density) may also influence the manufacturing outcome30. The mechanical properties evaluated in this study (flexural strength and Vickers hard- ness) are directly related to the degree of material polymerization, which depends on several factors affecting the printing process. Thus, better process control and improvements of the processing and post-processing phases are required for 3D printing. In this context, manufacturers of 3D printers should provide detailed guide- lines for printing protocols and polymerization methods as these factors potentially influence the clinical performance of printed materials29,30. Owing to the numerous advantages of the 3D printing process, including the elimi- nation of material waste, lower fabrication time, and reduced cost, additional stud- ies must be performed in the future to better utilize this important technique for dental applications. In the present study, an SLA printer was used, and samples with an orientation angle of 0º were prepared for flexural strength and Vickers hardness tests. A probable lim- itation of this study was that other orientation angles were not considered, suggesting that additional tests are needed in the future. 7 Souza et al. Braz J Oral Sci. 2023;22:e238439 Conclusion From the results of this study, the following conclusions have been drawn. 1. The highest mean flexural strength was obtained for the Evolux PMMA milled resin followed by the Structur 2 SC bis-acrylic and 3D-printed Cosmos Temp resins with a significant difference among the three groups of samples. 2. The Vickers hardness of the 3D-printed resin was statistically lower than those of the bis-acrylic and milled resins, which did not exhibit any significant differences. Author contributions Ana Luiza Caetano Souza: Contributed to conception, design, data acquisition, drafted the manuscript Jorge Luiz de Oliveira Cruvinel Filho: Contributed to conception, design, data interpre- tation and critically revised the manuscript Sicknan Soares da Rocha: Contributed to conception, design, data interpretation, per- formed all statistical analyses, drafted and critically revised the manuscript and criti- cally revised the manuscript All authors actively participated in the discussion of the manuscript’s findings, and have revised and approved the final version of the manuscript. Conflicts of interest None. Data availability Datasets related to this article will be available upon request to the corresponding author. References 1. Young HM, Smith CT, Morton D. Comparative in vitro evaluation of two provisional restorative materials. J Prosthet Dent. 2001 Feb;85(2):129-32. doi: 10.1067/mpr.2001.112797. 2. Haselton DR, Diaz-Arnold AM, Vargas MA. Flexural strength of provisional crown and fixed partial denture resins. J Prosthet Dent. 2002 Feb;87(2):225-8. doi: 10.1067/mpr.2002.121406. 3. Chen HL, Lai YL, Chou IC, Hu CJ, Lee SY. Shear bond strength of provisional restoration materials repaired with light-cured resins. Oper Dent. 2008 Sep-Oct;33(5):508-15. doi: 10.2341/07-130. 4. Dureja I, Yadav B, Malhotra P, Dabas N, Bhargava A, Pahwa R. A comparative evaluation of vertical marginal fit of provisional crowns fabricated by computer-aided design/computer-aided manufacturing technique and direct (intraoral technique) and flexural strength of the materials: An in vitro study. J Indian Prosthodont Soc. 2018 Oct-Dec;18(4):314-320. doi: 10.4103/jips.jips_306_17. 5. Lee S, Hong SJ, Paek J, Pae A, Kown KR, Noh K. Comparing accuracy of denture bases fabricated by injection molding, CAD/CAM milling, and rapid prototyping method. J Adv Prosthodont. 2019 Feb;11(1):55-64. doi: 10.4047/jap.2019.11.1.55. 8 Souza et al. Braz J Oral Sci. 2023;22:e238439 6. Cicciù M, Fiorillo L, D’Amico C, Gambino D, Amantia EM, Laino L, et al. 3D digital impression systems compared with traditional techniques in dentistry: A recent data systematic review. Materials (Basel). 2020 Apr 23;13(8):1982. doi: 10.3390/ma13081982. 7. Miyazaki T, Hotta Y. CAD/CAM systems available for the fabrication of crown and bridge restorations. Aust Dent J. 2011 Jun;56 Suppl 1:97-106. doi: 10.1111/j.1834-7819.2010.01300.x. 8. Yao J, Li J, Wang Y, Huang H. Comparison of the flexural strength and marginal accuracy of traditional and CAD/CAM interim materials before and after thermal cycling. J Prosthet Dent. 2014 Sep;112(3):649-57. doi: 10.1016/j.prosdent.2014.01.012. 9. Abduo J, Lyons K, Bennamoun M. Trends in computer-aided manufacturing in prosthodontics: a review of the available streams. Int J Dent. 2014;2014:783948. doi: 10.1155/2014/783948. 