Nova Biotechnologica et Chimica 11-2 (2012) 139 DOI 10.2478/v10296-012-0016-x © University of SS. Cyril and Methodius in Trnava REMOVAL OF Cd2+ AND Pb2+ FROM AQUEOUS SOLUTIONS USING BIO-CHAR RESIDUES KATARÍNA ŠTEFUŠOVÁ, MICHAL LOVÁS, ANTON ZUBRIK, MAREK MATIK, MIROSLAVA VÁCLAVÍKOVÁ Institute of Geotechnics of Slovak Academy of Sciences, Watsonova 45, Košice, SK- 043 53, Slovak Republic (stefusova@saske.sk) Abstract: In this paper, wheat straw and rapeseed residues before and after microwave pyrolysis during bio- oil production were studied as potential sorbents of heavy metals. The sorbents were characterized by elemental analysis and FTIR spectroscopy. Sorption properties of the materials were investigated using batch adsorption-equilibrium experiments and the effect of initial Cd and Pb concentration was studied. The experimental data fit Langmuir adsorption isotherm. The maximum sorption affinity of studied materials was observed in the case of rapeseed and its sorption capacity was 31.6 and 83.5 mg/g for Cd and Pb, respectively. Key words: biomass, microwave pyrolysis, char, cadmium, lead, sorption 1. Introduction Water pollution is one of the most important environmental problems. Among the aquatic pollutants, heavy metals have gained relatively more significance in view of their persistence, bio-magnification and toxicity. The main sources of heavy metal contamination are e.g. metal plating, mining operations, tanneries, radiator manufacturing, smelting, alloy industries and storage batteries manufactures (KADIRVELU et al., 2001). Treatment processes for heavy metals removal from wastewaters include precipitation, membrane filtration, ion exchange, adsorption and co-precipitation/adsorption. Cost-effective alternative technologies for the treatment of metal-containing wastewaters are needed. Adsorption has evolved as one of the most used treatment techniques for removing metal ions to lowers from water which cannot be removed by other techniques (MOHAN et al., 2007). In recent years, considerable attention has been focused on the removal of heavy metals from aqueous solution using adsorbents derived from low-cost materials, such as agricultural waste and by-products. Natural materials that are available in large quantities, or certain waste products from agricultural operations, may have potential as inexpensive adsorbents. Due to their low cost, after these materials have been expended, they can be disposed of without regeneration. In general, adsorbents can be assumed as low cost if they require little processing, are abundant in nature, or are a by-product or waste material from another industry (BAILEY et al., 1998). Several methods have been studied over the years, for the production of low-cost adsorbents. Pyrolysis is one of the methods that can be used for production of low-cost adsorbents (CHEN et al., 2011; LIU et al., 2011; LIU et al., 2012; MOHAN et al., 2007) Pyrolysis can be described as the direct thermal decomposition of the organic matrix in the absence of oxygen to obtain an array of solid, liquid and gas products. Bereitgestellt von Slovenská poľnohospodárska knižnica | Heruntergeladen 16.01.20 13:05 UTC 140 Štefušová, K. et al. Microwave heating technology has been shown to be more energy efficient than conventional methods in many applications. Microwave irradiation is rapid and volumetric with the whole material heated simultaneously. In contrast, conventional heating is slow and the heat is introduced into the sample from the surface. Microwave pyrolysis has gained momentous attraction because of the merits mentioned above. Existing