Microsoft Word - numero_49_art_47_2275 D. Kumar et alii, Frattura ed Integrità Strutturale, 49 (2019) 507-514; DOI: 10.3221/IGF-ESIS.49.47 507 Focused on Showcasing Structural Integrity Research in India Optimization of Vanadium Content for Achieving Higher Wear Resistance and Hardness in High Cr-V White Cast Irons for Ball Tube Mill Liner Application Dhirendra Kumar, G. Jayaraman, M. Swamy, A. H. V. Pavan , Antony M. C. Harison Corporate Research & Development Division, BHEL, Hyderabad, India, 500093 dkumar@bhel.in, jayaraman@bhel.in, smekala@bhel.in, pavanahv@bhel.in, harisonmc@bhel.in A. N. Sudhakar Heavy Power Equipment Plant, BHEL, Ramachandrapuram, Hyderabad, India, 502302 ansudhakar@bhel.in ABSTRACT. The liner materials in coal fired tube mills are less promising due to lower combination of abrasion wear resistance, hardness and impact toughness properties, thus giving service life of 25,000 to 35,000 hours. In this study, focus was given to develop a high Cr-V cast iron of high abrasion wear resistance with higher hardness and impact strength for ball tube mill liner application. The developed liner possesses high abrasive wear resistance and impact resistance simultaneously with expected service life of 40,000 to 50,000 hours. This grade was made using induction melting and sand casting method. The casting was heat treated in two stages to achieve higher abrasion wear resistance and mechanical properties. Various tests like chemical analysis, abrasion wear, hardness and impact tests were conducted on the above developed material. Abrasion wear test results show a low wear loss value (2.7 to 4.4 mg/min). Hardness and impact tests show a high combination of hardness (57 to 64 HRC) and impact strength (44 to 57 J/cm2). Prototype tube mill liners were manufactured and tested in a tube mill at 250MW site. Results obtained from site testing are also discussed in this study. KEYWORDS. High Cr cast iron; High Cr-V cast iron; Abrasion wear; Hardness; Impact strength. Citation: Kumar, D., Jayaraman, G., Swamy, M., Pavan, A.H.V., Harison, A.M.C., Sudhakar, A. N., Study of microstructure, abrasion wear and mechanical properties of high Cr-V white cast iron for ball tube mill liner application, Frattura ed Integrità Strutturale, 49 (2019) 507-514. Received: 24.11.2018 Accepted: 21.05.2019 Published: 01.07.2019 Copyright: © 2019 This is an open access article under the terms of the CC-BY 4.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited. INTRODUCTION urning coal with higher efficiency has been a great need in coal pulverizing sector wherein coal is burnt like gas. Burning coal like gas reduces the CO2 emission by reduction of coal consumption. Coal is pulverized with the help of liner plates inside the mill. These plates are mostly made of high chromium cast irons (HCrCIs) and B http://www.gruppofrattura.it/VA/49/2275.mp4 D. Kumar et alii, Frattura ed Integrità Strutturale, 49 (2019) 507-514; DOI: 10.3221/IGF-ESIS.49.47 508 possess high hardness and wear resistance. HCrCIs have M7C3 carbide in their matrices which enables them to have high wear resistance property [1, 2]. These cast irons have continuous distribution of rod-like M7C3 carbide in their respective matrices. The continuous distribution of M7C3 carbide makes their toughness lower. In order to improve their toughness, the morphology of carbides can be modified to chunk-like or even granular [3]. So, with discontinuous distribution of M7C3 carbide, a high chromium cast iron would be quite promising in wearing parts of machines