13 Journal of Multidisciplinary Applied Natural Science Vol. 1 No. 1 (2021) Research Article Structural, Morphological and Elemental Analysis of Selectively Etched and Exfoliated Ti3AlC2 MAX Phase Received : September 12, 2020 Revised : September 21, 2020 Accepted : October 19, 2020 Online : October 20, 2020 In the present research major focus is on the synthesis of materials that can be easily used in small portable devices and as energy storage devices. Here we focused on a new family of 2D materials Ti3C2 (MXenes). Ti3AlC2 (MAX phase) was intercalated using selective etching of aluminium present in the MAX phase. The etching was done using HF in combination with HCl followed by delaminated in DMSO medium using ultrasonication. The synthesized samples were physically characterized via XRD, SEM and EDX. The XRD diffractogram confirms the formation of MXene through its characteristic plane (002) arising at 2 θ~9°. The mor- phological study revealed the stacked layered sheet like structure obtained through SEM. The elemental confirmation of removal of aluminium was done as indicated by EDX spectroscopy. The 2D materials like graphene are widely known for their distinctive properties that are not found in their bulk counterparts, thus making them ideal for a vast range of applications extending from electronic and optoelectronic devices to electrochemical catalysis Generally, 2D materials are produced by exfoliating layered 3D materials with weak van der Waals-like coupling between layers Recent technological advancements have allowed the synthesis of various 2D materials by chemical exfoliation or mechanical cleavage of layered 3D precursors. MXene are newly discovered 2D ceramic materials belonging to the family of transition metal carbides, carbonitrides and nitrides Naguib et al. was the pioneer in synthesizing a 2D nanocrystalline material by exfoliation of layered solids in 2011 MAX phases are the precursors of MXene, they are a large family of ternary carbides or nitrides with a general chemical formula of Mn+1AXn, where M stands for early transition metal, A is an element generally from group IIIA or IVA, X is either carbon or nitrogen and n =1,2,3 and so on MAX phases have layered structure in which M- X units and A layers are alternately stacked. Because the M-X bonds are much stronger than M- A bonds, the A layer can be selectively removed from MAX phases by HF etching, thus creating MXenes The MXene made by HF etching are attached with functional groups like oxygen (=O), hydroxyl (-OH) or fluorine (-F) or a combination of these, due to its high surface energi Thus, the general formula of MXenes can be summarized as Mn+1XnTx, where T represents surface termination groups and x is the number of termination groups per formula unit MXenes exist in a multi-layered structure, which appears as planar sheets stacked in flakes. These multi-layered structures can be delaminated into single-layer flakes by sonication MXenes have hydrophilic surfaces, good chemical stability, fabulous electrical conductivity, and environment friendly. They have plenty of exciting mechanical, electronic, magnetic, and electrochemical properties which have drawn a huge research interest in this area MXene have a flexible and layered structure. Owning to their 2D morphology, they can easily form composites with other materials, so they can integrate the properties of different materials in a complementary way. Due to their low vapour pressure, excellent conductivity, non-flammability, and outstanding electrochemical activity, MXene and its composites Copyright Holder: © Jahan, N., Hussain, S., Rahman, H. U., Manzoor, I., Pandey, S., Habib, K., Ali, S. K., Pandita, R., and Upadhyay, C. (2021) First Publication Right: Journal of Multidisciplinary Applied Natural Science This Article is Licensed Under: https://doi.org/10.47352/jmans.v1i1.6 OPEN ACCESS https://creativecommons.org/licenses/by-sa/4.0/deed.id https://doi.org/10.47352/jmans.v1i1.6 https://crossmark.crossref.org/dialog/?doi=10.47352/jmans.v1i1.6&domain=pdf&date_stamp=2021-01-08 J. Multidiscip. Appl. Nat. Sci. 14 can operate at very high voltages compared to the other electrolytes. Therefore, they can find use as high-performance electrodes in energy storage devices, catalysis, supercapacitors, and pseudocapacitors They have cations intercalation capability so they can also work as anode material for