Microsoft Word - numero_37_art_14 K. Yanase et alii, Frattura ed Integrità Strutturale, 37 (2016) 101-107; DOI: 10.3221/IGF-ESIS.37.14 101 Focussed on Multiaxial Fatigue and Fracture High cycle torsional fatigue properties of 17-4PH stainless steel K. Yanase Fukuoka University kyanase@fukuoka-u.ac.jp, http://www.fukuoka-u.ac.jp/english/ B.M. Shönbauer University of Natural Resources and Life Sciences (BOKU) bernd.schoenbauer@boku.ac.at, https://www.boku.ac.at/en/ M. Endo Fukuoka University endo@fukuoka-u.ac.jp, http://www.fukuoka-u.ac.jp/english/ ABSTRACT. Sensitivity to small defects under torsional fatigue loading condition is examined in the high cycle fatigue regime. Fatigue crack initiation and small crack growth behaviors were observed during fatigue testing and fractographic investigations were performed. The results are compared to the data obtained in the uniaxial fatigue tests, which allows the effect of biaxial stresses on the surface of material to be discussed. Finally, an approach for predicting the fatigue limit of 17-4PH stainless steel under torsional and tension-compression fatigue loadings is presented. KEYWORDS. 17-4PH; Small defect; Torsion; Biaxial fatigue; Fatigue limit. INTRODUCTION recipitation-hardened chromium-nickel-copper stainless steel 17-4PH possesses high strength, toughness and good corrosion resistance. Therefore, it is widely used in applications where good corrosion resistance as well as high strength are required, e.g., in the aerospace, chemical, food processing, paper and power industry. In the last few decades, a number of investigations on the uniaxial fatigue properties of 17-4PH have been performed; however, no results of torsional fatigue tests are presently available. In practice, there are several applications for the material in which components (e.g., bearing outer rings, propeller shafts and pressure safety valve springs) are exposed to torsional fatigue loading and where a high number of load cycles is accumulated within service life. Given the substantial knowledge on uniaxial fatigue, it is of practical merit to propose a predictive method that can connect the fatigue strength under multiaxial loading with that under uniaxial loading. In our previous studies [1,2], a series of tension-compression fatigue tests were carried out to elucidate the uniaxial fatigue properties of 17-4PH stainless steel in the high and very high cycle fatigue regimes. It was found that the material exhibits interesting properties that are different from those noted for conventional steels. For example, the defect tolerance under cyclic loading is highly dependent on the notch root radius, which makes the prediction of the fatigue strength in the presence of small flaws challenging. P K. Yanase et alii, Frattura ed Integrità Strutturale, 37 (2016) 101-107; DOI: 10.3221/IGF-ESIS.37.14 102 As an extension of our previous work [1,2], further fatigue tests under torsional loading at R = ˗1 were conducted and the results yielded are reported in this paper. In particular, material sensitivity to small defects under torsional fatigue loading condition is examined in the high cycle fatigue regime. Furthermore, fatigue crack initiation and small crack growth behavior were observed during fatigue testing and fractographic investigations were performed. The results are compared to the data obtained in the tension-compression fatigue tests and the effects of biaxial stresses on the surface of material are discussed. Finally, the experimental data are evaluated to examine the predictive approach (cf. [3-7]) for the fatigue strength of 17-4PH stainless steel under torsional and tension-compression fatigue loadings. MATERIAL AND EXPERIMENT he testing material used in the present investigation was a chromium-nickel-copper stainless steel 17-4PH precipitation hardened at 913 °C and age hardened at 621 °C for 4 h (condition H1150). The material properties at room temperature are