in many industries like coal pulverizes. The demand of higher wear resistant material in coal pulverizing sector has always been encouraging to reduce the dwell time to the great extent. The need ‘to eliminate frequent shutdown of tube mill for replacement of worn out and/or broken liners and loss in terms of power productivity’ have encouraged to develop candidate alloys which provide superior abrasive wear resistance along with adequate toughness [4, 5]. The addition of strong carbide-forming elements, such as vanadium, tungsten, niobium and titanium, improves the mechanical properties of high chromium white irons [6]. Vanadium can form vanadium carbide (VC) with Vickers hardness of HV2800 which is much harder than that of M7C3 with Vickers hardness, HV 1200~1800 in high chromium cast iron [7]. The globular morphology of VC reduces splitting to matrix and enables to get superior toughness. The microstructure of high chromium iron becomes finer with vanadium addition. With good solubility in eutectic M7C3 carbides and austenite, vanadium influences the transformation of austenite in high chromium cast iron. Vanadium content favors precipitation of dispersive secondary carbides of VC type in austenite which is favorable for martensitic transformation [8, 9, 10]. With an increase in vanadium content, the impact toughness increases, while hardness decreases and thereby relative wear resistance improves [7]. Therefore, influence of vanadium on microstructure, hardness and impact strength and wear properties was studied in this work to develop a high chromium-vanadium cast iron (HCrVCI) material for the tube mill liner application. EXPERIMENTAL PROCEDURE arious grades of HCrCI blocks with varying weight percentages of vanadium were cast using induction melting and die casting method. HCrCI grade, NFA 32.401 or FB Cr26MoNi with 0.00 wt. % vanadium was considered as base material. The compositions of cast iron grades were analyzed through Spark Emission Spectroscopy (SES) method using Spectrax M5 machine. The cast iron blocks were hardened and tempered in two stages. Subsequent to this, Ultrasonic Testing (UT) was carried out on them to detect internal defects, if any. Samples were prepared from the casting blocks for microstructure evaluation, phase characterization, hardness, impact value and wear properties evaluation. Charpy un-notched impact test samples were prepared with dimensions as, Length: 10mm, Width: 10mm and Height: 55mm. Abrasion wear test samples were prepared with dimensions as, Length: 25+0.0/-0.2mm, Width: 6mm and Height: 75mm.The samples for metallographic examination were polished for obtaining extremely good surface finish. The polished samples were etched chemically using Villela’s etchant for 40 seconds each. The microstructures were analyzed through optical microscopy method. The etched samples were observed for features pertaining to morphology of grains and precipitates under Leica DMI 5000 M inverted metallurgical microscope using the bright field method. The samples were further examined under “Zeiss Supra® 55 VP make Field Emission Scanning Electron Microscope (FESEM) with compatible Energy Dispersive X-ray Spectroscopy (EDS) system to reveal morphologies present in the matrices. Hardness test with 10 kg load and 15 seconds dwell time was carried out on the surface of the samples from all cast iron grades using Shimadzu-HSV-30 hardness tester. Impact test was carried out on charpy un-notched test samples. The machine used for the impact test is IFFECT TECHNOLOGY, INC make