25 This work is licensed under a Creative Commons Attribution 4.0 International License. Enhancement of Antibacterial Activity of Face Mask with Gold Nanoparticles Abstract The emergence of new dangerous diseases worldwide has led to the need to think about the possibility of enhancing prevention by using new technologies. One of the most important requirements emphasized in the recent studies is the effectiveness of the masks against pathogenic bacteria. In this study, the efficiency of anti-infection protective face masks against bacteria was enhanced by using gold nanoparticles prepared by the chemical precipitation method. The absorption spectrum of the prepared gold suspension shows a clear plasmonic peak at 522 nm. The measurements showed that the sample was made of polypropylene fibers, where X-ray diffraction tests showed peaks matching its crystalline structure. Immersion with gold suspension led to the emergence of peaks belonging to the composition of gold. The immersion treatment increased Young's modulus from 36.5 to 61.7 Mpa. The antibacterial assay showed the efficacy of the samples against E-Coli bacteria with an inhibition zone of 3 cm. Keywords: Au NPs, antibacterial, precipitation method. 1. Introduction Due to the increasing demand for the use of protective face masks due to the emergence of new dangerous diseases, it is, therefore, necessary to study the efficiency of commercial face masks and study the possibility of improving them. One of the most important criteria that has been focused on in recent studies is the effectiveness of masks as an antibacterial agent [1]. One of the most important and most widely used materials in the manufacture of face masks is Polypropylene. Polypropylene (PP), is a synthetic resin built up by the polymerization Ibn Al-Haitham Journal for Pure and Applied Sciences http://jih.uobaghdad.edu.iq/index.php/j/index: Journal homepage Doi: 10.30526/35.3.2844 Article history: Received 26 April 2022, Accepted 14 June 2022, Published in July 2022. Farah Sadeq Khesro Department of Physics, College of Education for Pure Science \ Ibn Al-Haitham, Universityof Baghdad, Baghdad, Iraq. Farah.Sadek1204a@ihcoedu.uobaghdad.edu.iq Hanaa Shuker Mahmood Department of Physics, College of Education for Pure Science \ Ibn Al-Haitham, Universityof Baghdad, Baghdad, Iraq. Hanaa.s.m@ihcoedu.uobaghdad.edu.iq https://creativecommons.org/licenses/by/4.0/ file:///F:/العدد%20الثاني%202022/:%20http:/jih.uobaghdad.edu.iq/index.php/j/index mailto:Farah.Sadek1204a@ihcoedu.uobaghdad.edu.iq mailto:Farah.Sadek1204a@ihcoedu.uobaghdad.edu.iq mailto:Hanaa.s.m@ihcoedu.uobaghdad.edu.iq IHJPAS. 53 (3)2022 26 of propylene. The PP is molded or extruded into many plastic products. It is also spun into fibers for employment in industrial and household textiles[2]. In recent years, nanotechnology has played an essential role in the development of smart fabrics. Nanomaterials have been used to provide antibacterial, ultraviolet resistant, hydrophobic, and fire resistant qualities into textiles in a sustainable manner [3]. The nanomaterials have been used in the development of the new generation masks with the greatest effect in terms of filtration effectiveness, antibacterial efficiency and comfort [4]. Various methods for the fabrication of nanomaterials were revealed in the literature review, including vaporization under vacuum, chemical vapor deposition (CVD), chemical deposition, sol-gel, solid-state reaction, and laser ablation [5, 6, 7]. Silver is a popular nanomaterial because of its antibacterial effect against a wide variety of microorganisms such as bacteria and fungi [8]. Furthermore, gold nanoparticles (AuNPs) with chemical, optical, and surface engineering properties have been the focus of much research and applications in biology and medicine