research works on microwave pyrolysis of biomass includes pyrolysis of wheat straw (BUDARIN et al., 2009), corn stover (YU et al., 2007), rice straw (HUANG et al., 2008), biomass (WAN et al., 2009), coffee hulls (DOMÍNGUEZ et al., 2007), and pine wood sawdust (CHEN et al., 2008). The main purpose of this study was the evaluation of Pb and Cd adsorption from aqueous solutions onto straw and rapeseed char. Sorption properties of the materials were studied before and after their conversion into biochars through microwave pyrolysis treatment. 2. Materials and methods 2.1 Sorbent preparation Samples of the wheat straw and rapeseed (Palma Sečovce, s.r.o) were crushed by (Air Grinder MC – FDV), sieved to granulometric fraction under 1 mm and washed with deionized water and dried at temperature of 100°C. The material were press to briquettes and used for pyrolysis. After pyrolysis samples were crushed, sieved and dried again. Microwave pyrolysis experiments were carried out at nitrogen atmosphere and power 900 W. Samples were characterized by elemental analysis (CHNS Elementar Vario Macro Cube) and FTIR spectroscopy (FT-IR Bruker Tensor 27). 2.1 Adsorption experiments The sorption properties of raw materials and biomass char residues were tested under batch conditions. The initial Cd and Pb concentration was 10-200 and 10- 250 mg/L, respectively. Model solutions of Cd and Pb were prepared by dissolving Cd(NO3)2.4H2O and Pb(NO3)2 in deionized water, respectively. The sorbent concentration was 2 g/L. The pH of the solutions was adjusted to value of 5.0 with 0.01 and 0.1 M NaOH and HNO3. The experiments were performed at constant temperature of 25°C in a rotary shaker set at 30 rpm and equilibrium time 24 hours. The metal quantity in solutions was determined by AAS (Varian 240 RS/240 Z, Australia) before and after the sorption experiments. The amount of the metal sorbed (mg) per unit mass of sorbents (g) qeq, was calculated using the Eq. (1) s eq eq C CC q − = 0 (1) where C0 and Ceq are initial and equilibrium metal concentration (mg/L), respectively and Cs is the sorbent concentration in solution (g/L). Bereitgestellt von Slovenská poľnohospodárska knižnica | Heruntergeladen 16.01.20 13:05 UTC Nova Biotechnologica et Chimica 11-2 (2012) 141 3. Results and discussion 3.1 Characterization of sorbents The results of the elemental analysis of tested materials are given in Table 1 and 2. During the conversion of biomass to biochar the original carbon is retained in the biochar, which offers a significant opportunity for creating a carbon sink. As a consequence of the pyrolysis process, the carbon content of the carbonized residue increased with regard to the original biomass, along with a deoxygenation as a consequence of the loss of functional groups during the process. There was also a noticeable decrease in the hydrogen content, probably due to the great proportion of hydrogen compounds in the volatile matter. Table 1. Characterization of biomass samples (A – ash, V – volatile matter, W – moisture; Superscripts: d – dry basis, a – analytical specimen, Od – by difference - according to 100 - (Ad + Cd + Hd + Nd+ Sd). Sample Ad Wa V Nd[%] Cd[%] Hd[%] Sd[%] Od[%] rapeseed 7.0 4.2 74.6 5.44 46.07 6.59 0.79 34.11 wheat straw 7.3 4.7 74.8 1.7 39.67 5.96 0.24 45.13 Table 2. Characterization of biomass samples after microwave pyrolysis. Sample Recovery [%] Time of pyrolysis [min] N[%] C[%] H[%] S[%] rapeseed 27 25 4.26 59.83 1.237 0.414 wheat straw 24 30 1.56 63.92 1.635 0.315 FTIR spectroscopy was used to characterize the functional groups responsible for heavy metals adsorption. The