Microsoft Word - numero_37_art_1 A. Eberlein et alii, Frattura ed Integrità Strutturale, 37 (2016) 1-7; DOI: 10.3221/IGF-ESIS.37.01 1 Focussed on Multiaxial Fatigue and Fracture Crack front segmentation under combined mode I- and mode III- loading A. Eberlein University of Paderborn, Institute of Applied Mechanics, Pohlweg 47-49, 33098 Paderborn, Germany eberlein@fam.upb.de, http://mb.uni-paderborn.de/fam/ H. A. Richard University of Paderborn, Institute of Applied Mechanics, Pohlweg 47-49, 33098 Paderborn, Germany richard@fam.upb.de, http://mb.uni-paderborn.de/fam/ ABSTRACT. This article approaches the topic of crack initiation and crack growth behaviour under combined mode I- and mode III-loading conditions. Such loading combinations especially lead to a crack, which unscrew out of its initial orientation and segments into many single cracks respectively facets. This characteristic depicts the crucial difference to a crack growth under pure mode I-loading, pure in-plane shearing (mode II) as well as 2D-mixed-mode-loadings. Since this stepped fractured surfaces thus far are proved little and therefore their characterisation remains to be done, a facets quantification using some characteristic dimensions will be performed within this article. After the description of experiments for facet creation the facet’s quantification using the crack profile near the initial position each facet will be analysed concerning characteristic dimensions. Finally the findings will be illustrated and discussed in this contribution. KEYWORDS. 3D-mixed-mode; Facets; Fatigue; Fracture; CTSR-specimen. INTRODUCTION by today unsolved and long existing research matter in fracture mechanics is the characterisation of crack initiation and growth behaviour under combined mode I- and mode III-loading. This loading combination specially leads the initial crack to twist out of its previous direction and separate at once into multiple daughter cracks, afterwards called facets. Building on the researches and findings from Sommer [1], Knauss [2] as well as Pons and Karma [3] within this article a quantification of facets will be presented and discussed. The purpose is to get new insights and facts about facets creation and initiation. EXPERIMENTS FOR FACET CREATION reating facets experiments under mixed-mode I + III-loading were performed using the CTSR-specimen and corresponding loading device [4, 5]. A detailed explanation of the experimental procedure and CTSR-specimen’s geometry follows below. A C A. Eberlein et alii, Frattura ed Integrità Strutturale, 37 (2016) 1-7; DOI: 10.3221/IGF-ESIS.37.01 2 CTSR (Compact Tension Shear Rotation) -specimen Referring to the AFM-specimen a new specimen, so-called CTSR-specimen (Fig. 1) has been developed [4]. Relevant specimen’s dimensions are listed in the chart on the right hand side of Fig. 1. Hereby the specimen thickness t is a compromise between a thick specimen with a high torsional stiffness and high testing load levels. The appropriate loading device is shown in Fig. 2. In combination with the new specimen this loading device enables any combination of mixed- mode-loading including pure mode I-, pure mode II- and pure mode III-loading. A detailed explanation and illustration of adjusting the mixed-mode-loading can be found in [4, 5, 6]. specimen length l 103 mm specimen width w 55 mm initial crack length a0 27.5 mm specimen thickness t 15.5 mm Figure 1: CTSR-specimen with characteristic dimensions. Experimental Procedure under combined Mode I-Mode III-loading For the creation of facets crack growth experiments with changing loading directions were performed. After a crack growth of a crack length a = 3.5 mm under mode I-loading condition with a constant cyclic comparative stress intensity factor ΔKV the loading direction by turning the loading device and rotating the specimen was changed into mixed- mode I + III-loading with ΔKI ≠ 0 and ΔKIII ≠ 0 (Fig. 2). Figure 2: Mixed-mode I + III-loading by shifting the loading device. Then the tests started again under constant cyclic load range ΔF set so, that the cyclic comparative stress intensity factor ΔKV before and after the loading direction was identically. Crack length-Cycle Curves and Fractured Surfaces Typical