10. Park SM, Park JM, Kim SK, Heo SJ, Koak JY. Flexural strength of 3d-printing resin materials for provisional fixed dental prostheses. Materials (Basel). 2020 Sep;13(18):3970. doi: 10.3390/ma13183970. 11. Dawood A, Marti B, Sauret-Jackson V, Darwood A. 3D printing in dentistry. Br Dent J. 2015 Dec;219(11):521-9. doi: 10.1038/sj.bdj.2015.914. 12. Yen HH, Stathopoulou PG. CAD/CAM and 3D-printing applications for alveolar ridge augmentation. Curr Oral Health Rep. 2018 Jun;5(2):127-32. doi: 10.1007/s40496-018-0180-4. 13. Lutz AM, Hampe R, Roos M, Lumkemann N, Eichberger M, Stawarczyk B. Fracture resistance and 2-body wear of 3-dimensional-printed occlusal devices. J Prosthet Dent. 2019 Jan;121(1):166-72. doi: 10.1016/j.prosdent.2018.04.007. 14. American National Standard/American Dental Association Standard. Polymer-Based Restorative Materials; No. 27. Washington, DC: American National Standard; 2016. 15. Givens EJ Jr, Neiva G, Yaman P, Dennison JB. Marginal adaptation and color stability of four provisional materials. J Prosthodont. 2008 Feb;17(2):97-101. doi: 10.1111/j.1532-849X.2007.00256.x. 16. Jo LJ, Shenoy KK, Shetty S. Flexural strength and hardness of resins for interim fixed partial dentures. Indian J Dent Res. 2011 Jan-Feb;22(1):71-6. doi: 10.4103/0970-9290.79992. 17. Perea-Lowery L, Gibreel M, Vallittu PK, Lassila L. Characterization of the mechanical properties of CAD/CAM polymers for interim fixed restorations. Dent Mater J. 2020 Mar;39(2):319-25. doi: 10.4012/dmj.2019-042. 18. Digholkar S, Madhav VN, Palaskar J. Evaluation of the flexural strength and microhardness of provisional crown and bridge materials fabricated by different methods. J Indian Prosthodont Soc. 2016 Oct-Dec;16(4):328-34. doi: 10.4103/0972-4052.191288. 19. Diaz-Arnold AM, Dunne JT, Jones AH. Microhardness of provisional fixed prosthodontic materials. J Prosthet Dent. 1999 Nov;82(5):525-8. doi: 10.1016/s0022-3913(99)70050-8. 20. Derban P, Negrea R, Rominu M, Marsavina L. Influence of the printing angle and load direction on flexure strength in 3d printed materials for provisional dental restorations. Materials (Basel). 2021 Jun;14(12):3376. doi: 10.3390/ma14123376. 21. Tahayeri A, Morgan M, Fugolin AP, Bompolaki D, Athirasala A, Pfeifer CS, et al. 3D printed versus conventionally cured provisional crown and bridge dental materials. Dent Mater. 2018 Feb;34(2):192-200. doi: 10.1016/j.dental.2017.10.003. 22. Dedem P, Türp JC. Digital Michigan splint - from intraoral scanning to plasterless manufacturing. Int J Comput Dent. 2016;19(1):63-76. 23. Güth JF, Almeida e Silva JS, Beuer FF, Edelhoff d. Enhancing the predictability of complex rehabilitation with a removable CAD/CAM-fabricated long-term provisional prosthesis: a clinical report. J Prosthet Dent. 2012 Jan;107(1):1-6. doi: 10.1016/S0022-3913(11)00171-5. 9 Souza et al. Braz J Oral Sci. 2023;22:e238439 24. Alt V, Hannig M, Wöstmann B, Balkenhol M. Fracture strength of temporary fixed partial dentures: CAD/CAM versus directly fabricated restorations. Dent Mater. 2011 Apr;27(4):339-47. doi: 10.1016/j.dental.2010.11.012. 25. Tapie L, Lebon N, Mawussi B, Fron-Chabouis H, Duret F, Attal JP. Understanding dental CAD/CAM for restorations--accuracy from a mechanical engineering viewpoint. Int J Comput Dent. 2015;18(4):343-67. 26. Alharbi N, Osman R, Wismeijer D. Effects of build direction on the mechanical properties of 3D-printed complete coverage interim dental restorations. J Prosthet Dent. 2016 Jun;115(6):760-7. doi: 10.1016/j.prosdent.2015.12.002. 27. Osman RB, Alharbi N, Wismeijer D. Build angle: does it influence the accuracy of 3d-printed dental restorations using digital light-processing technology? Int J Prosthodont. 2017 Mar/Apr;30(2):182-88. doi: 10.11607/ijp.5117. 28. Cascón WP, Nuñez AP, Díez IC, Revilla-Leon M. Laboratory workflow to obtain long-term injected resin composite interim restorations from an additive manufactured esthetic diagnostic template. J Esthet Restor Dent. 2019 Jan;31(1):13-9. doi: 10.1111/jerd.12419. 29. Väyrynen VOE, Tanner J, Vallittu PK. The anisotropicity of the flexural properties of an occlusal device material processed by stereolithography. J Prosthet Dent. 2016 Nov;116(5):811-7. doi: 10.1016/j.prosdent.2016.03.018. 30. Unkovskiy A, Bui PH, Schille C, Geis-Gerstorfer J, Huettig F, Splintyzk S. Objects build orientation, positioning, and curing influence dimensional accuracy and flexural properties of stereolithographically printed resin. Dent Mater. 2018 Dec;34(12):e324-33. doi: 10.1016/j.dental.2018.09.011.