FTIR spectra of rapeseed and wheat straw before and after pyrolysis are given in Fig. 1 and 2, respectively. It is important to note that visible vibrations presented in the spectrum represent not only one structure, but there are several group/bond vibration, which are often overlapped. The broad peak at maximum of 3287 cm-1 represents hydroxyl groups (vibration frequencies of water, alcohols, and phenols) and N–H stretching vibrations (ABDEL-NASSER and EL- HENDAWY, 2006). The peaks at 2924 and 2854 cm-1 can be assigned to CH2 (asymmetric) and CH3 (symmetric) stretch of aliphatic structures. Vibration frequency at 1743 cm-1 can be assigned to esters. Theoretical vibration frequencies C=O functional group of aldehydes and ketones are shifted to lower values (around 1725 - 1700 cm-1), even though these compounds also contribute to this absorbance. Next peak at 1634 cm-1 can be associated with weaker H-O-H bending vibration of water. Moreover, in this region, there are also C=C bond of alkenes and aromatic compounds and C=O stretching vibration of carbonyl group. The aromatic skeletal C=C bonds are visible in the region at 1517 cm-1 and 1443 cm-1, respectively. C–O stretching Bereitgestellt von Slovenská poľnohospodárska knižnica | Heruntergeladen 16.01.20 13:05 UTC 142 Štefušová, K. et al. vibration can be also presented in this region (around 1423 cm-1) (BARKA et al., 2010). Asymmetric stretching vibration of C-O-C in esters and/or organic acids is presented at 1234 cm-1. Absorption bands at 1132 cm-1 and 1023 cm-1 are assigned to deformation vibrations of C-H bonds in aromatic ring and deformation vibrations of C-O bonds in alcohols and carboxylic acids (TUZEN et al., 2009). 0 0,02 0,04 0,06 0,08 5001000150020002500300035004000 Wavenumber [cm-1] A bs or ba nc e R S 3287 17432855 2924 1634 I 1234 I 1518 1023 1132 I 1421 I Fig. 1. FT-IR spectroscopy of wheat straw and rapeseed. Degradation of the organic phase was observed in both samples after process of pyrolysis (Fig. 2). Decreasing in the band intensities is visible in all regions and only some peaks are presented in the FT-IR spectrum. For example, a visible intensity was recorded at 1010 cm-1 in the case of wheat straw residue. 3.2 Adsorption The effect of initial metal concentration on sorption by tested materials is shown in Fig. 3-6. Isotherm studies provide information on the capacity of sorbent. Adsorption isotherms are characterized by certain constants and describe the mathematical relationship between the quantity of adsorbate and concentration of adsorbate remaining in the solution at equilibrium. The experimental data were evaluated using Langmiur isotherm (Eq. 2). eq eq eq bC1 bC qq + = max (2) where qeq (mg/g) is the weight adsorbed per unit mass of adsorbent at equilibrium, qmax (mg/g) is the theoretical monolayer adsorption capacity, b (L/mg) is the Langmuir constant related to the energy of adsorption and Ceq (mg/L) is the equilibrium concentration. Bereitgestellt von Slovenská poľnohospodárska knižnica | Heruntergeladen 16.01.20 13:05 UTC Nova Biotechnologica et Chimica 11-2 (2012) 143 0 0,02 0,04 0,06 5001000150020002500300035004000 Wavenumber [cm-1] A bs or ba nc e R (MP) S (MP) Fig. 2. FT-IR spectra of char residues (wheat straw and rapeseed) after microwave pyrolysis. The effect of initial Cd and Pb concentration on sorption capacity of tested sorbents is shown in Fig. 3-6. It was observed that the increase of initial metal concentration caused increasing of the metal amount adsorbed per mass unit. The maximum obtained sorption capacity of wheat straw was 5.5 and 14.0 mg/g for Cd and