id	author	title	date	pages	extension	mime	words	sentence	flesch	summary	cache	txt
fis-1658	Besel, Y.; Besel, M.; Alfaro Mercado, U.; Kakiuchi, T.; Uematsu, Y.	Influence of joint line remnant on crack paths under static and fatigue loadings in friction stir welded Al-Mg-Sc alloy	2015	11	.pdf	application/pdf	5837	359	60	Since the asperity of JLR fracture in the lower part of Fig. 13(b) was equivalent to the average grain size of weld-480 (1.67 µm), it is considered that the crack propagated intergranularly at JLR. Figure 11: Fatigue fracture surface of weld-480 tested at a = 220 MPa.	cache/fis-1658.pdf	txt/fis-1658.txt