Synthesis, crystal structure, and thermal stability of double borate Na3ErB2O6 Chimica Techno Acta ARTICLE published by Ural Federal University 2021, vol. 8(4), № 20218402 eISSN 2411-1414; chimicatechnoacta.ru DOI: 10.15826/chimtech.2021.8.4.02 1 of 5 Synthesis, crystal structure, and thermal stability of double borate Na3ErB2O6 Alexey K. Subanakov * , Evgeniy V. Kovtunets , Bair G. Bazarov, Jibzema G. Bazarova Baikal Institute of Nature Management SB RAS, 670047 Sakhyanovoy st., 6, Ulan-Ude, Russia * Corresponding author: subanakov@binm.bscnet.ru This article belongs to the regular issue. © 2021, The Authors. This article is published in open access form under the terms and conditions of the Creative Commons Attribution (CC BY) license (http://creativecommons.org/licenses/by/4.0/). Abstract Double borate Na3ErB2O6 was synthesized by the solid-state reaction. The crystal structure of Na3ErB2O6 was refined by the Rietveld meth- od: P21/c, a = 6.49775(14) Å, b = 8.50424(17) Å, c = 12.0067(3) Å, β = 118.4797(9)°, Z = 4. The crystal structure of Na3ErB2O6 consists of –[ErO6]∞-chains along the "b" axis, which are linked by BO3 trian- gles in a three-dimensional framework. Sodium atoms occupy empty positions inside the channels. The thermal behavior of Na3ErB2O6 was studied in detail in the range of 25–1150 °C range by DSC and TG methods. Na3ErB2O6 congruently melts at 1116 °C. Based on the re- sults of DSC measurements, three reversible phase transitions were found for Na3ErB2O6. Keywords sodium rare-earth borate solid-state reaction crystal structure Rietveld refinement thermal analysis Received: 05.10.2021 Revised: 18.10.2021 Accepted: 18.10.2021 Available online: 20.10.2021 1. Introduction Borates are considered to be attractive functional materi- als for non-linear optic and luminescence due to their wide variety of crystal structures, low synthesis tempera- ture, and environmental benignity [1–13]. Today commer- cially used nonlinear optical crystals of borates with supe- rior optical properties are β-BaB2O4 [14] and LiB3O5 [15]. Recent studies of borates are related to birefringent mate- rials [16] and self-frequency-doubling (SFD) laser ones [17]. SFD crystals belong to multi-functional materials and possess both laser and frequency doubling properties. The basic requirements for an efficient SFD laser crystal are excellent laser properties and excellent nonlinear optical properties with suitable birefringence. Therefore, SFD materials contained rare-earth elements and a nonlinear framework. To search new SFD materials, the oxide systems based on alkaline, rare earth, and boron were extensively stud- ied. Exploration of the Na2O–R2O–B2O3 systems revealed the existence of a number of double borates: Na2R2(BO3)2 [18–20], Na3RB2O6 [21–23], Na3R2B3O9 [21,24–26], Na3Y3B4O12 [27], Na3R9O3B8O24 [28,29]. Our attention was attracted by double borates with the general formula Na3RB2O6. This family of compounds includes borates with large lanthanides such as Na3LaB2O6 [21], Na3PrB2O6 [22], Na3SmB2O6 [22], Na3EuB2O6 [22], Na3YB2O6 [23] and Na3GdB2O6 [23]. The subject of our study is the possibility of replacing large lanthanides with erbium. The crystal structure and thermal stability of double borate Na3ErB2O9 was studied in the present work. 2. Experimental The title compounds were prepared by