In situ synthesis, structural chemistry and vibrational spectroscopy of Zn-doped Ca5Mg4(VO4)6 Chimica Techno Acta ARTICLE published by Ural Federal University 2022, vol. 9(2), No. 20229201 eISSN 2411-1414; chimicatechnoacta.ru DOI: 10.15826/chimtech.2022.9.2.01 1 of 8 In situ synthesis, structural chemistry and vibrational spectroscopy of Zn-doped Ca5Mg4(VO4)6 Anna S. Tolkacheva a* , Sergey N. Shkerin a , Sofya A. Petrova b , Olga M. Fedorova b , Svetlana G. Titova b , Ivan I. Leonidov a* a: Institute of High-Temperature Electrochemistry, 620990 Ekaterinburg, Russia b: Institute of Metallurgy, 620016 Ekaterinburg, Russia * Corresponding authors: asergeevnatolkacheva@gmail.com; ivanleonidov@ihim.uran.ru This paper belongs to the Regular Issue. © 2021, The Authors. This article is published in open access form under the terms and conditions of the Creative Commons Attribution (CC BY) license (http://creativecommons.org/licenses/by/4.0/). Abstract The phase formation of the solid solution Ca5Mg4–xZnx(VO4)6 (0≤x≤4) was studied in situ using differential scanning calorimetry and high- temperature X-Ray powder diffraction (XRPD). XRPD analysis shows the appearance of unavoidable secondary pyrovanadate phases using conventional synthesis methods. The local structure of the solid solu- tion was verified by vibrational spectroscopy. The analysis of the in- frared and Raman spectroscopy data allows establishing the main features between vanadate garnets and their isostructural analogs among natural silicates. Keywords crystal structure vibrational spectroscopy X-ray diffraction ceramics differential scanning calorimetry pyrovanadate garnet Received: 18.08.2021 Revised: 17.03.2022 Accepted: 17.03.2022 Available online: 23.03.2022 1. Introduction A wide range of compounds with the general formula A3B2V3O12 that belong to calcium vanadate garnets is known nowadays. This system includes complex oxides with substitution of calcium ions in A position by alkaline, (Li, Na, K), alkaline-earth (Sr) and other metal cations like Cu, Ag, Cd, Pb [1, 2]. Heterovalent substitution in B posi- tion in the garnet structure A3B2V3O12 (B = Mg2+, Mn2+, Co2+, Ni2+, Cu2+, Zn2+, Cd2+) has been analyzed by many research groups [1–3]. Ca5Mg3Zn(VO4)6 was first charac- terized as a garnet having the crystal symmetry of space group 𝐼4̅3𝑑 [4]. The lattice comprises the VO4 tetrahedra sharing edges with deformed CaO8 dodecahedrons. The crystal structure of most of garnet-related vanadates is described with the symmetry of space group 𝐼𝑎3̅𝑑 [1]. These compounds attract increasing attention due to a cation deficiency, where the vacancy concentration in A position varies from 1/10 to 3/10 [5–8]. The nonstoichi- ometry values in B position were evaluated for Ca5Co4(VO4)6 [9]. Inorganic materials based on calcium vanadates have been studied as a new series of low-temperature co-fired ceramics [3] with promising microwave characteristics below 100 °С [10–14]. The optical and photophysical prop- erties of compounds doped with In, Ta [15], and lantha- nide ions [16–18] have been considered in view of their application in solid-state lighting. Ca5Mg4(VO4)6 is charac- terized by cationic transport [19], whereas the vanadates Ca5Mg4−xCox(VО4)6 (1≤x≤4) demonstrate predominantly electronic conductivity about 10–2 S·cm−1 at 850 °C [20]. Different chemical routes are used to synthesize vana- dates as single crystals as well and in polycrystalline forms [11–14, 20, 21]. Among them, solid-state method can be car- ried out in a quartz ampule upon annealing at 975 °C [4]. The melting point of V2O5 is, nevertheless, about 650 °C, and, typically, vanadium oxide melt interacts with quartz. Some single-crystal fiber methods are also employed for preparation of calcium vanadates [22, 23]. However, most of the approaches for the synthesis of target compounds of this class of inorganic solids are highly time-consuming and require special equipment. The widely reported method implies a solid-state reaction [24–26]. For example, the synthesis of Ca5M4(VO4)6 (M = Mg and Zn) can be done tak- ing MgCO3, ZnO, CaCO3 and either NH4VO3, or V2O5 as initial reagents with further annealing of the reaction mixture at 800–850 °C. The attempt to obtain Ca5Zn4−xMgx(VO4)6 (0≤x≤3) via a solid-state reaction results in the appearance http://chimicatechnoacta.ru/ https://doi.org/10.15826/chimtech.2022.9.2.01 mailto:asergeevnatolkacheva@gmail.com mailto:ivanleonidov@ihim.uran.ru http://creativecommons.org/licenses/by/4.0/ https://orcid.org/0000-0002-7546-7807 https://orcid.org/0000-0003-4064-0670 http://orcid.org/0000-0002-9796-5794 