Li-Ion batteries Researchers are also looking to use MXene as reinforcement for other composites, to increase their mechanical properties. Recently MXenes and MXene-based composites find prominent use in the environment related fields. They have been used as efficient catalysts or co-catalysts for electro/photocatalytic water splitting and photocatalytic reduction of carbon dioxide (CO2). They can remove contaminants in water including heavy metal ions, organic dyes, eutrophic substances, and nuclear waste. They have also been applied to biosensors and gas sensors, and exhibiting excellent performances. Many theoretical papers have synthesized and MXene and predicted their properties and applications. Herein, we have analyzed the MXene Ti3C2 which was selectively etched and exfoliated from Ti3AlC2 MAX Phase. A complete analysis on its structural, morphological, and elemental properties has been done. The reports suggest that the synthesized MXene samples could be used for various sensing, electromagnetic shielding and energy harvesting, and storage applications. For the synthesis of MXenes, MAX phase Ti3AlC2 powder (Sigma Aldrich), the etchants which include hydrofluoric acid (HF) and hydrochloric acid (HCl), and dimethyl sulfoxide (DMSO) for delamination were used. All chemicals are analytical grade and used directly without further purification. Prior to the experiment, teflon and glass beakers were cleaned with aqua regia for 3 hours, soap solution, and de-ionized water, respectively. 2.2. Synthesis of Ti3C2Tx MXenes synthesis was done through selective etching of aluminium layers from the bulk MAX phase at room temperature. With a combination of HF and HCl of different concentrations of etchant is used to etch out of the MAX phase powder. Ti3C2Tx was synthesized by etching Al from Ti3AlC2 of 1 gram appropriated from teflon beaker and 20 mL of etchant in which 30%wt HF and 9M HCl is further blend for 48 hours. As the etching is concluded, the Figure 1. X-ray diffraction spectra of Ti3AlC2 (MAX phase) and Ti3C2Tx (MXene). Figure 2. (a) Represents the SEM pictograph of Ti3AlC2 (MAX Phase) and (b) represents the exfoliated accordion type morphology of stacked layers of Ti3C2Tx (MXene) flakes. a b J. Multidiscip. Appl. Nat. Sci. 15 solution is cleaned numerous times via centrifugation at 7,000 rpm for 10 minutes for the respective cycle until the pH value reached approx 6. The etching is not sufficient for complete removal of aluminium, so for further exfoliation, the above-exfoliated powder is intercalated with DMSO for 8 hours. Then, the intercalated sample is sonicated in deionized followed by washing several times at 7000 rpm to remove the residual. Then, the obtained powder sample is treated with 1 M NaOH and further washed away. After washing, the obtained sample is dried in an oven at 60 °C for 48 hours for obtaining flakes MXenes powder. 2.3. Material Characterization Techniques X-ray diffraction (XRD) analysis was carried out for structure characterization with a powder diffractometer (BRUKER, ecoD8 ADVANCE) with Cu Kα radiation (wavelength=1.5418 Å). A scanning electron microscope, SEM, (JEOL JSM - 7600F) equipped with an energy dispersive spectrometer, EXS was cast-off for getting surface morphological and elemental confirmation. 3. RESULTS AND DISCUSSIONS 3.1. Structural Analysis Figure 1 shows the X-ray diffraction plot of the prepared Ti3AlC2 MAX phase and Ti3C2Tx MXene. In this plot, the dominant peak of Ti3AlC2 MAX phase appears at 2θ~9° while for the Ti3C2Tx Mxene appears at 2θ ~11°. Those peaks correspond to the (002) planes of hexagonal crystal structure. The multiple peaks show that the MAX phase powder and MXene powder were polycrystalline in nature. The MAX phase powder had excellent crystallinity compared to MXene powder. The crystallite size of MAX phase powder and MXene powder were calculated by using the Debye- Scherrer formula: (1) Where λ is the wavelength of X-ray, θ is the Bragg’s angle, and β is the full width at half maxima (FWHM) of the dominating peak corresponding to the (002) plane. The average crystallite size of Ti3AlC2 MAX phase was 37.56 nm and Ti3C2Tx MXene was 14.68 nm as shown in table 1. It is observed that the crystallite size decreases after etching. In comparison of Ti3AlC2 MAX phase and Ti3C2Tx MXene, most of the diffraction peaks disappeared in Ti3C2Tx MXene. It shows the depletion of Ti3AlC2 