a-N-curves resulting from such experiments with changing loading directions are shown in Fig. 3. The mixed- mode I + III-loading was adjusted by varying both loading angles α and β. A crack length a of 3.5 mm under mode I- loading, due to that high cyclic stress intensity factor ΔKV = ΔKI, is reached after ca. N = 70,000 cycles. Afterwards changing the loading direction the crack growth delays. Significant crack growth retardations were noticed by stress intensity factor ratios 1 < KIII/KI < ∞. A. Eberlein et alii, Frattura ed Integrità Strutturale, 37 (2016) 1-7; DOI: 10.3221/IGF-ESIS.37.01 3 Figure 3: Crack growth retardation after changing the loading direction from mode I to mixed-mode I + III. On the one hand the retardation effects are caused by the new crack growth direction due to mode III-loading part. Hereby the crack twists at an angle ψ0 out of its previous orientation. Additionally the crack separates in many facets, which influence the crack growth rate too. Characteristic fractured surfaces with facet formation after changing the loading direction from mode I-loading to mixed-mode I + III-loading are pictured in Fig. 4. This row on fractured surfaces shows the facet formation depending on mode III-part on the total stress intensity factor KIII/(KI + KIII). The figures indicate that facet formation begins at a specific mode III-part on the total stress intensity factor of KIII/(KI + KIII) = 0.37. Within this experimental research no facets were observed below that ratio. The first fractured surface on the left hand side of Fig. 4, captured by mode III-part on the total stress intensity factor of KIII/(KI + KIII) = 0.26, shows that the crack continuously and smoothly without any facet initiation changes its direction. Furthermore, the crack front is still coherent. With increasing mode III-part on the mixed-mode I + III-loading the facets’ shape changes clearly. Figure 4: Facet formation with increasing mode III-part. A. Eberlein et alii, Frattura ed Integrità Strutturale, 37 (2016) 1-7; DOI: 10.3221/IGF-ESIS.37.01 4 To get a better knowledge of such facet formation under mixed-mode I + III-loading for its consideration in existing hypotheses for crack growth prediction under 3D-mixed-mode-loadings a facet quantification was performed, which is presented and discussed in the next section. CHARACTERIZATION OF CRACK FRONT SEGMENTATION he first step to understand the crack growth behaviour under mode I-mode III-loading conditions is to quantify the crack front segmentation respectively the facet formation. Therefor some characteristic dimensions and angles were defined. Definition of characteristic Dimensions First of all, the geometry of each facet will be simplified to a circular shape. Then due to the non-planar shear stress τz facets initiate twisted under a facet angle ψF as Fig. 5 a) shows. Reflecting the work of Lin et al. [7] this facet quantification distinguishes between two facet types – ascending facets fas indicated in Fig. 5 b) by red lines – and falling facets ffa indicated in Fig. 5 b) by dashed lines, which finally connects the ascending facets fas. Ascending facets fas initiate induced by a local opening mode-loading [8] whereas falling facets ffa form in a bridging region B making a connection to each fas facet. Figure 5: Definition of characteristic dimensions for facet quantification: a) Schematic facet formation at the crack front due to τz; b) Facet’s geometry and characteristic dimensions in the y-z-plane The ffa facets are unfavourable oriented to a local opening mode-loading. Consequently, another local mechanisms, like local friction or plasticity [7], are probably responsible for their formation. So higher energies respectively loads for the creation of ffa facets are required. As a conclusion such facet formation proceeds at a later crack growth stage as the initiation of fas facets [3, 7]. Other characteristic dimensions for facet quantification are the projected facet length d, the facet distance c and the width e of the bridging region B (see Fig. 5 b)). Approach for Quantification of Facet’s Geometry For facet quantification the fractured surfaces were analysed microscopically. Hereby the crack’s profile was measured close to the initial