https://orcid.org/0000-0002-0692-770X https://orcid.org/0000-0003-2891-3453 https://orcid.org/0000-0002-6635-4747 https://crossmark.crossref.org/dialog/?doi=https://doi.org/10.15826/chimtech.2022.9.2.01&domain=pdf&date_stamp=2022-3-23 Chimica Techno Acta 2022, vol. 9(2), No. 20229201 ARTICLE 2 of 8 of ZnO as a second phase [10]. The problems of synthesis of the single-phase powders are reported not only for the above-mentioned system but for other compositions of gar- net-type vanadates [1, 27, 28]. Wet-chemical synthesis procedure provides high homo- geneity of its products [29, 30]. Many modified sol-gel methods using the corresponding nitrates as initial reagents are often applied to prepare vadanate-based solid solutions [15, 31, 32]. Other changes in the chemical routes to synthe- size different inorganic solids include also mechanochemi- cal treatment, variation of educts and raw materials, addi- tional intermediate grindings and heat treatments, alterna- tion in temperature of annealing. The observations listed above forces us to pay more attention to phase formation of the vadanate subclass of inorganic compounds. This can be accompanied by possible vaporization of vanadium oxides [33]. Ca5Mg4–xZnx(VO4)6 (0≤x≤4) is chosen as a model solid solution among garnet-related vanadates. Differential scan- ning calorimetry (DSC) analysis supplemented by gas emis- sion analysis, in situ X-ray diffraction and evaluation of the local structure employing vibrational spectroscopy facilitate the solution of the problems in chemistry of vanadate-based materials more comprehensively than was reported earlier [4, 5, 10, 20, 31, 32]. The present study is also relevant to understanding of the synthesis processes of other garnet- type compounds such as silicates, hafnates, zirconates, germanates, etc. 2. Experimental 2.1. Reagents The target ceramic samples of Ca5Mg4–xZnx(VO4)6 (0≤x≤4) were synthesized via a salt decomposition reaction using CaCO3 (99%), MgCO3 (99.999%), ZnO (99%), V2O5 (99.999%) or NH4VO3 (98%), HCOOH (98%, concentra- tion 99%) and C6H8O7·H2O (99%) as initial reagents. Those taken in a stoichiometric ratio were dissolved in distilled water with HCOOH. Ethanol was used as a grind- ing medium. Next, C6H8O7·H2O was added with subsequent stirring and heating at 70–80 °C on a hot plate. Homoge- neous water reagent solutions were slowly evaporated into a gel, which then formed a dry residue. 2.2. In situ synthesis DSC and thermal gravimetric analysis (TG) were per- formed to estimate the optimal temperature of heat treatment of the final product. Thermal analysis was con- ducted with a Netzsch STA 449C Jupiter simultaneous ana- lyzer operating with the heating rate of 10 K/min. In situ phase formation was studied by collecting of the X-ray powder diffraction (XRPD) patterns upon heating of the reagents 5CaO:4MgO:3V2O5 and 5CaO:4ZnO:3V2O5 taken with the stoichiometric ratios. Room temperature XRPD patterns before heating and after the phase formation were recorded using a Shimadzu XRD-7000 Maxima dif- fractometer and Cu Kα radiation in the 2θ range between 10° and 90°. High temperature (HT) XRPD in the 2θ range between 15° and 60° was employed with Ni-filter instead of a graphite monochromator and a Shimadzu HA-1001 sample heating attachment (the scanning rate 1 °/min; the 2θ step of 0.02°). The temperature uncertainty was main- tained at less than 1 °C. The xerogels obtained during the HT XRPD experiments were placed on a Pt plate. The sam- ples were heated from 20 °C up to 700 °C at the rate <10 °C/min. Further heating was carried out from 700 °C to 785 °C in the steps of 15 °C and the rate <5 °C/min. The samples were maintained for 1 h prior to every measure- ment at the temperatures listed. Heat treatment at 785 °C was continued for over 12 h. Further heating was carried out on MgO-containing sample from 850 °C to 950 °C with the step 50 °C and the rate <5 °C/min with the dwell time of 1 h at every step. The scanning temperatures were se- lected according to the DSC curves of the precursor sam- ples. The highest scanning temperature (820 °C) was cho- sen for Ca5Zn4(VO4)6. 