for diagnostic and therapeutic purposes. These include cancer cell imaging, drug delivery, and phototherapy [9]. In previous study textile for a face mask was created with antibacterial capabilities using the renewable resources material oil of Folium [10]. The fractional concentration of nitric oxide from exhaled breath was assessed before and after mask wear. The results revealed that the mask was more comfortable, breathed better, has antimicrobial properties, and reduced allergy symptoms. The antimicrobial efficacy of Au NPs by contrasting the multiple techniques of synthesizing. By using the origins of antimicrobial properties [11], they found that the antibacterial effects are directly related to particle size, dispersibility, and surface modification by different reactions improved the nonwoven surgical mask by using spray nozzles to add nano-coating hybrid copper nanoparticles (CuNPs) to increase its hydrophobicity for repelling water droplets [12]. The resultant surface exhibited photocatalytic and photo-thermal capabilities for antimicrobial action during solar irradiation, creating a high amount of free reactive species, so the masks self-cleaning. This work aimed to optimize the antibacterial activity and mechanical properties of commercial face masks by using gold nanoparticles prepared by a simple one-step chemical precipitation method. 2. Experimental Gold(III) chloride tri-hydrate (HAuCl4 .3H2O) was used as the gold precursor. 0.0049 gm of gold chloride salt dissolved in 50 ml water. 0.5 gm of sodium triacetate dissolved in 50 ml distilled water, which acts as both stabilizing and reducing agents. The gold salt solution was heated to boiling point then the reducing solution was added gradually to the solution till the solution convert to red color. The optical properties of Au NPs suspension sample were examined by UV-visible absorbance (type SP-8001). The crystalline structure and crystallite size of the free PP textile sample and that immersed in Au-NPs suspension were examined using X–ray diffraction system (Shimadzu XRD 6000). The source of radiation was Cu (Kα) with a wavelength λ= 1.5405 Å, the current was 30.0 mA and the voltage was 40 kV with a speed of 5.00 (degree /min). Finally, the antimicrobial activity of the soaked mask samples against Escherichia coli microorganisms was evaluated inhibition zone around the sample attached to the agar surface. IHJPAS. 53 (3)2022 27 3. Results and discussions The prepared nanoparticle suspensions in water were examined by UV-Visible absorption. The solutions were put in sonication for 10 minutes before the optical studies. Figure 1 displays the UV-visible absorbance spectra of the Au NPs suspension in distilled water. The pattern shows a surface Plasmon resonance band at 522 nm, which is in the range of the specific peak of Au NPs [13]. This band was exposed due to the interaction of quantum size confined electrons. The free electrons within part of the wavelength dimension have resonance frequency due to interaction with electromagnetic wave frequency. These peaks confirm the formation of NPs in the solution [14]. Figure 1. UV-visible absorbance spectra for the Au NPs suspended in water The polypropylene (PP) polymer fibers are the basic material in the manufacture of most commercial face masks. Figure 2 shows the X-ray diffraction of samples taken from a mask before treatment compared to samples treated with the prepared Au NPs suspensions. The characteristic peaks of PP which appeared at the diffraction angles 2θ= 13.8985, 16.7384, 18.3161, 21.3454 and 25.2582º correspond to the diffractions from crystalline planes for PP with Miller's indices of (110), (040), (130), (111), and (060) respectively. The preferred direction of growth was along (110) and this agrees well with previous studies [15]. The samples treated with Au NPs show small peaks of gold particles appearing at a diffraction angle of 38.3219 º and 44.8537 º, which corresponds to the crystal planes of (111) and (200), respectively, for the crystalline structure of Au NPs matched with standard card No.96-901- 2954. The interlayer distances of the crystal planes were calculated using the Bragg equation [16]. n λ = 2 dhkl sin θ (1) 0 0.1 0.2 0.3 0.4 0.5 0.6 0.7 0.8 0.9 1 300 400 500 600 700 800 900 1000 1100 A b so r b a n c e λ (nm) IHJPAS. 