Pb, respectively. Microwave pyrolysis of straw caused a considerable increase of sorption capacity of material. The maximum sorption capacity of wheat straw after pyrolysis was 10.5 and 33.5 mg/g for Cd and Pb, respectively. The sorption capacity of rapeseed was 31.6 and 83.5 mg/g for Cd and Pb, respectively. Microwave pyrolysis of rapeseed caused a decrease of sorption affinity of material toward Cd and Pb ions. The sorption capacity of rapeseed after microwave pyrolysis was 4.8 and 26.2 mg/g for Cd and Pb, respectively. Experimental data were in good agreement with Langmuir isotherms. Langmuir adsorption parameters are given in Table 3. Table 3. Langmuir adsorption parameters. Cd Pb qmax[mg/g] b[L/mg] R 2 qmax[mg/g] b[L/mg] R 2 S 6.71 0.02 0.98 14.24 0.12 0.99 SMP 11.99 0.04 0.99 23.91 0.72 0.97 R 49.36 0.02 0.98 88.53 0.24 0.99 RMP 5.60 0.08 0.98 26.89 0.41 0.97 The sorption of Cd and Pb by biomass char residues has been studied by several authors, as well. MOHAN et al. (2007) studied Cd and Pb sorption by chars produced from pyrolysis of pine wood, pine bark, oak wood and oak bark during bio-oil production. The most efficient sorbent was oak bark char with sorption capacity Bereitgestellt von Slovenská poľnohospodárska knižnica | Heruntergeladen 16.01.20 13:05 UTC 144 Štefušová, K. et al. 2.9 and 11.3 mg/g for Cd and Pb (C0=10 mg/L), respectively. TANGJUANK et al. (2009) studied removal of Cd and Pb by activated carbon prepared from cashew nut shells. The maximum sorption capacity of sorbent was 14.3 and 28.9 mg/g for Cd and Pb (C0=40 mg/L), respectively. 0 20 40 60 80 100 120 140 160 180 200 0 2 4 6 8 10 12 S S MP q e q[m g/ g] C eq [mg/L] Fig. 3. Cd adsorption on wheat straw (S) and wheat straw char residues (SMP). 0 20 40 60 80 100 120 140 160 0 5 10 15 20 25 30 35 R R MP q e q[m g/ g] C eq [mg/L] Fig. 4. Cd adsorption on rapeseed (R) and rapeseed char residues (RMP). 0 20 40 60 80 100 120 140 0 5 10 15 20 25 30 35 S S MP q e q[m g/ g] C eq [mg/L] Fig. 5. Pb adsorption on wheat straw (S) and wheat straw char residues (SMP). 0 20 40 60 80 100 120 140 160 180 200 0 10 20 30 40 50 60 70 80 90 R R MP q e q[m g/ g] C eq [mg/L] Fig. 6. Pb adsorption on rapeseed (R) and rapeseed char residues (RMP). 4. Conclusions In this work straw and rapeseed before and after microwave pyrolysis were studied as Pb and Cd sorbents. The chars produced from microwave pyrolysis of straw and rapeseed during bio-oil production were characterized and used successfully without activation for the removal of Cd and Pb from water. Microwave pyrolysis caused significant changes in sorption properties of materials. After pyrolysis the sorption capacity of straw increased while in the case of rapeseed it decreased. The Cd sorption on the sorbents followed the order: R>>SMP>S~RMP. The Pb sorption on the sorbents followed the order: R>>SMP>RMP>S. The sample of untreated rapeseed has shown the highest sorption affinity toward Cd and Pb ions. The maximum sorption capacity of the untreated rapeseed was 31.6 mg and 83.5 mg/g for Cd and Pb, respectively. Bereitgestellt von Slovenská poľnohospodárska knižnica | Heruntergeladen 16.01.20 13:05 UTC Nova Biotechnologica et Chimica 11-2 (2012) 145 Acknowledgements: This work has been supported by Science and Scientific Grant Agency VEGA, project No. 0141 and the Slovak Research and Development Agency under the contract No. APVV-0252-10. References BAILEY, S.E., OLIN, T.J., BRIKA, R.M., ADRIAN D.A.: A review of potentially low-cost sorbent for heavy metals. Water Res., 33, 1998, 2469-2479. BARKA, N., ABDENNOURI, M., BOUSSAOUD, A., EL MAKHFOUK, M.: Biosorption characteristics of Cadmium(II) onto Scolymus hispanicus L. as low- cost natural biosorbent. Desalination, 258, 2010, 66–71. BUDARIN, V.L., CLARK, J.H., LANIGAN, B.A., SHUTTLEWORTH, P., BREEDEN, S.W., WILSON, A.J., MACQUARRIE, D.J., MILKOWSKI, K., JONES, J., BRIDGEMAN, T., ROSS, A.: The preparation of high-grade bio-oils through the controlled, low temperature microwave activation of wheat straw. Bioresour. Technol., 100, 2009, 6064-6068. CHEN, M.Q., WANG, J., ZHANG, M.X., CHEN, M.G., ZHU, X.F., MIN, F.F., TAN, Z.C.: Catalytic effects of eight inorganics additives on pyrolysis of pine wood sawdust by microwave heating. J. Anal. Appl. Pyrolysis, 82, 2008, 145-150. CHEN, X., CHEN, G., CHEN, L., CHEN, Y., LEHMANN, J., McBRIDE M.B., HAY, A.J:: Adsorption of copper and zinc by biochars produced from pyrolysis of hardwood and corn straw in aqueous solution. Bioresour. Technol., 102, 2011, 8877-8884. DOMÍNGUEZ, A., MENÉNDEZ, J.A., FERNÁNDEZ, Y., PIS, J.J., VALENTE NABAIS, J.M., CARROTT, P.J.M., RIBEIRO CARROTT, M.M.L.: Conventional and microwave induced pyrolysis of coffee hulls for the production of a hydrogen rich fuel gas. J. Anal. Appl. Pyrolysis, 79, 2007, 128-135. EL-HENDAWY, A.N.A.: Variation in the FTIR spectra of a biomass under impregnation, carbonization and oxidation conditions. J. Anal. Appl. Pyrolysis, 75, 2006, 159–166. HUANG, Y.F., KUAN, W.H., LO, S.L., LIN, C.F.: Total recovery of resources and energy from rice straw using microwave-induced pyrolysis. Bioresour. Technol., 99, 2008, 8252-8258. KADIRVELU, K., THAMARAISELVI, K., NAMASIVAYAM, C.: Removal of heavy metals from industrial wastewaters by adsorption onto activated carbon prepared from an agricultural solid waste. Bioresour. Technol., 76, 2001, 63-65. LIU W.J., ZENG, F.X., JIANG, H., ZHANG, X:S.: Preparation of high adsorption capacity bio-chars from waste biomass. Bioresour. Technol., 102, 2011, 8247- 8252. LIU, Y., ZHAO, X., LI, J., MA, D., HAN, R.: Characterization of bio-char from pyrolysis of wheat straw and its evaluation on methylene blue adsorption. Desalin. Water Treat., 46, 2012, 115-123. MOHAN, D., PITTMAN, C.U., BRICKA, M., SMITH, F., YANCEY, B., MAHAMMAD, J., STEELE, P.H., ALEXANDRE-FRANCO, M.F., GÓMEZ- SERRANO, V., GONG, H.: Sorption of arsenic, cadmium, and lead by chars Bereitgestellt von Slovenská poľnohospodárska knižnica | Heruntergeladen 16.01.20 13:05 UTC 146 Štefušová, K. et al. produced from fast pyrolysis of wood and bark during bio-oil production. J. Colloid Interface Sci., 310, 2007, 57-73. TANGJUANK, S., INSUK, N., TONTRAKOON, J., UDEYE, V.: Adsorption of Lead(II) and Cadmium(II) ions from aqueous solutions by adsorption on activated carbon prepared from cashew nut shells. World Academy of Science, Engineering and Technology, 52, 2009, 110-116. TUZEN, M., SARI, A., MENDIL, D., ULUOZLU O.D.,, SOYLAK, M., DOGAN, M.: Characterization of biosorption process of As(III) on green algae Ulothrix cylindricum. J. Hazard. Mater., 165, 2009, 566-572. WAN, Y., CHEN, P., ZHANG, B., YANG, C., LIU, Y., LIN, X., RUAN, R.: Microwave-assisted pyrolysis of biomass: Catalyst to improve product selectivity. J. Anal. Appl. Pyrolysis, 86, 2009, 161-167. YU, F., DENG, S., CHEN, P., LIU, Y., WAN, Y., OLSON, A., KITTELSON, D., RUAN, R.: Physical and chemical properties of bio-oils from microwave pyrolysis of corn stover. Appl. Biochem. Biotechnol., 136-140, 2007, 957-970. Presented at the 2nd International Conference “Biotechnology and Metals - 2011”, September 22–23, 2011, Košice, Slovak Republic. Bereitgestellt von Slovenská poľnohospodárska knižnica | Heruntergeladen 16.01.20 13:05 UTC