2.3. Characterization XRPD patterns were collected at room temperature using a Rigaku DMAX-2200 diffractometer operating with Cu Kα1 radiation over the angular range 15°≤2θ≤80° with the step increment Δ2θ = 0.02°. The XRPD patterns were compared with those in the ICSD-Web database (2021). Rietveld re- finement of the crystal structures was performed using the XRPD data collected on a Bruker D8 ADVANCE diffrac- tometer with position-sensitive detector VÅNTEC-1 operat- ing with Cu Kα1 radiation (the angular range 10°≤2θ≤134°; the step increment Δ2θ=0.021°). The XRPD patterns were compared with those in the PDF4+ICDD (2018) [34]. The crystallographic computing system JANA2006 [35] was employed for Rietveld refinements (Figs. S1–S5). Raman spectra were recorded on a Renishaw Ramascope U1000. This setup comprised a confocal Leica DML microscope, 50× Olympus objective lens (the numerical aperture of 0.55), a notch filter, and a cooled charge-coupled device detector. A Renishaw HeNe laser operating at 632.8 nm and 4 mW at the sample was employed as an excitation source. Typical spectra acquisition time was 300 s and the resolution was 1 cm−1. The Raman spectrum of silica was used for spectral calibration. Fourier transform infrared (FTIR) measurements were carried out on a Bruker vacuum spectrometer Tensor 27 using KBr pellets. The FTIR spectra were collected in a transmittance mode in the range from 400 cm–1 to 1000 cm–1 with the resolution of 2 cm−1. The FTIR spectra in the range of 50–600 cm–1 were recorded using ATR technique with a diamond optical element em- ployed at a Bruker Vertex 70v spectrometer. Vibrational spectroscopy was performed at room temperature. 3. Results and Discussion Decomposition of the precursor colloidal solution upon heating in air is an exothermic process with the mass loss Chimica Techno Acta 2022, vol. 9(2), No. 20229201 ARTICLE 3 of 8 mainly between 200 °C and 730 °C (Fig. 1). The total mass loss of the precursor mixture of Ca5Mg4(VO4)6 is 61.02 wt%, whereas the value of 52.57 wt% was obtained in the case of Ca5Zn4(VO4)6 up to 730 °C. Following the DSC data of a dried mixture of reagents, one can observe the water de- sorption at ~220 °C (Fig. 1) with the maximum of the DSC signal at 250 °C. It is accompanied by emission of СО2 and NO2 after decomposition of organics and (HN4)− groups with energy uptake. The slow exothermal process at 270 °C associated with the prolonged emission of H2O, СО2, NO2 and NO was reported in earlier papers [31]. However, the next stages depicted in the DSC plots differ due to the other precursors chosen for synthesis. At 350 °C, there is an exo- thermal stage with the ongoing emission of the gases listed above (СО2 and NO2). After the known exothermal effect at 372 °C [31], a well pronounced exothermal peak near 450 °C correlates with emission of СО2, NO2 and H2O. This can evidently be explained by the exhaust that forms during the decomposition of the available organic matrix. The en- ergy output at 510–528 °C is accompanied by emission of СО2, NO and NO2. Extraction of СО2 and NO2 occurs up to 730 °C with energy consumption. The observed disagree- ment between the obtained results and those reported ear- lier [31] arises from two main reasons. First, this difference may be caused by the reactants used to synthesize the tar- get compositions. Second, the DSC data are analyzed in this study, whereas only the DTA results were presented previ- ously [31]. The DSC curves of the dried precursor of Ca5Zn4(VO4)6 demonstrate several exothermal peaks at 396 °C, 451 °C, 528 °C and 727 °C and one endothermal one at 689.5 °C (Fig. 1). Some of the processes listed above can be evaluated more accurately employing in situ X-ray dif- fraction as an additional method. The XRPD patterns of dried sol-gel precursors show the phase formation of CaCO3 at 360 °C which is stable up to 785 °C (Fig. 2 and 3). Its appearance is accompanied by the emission of СО2 from the decomposition of an organic matrix. The pyrovanadates CaMgV2O7 and Mg2V2O7 are formed at 360 °C along with calcium carbonate (Fig. 2). The exothermal process near 450 °C is assigned to the formation of the intermediates α-Zn2V2O7 and Ca2V2O7 whose crystal structures are characterized by monoclinic symmetry (Fig. 1–3). The energy output at 510 °C (or 566 °C in Ref. [31]) corresponds to the phase with a cubic structure (space group 𝐼𝑎3̅𝑑). Extraction of СО2 observed up to 730 °C with energy consumption is caused by the start of calcite decomposition, which ends at 785 °C, ac- cording to the XRPD data (Fig. 1–3). The mixture of phases is observed from 460 °C to 950 °C in the magnesium-containing powder sample (Fig. 2), where- as the zinc-containing sample is characterized by coexistence of the phases like CaCO3, pyrovanadates, garnet-type vana- date in the temperature range 460–820 °C (Fig. 3). Fig. 2 HT XRPD profiles of Ca5Mg4(VO4)6 prepared via a sol-gel process: * – Ca5Mg4(VO4)6, ♦ – Mg2V2O7, ● – CaMgV2O7,  – Ca2V2O7 (P21/c),  – Ca2V2O7 (P1̅),  – CaCO3 Fig. 1 DSC and TG curves with mass spectrometry