MAX phase into Ti3C2Tx MXene phase (i.e. removal of Al). The intensity of the peak at 39° almost decreased, which shows the removal of Al [12]. In addition, the shift of Ti3C2Tx MXene peaks from 9.74° to 11.11° shows the compression of the interlayer distance from 9.07Å to 8.03Å. 3.2. Morphological study through SEM The surface topography image analysis of obtained synthesize MXenes flakes were carried- Table 1. Average crystallite size and Interplanar spacing of MAX phase and MXene. Parameters Ti3AlC2 (MAXphase) Ti3C2Tx (MXene) Avg. Crystallite size (nm) 37.56 14.68 Interlayer spacing (Å) 9.07 8.03 Figure 3. Typical EDX spectra of Ti3C2TX after the selective etching of aluminium layers from the MAX Phase. J. Multidiscip. Appl. Nat. Sci. 16 out via SEM. The tightly bonded layer of the MAX phase flakes are found be exfoliated following HF and HCl etchings. In general, the stacked layers of MXene resemble to the shape of accordion with irregular profile bounded by weak Van der Waals force. The layers could be more exfoliated via the delamination process. Figure 2 shows the SEM image of Ti3AlC2 (MAX phase) and Ti3C2Tx (MXene). 3.3. Elemental Analysis from EDX spectroscopy The information about the elemental composition in the exfoliated MXene sample is given by the energy-dispersive X-ray (EDX) spectroscopy in figure 3. It is evident from the plot that the traces of aluminium in the sample are negligible, i.e. below 0.5%. The presence of chlorine is in small amount but it is assumed to be as a result of HCl used in the process of etching of the sample and is proportionately higher than aluminium. A greater intensity peak of silicon is noticed because of the silicon substrate upon which the MXene sample is drop casted for various analyses. Carbon is present in large quantity whereas titanium is comparatively low in concentration. Table 2 gives a tabular representation of the concentration in weight percentage of each element present in the sample. 4. CONCLUSIONS 2D materials like MXene are newly discovered ceramic materials, which have the features to incorporate the properties of different materials. This paper highlights the MXene synthesis with a fusion of etchants like HF in combination with HCl that precisely etched the aluminium layer. The XRD demonstration of phase represents the excellent crystallinity and the most prominent peak arises in the range of 9-11° representing the (002) plane. SEM displays non-uniform profile of MXene having accordion like structure after further delamination process. The EDX plot reveals that most of the aluminium are easily etched from the MAX phase, although the negligible traces of aluminium < 0.5% is still present. MXene synthesized by the selectively etching process can be best suited for applications in energy storage devices where the high voltage operation of its composites can swiftly carry out the Faradaic reactions. AUTHOR INFORMATION Corresponding Author Chandramani Upadhyay — Centre for Nano- science and Nanotechnology, Jamia Millia Is- lamia, New Delhi-110025 (India); orcid.org/0000-0002-7307-6968 Email: cupadhyay012@gmail.com Authors Nushrat Jahan — Centre for Nanoscience and Nanotechnology, Jamia Millia Islamia, New Del- hi-110025 (India); orcid.org/0000-0001-7888-4166 Salim Hussain — Centre for Nanoscience and Nanotechnology, Jamia Millia Islamia, New Del- hi-110025 (India); orcid.org/0000-0002-1775-8630 Huzef Ur Rahman — Centre for Nanoscience and Nanotechnology, Jamia Millia Islamia, New Delhi-110025 (India); orcid.org/0000-0002-6041-1034 Insha Manzoor — Centre for Nanoscience and Nanotechnology, Jamia Millia Islamia, New Del- hi-110025 (India); orcid.org/0000-0001-5629-6347 Shashank Pandey — Centre for Nanoscience and Nanotechnology, Jamia Millia Islamia, New Delhi-110025 (India); orcid.org/0000-0001-6963-1271 Kamran Habib — Centre for Nanoscience and Nanotechnology, Jamia Millia Islamia, New Del- hi-110025 (India); orcid.org/0000-0001-9891-0042 Syed Kaabir Ali — Centre for Nanoscience and Table 2. The percentage of elements present in the sam- ple after the formation of MXene. Element Series Atomic % Silicon K-Series 36.48 Titanium K-Series 13.69 Carbon K-Series 48.49 Chlorine K-Series 0.85 Aluminium K-Series 0.49 Total 100 https://orcid.org/0000-0002-7307-6968 mailto:cupadhyay012@gmail.com https://orcid.org/0000-0001-7888-4166 https://orcid.org/0000-0002-1775-8630 