Dynatup, Model 500. The working range of the machine as per the ASTM-E-23 is 25J to 286.4J. The wear test experiment was carried out as per the ASTM G 65. Abrasion wear test setup and schematic diagram of test apparatus is shown in Fig. 1. The samples for wear test were cleaned with methanol and dried. The specimens were weighed to the nearest 0.0001g. Each specimen was fixed securely in the holder and erodent (quartz sand; size: 180µm to 250µm) was poured in the hopper. A load of 80N was applied to the specimen against the wheel. The applied force was measured accurately by means of a spring scale which was hooked around the specimen and pulled back to lift the specimen away from the wheel. Revolution was set to 200 rpm. The erodent flow rate through the nozzles was approximately 330 g/min. The dwell time between the two tests was considered as 40 minutes. The each test was run for 15 minutes. Each time, the specimen was removed and reweighed to the nearest 0.0001 g. Using the HCrCI Grade, FB Cr26MoNi with 0.50 wt. % vanadium, few prototype liners were manufactured and installed in a coal pulverizing tube mill at an identified site along with freshly installed HCrCI Grade, FB Cr26MoNi liners for their comparative wear study and service life evaluation. V D. Kumar et alii, Frattura ed Integrità Strutturale, 49 (2019) 507-514; DOI: 10.3221/IGF-ESIS.49.47 509 Figure 1: Abrasion wear testing setup and schematic diagram of test apparatus RESULT AND DISCUSSION Chemical analysis fter successful casting, the chemical compositions of cast HCrCI and HCrVCI grades were analyzed and they were found within the range. Tab. 1 describes the compositions achieved for the various grades of cast irons. All castings were hardened at 960oC for 10 hours and tempered at 295oC for 7 hours. Through ultrasonic testing (UT), all cast iron blocks were confirmed with good homogeneity. Grade of cast iron Element (wt. %) C Si Mn Ni Mo S P Cr Cu V Fe FB Cr26MoNi 2.69 0.99 0.99 0.21 0.29 0.05 0.04 25.09 0.30 Nil Bal. FB Cr26MoNi +0.25V 2.75 0.95 0.89 0.36 0.21 0.09 0.05 25.20 0.29 0.29 Bal. FB Cr26MoNi +0.5V 2.74 0.80 0.99 0.35 0.39 0.05 0.04 24.99 0.39 0.53 Bal. FB Cr26MoNi +1.0V 2.68 0.90 0.93 0.19 0.29 0.05 0.05 24.96 0.29 1.01 Bal. FB Cr26MoNi +2.0V 2.69 0.72 1.02 0.22 0.30 0.03 0.04 24.99 0.35 2.03 Bal. FB Cr26MoNi +3.0V 2.70 0.90 1.00 0.29 0.35 0.05 0.05 24.80 0.20 3.01 Bal. FB Cr26MoNi +4.0V 2.58 0.89 1.05 0.22 0.29 0.05 0.05 25.02 0.29 4.02 Bal. FB Cr26MoNi +5.0V 2.51 0.91 1.01 0.19 0.21 0.05 0.04 24.99 0.25 5.03 Bal. FB Cr26MoNi +6.0V 2.50 0.80 1.10 0.20 0.41 0.05 0.04 25.10 0.19 6.00 Bal. FB Cr26MoNi +7.0V 2.69 0.81 0.95 0.22 0.20 0.05 0.05 24.85 0.15 7.02 Bal. FB Cr26MoNi +8.0V 2.70 0.80 0.90 0.21 0.29 0.04 0.04 24.90 0.20 8.01 Bal. Table 1: Compositions of the various grades of HCrCIs with varying vanadium content Microscopic examination The HCrVCI grade, FB Cr26MoNi+0.5V has achieved the best combination of hardness and impact strength which are discussed in the later stage. Therefore, the microstructures of base material (FB Cr26MoNi) and developed material (FB Cr26MoNi+0.5V) were exclusively examined. Microstructure of FB Cr26MoNi material in Fig. 2: A) resembles coarse eutectic interdendritic rod-like continuous M7C3 carbides network in the gray tempered martensite matrix. Microstructure A D. Kumar et alii, Frattura ed Integrità Strutturale, 49 (2019) 507-514; DOI: 10.3221/IGF-ESIS.49.47 510 of FB Cr26MoNi+0.5V material in Fig. 2: B) shows fine globular MC type carbides and chunk like M7C3 carbides more