analysis of the gaseous phase during heating of the xerogel powders Ca5Mg4(VO4)6 (left) and Ca5Zn4(VO4)6 (right) prepared by the sol-gel process (a) (b) Chimica Techno Acta 2022, vol. 9(2), No. 20229201 ARTICLE 4 of 8 In turn, the phase transition in Zn2V2O7 implies the change of space group C2/c→C2/m at 620 °C [36]. Ca2V2O7 undergoes also the phase transition P1̅→P21/c above 900 °C. CaMgV2O7 melts incongruently at 885 °C, whereas Ca2V2O7 and Mg2V2O7 are thermally stable even at 950 °C. The coexistence of Ca5Mg4(VO4)6 (space group Ia3̅d) and CaMgV2O7 (space group P21/c) is detected at room temperature in the reaction products (Fig. 2). In this way, one can carry out synthesis at 850 °C and, after short- term heat treatment, can obtain the target product with contamination of Ca2V2O7. The presence of satellite pyro- vanadate phases was revealed in many earlier studies on evaluation of the most efficient chemical route to synthe- size garnet-type vanadates [3, 5, 15]. The elimination of these satellite pyrovanadates is a complex problem which is often dismissed when the target chemical products of Ca5M4(VO4)6 (M = Mg, Zn, Co, etc.) are synthesized. Fortu- nately, the impurity-free samples can be obtained. However, this usually requires a long duration of thermal treatment [4, 5]. Indeed, the heat treatment at 980 °C for 150 h allows a single-phase sample of Ca5Mg4(VO4)6 to be prepared. This temperature of the final annealing during the synthesis pro- cedure corresponds to the melting point of Mg2V2O7. Fig. 3 HT XRPD profiles of Ca5Zn4(VO4)6 prepared via a sol-gel process: * – Ca5Zn4(VO4)6,  – Ca2V2O7 (P21/c),  – Ca2V2O7 (P1̅),  – CaCO3,  – α-Zn2V2O7,  – β-Zn2V2O7 The XRPD analysis shows that polycrystalline Ca5Mg4–xZnx(VO4)6 (0≤x≤4) with some quantity (2–3 wt%) of pyrovanadate phases is formed via the sol-gel process (Fig. 4). The crystal structures of Ca5Mg4–xZnx(VO4)6 (0≤x≤4) were refined using the Rietveld method (Table S1; Supporting Information). The solid solution Ca5Mg4-xZnx(VO4)6 (0≤x≤4) crystallizes in the cubic space group Ia3̅d, Z = 8 (Supporting Information: Fig. S1–S5). The fractional atomic coordinates and refinement parame- ters are listed in Table 1. Magnesium and zinc cations have close radii that promotes the formation of solid solutions [38]. Both Mg and Zn ions occupy the octahedral position (16a) and the formation of the solid solutions is proved by a linear change in the cell parameter and volume when zinc concentration increases (Fig. 4). The lattice parame- ter a refined for Ca5Mg3Zn(VO4)6 deviates from the linear dependence because of a relatively large amount of CaMgV2O7 impurity (Supporting Information: Table S1). The site occupancy factor of Ca2+ positions is chosen to be about 5/6 that is close to the data reported by Ronniger and Mill [6]. Cation deficiency from 1/10 to 3/10 is not surprising and was also observed in other garnet-type vanadates [6, 39]. Therefore, a study of the local structure of these compounds becomes highly relevant in view of high deficiency in the cation sublattice. Eight molecules of Ca2.5MII2(VO4)3 (MII = Mg, Zn) per primitive cell in the 𝐼𝑎3̅𝑑, (𝑂h 10) structure support 3×8×19.5 = 468 modes of vibration with K=0 involving the zero-frequency translational motion of the crystal. These vibrations are classified according to irreducible representations of the point group of the elementary cell [40]. Given that the number of equivalent sites in any set is defined by the order of the point group divided by the order of the site symmetry subgroup for the primitive or primitive rhombohedral lattices, the number is greater for the centered lattices. The body-centered unit cells have twice as many points as the primitive ones (Table 1). Fig. 4 XRPD patterns of Ca5Mg4–xZnx(VO4)6 (0≤x≤4) (a), concentration dependence of the lattice parameters in Ca5Mg4–xZnx(VO4)6 (0≤x≤4) (b) Chimica Techno Acta 2022, vol. 9(2), No. 20229201 ARTICLE 5 of 8 The vibration modes of the full symmetry group are char- acterized by the following irreducible representations of Oh Γ 𝑐𝑟𝑦𝑠𝑡 = 3𝐴1g + 5𝐴1u + 5𝐴 2g + 5𝐴 2u + 8𝐸g + 10𝐸u + 13𝐹 1g + 18𝐹 1u + 14𝐹 2g + 15𝐹2u (1) Three acoustic modes are described by Γacoust = F1u and the remaining ones, Γ𝑣𝑖𝑏 𝑐𝑟𝑦𝑠𝑡 = 3𝐴1g + 5𝐴1u + 5𝐴2g + 5𝐴2u + 8𝐸g + 10𝐸u + 13𝐹1g + 17𝐹1u + 14𝐹2g + 15𝐹2u, (2) correspond to the optical modes, among which A1u, A2g, A2u, Eu, F1g and F2u are inactive. The modes of the F1u sym- metry are infrared active and the combination of A1g, Eg and F2g is Raman active. Infrared and Raman activities are presented in Table 2. Vibrational modes can be classified in two