notch that is after a short crack extension Δa. Fig. 6 illustrates a typical crack’s profile of a mode III fractured surface. The measurement plane of crack’s profile, indicated by the arrow, lies in a distance of about Δa ≈ 285 µm from the wire eroded notch. In the front view (indicated by the red arrow) the crack’s profile looks as in Fig. 6 b) shown. Thereby the fas facets, which were considered for the quantification, are marked in the graph. Furthermore, it is visible that in the middle of the specimen the biggest facets creates. The analysis of all fas facets reveals an average projected facet length of d = 1.23 mm and an average distance of c = 1.63 mm. The biggest facet angles ψF exhibit the fas facets fas,3, fas,4 and fas,5 (see Fig. 6 b)). The angles ψF lie within an expected range between 42.3° and 49.3°. Starting from the middle of the specimen to the specimen borders a decreasing facet angle was noted. The reason for this is the decreasing shear stress τz and an increasing mode II-part by moving from the middle of the specimen to the border. Due to no pure mode III-loading condition facets near the specimen border initiate under smaller twist angles. The measurement of the bridging regions B exposed an average width e of 342 µm. Such a systematic analysis approach for facet quantification was performed for all fractured surfaces within this experimental research. In the next section the results of facet quantification are shown and discussed. T A. Eberlein et alii, Frattura ed Integrità Strutturale, 37 (2016) 1-7; DOI: 10.3221/IGF-ESIS.37.01 5 Figure 6: Analysis of facet formation: a) Fractured surface under pure mode III-loading; b) Crack’s profile: measurement of each formed facet. Results of Facet’s Quantification The results of facet’s quantification are illustrated in Fig. 7. Due to the fact that within this experimental research no facets below KIII/(KI + KIII) of 0.37 initiated, the number of facets in Fig. 7 a) for lower KIII/(KI + KIII)-ratios is zero. When facets create their quantity decreases with increasing mode III-part to an average number of five facets at pure mode III- loading. Moreover, an increasing projected facet length d and facet distance c can be detected by means of fractured surfaces (shown in Fig. 7 b)). At pure mode III-loading an average projected facet length d of 2.5 mm and an average facet distance c of 3.4 mm result. Since the shear stress τz declines by moving along the specimen thickness from the middle of the specimen to the border, the conditions for pure mode III-loading are mostly given only in a limited range around the centre plane [9]. Therefore, for the measurement of the facet angles ψF only three facets around the centre plane of the specimen thickness are considered. Fig. 7 c) displays the results of the measured facet angles. In contrast to the hypothesis by Richard for the crack twisting angle ψ0 the measured facet angles partially are ca. 10° smaller as the hypothesis predicts. However, the measured facet angle ψF for pure mode III-loading coincides very well with the hypothesis by Richard. The determination of the facet angles respectively the crack twisting angles is principally very difficult. The measured deviations can be formed e. g. by local plastic deformations of the facets while final rupture. In addition a strong correlation between the projected facet length d, the facet distance c and the bridging width e (see Fig. 7 d)) of the bridging regions B (see Fig. 7 e)) with the measured facet angles ψF exist. Such a correlation between this characteristic dimensions Lin et al. found too [7]. This correlation they explain on the basis of energy’s balance consideration. The result of the bridging regions analyses is pictured in Fig. 7 d). Here the characteristic width e increases with rising mode III-part. The magnitude of the bridging width e is in comparison with the projected facet length d and the facet distance c significantly smaller and is in a direct contact with both values. At pure mode III-loading the bridging width e is almost 1 mm. Further the fractured surfaces with higher mode III-loading parts in the bridging regions B exhibit no fatigue characteristics. Instead the fractured surfaces show a