fis-1287	Di Cocco, Vittorio; Iacoviello, Francesco; Rossi, Alessandra; Cavallini, Mauro	Damaging micromechanisms characterization in a ferritic-pearlitic ductile cast iron	2014	6	.pdf	application/pdf	2546	102	39	The increase of the macroscopic deformation implies the activation of different damaging micromechanisms with cracks that initiate and propagate in the graphite nodules (Fig. 4a), with the debonding at the interface ferritic shield – graphite nodules that is more and more evident (Fig. Main D V. Di Cocco et alii, Frattura ed Integrità Strutturale, 30 (2014) 62-67; DOI: 10.3221/IGF-ESIS.30.09 63 damaging micromechanism of ferritic DCIs (maybe, the most investigated grades) was usually identified with the ferritic matrix - graphite nodules debonding [2]: microcracks in graphite nodules were also observed, but their influence was considered as practically negligible and ferritic DCIs were considered as a ductile porous material	cache/fis-1287.pdf	txt/fis-1287.txt