uniformly distributed in the martensite structure which is reported to contribute better combination of hardness and impact strength. During eutectic solidification of HCrCI with vanadium addition, eutectic colonies diameter, ‘de’ is directly proportional to eutectic transition temperature range, ‘∆TE’. This can be expressed as Eqn. (1) [15]: 𝑑𝑒 ∝ ∆𝑇𝐸   (1) Vanadium is found to narrow the eutectic transition temperature range and hence, refines the microstructure. Globular and chunk like uniform carbides precipitates distribution in the matrix of martensite is highly favorable for stabilizing the microstructure and imparting a better combination of higher hardness and impact toughness properties. Therefore, morphology of FB Cr26MoNi+0.5V cast iron is more suitable for tube mill liner application. Figure 2: A) Microstructure of HCrCI grade, FB Cr26MoNi at 200X magnification and B) Microstructure of HCrVCI grade, FB Cr26MoNi +0.5V at 200X magnification. Field emission scanning electron microscopic analysis After microstructure evaluation, the high chromium cast iron (FB Cr26MoNi) and high chromium-vanadium cast iron (FB Cr26MoNi+0.5V) materials were examined under Field Emission Scanning Electron Microscope. FESEM images and EDS spectrums shown in Fig. 3: A) confirm the rod-like M7C3 carbide as chromium carbides in the continuous carbide network in the matrix of FB Cr26MoNi material and Fig. 3: B) & C) confirm the globular MC type carbide as vanadium carbide and modified chunk like M7C3 type carbide as chromium carbide distribution with vanadium content in the matrix of FB Cr26MoNi+0.5V material. There is more uniform distribution of carbides and the presence of vanadium in the matrix. Coarse eutectic interdendritic rod-like continuous M7C3 carbides network in the gray tempered martensite matrix of FB Cr26MoNi material is more prone to easy crack propagation. Since, carbides are brittle, their continuous network would provide a preferred path for fast crack growth. Tempered martensite matrix holds carbides less firmly which results in splitting of carbides from the surface. More uniform distribution of globular MC type carbides and chunk like M7C3 carbides in the martensite matrix of FB Cr26MoNi+0.5V material is quite favorable for delaying the crack propagation. This type of distribution is studied and found to have a better combination of hardness and impact strength. Therefore, morphology of FB Cr26MoNi+0.5V material is highly stable as compared to that of FB Cr26MoNi material. Since, EDS analysis has shown that MC type carbide is vanadium carbide (VC) and M7C3 carbide is chromium carbide (Cr7C3), VC precipitates with 2800HV hardness along with M7C3 precipitates with 1200 ~ 1800HV hardness induce more hardness in the matrix. Presence of vanadium in the matrix of cast iron material is reported to gives additional strengthening effect [4] which helps in delaying crack initiation and propagation. Hardness behavior Hardness was tested on samples from different cast iron blocks. A graph of ‘Hardness Value’ (HV) with ‘Vanadium’ content (wt. %) was plotted and it is shown in Fig. 4. Hardness test result shows that the HCrCI grade, FB Cr26MoNi with vanadium content of 0.5 wt. % has achieved the highest hardness value. Vanadium addition, initially, would have led to precipitation of fine vanadium carbides (VC type) which favors martensitic transformation [8, 9, 10]. With vanadium D. Kumar et alii, Frattura ed Integrità Strutturale, 49 (2019) 507-514; DOI: 10.3221/IGF-ESIS.49.47 511 addition, M7C3 type