id	author	title	date	pages	extension	mime	words	sentence	flesch	summary	cache	txt
fumecheng-12769	Alparslan, Cem; Bayraktar, Şenol; Gupta, Kapil	A COMPARATIVE STUDY ON MECHANICAL PERFORMANCE OF PLA, ABS, AND CF MATERIALS FABRICATED BY FUSED DEPOSITION MODELING	2024	18	.pdf	application/pdf	7130	386	49	While the fracture surfaces of PLA samples were smooth, and the layer lines were evident. In PLA samples, the highest YS (18.95 MPa) and TS (20.45 MPa) were obtained in the hexagon pattern and LT of 0.15 mm, while the lowest YS value (10.17 MPa) was measured in line pattern and LT of 0.35 mm, and the TS value was (8.48 MPa) in the triangle pattern and LT of 0.35 mm (Fig 6a).	cache/fumecheng-12769.pdf	txt/fumecheng-12769.txt