https://orcid.org/0000-0002-6041-1034 https://orcid.org/0000-0001-5629-6347 https://orcid.org/0000-0001-6963-1271 https://orcid.org/0000-0001-9891-0042 J. Multidiscip. Appl. Nat. Sci. 17 Nanotechnology, Jamia Millia Islamia, New Del- hi-110025 (India); orcid.org/0000-0002-8111-2244 Reetika Pandita — Centre for Nanoscience and Nanotechnology, Jamia Millia Islamia, New Del- hi-110025 (India); orcid.org/0000-0003-0316-5647 REFERENCES [1] B. Anasori, C. Shi, E. J. Moon, Y. Xie, C. A. Voigt, P. R. C. Kent, S. J. May, S. J. L. Billinge, M. W. Barsoum, and Y. Gogotsi. (2016). “Control of electronic properties of 2D carbides (MXenes) by manipulating theirtransition metal layers”. Nanoscale Horizons. 1(3): 227–234. 10.1039/ C5NH00125K. [2] H. Wang, Y. Wu, J. Zhang, G. Li, H. Huang, X. Zhang, and Q. Jiang. (2015). “Enhancement of the electrical properties of MXene Ti3C2 nanosheets by post-treatments of alkalization and calcination”.Materials Letters. 160: 537–540. 10.1016/ j.matlet.2015.08.046. [3] R. Meshkian, L. Å. Näslund, J. Halim, J. Lu, M. W. Barsoum, and J. Rosen. (2015). “Synthesis of two-dimensional molybdenum carbide, Mo2C, from the gallium based atomic laminate Mo2Ga2C,” Scripta Materialia. 108: 147–150. 10.1016/ j.scriptamat.2015.07.003. [4] Z. Li, L. Wang, D. Sun, Y. Zhang, B. Liu, Q. Hu, and A. Zhou. (2015). “Synthesis and thermal stability of two-dimensional carbide MXene Ti3C2”. Materials Science and Engineering: B Solid-State Materials Advances Technology. 191: 33–40. 10.1016/ j.mseb.2014.10.009. [5] X. Zhan, C. Si, J. Zhou, and Z. Sun. (2020). “MXene and MXene-based composites: Synthesis, properties and environment-related applications”.Nanoscale Horizons, 5(2): 235– 258. 10.1039/C9NH00571D. [6] Y. Gao, L. Wang, A. Zhou, Z. Li, J. Chen, H. Bala, Q. Hu, and X. Cao. (2015). “Hydrothermal synthesis of TiO2/Ti3C2 nanocomposites with enhanced photocatalytic activity”. Materials Letters. 150: 62–64. 10.1016/j.matlet.2015.02.135. [7] P. Yan, R. Zhang, J. Jia, C. Wu, A. Zhou, J. Xu, and X. Zhang. (2015). “Enhanced supercapacitive performance of delaminated two-dimensional titanium carbide/carbon nanotube composites in alkaline electrolyte”. Journal of Power Sources. 284: 38–43. 10.1016/j.jpowsour.2015.03.017. [8] S. J. Kim, M. Naguib, M. Zhao, C. Zhang, H. Jung, M. W. Barsoum, and Y. Gogotsi. (2015). “High mass loading, binder-free MXene anodes for high areal capacity Li-ion batteries”. Electrochimica Acta. 163: 246– 251. 10.1016/j.electacta.2015.02.132. [9] G. Zou, J. Guo, Q. Peng, A. Zhou, Q. Zhang, and B. Liu. (2015). “Synthesis of urchin-like rutiletitania carbon nanocomposites by iron- facilitated phase transformation of MXene for environmental remediation”. Journal of Materials Chemistry A. 4(2): 489–499. 10.1039/C5TA07343J. [10] Z. Lin, D. Barbara, P. Taberna, K. L. Van Aken, B. Anasori, Y. Gogotsi, and P. Simon. (2016). “Capacitance of Ti3C2Tx MXene in ionic liquid electrolyte”. Journal of Power Sources. 326: 575–579. 10.1016/ j.jpowsour.2016.04.035. [11] A. Byeon, M. Zhao, C. E. Ren, J. Halim, S. Kota, P. Urbankowski, B. Ansori, M. W. Barsoum, and Y. Gogotsi. (2017). “Two- Dimensional Titanium Carbide MXene as a Cathode Material for Hybrid Magnesium/ Lithium-Ion Batteries”. ACS Applied Materials and Interfaces, 9 (5): 4296–4300. 10.1021/acsami.6b04198. [12] R. Syamsai, P. Kollu, S. K. Jeong, and A. N. Grace. (2017). “Synthesis and properties of 2D-titanium carbide MXene sheets towards electrochemical energy storage applications”. Ceramics International. 43 (16), 13119-13126. 10.1016/ j.ceramint.2017.07.003. https://orcid.org/0000-0002-8111-2244 https://orcid.org/0000-0003-0316-5647 https://doi.org/10.1039/C5NH00125K https://doi.org/10.1039/C5NH00125K https://doi.org/10.1016/j.matlet.2015.08.046 https://doi.org/10.1016/j.matlet.2015.08.046 https://doi.org/10.1016/j.scriptamat.2015.07.003 https://doi.org/10.1016/j.scriptamat.2015.07.003 https://doi.org/10.1016/j.mseb.2014.10.009 https://doi.org/10.1016/j.mseb.2014.10.009 https://doi.org/10.1039/C9NH00571D https://doi.org/10.1016/j.matlet.2015.02.135 https://doi.org/10.1016/j.jpowsour.2015.03.017 https://doi.org/10.1016/j.electacta.2015.02.132 https://doi.org/10.1039/C5TA07343J https://doi.org/10.1016/j.jpowsour.2016.04.035 https://doi.org/10.1016/j.jpowsour.2016.04.035 https://doi.org/10.1021/acsami.6b04198 https://doi.org/10.1016/j.ceramint.2017.07.003 https://doi.org/10.1016/j.ceramint.2017.07.003