carbides are reported to restrict continuous needle like carbides precipitation to discontinuous and chunk like carbides. Higher hardness and higher affinity to carbon of VC as compared to M7C3 type carbides and the martensitic transformation might have imparted more hardness to the matrix of base material with 0.5 wt. % V content. Higher vanadium content is found to stabilize austenite further and thereby reduces hardness value [7]. Therefore, Fig. 4 shows first increase and then decrease in hardness. Figure 3: FESEM image and EDS spectrum of A) FB Cr26MoNi material precipitate, B) FB Cr26MoNi+0.5V material precipitate and C) FB Cr26MoNi+0.5V material matrix D. Kumar et alii, Frattura ed Integrità Strutturale, 49 (2019) 507-514; DOI: 10.3221/IGF-ESIS.49.47 512 Figure 4: Hardness of cast iron grades with varying vanadium content Impact strength Since, HCrCI with 0.50 wt. % vanadium has the highest hardness, impact strength study was made for the HCrCI with vanadium content from 0.00 wt. % to 2.00 wt. % V range only. The Charpy impact test results (Fig. 5) show that the impact strength of the base material improves with increase in the vanadium content. Higher impact value with higher hardness is very much favorable for tube mill liner to ensure its higher service life. Vanadium forms VC type carbides first at higher temperature and act as heterogeneous nucleation nuclei for chromium carbide precipitation which leads to refinement of carbides and their improved distribution [11, 12, 13, 14]. These morphological changes are observed to improve the impact strength of the cast iron grades. Therefore, it is found that the HCrCI with 0.5wt% vanadium has the well suited combination of hardness and toughness properties for the parts experiencing impact and wear actions simultaneously. Figure 5: Impact strength of cast iron grades with varying vanadium content Abrasion wear testing The HCrCI with 0.5% vanadium content is found to have the highest combination of hardness and impact strength. Therefore, an exclusive abrasive wear study of the base material (FB Cr26MoNi) and the developed material (FB Cr26MoNi+0.5V) was made as per the standard ASTM G 65. The volume loss of materials was calculated as per the Eqn. (2). 𝑉𝑜𝑙𝑢𝑚𝑒 𝑙𝑜𝑠𝑠, 𝑚𝑚3 𝑀𝑎𝑠𝑠 𝑙𝑜𝑠𝑠 𝑔 𝐷𝑒𝑛𝑠𝑖𝑡𝑦 𝑔/𝑐𝑚 3 𝑋 1000 (2) D. Kumar et alii, Frattura ed Integrità Strutturale, 49 (2019) 507-514; DOI: 10.3221/IGF-ESIS.49.47 513 The test results are given in Tab. 2. The results show that the HCrCI grade, FB Cr26MoNi with 0.5wt% vanadium addition is comparatively a higher wear resistant alloy which is more suitable for wear resistance application. The wear resistance of the developed cast iron grade (FB Cr26MoNi +0.5V) was calculated as the ratio of volume loss of the reference material (FB Cr26MoNi) to the volume loss of that material. The average abrasive wear resistance of FB Cr26MoNi +0.5V material as compared to FB Cr26MoNi material is 2.33. This shows that FB Cr26MoNi +0.5V material has higher wear resistance and it is more suitable for liner applications in coal pulverizers. Therefore, the comparative wear study of prototype liners of these materials for 2,667 hours was made by installing them in a coal pulverizing tube mill. The average wear out thickness of the developed liner (FB Cr26MoNi +0.5V) and the normal liner (FB Cr26MoNi) were found to be 0.83mm and 2.08mm, respectively. The above data shows a higher wear life for the cast iron grade, FB Cr26MoNi +0.5V. Material: FB Cr26MoNi FB Cr26MoNi +0.5V Sample No: A11 A12 A13 A3H1 A3H2 A3H3 Test time, min: 