main cate- gories [41, 42], i.e., internal modes of the tetrahedral VO4 unit with the molecular symmetry S4 and external modes, which include translations of Ca2+, Mg2+, Zn2+ and [VO4]3− ions, and librations of [VO4]3−. In a lattice of A2.5B2(VO4)3, zone-center Raman active vibrational modes can be distin- guished for Ca2+ cations (A-site in A2.5B2(VO4)3) and VO4 tetrahedra, whereas Mg2+/Zn2 cations (B-site) do not pro- duce Raman active vibrations. Table 1 Fractional atomic coordinates and isotropic thermal displacement parameters (B) of Ca5Mg4–xZnx(VO4)6, 0≤x≤4 (SG Ia3̅d, Z = 8) Atom Wyckoff position x y z SOF* B Ca5Mg4(VO4)6 Rwp = 0.112, Rp = 0.062, GOF = 0.058 Ca 24c 0.125 0 0.25 0.83 0.68(5) Mg 16a 0 0 0 1.00 0.10(4) V 24d 0.375 0 0.25 1.00 0.18(3) O 96h 0.0980(2) 0.2001(1) 0.2887(1) 1.00 0.67(7) Ca5Mg3Zn(VO4)6 Rwp = 0.163, Rp = 0.099, GOF = 0.041 Ca 24c 0.125 0 0.25 0.83 0.10(4) Mg/Zn 16a 0 0 0 0.75/0.25 0.57(5) V 24d 0.375 0 0.25 1.00 0.10(3) O 96h 0.0938(3) 0.2032(1) 0.2896(1) 1.00 0.39(6) Ca5Mg2Zn2(VO4)6 Rwp = 0.128, Rp = 0.086, GOF = 0.020 Ca 24c 0.125 0 0.25 0.83 0.51(6) Mg/Zn 16a 0 0 0 0.5/0.5 0.09(3) V 24d 0.375 0 0.25 1.00 0.20(4) O 96h 0.0961(2) 0.1966(2) 0.2879(2) 1.00 0.58(8) Ca5MgZn3(VO4)6 Rwp = 0.162, Rp = 0.089, GOF = 0.037 Ca 24c 0.125 0 0.25 0.83 0.16(2) Mg/Zn 16a 0 0 0 0.25/0.75 0.30(4) V 24d 0.375 0 0.25 1.00 0.25(3) O 96h 0.0929(2) 0.1969(1) 0.2891(1) 1.00 0.40(6) Ca5Zn4(VO4)6 Rwp = 0.142, Rp = 0.078, GOF = 0.045 Ca 24c 0.125 0 0.25 0.83 0.63(2) Zn 16a 0 0 0 1.00 0.22(1) V 24d 0.375 0 0.25 1.00 0.10(2) O 96h 0.0955(5) 0.1977(3) 0.2885(1) 1.00 0.73(4) * SOF stands for site occupancy factor Table 2 Classification of the k = 0 unit cell modes* for Ca2.5M II 2(VO4)3, M II = Mg, Zn (SG 𝐼𝑎3̅𝑑, Z = 8) Factor group Oh Lattice modes Internal modes [VO4] 3− Selection rules Acoustic Librational Translational infrared Raman A1g 1 2 xx + yy + zz A1u 2 3 A2g 2 3 A2u 1 2 2 Eg 1 2 5 xx + yy + 2zz, √3xx − √3yy Eu 1 4 5 F1g 3 4 6 F1u 1 2 8 7 T F2g 2 5 7 xy, yz, xz F2u 3 6 6 Overall 3 36 87 108 ∑ = 234 * The F1u modes are infrared and the A1g, Eg and F2g modes are Raman active. Chimica Techno Acta 2022, vol. 9(2), No. 20229201 ARTICLE 6 of 8 Translations and librations of the VO4 unit are associ- ated with the representations below: T′(VO4) = A1u + A2g + Eg + Eu + 2F 1g + 3F1u + 3F 2g + 2F 2u (3) L(VO4) = A1g + A2u + Eg + Eu + 3F 1g + 2F1u + 2F 2g + 3F 2u . (4) Once acoustic modes are subtracted, the external modes are distributed among the irreducible representa- tion A1g + 2A1u + 2A2g + 3A2u + 3Eg + 5Eu + 7F1g + 10F1u + 7F2g + 9F2u. Therefore, the internal modes of the tetrahe- dral VO4 unit can be characterized by Γ𝑣𝑖𝑏 𝑐𝑟𝑦𝑠𝑡 = 2𝐴1g + 3𝐴1u + 3𝐴2g + 2𝐴2u + 5𝐸g + 5𝐸u + 6𝐹1g + 7𝐹1u + 7𝐹2g + 6𝐹2u. (5) In Ca2.5MII2(VO4)3 (MII = Mg, Zn), the symmetry of the VO4 tetrahedron changes due to the site symmetry and crystal field effects, and all the internal modes are split. The latter are summarized in Table 3. FTIR and Raman spectroscopy techniques are employed to study possible structural changes when Mg2+ cations are sub- stituted for Zn2+ in the solid solution Ca5Mg4−xZnx(VO4)6. Both types of vibrational spectra of Ca5Mg4−xZnx(VO4)6 (0≤x≤4) are similar and do not indicate any significant changes in the crystal structure (Fig. 5). Whereas 25 Raman and 17 infrared modes are active according to the group theory, not all of them can actually be detected [10]. This discrepancy origi- nates from the negligible changes in polarizability and dipole moment, which do not give rise to observable Raman and infrared modes [43]. According to the previous studies on garnet compounds [41, 44, 45], the Raman lines between 910 cm−1 and 950 cm−1 and infrared bands in the range of 700–950 cm−1 correspond to the internal anti-symmetric (ν3) stretching vibrations of [VO4]3− ions, whereas the symmetric (ν1) stretching modes of [VO4]3− are revealed only in the Ra- man spectra between 690 cm−1 and 875 cm−1. Typical weak Raman lines at ~450 cm−1 with the shoulder at ~430 cm−1 are expected for the VO4 bending vibrations. An observed general order of mode frequencies, i.e., L(VO4) > T′ (the metal cati- on) > T′(VO4) is also presented in most garnet-type silicates. A very strong Raman peak (as well as some weak ones) at ~320 cm−1 is attributed to the librational VO4 modes which can be also distinguished as the infrared band in the range of 340–380 cm−1 (Fig. 5). Fig. 5 Infrared (a) and Raman (b) spectra of Ca5Mg4–xZnx(VO4)6 (0≤x≤4) Table 3 Correlation table for the internal vibrations of [VO4] 3− in Ca2.5M II 2(VO4)3, M II = Mg, Zn (SG 𝐼𝑎3̅𝑑, Z = 8) Normal modes of