summarized in Tab. 1, and the average grain size is 11 m (independent of orientation). For more details, we refer to Schönbauer et al. [1]. The surface of a round-bar specimen was ground and electropolished to remove the residual stress. Artificial defects (one- hole, two-hole, and three-hole, respectively) were introduced in the gage length of the specimen (length = 10 mm, Fig. 1). The major axes of two-hole and three-hole defects were intentionally set to be perpendicular to the direction of the major principal stress. To remove any residual stresses that were possibly generated during drilling, the specimens were stress- relief annealed in a vacuum at 600°C for one hour. Fatigue tests were performed by using a servohydraulic testing machine at stress ratio R = ˗1. Tensile strength (MPa) Yield strength (MPa) Elongation (%) Reduction of area (%) Vickers hardness (kgf/mm2) 1030 983 21 61 352 Table 1: Mechanical properties of the 17-4PH at room temperature. Figure 1: Specimen shape and geometry for the torsional fatigue test. RESULTS AND DISCUSSION n this section, the obtained experimental data are examined by considering the effects of the principal stresses on the surface of specimen and area [8]. Here, area is defined as the square root of the projection area perpendicular to the major principal stress direction. Furthermore, the characteristic properties of 17-4PH stainless steel are discussed. Fatigue Crack Growth Behavior Concerning the one-hole defect (diameter = 100 µm, depth = 63 µm, area = 70 µm), all specimens failed from smooth part rather than originating from the hole. Accordingly, this defect had no influence on the fatigue limit. However, small mixed mode cracks (Mode III and I) were observed at the bottom and at the edge of the hole, respectively, as shown in Fig. 2. Examination of the specimens with the two-hole defect (diameter = 2100 µm, depth = 131 µm, area = 161 µm) and the three-hole defect (diameter = 3100 µm, depth = 280 µm, area = 274 µm) showed that failure originated from T I K. Yanase et alii, Frattura ed Integrità Strutturale, 37 (2016) 101-107; DOI: 10.3221/IGF-ESIS.37.14 103 holes associated with Mode I fatigue crack growth in the principal stress direction (i.e., 45 degrees from the specimen axis), as shown in Fig. 3. Figure 2: One-hole defect (a) before and (b) after fatigue testing at shear stress amplitude, a = 320 MPa and number of cycles, N = 2.8107 cycles. Figure 3: Mode I fatigue crack growth from a two-hole defect under torsional loading at shear stress amplitude, a = 290 MPa. 10 0 10 1 10 2 10 ‐13 10 ‐12 10 ‐11 10 ‐10 10 ‐9 10 ‐8 10 ‐7 Stress intensity factor range K I  (MPam) C ra ck  g ro w th  r a te  d a /d N  ( m /c y cl e ) * For torsional loading, the crack is assumed as a semicircular crack Fitting curve Torsion Tension‐Compression Figure 4: FCGR curves for Mode I crack under torsional loading and tension-compression loading [9]. Specimen axis Specimen axis K. Yanase et alii, Frattura ed Integrità Strutturale, 37 (2016) 101-107; DOI: 10.3221/IGF-ESIS.37.14 104 In Fig. 4, the fatigue crack growth rate (FCGR) under torsional loading is compared to that under tension-compression loading [9]. It is noted that, for torsional loading, the stress intensity factor range is calculated by assuming a semi-circular crack. As shown, FCGR can be uniquely characterized irrespective of the difference of loading condition. However, the crack shape is not necessarily semi-circular, as was noted for a medium carbon steel (JIS S35C) (Fig. 5, [10]). Accordingly, a further study is necessary to inspect the evolution of crack shape and its effect on the torsional fatigue behavior of 17- 4PH. Figure 5: Crack profile propagating from an artificial defect in a medium carbon steel (JIS S35C) under torsional loading (R = ˗1) [10]. Fatigue Limit By considering the major principal stress 1 and the minor principal stress 2 on the surface of material, the fatigue limit