45 45 45 45 45 45 Initial mass, g: 84.5123 84.7395 84.5744 86.8523 86.8457 81.5244 Final mass, g: 84.1666 84.3957 84.1764 86.7301 86.6998 81.3267 Mass loss, g: 0.3457 0.3438 0.3980 0.1222 0.1459 0.1977 Mass loss, mg/min: 7.7 7.6 8.8 2.7 3.2 4.4 Volume loss, mm3: 46.2784 46.0241 53.2798 16.3588 19.5315 26.4659 Volume loss per kg of erodent, mm3/Kg: 9.3492 9.2978 10.7636 3.3048 3.9457 5.3466 Average volume loss per kg of erodent, mm3/Kg: 9.8035 4.1991 Table 2: Abrasive wear test result of the base material and the developed material CONCLUSIONS etailed study on the abrasion wear, mechanical behavior, microscopic examination and characterization of HCrCI and HCrVCI grades leads to the following major conclusions: 1. All grades of cast irons were cast using die casting method and chemical compositions were achieved successfully with homogeneous matrix in the respective casting blocks. 2. 0.5 wt. % vanadium addition to the base HCrCI grade (FB Cr26MoNi) has refined the microstructure to form globular VC type carbides and chunk like Cr7C3 carbides distribution in the martensite matrix. This is quite favorable for improved life of liners in tube mills. 3. HCrVCI grade, FB Cr26MoNi+0.5V has higher abrasion wear resistance and higher combination of hardness and impact strength as compared to the reference HCrCI grade, FB Cr26MoNi. Hence, the HCrCI with 0.5 wt. % vanadium addition is more promising with enhanced properties of hardness, impact toughness and higher abrasion wear resistance for tube mill liner application. 4. The study of prototype liners of the developed cast iron shows a higher service life as compared to the existing base material liners. ACKNOWLEDGEMENT uthors express their gratitude to the managements of BHEL, Corporate R&D, Hyderabad for financially supporting this study. They acknowledge the officials at Surface Coating Department, BHEL, Corporate R&D, Hyderabad for their support in carrying out the wear test of cast iron samples. They acknowledge the concerned D A D. Kumar et alii, Frattura ed Integrità Strutturale, 49 (2019) 507-514; DOI: 10.3221/IGF-ESIS.49.47 514 officials at Quality Labs, BHEL Ramachandrapuram for the chemical analysis and officials at Heat Treatment Shop, BHEL, Ramchandrapuram for the heat treatment of cast iron blocks. REFERENCES [1] Zhi, X., Xing, J., Fu, H., Gao, Y. (2008). Effect of titanium on the as-cast microstructure of hypereutectic high chromium cast iron, J. Mater. Charact. 59, pp. 1221–1226. DOI: 10.1016/j.matchar.2007.10.010. [2] Filipovic, M., Kamberovic, Z., Korac, M. (2013). Microstructure and mechanical properties of Fe–Cr–C–Nb white cast irons, J. Mater. Des. 47, pp. 41–48. DOI: 10.1016/j.matdes.2012.12.034. [3] Xinhui, F., Lin, H., Qingde, Z. (1989) A Structural Study of High Chromium Cast Iron as a Grinding Ball Material, J. Met. Sci. Technol., 5, pp. 401-406. [4] Sawamoto, A., Ogi, K., Matsuda, K. (1986). Solidification Structures of Fe-C-Cr-(V-Nb-W) Alloys, J. AFS Transactions, 72, pp. 403-416. [5] Dodd, J., Parks, J. L. (1980). Factors Affecting the Production and Performance of Thick-Section High Chromium- Molybdenum Alloy Iron Castings, J. Metals Forum, 3 (1), pp. 3-12. [6] Radulovic, M., Fiset, M., Peev, K., Tomovic, M. (1994). The Influence of Vanadium on Fracture Toughness and Abrasion Resistance in High Chromium White Cast Irons, J. Journal of Materials Science, 29, pp. 5085-5094. [7] Keming, L., Fuming, W, Changrong, L., Liuyan, S. (2005). Influence of Vanadium on microstructure and Properties of Medium-chromium White Cast