solid state reac- tions using high purity starting reagents: Na2CO3 (99.8%, Sigma Aldrich Ltd.), Er2O3 (99.9%, Red Chemist, Ltd., Russia), and H3BO3 (99.5%, Sigma Aldrich Ltd.). Before weighing, Er2O3 had been preheated at 850 °C for 8 hours to remove absorbed water. The reagents were weighed on an analytical balance with an accuracy of 0.5 mg. The mixtures of Na2CO3, Er2O3, and H3BO3 at mo- lar ratio 3:1:2 were thoroughly ground in an agate mor- tar, slowly heated up to 300 °C, and were kept for 5 hours. Then the samples were reground and annealed at 600 °C for 5 hours and finally at 700 °C for 40 hours with intermediate grindings until equilibrium was reached. Temperature was measured with a Pt–PtRh thermocouple. The temperatures up to 1200 °C were con- trolled with an accuracy of ±2 °C with an OMRON in- strument. The equilibrium was considered to be reached only when two successive heat treatments resulted in identical X-ray diffraction patterns. Powder X-ray diffraction data were recorded by a D8 ADVANCE Bruker AXS diffractometer (Vantec-1 detector) at room temperature using Cu Kα radiation and scanning http://chimicatechnoacta.ru/ https://doi.org/10.15826/chimtech.2021.8.4.02 https://orcid.org/0000-0002-1674-283X https://orcid.org/0000-0003-1301-1983 http://creativecommons.org/licenses/by/4.0/ Chimica Techno Acta 2021, vol. 8(4), № 20218402 ARTICLE 2 of 5 from 2θ = 8° to 100° in increments of 0.02° and a count- ing time of 0.1 s/step. Phase purity was verified by pow- der X-ray diffraction (XRD) and the profile was compared to that reported for the isostructural phase Na3NdB2O6. The TOPAS 4.2 [30] software suite was used to analyze the experimental data and to perform the Rietveld refine- ment of the obtained compound. All peaks in the X-ray powder diffraction pattern for Na3ErB2O9 were indexed satisfactory in a monoclinic cell (space group P21/c). Differential scanning calorimetry (DSC) and thermo- gravimetric (TG) measurements were performed on an STA 449 F1 Jupiter thermoanalyzer (NETZSCH) in the temperature range of 30–1150 °C in argon flow. Pt cruci- bles were used as vessels. Pt–PtRh thermocouples were used for temperature measurement. The precision of tem- perature measurement was ±1 °C. The heating and cooling rates were 10 °C/min. 3. Results and discussion The synthesized sample of Na3ErB2O6 is pink powder, which is characteristic for the Er-containing oxides. The structure of Na3NdB2O6 was used as initial model for the Rietveld refinement to define the positions of atoms. They were refined by isotropic approximation with “soft” limi- tations of the B–O distance and the B–O–B bond angles. The refined parameters were added sequentially with the graphical simulation of the background in continuous. The Pearson VII function was used to describe the shape of peaks. The isotropic displacement parameters (Biso) for the Er and Na atoms were refined separately, while for the O and B atoms they were taken as equivalent. The refine- ment process included corrections for the sample pre- ferred orientation and anisotropic broadening of peaks within the model of spherical harmonics. The refinement was stable and gave low R-factors (Fig. 1, Table 1). Na3ErB2O6 was crystallized in the monoclinic system with the space group P21/c. The unit cell parameters are: a = 6.49775(14) Å, b = 