can be expressed as [3]:       1 2 w 1/6 1.43( 120) ( ) k HV area (1) where HV signifies the Vickers hardness. Under torsional loading, the principal stresses are rendered as  1 and   2 (Fig. 6). Therefore, Eq. (1) can be rewritten to yield:            w w1/6 1/6 1.43( 120) 1.43( 120)1 (1 ) 1( ) ( ) HV HV k karea area (2)    Two‐hole defect Applied torque Applied torque Figure 6: Stress transformation on the specimen surface (cf. Fig. 3). K. Yanase et alii, Frattura ed Integrità Strutturale, 37 (2016) 101-107; DOI: 10.3221/IGF-ESIS.37.14 105 According to the previously reported results [3-7],  0.18k holds for carbon steels, Cr-Mo steel, ductile cast irons, and high tension brass. If the effect of biaxial stress is negligible (i.e.,  0k ), the torsional fatigue limit is solely determined by the major principal stress as follows (cf. Fig. 6):     w w1/6 1.43( 120) ( ) HV area (3) On the other hand, Schönbauer et al. proposed that the fatigue limit in the presence of a large defect or a long crack can be estimated by the following equation [2]:      th,lc w 2 0.65 K area (4) where the threshold stress intensity factor range of th,lcΔK =6.7 MPa m for the investigated 17-4PH steel at R = ˗1 was determined by Schönbauer et al. [9]. Fig. 7 shows the relationship between the shear stress amplitude a and area . When a specimen endured the number of cycles N = 1.2107, it was regarded as a run-out specimen. As shown, the prediction for fatigue limit with k = 0 (Fig. 7(b)) renders higher correlation to the experimental data than using k = ˗0.18 (Fig. 7(a)). Further, for the torsional loading, fatigue limit can be reasonably estimated by the two prediction lines:   0.6 (1.6 )a HV and the threshold for long crack (cf. Eq. (4)). 10 1 10 2 10 3 100 150 200 250 300 350 400 area (m) S h e a r  st re ss  a m p li tu d e ,   a  ( M P a ) "1‐hole defect" "2‐hole defect" "3‐hole defect"  a  = 0.6(1.6HV) Threshold for long crack area parameter model  with "k = ‐0.18" Failure Run‐out Prediction for fatigue limit (a) Prediction with k = ˗ 0.18 (b) Prediction with k = 0 Figure 7: Relationship between shear stress amplitudea and area . In Fig. 8, fatigue limit for torsional loading and tension-compression loading is compared [2]. It is noted that, in the tension-compression data, various types of defects are considered (e.g., drilled hole, circumferential notch, corrosion pit). As shown, the respective fatigue limit can be reasonably estimated by considering the major principal stress (i.e., k = 0) and area . The torsional fatigue limit becomes insensitive to the defect when  100μmarea , which is in strong contrast 10 1 10 2 10 3 100 150 200 250 300 350 400 area (m) S h e a r  st re ss  a m p li tu d e ,  a  ( M P a ) "1‐hole defect" "2‐hole defect" "3‐hole defect"  a  = 0.6(1.6HV) Threshold for long crack area parameter model with "k = 0"              Failure Run‐out Prediction for fatigue limit K. Yanase et alii, Frattura ed Integrità Strutturale, 37 (2016) 101-107; DOI: 10.3221/IGF-ESIS.37.14 106 to that for tension-compression loading. Concerning the tension-compression loading, the area parameter model (cf. Eq. (3)) can be used for 17-4PH when  100μmarea , which is much less than area < 1000 µm for the conventional carbon steels. Fig. 8 clearly shows that the aforementioned one-hole defect ( area = 70 µm) has negligible influence on fatigue limit under torsional loading. Finally, as some experimental data significantly deviate from the prediction line, a further study is necessary to elucidate the reasons behind these discrepancies. 