53 (3)2022 28 where λ, n are the monochromatic X-ray wavelength corresponding to Kα transition of Cu target and the diffraction order respectively. The crystal size was calculated according to the full width of diffraction lines (FWHM) using Scherrer’s formula as follows [17]. As shown in Table 1. 𝐶. 𝑆 = 0.9 𝜆 𝐹𝑊𝐻𝑀 .𝑐𝑜𝑠(𝜃) (2) Figure 2. XRD patterns for pure mask and decorated samples with Au NPs. Table 1. XRD peaks for pure mask and decorated samples with Au NPs. Sample 2θ (Deg.) FWHM (Deg.) dhkl Exp.(Å) G.S (nm) Phase hkl Free mask 13.8985 0.5996 6.3666 13.3 PP (110) 16.7384 0.6626 5.2923 12.1 PP (040) 18.3161 0.6942 4.8398 11.6 PP (130) 21.3454 1.0097 4.1593 8.0 PP (111) 25.2582 0.8204 3.5232 9.9 PP (060) With Au NPs 14.4033 0.8204 6.1446 9.8 PP (110) 17.2117 0.6942 5.1478 11.6 PP (040) 18.8526 0.7574 4.7033 10.6 PP (130) 21.8503 1.0097 4.0643 8.0 PP (111) 25.7631 0.8204 3.4552 9.9 PP (060) 28.5714 0.7257 3.1217 11.3 PP (220) 38.3219 0.5680 2.3469 14.8 Au (111) 44.8537 0.5048 2.0191 17.0 Au (200) Figure 3 displays the tensile test curves for the free mask sample and that immersed in Au-NPs suspension and treated at 60 ºC. The two patterns show typical stress–strain behavior[18], starting with the elastic linear region which end at the elastic limit at about 0.15% strain. Then followed by the plastic region and ends at the fracture point. It seems that the Young Modulus slightly increased after immersing in the Au NPs and heat treated. On the IHJPAS. 53 (3)2022 29 other hand, reducing the sample elasticity. Table2 illustrates the Young modulus and maximum elongation for a sample before and after treatment with Au NPs. Figure 3. Stress- strain test for pure mask and decorated samples with Au NPs. Table 2. Stress- strain parameters for pure mask and decorated samples with Au NPs. Sample Max Stress Max elongation (%) Young Modulus (Mpa) Free mask 13.455 116.80 36.5 With Au-NPs 18.949 91.50 61.7 Figure 4 shows the antibacterial test against E-Coli bacteria. It seems highly affected of the mask samples soaked with the Au NPs with inhibition zone 3 cm compared with the untreated samples. The antibacterial activity of Au-NPs is mainly by two mechanisms: the first is to alter cell membrane permeability, which causes a decline in its metabolic activities; the second is to inhibit the ribosome subunit for RNA binding causing a collapse of the biological process[19]. Furthermore, bactericidal gold NPs do not produce any ROS-related processes, even though the formation of ROS is the cause of cellular death for the majority of bactericidal medicines and antibacterial nanomaterials. The low toxicity of gold NPs to mammalian cells is explained by their ROS-independent mechanism of action [20]. IHJPAS. 53 (3)2022 30 Figure 4. Antibacterial test against E-Coli (the three samples to the left for pure mask as control samples and three ones to the right for the decorated samples with Au NPs). 4. Conclusions Au-NPs were successfully synthesized by simple precipitation. The plasmonic peak appeared at522 nm. The study showed the efficiency of the method of dipping face masks in the gold suspension that was prepared to be anti-bacterial, which supports the possibility of wearing the masks for a longer period. The mechanical properties showed an increase in Young's modulus of the samples after treatment. References 1. Stokes, K.; Peltrini, R.; Bracale, U.; Trombetta, M.; Pecchia, L.; Basoli, F. Enhanced Medical and Community Face Masks with Antimicrobial Properties: A Systematic Review. Journal of Clinical Medicine, 2021. 