free [VO4] 3− with Td symmetry [VO4] 3− site symmetry and factor group ν1 (A1) ν2 (E) ν3 (F2) ν4 (F2) Splitting of normal modes of Td symmetry due to site symmetry and factor group effects S4 A A + B B + E B + E Oh A1g + A2u + Eg + Eu + F1g + F2u A1g + A1u + A2g + A2u + 2Eg + 2Eu + F1g + F1u + F2g + F2u A1u + A2g + Eg + Eu + 2F1g + 3F1u + 3F2g + 2F2u A1u + A2g + Eg + Eu + 2F1g + 3F1u + 3F2g + 2F2u Chimica Techno Acta 2022, vol. 9(2), No. 20229201 ARTICLE 7 of 8 The Raman line at ~245 cm−1 is assigned to translation modes of Ca2+. Meanwhile, T′(Ca2+) and T′(Mg2+/Zn2+) modes are associated with the infrared band at 190–250 cm−1. Very weak Raman lines below 200 cm−1 correspond to external translations of VO4 tetrahedrons. The latter stand in the line with the T′(SiO4) modes ana- lyzed previously for A3B2(SiO4)3 (A = Mg, Ca, Mn, Fe; B = Al, Cr, Fe) [44, 45]. Substitution of Mg2+ by Zn2+ in Ca5Mg4−xZnx(VO4)6 leads to the monotonic increase of the unit cell parameter (Fig. 4b) and a slight shift (not exceed- ing ~10 cm−1) of most of the vibrational bands towards lower wavenumbers (Fig. 5). The similar dependencies of vibrational frequencies on the lattice parameter were ear- lier found in silicate garnets [44, 45]. Given that the den- sity of modes is relatively high to allow a clear assignment of all the lines, it is obviously not complete. Therefore, first-principle calculations in the density functional theory (DFT) framework based on the geometry optimization of Ca5M4(VO4)6 (M = Mg, Zn) are needed to perform an accu- rate assignment of vibrational bands and will be discussed elsewhere. 4. Conclusions High-temperature X-Ray diffraction supported by DSC technique allowed studying Ca5Mg4–xZnx(VO4)6 (0≤x≤4) so as to provide more detailed and reliable data on the phase formation of garnet-type vanadates. The synthesis of Zn- doped Ca5Mg4(VO4)6 is accompanied by the appearance of Ca2V2O7, Mg2V2O7 or Zn2V2O7. These satellite pyrovanadate phases are stable up to 950 °C and disappear only above their melting point. The single-phase samples of Ca5Mg4(VO4)6 and Ca5Zn4(VO4)6 can be obtained following heat treatment for 150 h at 980 °C and at 750 °C, respec- tively. The formation of the solid solution Ca5Mg4–xZnx(VO4)6 (0≤x≤4) was confirmed by XRPD and vibrational spectroscopy. The findings in structural chem- istry contribute to understanding of the impact of synthe- sis procedures on crystal engineering of vanadates and other garnet-type oxides. Supplementary materials Supplementary materials in the online format are availa- ble at the website of this paper. These data contain: Table S1: Phase composition and lattice parameters of Ca5Mg4–xZnx(VO4)6 (0 ≤ x ≤ 4). Fig. S1: Rietveld refine- ment of Ca5Mg4(VO4)6 from XRPD data. Fig. S2: Rietveld refinement of Ca5Mg3Zn(VO4)6 from XRPD data. Fig. S3: Rietveld refinement of Ca5Mg2Zn2(VO4)6 from XRPD data. Fig. S4: Rietveld refinement of Ca5MgZn3(VO4)6 from XRPD data. Fig. S5: Rietveld refinement of Ca5Zn4(VO4)6 from XRPD data. Funding This study was funded by the Research Programs No. AAAA-A19-119020190042-7 and No. АААА-А19- 119020190044-1 (IHTE UB RAS). Acknowledgments We are grateful to Dr. Olga G. Reznitskikh (ISSC UB RAS), Dr. Elena A. Sherstobitova (IMP UB RAS) and Dr. Nikolai I. Moskalenko (IHTE UB RAS) for technical assistance. The crystallographic and spectroscopic studies were carried out in the Shared Access Centers at IMET UB RAS and IHTE UB RAS, respectively. Author contributions Conceptualization: A.S.T. Data curation: I.I.L., A.S.T. Formal Analysis: S.A.P., O.M.F., I.I.L. Funding acquisition: I.I.L., A.S.T. Methodology: S.N.S. Project administration: A.S.T. Resources: S.G.T. Supervision: S.G.T., S.N.S. Validation: S.N.S. Visualization: I.I.L., A.S.T. Writing – original draft: A.S.T. Writing – review & editing: I.I.L. Conflict of interest The authors declare no conflict of interest. Additional information Webpages of Institute of High-Temperature electrochemistry: http://www.ihte.uran.ru/?page_id=3106; Institute of Metallurgy: http://www.imet-uran.ru. References 1. Mill BV, Ronniger G, Kabalov YuK. New garnet compounds A3 2+B2 2+C4+V2 5+O12 (A = Ca, Cd; B = Mg, Zn, Co, Ni, Cu, Mn, Cd; C = Ge, Si). Russ J Inorg Chem. 2014;59:1208–1213. doi:10.1134/S0036023614110151 2. Ishi K, Ikuta Y. Isomorphous substitutions in vanadate gar- nets. N Jb Miner Abh. 2006;182:157–163. doi:10.1127/0077-7757/2006/0038 3. Yao GG, Liu P, Zhang HW. Novel series of low-firing micro- wave dielectric ceramics: Ca5A4(VO4)6 (A 2+ = Mg, Zn). J Am Ceram Soc 2013;96:1691–1693. doi:10.1111/jace.12359 4. Müller-Buschbaum Hk, von Postel M. Eine weitere Oxovana- dat-Phase mit Granatstruktur: Ca5Mg3ZnV6O24. Z Anorg Allg Chem. 1992;615:101–103. doi:10.1002/zaac.19926150920 5. Krasnenko TI, Zolotukhina LV, Zabolotskaya EV, Svetlakov SV, Dobosh VG. Defect structure and electrical and magnetic properties of calcium manganese vanadium garnets. Inorg Mater. 