8.50424(17) Å, c = 12.0067(3) Å, β = 118.4797(9)°, Z = 4. Coordinates of atoms are given in Table 2. Further details of the crystal structure may be ob- tained from supplementary material. In the structure of Na3ErB2O6 (Fig. 2a), Er atoms are coordinated by seven O atoms in a distorted pentagonal bipyramid. The bipyramids share corners, forming a zig- zag chain along the “b” direction, and the chain is rein- forced by the B1O3 group, which uses all its three B–O bonds to join the neighboring bipyramids (Fig. 2a). Along with the “a” and “c” directions, these chains are connected via the B2O3 groups, thereby constructing a three- dimensional framework. Na1 and Na3 atoms are located in the interlayer channels and Na2 atom sits in the inlayer empty positions (Fig. 2b–d). Three Na atoms are coordi- nated by seven, six, and four O atoms, respectively. The main bond lengths (Å) and angles (°) of Na3ErB2O6 are shown in Table 3. Fig. 1 XRD data for Na3ErB2O6 refined by the Rietveld analysis: measured (red points), calculated (black profile) and difference between experimental points and calculated profile (grey curve) Table 1 Crystallographic data for Na3ErB2O6 phase at room temperature Chemical formula Na3ErB2O6 Space group P21/c (14) Formula weight, g/mol 353.9 Unit cell dimensions, Å α = γ = 90° a = 6.49775(14) b = 8.50424(17) c = 12.0067(3) β = 118.4797(9)° Cell volume, Å3 583.18(2) Z 4 Calculated density (g/cm3) 4.163 Rp, % 2.571 Rwp, % 3.534 Rexp, % 1.572 Bragg R-factor, % 1.864 χ2 2.249 Table 2 Fractional atomic coordinates and isotropic or equivalent isotropic displacement parameters of Na3ErB2O6 structure x y z Biso*/Beq Er 0.0970(3) 0.1261(1) 0.3287(1) 0.9(2) Na1 0.380(2) 0.8039(8) 0.3841(7) 1.1(3) Na2 0.058(2) 0.2963(8) 0.0802(8) 0.9(3) Na3 0.331(2) 0.9488(8) 0.1134(7) 3.1(3) B1 0.139(3) 0.4379(7) 0.3695(8) 1.0(6) B2 0.351(1) 0.5864(8) 0.1209(5) 1.0(6) O1 0.255(2) 0.334(1) 0.4714(9) 0.5(2) O2 0.049(2) 0.373(2) 0.2513(7) 0.5(2) O3 0.137(2) 0.600(1) 0.3911(9) 0.5(2) O4 0.226(1) 0.674(1) 0.1611(5) 0.5(2) O5 0.251(2) 0.505(1) 0.0086(7) 0.5(2) O6 0.413(1) 0.080(1) 0.3075(5) 0.5(2) Chimica Techno Acta 2021, vol. 8(4), № 20218402 ARTICLE 3 of 5 Fig. 2 The crystal structure of Na3RB2O9: a, b) ErO7 chains, BO3 triangles (a) and Na atoms (b) along a axis; b, c) a general view along b and c axes The DSC curves recorded for Na3ErB2O6 are shown in Fig. 3. Four endothermic signals at 717, 907, 1014, and 1116 °С were detected during the sample’s first heating, as shown in Fig. 3. The endothermic peak at 1116 °С corresponds to the melting point of Na3ErB2O6. The X-ray diffraction measurements indicate the congruent melting of the borate (Fig. 4). To determine the nature of the endothermal effects at 717, 907, 1014 °С and prove congruent melting, the same sample was recorded in the ‘‘heating-cooling” mode over the temperature range of 100–1150 °С (with melting). At first cooling, Na3ErB2O6 shows exothermic effects at 712, 831, 1000, 1098 °С. The second cooling reveals a new exothermic effect at 706 °С that seems to correspond to Na3ErB2O6 partial decomposition, which is confirmed by X-ray analysis. The observed temperatures hystereses are about 5, 76, 14, 18 degrees. Thus, the signature observed at 600–1150 °С reveals the existence of reversible phase transitions (type I) in Na3ErB2O6 and, respectively, additional