10 1 10 2 10 3 0 100 200 300 400 500 600 area (m) S tr e ss  a m p li tu d e  ( M P a )  a  = 1.6HV  a  = 0.6(1.6HV) Threshold for long crack area parameter model with k = 0                Torsion Tension‐Compression Failure Run‐out Prediction for fatigue limit Failure Run‐out Prediction for fatigue limit Figure 8: Relationship between stress amplitude and area . CONCLUSIONS n this study, the torsional fatigue behavior of precipitation-hardened chromium-nickel-copper stainless steel 17-4PH was investigated in the presence of small defects. It was shown that the dimensions of defects can be evaluated by the square root of the projection area perpendicular to the major principal stress direction, area . The results pertaining to the fatigue crack growth behavior and fatigue limit demonstrate that the effect of biaxial stress on the surface of specimen is negligible and the major principal stress governs the fatigue behavior under torsional loading. REFERENCES [1] Schönbauer, B.M., Yanase, K. and Endo, M., VHCF properties and fatigue limit prediction of precipitation hardened 17-4PH stainless steel, Int. J. Fatigue, 88 (2016) 205-216. DOI: 10.1016/j.ijfatigue.2016.03.034. [2] Schönbauer, B.M., Yanase, K. and Endo, M., to be submitted to Int. J. Fatigue. [3] Endo, M. and Ishimoto, I., The fatigue strength of steels containing small holes under out-of-phase combined loading, Int. J. Fatigue, 28 (2006) 592-597. DOI: 10.1016/j.ijfatigue.2005.05.013. [4] Endo, M. and Ishimoto, I., J. Solid Mech. Mater. Engng. (JSME), 1 (2007), 343-354, DOI: 10.1299/jmmp.1.343. [5] Yanase, K., A study on the multiaxial fatigue failure criterion with small defects, ASTM Mater. Perform. Charact., 2 (2013) 1-9. DOI: 10.1520/MPC20130013. [6] Yanase K., Endo M., Multiaxial high cycle fatigue threshold with small defects and cracks, Engng. Fract. Mech., 123 (2014) 182-196. DOI: 10.1016/j.engfracmech.2014.03.017. I K. Yanase et alii, Frattura ed Integrità Strutturale, 37 (2016) 101-107; DOI: 10.3221/IGF-ESIS.37.14 107 [7] Endo, M., Yanase, K., Effects of small defects, matrix structures and loading conditions on the fatigue strength of ductile cast irons, Theor. Appl. Fract. Mech., 69 (2014) 34-43. DOI: 10.1016/j.tafmec.2013.12.005. [8] Murakami, Y., Metal Fatigue: Effects of Small Defects and Nonmetallic Inclusions, Elsevier, Oxford (2002), Chapter 4 – Effects of size and geometry of small defects on the fatigue limit. DOI: 10.1016/B978-008044064-4/50004-9. [9] Schönbauer, B.M., Stanzl-Tschegg, S.E., Perlega, A., Salzman R.N., Rieger, N.F., Turnbull, A., Zhou, S., Lukaszewicz, M., Gandy, D., The influence of corrosion pits on the fatigue life of 17-4PH steam turbine blade steel, Engng. Fract. Mech., 147 (2015) 158-175. DOI: 10.1016/j.engfracmech.2015.08.011. [10] Ikeda, S. The effects of biaxial stress and stress gradient on fatigue crack growth behavior, Master Thesis (2008), Fukuoka University. << /ASCII85EncodePages false /AllowTransparency false /AutoPositionEPSFiles true /AutoRotatePages /None /Binding /Left /CalGrayProfile (Dot Gain 20%) /CalRGBProfile (sRGB IEC61966-2.1) /CalCMYKProfile (U.S. Web Coated \050SWOP\051 v2) /sRGBProfile (sRGB IEC61966-2.1) /CannotEmbedFontPolicy /Error /CompatibilityLevel 1.4 /CompressObjects /Tags /CompressPages true /ConvertImagesToIndexed true /PassThroughJPEGImages true /CreateJobTicket false /DefaultRenderingIntent /Default /DetectBlends true /DetectCurves 0.0000 /ColorConversionStrategy /CMYK /DoThumbnails false /EmbedAllFonts true /EmbedOpenType false /ParseICCProfilesInComments true /EmbedJobOptions true /DSCReportingLevel 0 /EmitDSCWarnings false /EndPage -1 /ImageMemory 1048576 /LockDistillerParams false /MaxSubsetPct 100 /Optimize true /OPM 1 /ParseDSCComments true /ParseDSCCommentsForDocInfo true /PreserveCopyPage true /PreserveDICMYKValues true /PreserveEPSInfo true /PreserveFlatness true /PreserveHalftoneInfo false /PreserveOPIComments true /PreserveOverprintSettings true /StartPage 1 /SubsetFonts true /TransferFunctionInfo /Apply /UCRandBGInfo /Preserve /UsePrologue false /ColorSettingsFile () /AlwaysEmbed [ true ] /NeverEmbed [ true ] /AntiAliasColorImages false /CropColorImages true /ColorImageMinResolution 300 /ColorImageMinResolutionPolicy /OK /DownsampleColorImages true /ColorImageDownsampleType /Bicubic /ColorImageResolution 300 /ColorImageDepth -1 /ColorImageMinDownsampleDepth 1 /ColorImageDownsampleThreshold 1.50000 /EncodeColorImages true /ColorImageFilter /DCTEncode /AutoFilterColorImages true /ColorImageAutoFilterStrategy /JPEG /ColorACSImageDict << /QFactor 0.15 /HSamples [1 1 1 1] /VSamples [1 1 1 1] >> /ColorImageDict << /QFactor 0.15 /HSamples [1 1 1 1] /VSamples [1 1 1 1] >> /JPEG2000ColorACSImageDict << /TileWidth 256 /TileHeight 256 /Quality 30 >> /JPEG2000ColorImageDict << /TileWidth 256 /TileHeight 256 /Quality 30 >> /AntiAliasGrayImages false /CropGrayImages true /GrayImageMinResolution 300 /GrayImageMinResolutionPolicy /OK /DownsampleGrayImages true /GrayImageDownsampleType /Bicubic /GrayImageResolution 300 /GrayImageDepth -1 /GrayImageMinDownsampleDepth 2 /GrayImageDownsampleThreshold 1.50000 /EncodeGrayImages true /GrayImageFilter /DCTEncode /AutoFilterGrayImages true /GrayImageAutoFilterStrategy /JPEG /GrayACSImageDict << /QFactor 0.15 /HSamples [1 1 1 1] /VSamples [1 1 1 1] >> /GrayImageDict << /QFactor 0.15 /HSamples [1 1 1 1] /VSamples [1 1 1 1] >> /JPEG2000GrayACSImageDict << /TileWidth 256 /TileHeight 256 /Quality 30 >> /JPEG2000GrayImageDict << /TileWidth 256 /TileHeight 256 /Quality 30 >> /AntiAliasMonoImages false /CropMonoImages true /MonoImageMinResolution 1200 /MonoImageMinResolutionPolicy /OK /DownsampleMonoImages true /MonoImageDownsampleType /Bicubic /MonoImageResolution 1200 /MonoImageDepth -1 /MonoImageDownsampleThreshold 1.50000 /EncodeMonoImages true /MonoImageFilter /CCITTFaxEncode /MonoImageDict << /K -1 >> /AllowPSXObjects false /CheckCompliance [ /None ] /PDFX1aCheck false /PDFX3Check false /PDFXCompliantPDFOnly false /PDFXNoTrimBoxError true /PDFXTrimBoxToMediaBoxOffset [ 0.00000 0.00000 0.00000 0.00000 ] /PDFXSetBleedBoxToMediaBox true /PDFXBleedBoxToTrimBoxOffset [ 0.00000 0.00000 0.00000 0.00000 ] /PDFXOutputIntentProfile () /PDFXOutputConditionIdentifier () /PDFXOutputCondition () /PDFXRegistryName () /PDFXTrapped /False /CreateJDFFile false /Description << /ARA /BGR /CHS /CHT /CZE /DAN /DEU /ESP /ETI /FRA /GRE /HEB /HRV (Za stvaranje Adobe PDF dokumenata najpogodnijih za visokokvalitetni ispis prije tiskanja koristite ove postavke. Stvoreni PDF dokumenti mogu se otvoriti Acrobat i Adobe Reader 5.0 i kasnijim verzijama.) /HUN /ITA /JPN /KOR /LTH /LVI /NLD (Gebruik deze instellingen om Adobe PDF-documenten te maken die zijn geoptimaliseerd voor prepress-afdrukken van hoge kwaliteit. De gemaakte PDF-documenten kunnen worden geopend met Acrobat en Adobe Reader 5.0 en hoger.) /NOR /POL /PTB /RUM /RUS /SKY /SLV /SUO /SVE /TUR /UKR /ENU (Use these settings to create Adobe PDF documents best suited for high-quality prepress printing. Created PDF documents can be opened with Acrobat and Adobe Reader 5.0 and later.) >> /Namespace [ (Adobe) (Common) (1.0) ] /OtherNamespaces [ << /AsReaderSpreads false /CropImagesToFrames true /ErrorControl /WarnAndContinue /FlattenerIgnoreSpreadOverrides false /IncludeGuidesGrids false /IncludeNonPrinting false /IncludeSlug false /Namespace [ (Adobe) (InDesign) (4.0) ] /OmitPlacedBitmaps false /OmitPlacedEPS false /OmitPlacedPDF false /SimulateOverprint /Legacy >> << /AddBleedMarks false /AddColorBars false /AddCropMarks false /AddPageInfo false /AddRegMarks false /ConvertColors /ConvertToCMYK /DestinationProfileName () /DestinationProfileSelector /DocumentCMYK /Downsample16BitImages true /FlattenerPreset << /PresetSelector /MediumResolution >> /FormElements false /GenerateStructure false /IncludeBookmarks false /IncludeHyperlinks false /IncludeInteractive false /IncludeLayers false /IncludeProfiles false /MultimediaHandling /UseObjectSettings /Namespace [ (Adobe) (CreativeSuite) (2.0) ] /PDFXOutputIntentProfileSelector /DocumentCMYK /PreserveEditing true /UntaggedCMYKHandling /LeaveUntagged /UntaggedRGBHandling /UseDocumentProfile /UseDocumentBleed false >> ] >> setdistillerparams << /HWResolution [2400 2400] /PageSize [612.000 792.000] >> setpagedevice