1999;35:1179–1182. http://www.ihte.uran.ru/?page_id=3106 http://www.imet-uran.ru/ https://doi.org/10.1134/S0036023614110151 https://doi.org/10.1127/0077-7757/2006/0038 https://doi.org/10.1111/jace.12359 https://doi.org/10.1002/zaac.19926150920 Chimica Techno Acta 2022, vol. 9(2), No. 20229201 ARTICLE 8 of 8 6. Ronniger G, Mill BV. Vanadates with a defect garnet struc- ture. Sov Phys Crystallogr. 1973;18:303–307. 7. Surat LL, Fotiev AA, Dobosh VG. V2O5–MgO–CaO–MnO(Mn2O3) system. Zh. Neorg. Khim. 1989;34:2924–2928. 8. Slobodin BV, Fotiev AA, Sharova NG. Phase composition of the CaO–MgO–V2O5 system. Zh Neorg Khim. 1977;23:184–187. 9. Li B, Zheng JG, Li W. Influence of cobalt ions non- stoichiometry on the microstructure and microwave proper- ties of Ca5Co4(VO4)6 ceramics. Ceram Int. 2017;43:13956– 13962. doi:10.1016/j.ceramint.2017.07.127 10. Li B, Tian J, Qiu L. Crystal structures and microwave dielec- tric properties of low-firing Ca5Zn4−xMgxV6O24 ceramics. Ce- ram Int. 2018;44:18250–18255. doi:10.1016/j.ceramint.2018.07.035 11. Wang D, Xiang HC, Tang Y. Fang L, Khaliq J, Li CC. A low- firing Ca5Ni4(VO4)6 ceramic with tunable microwave dielec- tric properties and chemical compatibility with Ag. Ceram Int. 2016;42:15094–15098. doi:10.1016/j.ceramint.2016.06.085 12. Fang L, Xiang F, Su CX, Zhang H. A novel low firing micro- wave dielectric ceramic NaCa2Mg2V3O12. Ceram Int. 2013;39:9779–9783. doi:10.1016/j.ceramint.2013.05.041 13. Xiang HC, Fang L, Jiang XW, Li CC. Low-firing and microwave dielectric properties of Na2YMg2V3O12 ceramic. Ceram Int. 2016;42:3701–3705. doi:10.1016/j.ceramint.2015.10.163 14. Yao GG, Liu P, Zhao XG, Zhou JP, Zhang HW. Low- temperature sintering and microwave dielectric properties of Ca5Co4(VO4)6 ceramics. J Eur Ceram Soc. 2014;34:2983–2987. doi:10.1016/j.jeurceramsoc.2014.03.026 15. Pavitra E, Raju GSR, Park JY, Wang L, Moon BK, Yu JS. Novel rare-earth-free yellow Ca5Zn3.92In0.08(V0.99Ta0.01O4)6 phosphors for dazzling white light-emitting diodes. Sci Rep. 2015;5:10296. doi:10.1038/srep10296 16. Li JF, Qiu KH, Li JF, Li W, Yang Q, Li JH. A novel broadband emission phosphor Ca2KMg2V3O12 for white light emitting di- odes. Mater Res Bull. 2010;45:598–602. doi:10.1016/j.materresbull.2010.01.014 17. Song D, Guo CF, Zhao J, Suo H, Zhao XQ, Zhou XJ, Liu GZ. Host sensitized near-infrared emission in Nd3+-Yb3+ Co-doped Na2GdMg2V3O12 phosphor. Ceram Int. 2016;42:12988–12994. doi:10.1016/j.ceramint.2016.05.072 18. Dhobale AR, Mohapatra M, Natarajan V, Godbole SV. Synthe- sis and photoluminescence investigations of the white light emitting phosphor, vanadate garnet, Ca2NaMg2V3O12 co-doped with Dy and Sm. J Lumin. 2012;132:293–298. doi:10.1016/j.jlumin.2011.09.004 19. Leonidova ON, Patrakeev MV, Leonidov IA. Ionic and elec- tronic transport in the garnet-type vanadate Ca2.5Mg2V3O12. J Solid State Electrochem. 2019;23:1083–1088. doi:10.1007/s10008-019-04202-y 20. Tolkacheva AS, Shkerin SN, Nikonov AV, Pershina SV, Khavlyuk PD, Leonidov II. Electrical and thermal properties of Ca5Mg4−xCox(VO4)6 (0≤x≤4), a promising electrode materi- al. Mater. Lett. 2021;305:30811. doi:10.1016/j.matlet.2021.130811 21. Blanzat B, Loriers J. Synthese et etude des proprietes spec- trales de monocristaux de vanadate a structure grenat Ca2NaMg2V3O12 active par l'europium trivalent. Mater Res Bull. 1974;9:1647–1654. doi:10.1016/0025-5408(74)90156-1 22. Dhanaraj G, Byrappa K, Prasad V, Dudley M. (Eds.). Springer Handbook of Crystal Growth. Heidelberg, Germany: Springer- Verlag GmbH; 2010. 1736 p. 23. Yu YM, Chani VI, Shimamura K, Inaba K, Fukuda T. Growth of vanadium garnet fiber crystals and variations of lattice pa- rameter. J Cryst Growth 1997;177:74–78. doi:10.1016/S0022-0248(97)01070-1 24. Levina AA, Tadevosyan NO, Petrova SA, Buyanova ES, Moro- zova MV. Phase formation processes and synthesis of solid solutions in Ca–R–Nb–M–O systems. Chimica Techno Acta. 2020;7:17–25. doi:10.15826/chimtech.2020.7.1.03 25. Klyndyuk AI, Chizhova EA, Shevchenko SV. Spin-state transi- tion in the layered barium cobaltite derivatives and their thermoelectric properties. Chimica Techno Acta. 2020;7:26– 33. doi:10.15826/chimtech.2020.7.1.04 26. Klyndyuk AI, Zhuravleva YY, Gundilovich NN. Crystal struc- ture, thermal and electrotransport properties of