experi- ments are needed to define the structure of the high- temperature modification of β, γ – Na3ErB2O6. Table 3 Main bond lengths (Å) and angles (°) of Na3ErB2O6 Er—O1 2.33(1) Na2—O5 2.55(1) Er—O2i 2.36(1) Na2—O6 3.19(1) Er—O2 2.26(2) Na3—O1x 2.40(1) Er—O3i 2.32(1) Na3—O3x 2.38(1) Er—O4i 2.20(1) Na3—O4 2.57(1) Er—O5ii 2.20(1) Na3—O6vii 2.40(1) Er—O6 2.22(1) B1—O1 1.40(1) Na1—O1iii 2.50(1) B1—O2 1.37(1) Na1—O2iv 2.53(1) B1—O3 1.40(1) Na1—O3 2.38(1) B2—O4 1.35(1) Na1—O4 2.61(1) B2—O5 1.37(1) Na1—O5v 2.72(1) B2—O6v 1.36(1) Na1—O5vi 2.60(1) O1—B1—O2 116(1) Na1—O6vii 2.56(1) O1—B1—O3 120(1) Na2—O1viii 2.48(1) O2—B1—O3 123(1) Na2—O2 2.18(1) O4—B2—O5 123(7) Na2—O3i 2.22(1) O4—B2—O6v 120(5) Na2—O4ix 2.60(1) O5—B2—O6v 118(1) Na2—O5ix 2.44(1) Symmetry codes: (i) –x, y–1/2, –z+1/2; (ii) x, –y+1/2, z+1/2; (iii) –x+1, –y+1, –z+1; (iv) –x, y+1/2, –z+1/2; (v) –x+1, y+1/2, –z+1/2; (vi) x, –y+3/2, z+1/2; (vii) x, y+1, z; (viii) x, –y+1/2, z–1/2; (ix) –x, –y+1, –z; (x) x, –y+3/2, z–1/2. Chimica Techno Acta 2021, vol. 8(4), № 20218402 ARTICLE 4 of 5 It should be pointed out that the transition was not found in Na3RB2O6 (R = Pr, Sm, Eu) [22]. Respectively, it can be reasonably assumed that the appearance of the phase transitions is observed only for the Na3RB2O6 borates where rare earth elements have small ionic radius. An X-ray examination of solid-state interactions be- tween the components of the Na2O–Er2O3–B2O3 system resulted in finding double borate Na3ErB2O6. Na3ErB2O6 was synthesized by solid-state reaction. The crystal struc- ture of Na3ErB2O6 was refined by the Rietveld analysis. Na3ErB2O6 consists of ErO7 distorted pentagonal bipyra- mids and BO3 groups. Na3ErB2O6 congruently melts at 1116 °C. The DSC and TG experiments assume that after melting Na3ErB2O6 decomposing with formation of Er2O3. The observed endothermic effects on the DSC curve are assumed to be attributed to high-temperature phase tran- sitions of the title compound. This assumption prompts us to thoroughly investigate this family of compounds in the future. Fig. 3 DSC measurement results Fig. 4 X-ray patterns of unmelted and melted Na3ErB2O6 specimen Conclusions An X-ray examination of solid-state interactions between the components of the Na2O–Er2O3–B2O3 system resulted in finding the double borate, Na3ErB2O6. Na3ErB2O6 was synthesized by solid-state reactions. The crystal structure of Na3ErB2O6 was refined by the Rietveld analysis. Na3ErB2O6 consists of ErO7 distorted pentagonal bipyra- mids and BO3 groups. Na3ErB2O6 congruently melts at 1116 °C. The DSC and TG experiments demonstrated that after melting Na3ErB2O6 decomposes with formation of Er2O3. The observed endothermic effects on the DSC curve are assumed to be attributed to high-temperature phase transitions of the title compound. This assumption prompts us to thoroughly investigate this family of com- pounds in the future. Acknowledgments The work was supported by Basic Project of BINM SB RAS № 0273-2021-0008. X-ray powder diffraction and thermal analysis were obtained using the equipment of the Collec- tive Use Center BINM SB RAS. References 1. Mutailipu M, Poeppelmeier KR, Pan S. Borates: A Rich Source for Optical Materials. Chem Rev. 2021;121:1130–1202. doi:10.1021/acs.chemrev.0c00796 2. Yang SH, Xue H, Guo SP. Borates as promising electrode mate- rials for rechargeable batteries. Coord Chem Rev. 2021;427. doi:10.1016/j.ccr.2020.213551 3. Leonyuk NI, Maltsev VV, Volkova EA. Crystal chemistry of high-temperature borates. Molecules. 