10(18), 4066. 2. Jeemol, P.A.; Mathew, S.; Nair,C.P.R. Maleimide end- capped polyether telechelics as novel toughening agents for unsaturated polyester resin. Journal of Polymer Research, 2020. 27(10), 300. 3. Alwash, S.; Al-saadi, T.M. Assessment of the Mint-Copper Nanoparticles Treatment to Control the Infection of Saprolegniasis in Cyprinus carpio L, Annals of R.S.C.B. 2021. 16010 – 16019. 4. Syduzzaman, M.; Patwary, S.U. Smart Textiles and Nano-Technology: A General Overview, J. Text. Sci. Eng. 2015, 05, 1000181. 5. Mahdie, S.H. Preparation of unsaturated polyester/nano ceramic composite and study electric, thermal and mechanical properties. Iraqi Journal of Physics, 2018,15(35), 188– 201. 6. Thejeel, M.A.; Mahdi, S. Preparation and investigation of the structural and mechanical properties of Nanobiomaterial zirconolite. Solid State Technology, 2020, 63, 1949–1961. 7. Rajput, N. Methods Of Preparation of Nanoparticles – A Review. International Journal of Advances in Engineering & Technology, 2015,7(4), 1806–1811. 8. Jeyaraj, M.; Sathishkumar, G.; Sivanandhan, G. Biogenic silver nanoparticles for cancer treatment: An experimental report. Colloids and Surfaces B: Biointerfaces, 2013, 106, 86– 92. IHJPAS. 53 (3)2022 31 9. Kong, F.; Zhang, J.; Li. R.; Wang, Z. Unique roles of gold nanoparticles in drug delivery, targeting and imaging applications, Molecules, 2017, 22, 1–7. 10. Duong-Quy, S.; Ngo-Minh. X.; Tang-Le-Quynh. T. The use of exhaled nitric oxide and peak expiratory flow to demonstrate improved breathability and antimicrobial properties of novel face mask made with sustainable filter paper and folium plectranthii amboinicii oil: Additional option for mask shortage d, Multidisciplinary Respiratory Medicine, 2020, 15, 664. 11. Gu, X.; Xu, Z., Gu; L. Preparation and antibacterial properties of gold nanoparticles: a review, Environmental Chemistry Letters, 2021, 19(1), 167–187. 12. Kumar, S.; Karmacharya, M.; Joshi, S.R. Photoactive Antiviral Face Mask with Self- Sterilization and Reusability, Nano Letters, 2021, 21(1), 337–343. 13. Raja, D.A.; Munir, F.; Shah, M.R.; Bhanger, M.I.;Malik. M.I. Colorimetric sensing of cephradine through polypropylene glycol functionalized gold nanoparticles .Royal Society Open Science, 2021, 8(5), 210185. 14. Chen, D.H.; Chen, C.J.; Formation and characterization of Au–Ag bimetallic nanoparticles in water-in-oil microemulsions, Journal of Materials Chemistry, 2002, 12(5), 1557–1562. 15. Andric,Z.; Anin, M.D.D.; Jokanovic, V.; Canin, T.D. Mitric, M.; Viana, B. Luminescent properties of nano-SiO2:Eu3+/polypropylene composite, Journal of Optoelectronics and Advanced Materials, 2006,8(2), 829–834. 16. Rajendran, A., Antibacterial Properties and Mechanism of Gold Nanoparticles Obtained from Pergularia Daemia Leaf Extract, Journal of Nanomedicine Research, 2017, 6(1), 00146. 17. Paul, D.; Neogi, S., Synthesis, characterization and a comparative antibacterial study of CuO, NiO and CuO-NiO mixed metal oxide, Materials Research Express 6, 2019. 18. Mahmood, H.S.; Jawad, M.K., Antibacterial activity of chitosan/PAN blend prepared at different ratios, AIP Conference Proceedings, 2019, 020078. 19. Mahmood, H.S.; Jawad, M.K. Investigation of Chitosan/PEO Reinforced with AgNPs for Antibacterial Activity Prepared by Solution Casting Method, Annals of Tropical Medicine and Public Health, 2019, 22(09), 70–82. 20. Cui, Y.; Zhao, Y.; Tian, Y.; Zhang. W.; Lü, X.; Jiang, X. The molecular mechanism of action of bactericidal gold nanoparticles on Escherichia coli, .Biomaterials, 2012, 33(7), 2327–2333.