NdBa1−xSrxFeCo0.5Cu0.5O5+δ (0.02≤x≤0.20) solid solutions. Chimica Techno Acta. 2021;8:20218301. doi:10.15826/chimtech.2021.8.3.01 27. Huang XY, Wang SY, Rtimi S, Devakumar B. KCa2Mg2V3O12: A novel efficient rare-earth-free self-activated yellow emitting phosphor. J Photochem Photobiol A Chem. 2020;401:112765. doi:10.1016/j.jphotochem.2020.112765 28. Tsirlin AA, Dikarev EV, Velikodny YA, Shpanchenko RV, An- tipov EV. Pb2.63Cd2V3O12, a cation-deficient garnet-type vana- date. Acta Crystallogr C Struct Chem. 2007;63:140–142. doi:10.1107/S0108270107021233 29. Dutta U, Haque A, Seikh MM. Synthesis, structure and mag- netic properties of Ti doped La2MnNiO6 double perovskite. Chimica Techno Acta. 2019;6:80–92. doi:10.15826/chimtech.2019.6.3.01 30. Anokhina IA, Animitsa IE, Buzina AF, Voronin VI, Vykhodets VB, Kurennykh TЕ, Zaikov YP. Synthesis, structure and elec- trical properties of Li+-doped pyrochlore Gd2Zr2O7. Chimica Techno Acta. 2020;7:51–60. doi:10.15826/chimtech.2020.7.2.02 31. Park JY, Chung JW, Yang HK. Synthesis and photolumines- cence properties of yellow-emitting Ca5(Zn1−xMgx)4(VO4)6 self-activated phosphors. Optik. 2018;155:384–389. doi:10.1016/j.ijleo.2017.11.046 32. Tolkacheva AS, Shkerin SN, Zemlyanoi KG, Reznitskikh OG, Pershina SV, Khavlyuk PD. Thermal and electrical properties of Ca5Mg4−xZnx(VO4)6 (0≤x≤4). J Therm Anal Calorim. 2019;136:1003–1009. doi:10.1007/s10973-018-7780-z 33. Lide DR. Handbook of Chemistry and Physics. 84th ed., Boca Raton, FL: CRC Press LLC; 2003. p. 4–93. 34. Powder Diffraction File PDF4+ ICDD 2018. 35. Petříček V, Dušek M, Palatinus L, Crystallographic computing system JANA2006: General features. Z. Kristallogr. 2014;229:345–352. doi:10.1515/zkri-2014-1737 36. Krasnenko TI, Zubkov VG, Tyutyunnik AP, Zolotukhina LV, Vasyutinskaya EF. Crystal structure of β′-Zn2V2O7. Crystal- logr. Rep. 2003;48:35–38. doi:10.1134/1.1541739 37. Miyauchi A, Okabe TH. Production of metallic vanadium by preform reduction process. Mater Trans. 2010;51(6):1102– 1108. doi:10.2320/matertrans.M2010027 38. Shannon RD, Prewitt CT. Effective ionic radii in oxides and fluorides. Acta Crystallogr B Struct Sci Cryst Eng Mater. 1969;25:925–946. doi:10.1107/S0567740869003220 39. Fotiev AA. Vanadaty: Sostav, Sintez, Struktura, Svoĭstva [Vanadates: composition, synthesis, structure, properties] Moscow: Nauka; 1988. 272 p. Russian. 40. Rousseau DL, Bauman RP, Porto SPS. Normal mode determi- nation in crystals. J Raman Spectrosc. 1981;10:253–290. doi:10.1002/jrs.1250100152 41. Koningstein JA, Mortensen OS. Laser-excited phonon Raman spectrum of garnets. J Mol Spectrosc. 1968;27:343-350. doi:10.1016/0022-2852(68)90043-X 42. Mingsheng P, Mao HK, Dien L, Chao ECT. Raman spectrosco- py of garnet-group minerals. Chin J Geochem. 1994;13:176– 183. doi:10.1007/BF02838517 43. Nakamoto K. Infrared and Raman Spectra of Inorganic and Coordination Compounds. Part A: Theory and Applications in Inorganic Chemistry. 6th ed. Hoboken, NJ: John Wiley & Sons, Inc.; 2009. 419 p. 44. Kolesov BA, Geiger CA. Raman spectra of silicate garnets. Phys Chem Minerals. 1998;25:142–151. doi:10.1007/s002690050097 45. Moore RK, White WB, Long TV. Vibrational spectra of the com- mon silicates: I. The garnets. Am. Mineral. 1971;56:54–71. https://doi.org/10.1016/j.ceramint.2017.07.127 https://doi.org/10.1016/j.ceramint.2018.07.035 https://doi.org/10.1016/j.ceramint.2016.06.085 https://doi.org/10.1016/j.ceramint.2013.05.041 https://doi.org/10.1016/j.ceramint.2015.10.163 https://doi.org/10.1016/j.jeurceramsoc.2014.03.026 https://doi.org/10.1038/srep10296 https://doi.org/10.1016/j.materresbull.2010.01.014 https://doi.org/10.1016/j.ceramint.2016.05.072 https://doi.org/10.1016/j.jlumin.2011.09.004 https://doi.org/10.1007/s10008-019-04202-y https://doi.org/10.1016/j.matlet.2021.130811 https://doi.org/10.1016/0025-5408(74)90156-1 https://doi.org/10.1016/S0022-0248(97)01070-1 https://doi.org/10.15826/chimtech.2020.7.1.03 https://doi.org/10.15826/chimtech.2020.7.1.04 https://doi.org/10.15826/chimtech.2021.8.3.01 https://doi.org/10.1016/j.jphotochem.2020.112765 https://doi.org/10.1107/S0108270107021233 https://doi.org/10.15826/chimtech.2019.6.3.01 https://doi.org/10.15826/chimtech.2020.7.2.02 https://doi.org/10.1016/j.ijleo.2017.11.046 https://doi.org/10.1007/s10973-018-7780-z https://doi.org/10.1515/zkri-2014-1737 https://doi.org/10.1134/1.1541739 https://doi.org/10.2320/matertrans.M2010027 https://doi.org/10.1107/S0567740869003220 https://doi.org/10.1002/jrs.1250100152 https://doi.org/10.1016/0022-2852(68)90043-X https://doi.org/10.1007/BF02838517 https://doi.org/10.1007/s002690050097