Iron, Available at: http://vanitec.org/technical-library/paper/influence-of- vanadium-on-microstructure-and-properties-of-medium-chromium-w. [8] Yuwei, W., Wen S., (1989). The Effect of V in High Cr Cast Iron, J. Foundry, 5, pp. 9-12. [9] Junyi, S., Xiangzhong, G., Enze, W. (1984). Study on High Chromium White Cast Iron Containing Vanadium with Martensite Matrix in the As-cast Condition, J. Journal of Xi’an Jiaotong University, 18(5), pp. 23-28. [10] Yifu, Y., Tongxiang, F. (1995). Spheroidizing of Carbides of White Cast Iron, J. Modern Cast Iron, 3 pp. 28-32. [11] Scandian, C., Boher, C., De Mello, J.D.B., Rézaï-Aria F., (2009). Effect of molybdenum and chromium contents in sliding wear of high-chromium white cast iron: the relationship between microstructure and wear, Wear, 267, pp. 401–408. DOI: 10.1016/j.wear.2008.12.095 [12] Pierson, H.O., (1996). Handbook of refractory carbides and nitrides, 1st ed. Sandia National Laboratories, Available at: file:///E:/Paper%20published_to%20be%20published/ICON2018%20Papers/Paper%20submission_Frattura%20e d%20Integrita/References%20HCrVWCI/Ref%2013.pdf [13] Xiang, C., Yanxiang, L., (2010). Effect of heat treatment on microstructure and mechanical properties of high boron white cast ,iron, J. Mater Sci Eng A, 528, pp. 770–775. DOI: 10.1016/j.msea.2007.10.009 [14] Xiaohui, Z., Jiandong, X., Yimin, G., (2008). Effect of heat treatment on microstructure and mechanical properties of a Ti-bearing hypereutectic high chromium white cast iron, Mater Sci Eng A, 487, pp. 171–179. DOI: 10.1016/j.msea.2007.10.009 [15] Ogi, K., Matsubara, Y., Matsuda, K., (1982). Eutectic solidification of high chromium cast iron-mechanism of eutectic growth, AFS Transactions, 89, pp. 197–204. << /ASCII85EncodePages false /AllowTransparency false /AutoPositionEPSFiles true /AutoRotatePages /None /Binding /Left /CalGrayProfile (Dot Gain 20%) /CalRGBProfile (sRGB IEC61966-2.1) /CalCMYKProfile (U.S. Web Coated \050SWOP\051 v2) /sRGBProfile (sRGB IEC61966-2.1) /CannotEmbedFontPolicy /Error /CompatibilityLevel 1.4 /CompressObjects /Tags /CompressPages true /ConvertImagesToIndexed true /PassThroughJPEGImages true /CreateJobTicket false /DefaultRenderingIntent /Default /DetectBlends true /DetectCurves 0.0000 /ColorConversionStrategy /CMYK /DoThumbnails false /EmbedAllFonts true /EmbedOpenType false /ParseICCProfilesInComments true /EmbedJobOptions true /DSCReportingLevel 0 /EmitDSCWarnings false /EndPage -1 /ImageMemory 1048576 /LockDistillerParams false /MaxSubsetPct 100 /Optimize true /OPM 1 /ParseDSCComments true /ParseDSCCommentsForDocInfo true /PreserveCopyPage true /PreserveDICMYKValues true /PreserveEPSInfo true /PreserveFlatness true /PreserveHalftoneInfo false /PreserveOPIComments true /PreserveOverprintSettings true /StartPage 1 /SubsetFonts true /TransferFunctionInfo /Apply /UCRandBGInfo /Preserve /UsePrologue false /ColorSettingsFile () /AlwaysEmbed [ true ] /NeverEmbed [ true ] /AntiAliasColorImages false /CropColorImages true /ColorImageMinResolution 300 /ColorImageMinResolutionPolicy /OK /DownsampleColorImages true /ColorImageDownsampleType /Bicubic /ColorImageResolution 300 /ColorImageDepth -1 /ColorImageMinDownsampleDepth 1 /ColorImageDownsampleThreshold 1.50000 /EncodeColorImages true /ColorImageFilter /DCTEncode /AutoFilterColorImages true /ColorImageAutoFilterStrategy /JPEG /ColorACSImageDict << /QFactor 0.15 /HSamples [1 1 1 1] /VSamples [1 1 1 1] >> /ColorImageDict << /QFactor 0.15 /HSamples [1 1 1 1] /VSamples [1 1 1 1] >> /JPEG2000ColorACSImageDict << /TileWidth 256 /TileHeight 256 /Quality 30 >> /JPEG2000ColorImageDict << /TileWidth 256 /TileHeight 256 /Quality 30 >> /AntiAliasGrayImages false /CropGrayImages true /GrayImageMinResolution 300 /GrayImageMinResolutionPolicy /OK /DownsampleGrayImages true /GrayImageDownsampleType /Bicubic /GrayImageResolution 300 /GrayImageDepth -1 /GrayImageMinDownsampleDepth 2 /GrayImageDownsampleThreshold 1.50000 /EncodeGrayImages true /GrayImageFilter /DCTEncode /AutoFilterGrayImages true /GrayImageAutoFilterStrategy /JPEG /GrayACSImageDict << /QFactor 0.15 /HSamples [1 1 1 1] /VSamples [1 1 1 1] >> /GrayImageDict << /QFactor 0.15 /HSamples [1 1 1 1] /VSamples [1 1 1 1] >> /JPEG2000GrayACSImageDict << /TileWidth 256 /TileHeight 256 /Quality 30 >> /JPEG2000GrayImageDict << /TileWidth 256 /TileHeight 256 /Quality 30 >> /AntiAliasMonoImages false /CropMonoImages true /MonoImageMinResolution 1200 /MonoImageMinResolutionPolicy /OK /DownsampleMonoImages true /MonoImageDownsampleType /Bicubic /MonoImageResolution 1200 /MonoImageDepth -1 /MonoImageDownsampleThreshold 1.50000 /EncodeMonoImages true /MonoImageFilter /CCITTFaxEncode /MonoImageDict << /K -1 >> /AllowPSXObjects false /CheckCompliance [ /None ] /PDFX1aCheck false /PDFX3Check false /PDFXCompliantPDFOnly false /PDFXNoTrimBoxError true /PDFXTrimBoxToMediaBoxOffset [ 0.00000 0.00000 0.00000 0.00000 ] /PDFXSetBleedBoxToMediaBox true /PDFXBleedBoxToTrimBoxOffset [ 0.00000 0.00000 0.00000 0.00000 ] /PDFXOutputIntentProfile () /PDFXOutputConditionIdentifier () /PDFXOutputCondition () /PDFXRegistryName () /PDFXTrapped /False /CreateJDFFile false /Description << /ARA /BGR /CHS /CHT /CZE /DAN /DEU /ESP /ETI /FRA /GRE /HEB /HRV (Za stvaranje Adobe PDF dokumenata najpogodnijih za visokokvalitetni ispis prije tiskanja koristite ove postavke. Stvoreni PDF dokumenti mogu se otvoriti Acrobat i Adobe Reader 5.0 i kasnijim verzijama.) /HUN /ITA /JPN /KOR /LTH /LVI /NLD (Gebruik deze instellingen om Adobe PDF-documenten te maken die zijn geoptimaliseerd voor prepress-afdrukken van hoge kwaliteit. De gemaakte PDF-documenten kunnen worden geopend met Acrobat en Adobe Reader 5.0 en hoger.) /NOR /POL /PTB /RUM /RUS /SKY /SLV /SUO /SVE /TUR /UKR /ENU (Use these settings to create Adobe PDF documents best suited for high-quality prepress printing. Created PDF documents can be opened with Acrobat and Adobe Reader 5.0 and later.) >> /Namespace [ (Adobe) (Common) (1.0) ] /OtherNamespaces [ << /AsReaderSpreads false /CropImagesToFrames true /ErrorControl /WarnAndContinue /FlattenerIgnoreSpreadOverrides false /IncludeGuidesGrids false /IncludeNonPrinting false /IncludeSlug false /Namespace [ (Adobe) (InDesign) (4.0) ] /OmitPlacedBitmaps false /OmitPlacedEPS false /OmitPlacedPDF false /SimulateOverprint /Legacy >> << /AddBleedMarks false /AddColorBars false /AddCropMarks false /AddPageInfo false /AddRegMarks false /ConvertColors /ConvertToCMYK /DestinationProfileName () /DestinationProfileSelector /DocumentCMYK /Downsample16BitImages true /FlattenerPreset << /PresetSelector /MediumResolution >> /FormElements false /GenerateStructure false /IncludeBookmarks false /IncludeHyperlinks false /IncludeInteractive false /IncludeLayers false /IncludeProfiles false /MultimediaHandling /UseObjectSettings /Namespace [ (Adobe) (CreativeSuite) (2.0) ] /PDFXOutputIntentProfileSelector /DocumentCMYK /PreserveEditing true /UntaggedCMYKHandling /LeaveUntagged /UntaggedRGBHandling /UseDocumentProfile /UseDocumentBleed false >> ] >> setdistillerparams << /HWResolution [2400 2400] /PageSize [612.000 792.000] >> setpagedevice