2020;25. doi:10.3390/MOLECULES25102450 4. Topnikova AP, Belokoneva EL. The structure and classification of complex borates. Russ Chem Rev. 2019;88:204–228. doi:10.1070/rcr4835 5. Mutailipu M, Zhang M, Yang Z, Pan S. Targeting the Next Gen- eration of Deep-Ultraviolet Nonlinear Optical Materials: Ex- panding from Borates to Borate Fluorides to Fluorooxobo- rates. Acc Chem Res. 2019;52:791–801. doi:10.1021/acs.accounts.8b00649 6. Becker P. Borate materials in nonlinear optics. Adv Mater. 1998;10:979–992. doi:10.1002/(SICI)1521- 4095(199809)10:13<979::AID-ADMA979>3.0.CO;2-N 7. Chen C, Wu Y, Li R. The development of new NLO crystals in the borate series. J Cryst Growth. 1990;99:790–798. doi:10.1016/S0022-0248(08)80028-0 8. Kovtunets EV, Subanakov AK, Bazarov BG. Synthesis, struc- ture and luminescent properties of the new double borate K3Eu3B4O12. Kondens Sredy Mezhfaznye Granitsy. 2020;22:219–224. doi:10.17308/kcmf.2020.22/2823 9. Subanakov AK, Kovtunets EV, Bazarov BG, Dorzhieva SG, Ba- zarova JG. New double holmium borates: Rb3HoB6O12 and Rb3Ho2B3O9. Solid State Sci. 2020;105. doi:10.1016/j.solidstatesciences.2020.106231 10. Subanakov AK, Kovtunets EV, Bazarov BG, Pugachev AM, So- fich DO, Bazarova JG. Exploration of structural, thermal and vibrational properties of new noncentrosymmetric double bo- rate Rb3Tm2B3O9. Solid State Sci. 2021;120. doi:10.1016/j.solidstatesciences.2021.106719 11. Xia M, Shen S, Lu J, Sun Y, Li R. K3Li3Gd7(BO3)9: A New Gad- olinium-Rich Orthoborate for Cryogenic Magnetic Cooling. https://doi.org/10.1021/acs.chemrev.0c00796 https://doi.org/10.1016/j.ccr.2020.213551 https://doi.org/10.3390/MOLECULES25102450 https://doi.org/10.1070/rcr4835 https://doi.org/10.1021/acs.accounts.8b00649 https://doi.org/10.1002/(SICI)1521-4095(199809)10:13%3c979::AID-ADMA979%3e3.0.CO;2-N https://doi.org/10.1002/(SICI)1521-4095(199809)10:13%3c979::AID-ADMA979%3e3.0.CO;2-N https://doi.org/10.1016/S0022-0248(08)80028-0 https://doi.org/10.17308/kcmf.2020.22/2823 https://doi.org/10.1016/j.solidstatesciences.2020.106231 https://doi.org/10.1016/j.solidstatesciences.2021.106719 Chimica Techno Acta 2021, vol. 8(4), № 20218402 ARTICLE 5 of 5 Chem – A Eur J. 2018;24:3147–3150. doi:10.1002/chem.201705669 12. Xia M, Zhai K, Lu J, Sun Y, Li RK. Orthoborates LiCdRE5(BO3)6 (RE = Sm–Lu and Y) with Rare-Earth Ions on a Triangular Lat- tice: Synthesis, Crystal Structure, and Optical and Magnetic Properties. Inorg Chem. 2017;56:8100–8105. doi:10.1021/acs.inorgchem.7b00756 13. Xia M-J, Li RK. A new quaternary rare earth borate, CsLi2Gd4(BO3)5. Acta Crystallogr Sect E Struct Reports Online. 2007;63. doi:10.1107/S1600536807036586 14. Chen C, Wu Y, Li R. The development of new NLO crystals in the borate series. J Cryst Growth. 1990;99:790–798. doi:10.1016/S0022-0248(08)80028-0 15. Chen C, Li R. The anionic group theory of the non-linear opti- cal effect and its applications in the development of new high- quality NLO crystals in the borate series. Int Rev Phys Chem. 1988;8:65–91. doi:10.1080/01442358909353223 16. Qin F, Li RK. Predicting refractive indices of the borate optical crystals. J Cryst Growth. 