classical strength failure due to cleavage fracture as well as shear fracture. Based on this experimental knowledge of facet’s creation and crack front segmentation under combined mode I- mode III-loading the next step will be an establishing of a criterion for crack growth initiation under mixed-mode I + III- loadings. In this field today only a few approaches subsist, which are subjected to many assumptions and restrictions [7, 10, 11, 12, 13]. A. Eberlein et alii, Frattura ed Integrità Strutturale, 37 (2016) 1-7; DOI: 10.3221/IGF-ESIS.37.01 6 Figure 7: Overview of facets quantification’s results (averages): a) Number of facets depending on mode III-part; b) Projected facet length d and facet distance c depending on mode III-part; c) Facet angle ψF depending on mode III-part in contrast to the crack twisting angle ψ0 by Richard [6]; d) Bridging width e of regions B depending on mode III-part; e) Bridging regions B of a pure mode III fractured surface REFERENCES [1] Sommer, E., Formation of fracture ‘lances’ in glass, Engng. Frac. Mech., 1 (1969) 539–546. [2] Knauss, W.G., An observation of crack propagation in anti-plane shear, Int. J. Frac., 6 (1970) 183-187. [3] Pons, A.J., Karma, A., Helical crack-front instability in mixed-mode fracture, Nature, 464 (2010) 85-89. [4] Schirmeisen, N.-H., Risswachstum unter 3D-Mixed-Mode-Beanspruchung, VDI-Verlag, Düsseldorf, (2012). [5] Eberlein, A., Einfluss von Mixed-Mode-Beanspruchung auf das Ermüdungsrisswachstum in Bauteilen und Strukturen. VDI-Verlag, Düsseldorf, (2016). [6] Richard, H.A., Schramm, B., Schirmeisen, N.-H., Cracks on Mixed-Mode loading – Theories, experiments, simulations, Int. J. Fat., 62 (2014) 93-103. A. Eberlein et alii, Frattura ed Integrità Strutturale, 37 (2016) 1-7; DOI: 10.3221/IGF-ESIS.37.01 7 [7] Lin, B., Mear, M.E., Ravi-Chandar, K., Criterion for initiation of cracks under mixed-mode I + III loading, Int. j. Frac., 165 (2010) 175-188. [8] Pollard, D.D., Segall, P.E., Delaney, P.T., Formation and interpretation of dilatant echelon cracks, Geol. Soc. Am. Bull., 93 (1982) 1291-1303. [9] Kullmer, G., Richard, H.A., Wang, C., Eberlein, A., Numerische Untersuchungen zur Ermittlung der Rissablenkungs- und Rissverdrehungswinkel bei allgemeiner Mixed-Mode-Belastung, DVM-Bericht 245, Bruchmechanische Werkstoff- und Bauteilbewertung: Beanspruchungsanalyse, Prüfmethoden und Anwendungen, Deutscher Verband für Materialforschung und –prüfung e.V. Berlin (2013) 59-68. [10] Cambonie, T., Lazarus, V., Quantification of the crack fragmentation resulting from mode I + III loading, Proc. Mater. Science 3 (2014) 1816-1821. [11] Pham, K.H., Ravi-Chandar, K., Further examination of the criterion for crack initiation under mixed-mode I + III loading, Int. J. Frac. 189 (2014) 121-138. [12] Leblond, J.-B., Lazarus, V., Karma, A., Multiscale cohesive zone model for propagation of segmented crack fronts in mode I + III fracture, Int. J. Frac. 191 (2015) 167-189. [13] Ronsin, O., Caroli, C., Baumberger, T., Crack front echelon instability in mixed mode fracture of a strong nonlinear elastic solid, Europhys. Lett. 105 (2014) 34001. << /ASCII85EncodePages false /AllowTransparency false /AutoPositionEPSFiles true /AutoRotatePages /None /Binding /Left /CalGrayProfile (Dot Gain 20%) /CalRGBProfile (sRGB IEC61966-2.1) /CalCMYKProfile (U.S. Web Coated \050SWOP\051 v2) /sRGBProfile (sRGB IEC61966-2.1) /CannotEmbedFontPolicy /Error /CompatibilityLevel 1.4 /CompressObjects /Tags /CompressPages true /ConvertImagesToIndexed true /PassThroughJPEGImages true /CreateJobTicket false /DefaultRenderingIntent /Default /DetectBlends true /DetectCurves 0.0000 /ColorConversionStrategy /CMYK /DoThumbnails false /EmbedAllFonts true /EmbedOpenType false /ParseICCProfilesInComments true /EmbedJobOptions true /DSCReportingLevel 0 /EmitDSCWarnings false /EndPage -1 /ImageMemory 1048576 /LockDistillerParams false /MaxSubsetPct 100 /Optimize true /OPM 1 /ParseDSCComments true /ParseDSCCommentsForDocInfo true /PreserveCopyPage true /PreserveDICMYKValues true /PreserveEPSInfo true /PreserveFlatness true /PreserveHalftoneInfo false /PreserveOPIComments true /PreserveOverprintSettings true /StartPage 1 /SubsetFonts true /TransferFunctionInfo /Apply /UCRandBGInfo /Preserve /UsePrologue false /ColorSettingsFile () /AlwaysEmbed [ true ] /NeverEmbed [ true ] /AntiAliasColorImages false /CropColorImages true /ColorImageMinResolution 300 /ColorImageMinResolutionPolicy /OK /DownsampleColorImages true /ColorImageDownsampleType /Bicubic /ColorImageResolution 300 /ColorImageDepth -1 /ColorImageMinDownsampleDepth 1 /ColorImageDownsampleThreshold 1.50000 /EncodeColorImages true /ColorImageFilter /DCTEncode /AutoFilterColorImages true /ColorImageAutoFilterStrategy /JPEG /ColorACSImageDict << /QFactor 0.15 /HSamples [1 1 1 1] /VSamples [1 1 1 1] >> /ColorImageDict << /QFactor 0.15 /HSamples [1 1 1 1] /VSamples [1 1 1 1] >> /JPEG2000ColorACSImageDict << /TileWidth 256 /TileHeight 256 /Quality 30 >> /JPEG2000ColorImageDict << /TileWidth 256 /TileHeight 256 /Quality 30 >> /AntiAliasGrayImages false /CropGrayImages true /GrayImageMinResolution 300 /GrayImageMinResolutionPolicy /OK /DownsampleGrayImages true /GrayImageDownsampleType /Bicubic /GrayImageResolution 300 /GrayImageDepth -1 /GrayImageMinDownsampleDepth 2 /GrayImageDownsampleThreshold 1.50000 /EncodeGrayImages true /GrayImageFilter /DCTEncode /AutoFilterGrayImages true /GrayImageAutoFilterStrategy /JPEG /GrayACSImageDict << /QFactor 0.15 /HSamples [1 1 1 1] /VSamples [1 1 1 1] >> /GrayImageDict << /QFactor 0.15 /HSamples [1 1 1 1] /VSamples [1 1 1 1] >> /JPEG2000GrayACSImageDict << /TileWidth 256 /TileHeight 256 /Quality 30 >> /JPEG2000GrayImageDict << /TileWidth 256 /TileHeight 256 /Quality 30 >> /AntiAliasMonoImages false /CropMonoImages true /MonoImageMinResolution 1200 /MonoImageMinResolutionPolicy /OK /DownsampleMonoImages true /MonoImageDownsampleType /Bicubic /MonoImageResolution 1200 /MonoImageDepth -1 /MonoImageDownsampleThreshold 1.50000 /EncodeMonoImages true /MonoImageFilter /CCITTFaxEncode /MonoImageDict << /K -1 >> /AllowPSXObjects false /CheckCompliance [ /None ] /PDFX1aCheck false /PDFX3Check false /PDFXCompliantPDFOnly false /PDFXNoTrimBoxError true /PDFXTrimBoxToMediaBoxOffset [ 0.00000 0.00000 0.00000 0.00000 ] /PDFXSetBleedBoxToMediaBox true /PDFXBleedBoxToTrimBoxOffset [ 0.00000 0.00000 0.00000 0.00000 ] /PDFXOutputIntentProfile () /PDFXOutputConditionIdentifier () /PDFXOutputCondition () /PDFXRegistryName () /PDFXTrapped /False /CreateJDFFile false /Description << /ARA /BGR /CHS /CHT /CZE /DAN /DEU /ESP /ETI /FRA /GRE /HEB /HRV (Za stvaranje Adobe PDF dokumenata najpogodnijih za visokokvalitetni ispis prije tiskanja koristite ove postavke. Stvoreni PDF dokumenti mogu se otvoriti Acrobat i Adobe Reader 5.0 i kasnijim verzijama.) /HUN /ITA /JPN /KOR /LTH /LVI /NLD (Gebruik deze instellingen om Adobe PDF-documenten te maken die zijn geoptimaliseerd voor prepress-afdrukken van hoge kwaliteit. De gemaakte PDF-documenten kunnen worden geopend met Acrobat en Adobe Reader 5.0 en hoger.) /NOR /POL /PTB /RUM /RUS /SKY /SLV /SUO /SVE /TUR /UKR /ENU (Use these settings to create Adobe PDF documents best suited for high-quality prepress printing. Created PDF documents can be opened with Acrobat and Adobe Reader 5.0 and later.) >> /Namespace [ (Adobe) (Common) (1.0) ] /OtherNamespaces [ << /AsReaderSpreads false /CropImagesToFrames true /ErrorControl /WarnAndContinue /FlattenerIgnoreSpreadOverrides false /IncludeGuidesGrids false /IncludeNonPrinting false /IncludeSlug false /Namespace [ (Adobe) (InDesign) (4.0) ] /OmitPlacedBitmaps false /OmitPlacedEPS false /OmitPlacedPDF false /SimulateOverprint /Legacy >> << /AddBleedMarks false /AddColorBars false /AddCropMarks false /AddPageInfo false /AddRegMarks false /ConvertColors /ConvertToCMYK /DestinationProfileName () /DestinationProfileSelector /DocumentCMYK /Downsample16BitImages true /FlattenerPreset << /PresetSelector /MediumResolution >> /FormElements false /GenerateStructure false /IncludeBookmarks false /IncludeHyperlinks false /IncludeInteractive false /IncludeLayers false /IncludeProfiles false /MultimediaHandling /UseObjectSettings /Namespace [ (Adobe) (CreativeSuite) (2.0) ] /PDFXOutputIntentProfileSelector /DocumentCMYK /PreserveEditing true /UntaggedCMYKHandling /LeaveUntagged /UntaggedRGBHandling /UseDocumentProfile /UseDocumentBleed false >> ] >> setdistillerparams << /HWResolution [2400 2400] /PageSize [612.000 792.000] >> setpagedevice