2011;318:642–644. doi:10.1016/J.JCRYSGRO.2010.08.037 17. Yu H, Pan Z, Zhang H, Wang J. Recent advances in self- frequency-doubling crystals. J Mater. 2016;2:55–65. doi:10.1016/j.jmat.2015.12.001 18. Jia Z, Xia M. Congruent melt terbium-rich borate Na2Tb2B2O7: Synthesis, crystal structure, optical and magnetic properties. J Alloys Compd. 2018;743:537–542. doi:10.1016/j.jallcom.2018.02.031 19. Shan F, Zhang G, Yao J, Xu T, Zhang X, Fu Y, et al. Growth, structure, and optical properties of a self-activated crystal: Na2Nd2O(BO3)2. Opt Mater (Amst). 2015;46:461–466. doi:10.1016/j.optmat.2015.05.004 20. Nagpure PA, Omanwar SK. Synthesis and photoluminescence study of rare earth activated phosphor Na2La2B2O7. J Lumin. 2012;132:2088–2091. doi:10.1016/j.jlumin.2012.03.068 21. Mascetti J, Fouassier C, Hagenmuller P. Concentration quenching of the Nd3+ emission in alkali rare earth borates. J Solid State Chem. 1983;50:204–212. doi:10.1016/0022-4596(83)90189-5 22. Wang Z, Li H, Cai G, Jin Z. Synthesis, crystal structure, and thermal stability of new borates Na3REB2O6 (RE = Pr, Sm, Eu). Powder Diffr. 2016;31:110–117. doi:10.1017/S0885715616000051 23. Zhang Y, Chen XL, Liang JK, Xu T. Synthesis and structural study of new rare earth sodium borates Na3Ln(BO3)2 (Ln=Y, Gd). J Alloys Compd. 2002;333:72–75. doi:10.1016/S0925-8388(01)01689-9 24. Zhang G, Wu Y, Fu P, Wang G, Liu H, Fan G, et al. A new sodi- um samarium borate Na3Sm2(BO3)3. J Phys Chem Solids. 2001;63:145–9. doi:10.1016/S0022-3697(01)00090-7 25. Yang Z, Ning Y, Keszler DA. Na3Sc2(BO3)3. Acta Crystallogr Sect E Struct Reports Online. 2006;62:266–268. doi:10.1107/S1600536806036737 26. Zhou WW, Zhuang RZ, Zhao W, Wang GF, Zhang LZ, Ma JG, et al. Second harmonic generation in Na3Gd2(BO3)3 crystals. Cryst Res Technol. 2011;46:926–930. doi:10.1002/crat.201100077 27. Shan F, Kang L, Zhang G, Yao J, Lin Z, Xia M, et al. Na3Y3(BO3)4: A new noncentrosymmetric borate with an open- framework structure. Dalt Trans. 2016;45:7205–7208. doi:10.1039/c6dt00950f 28. Gravereau P, Chaminade JP, Pechev S, Nikolov V, Ivanova D, Peshev P. Na3La9O3(BO3)8, a new oxyborate in the ternary sys- tem Na2O–La2O3–B2O3: Preparation and crystal structure. Solid State Sci. 2002. doi:10.1016/S1293-2558(02)01344-4 29. Zhang J, Zhang G, Li Y, Wu Y, Fu P, Wu Y. Thermophysical properties of a new nonlinear optical Na3La9O3(BO3)8 crystal. Cryst Growth Des. 2010;10:4965–4967. doi:10.1021/cg1010743 30. Coelho AA. Topas: General Profile and Structure Analysis Software for Powder Diffraction Data. Bruker AXS, 2005. https://doi.org/10.1002/chem.201705669 https://doi.org/10.1021/acs.inorgchem.7b00756 https://doi.org/10.1107/S1600536807036586 https://doi.org/10.1016/S0022-0248(08)80028-0 https://doi.org/10.1080/01442358909353223 https://doi.org/10.1016/J.JCRYSGRO.2010.08.037 https://doi.org/10.1016/j.jmat.2015.12.001 https://doi.org/10.1016/j.jallcom.2018.02.031 https://doi.org/10.1016/j.optmat.2015.05.004 https://doi.org/10.1016/j.jlumin.2012.03.068 https://doi.org/10.1016/0022-4596(83)90189-5 https://doi.org/10.1017/S0885715616000051 https://doi.org/10.1016/S0925-8388(01)01689-9 https://doi.org/10.1016/S0022-3697(01)00090-7 https://doi.org/10.1107/S1600536806036737 https://doi.org/10.1002/crat.201100077 https://doi.org/10.1039/c6dt00950f https://doi.org/10.1016/S1293-2558(02)01344-4 https://doi.org/10.1021/cg1010743