Photovoltaic Cells and Systems: SQU Journal for Science, 2014, 19(1), 43-53 © 2014 Sultan Qaboos University 43 Fabrication and Surface Characterization of Poly(4-aminodiphenylamine) Film Modified Electrode and its Application for Lead and Cadmium Determination Mohammed M. Al-Hinaai 1 , Salim H. Al-Harthi 2 and Emad A. Khudaish 1* 1 Department of Chemistry, College of Science, Sultan Qaboos University, PO Box: 36, PC 123, Al- Khod, Muscat, Sultanate of Oman; 2 Department of Physics, College of Science, Sultan Qaboos University, PO Box: 36, PC 123, Al-Khod, Muscat, Sultanate of Oman. *Email: ejoudi@squ.edu.om. ABSTRACT: Poly(4-aminodiphenylamine), Padpa, film was synthesized electrochemically on a glassy carbon electrode by potentiodynamic repetitive cycling of 4-aminodiphenylamine (4-adpa) in 1.0 M HCl. The mechanistic steps involved the oxidation of the protonated monomer to diimine species followed by its dimerization to form the mono-charged radical intermediate, which was considered as the initiation step for the progress of polymerization. The electrochemical properties and surface morphology of the film modified electrode were characterized using electrochemical and various surface scanning techniques. The XPS data demonstrated the existence of =N bonding responsible for polymer formation, while the AFM image revealed a uniform and symmetrical fiber structure with low energy dissipation. The modified electrode was primarily applied as an environmental sensor for the simultaneous and selective determination of Cd 2+ and Pb 2+ ions in water samples. The detection limit for Cd 2+ and Pb 2+ ions was 25 and 14 g L 1 , respectively. Keywords: Electropolymerization; 4-Aminodiphenylamine; Sensors; Cadmium; Lead. أيينىا داي فنيم أيين( نقطب كهربائي يعذل واستخذاياته في تقذير أيىنات انرطاص – 4تشييذ وتقييى نغالف رقيق ين بىنيًر ) وانكادييىو عًاد خذيشو يحًذ انهنائي، سانى انحارثي أيٍُٕ داي فٍُم أيٍٍ(عهى سطخ قطت انكشثٌٕ انزجبجً ٔرنك ثإيشاس جٓذ كٓشثبئً – 4رصٍُع طجقخ سقٍقخ يٍ ثٕنًٍش ) رى :يهخض . رزضًٍ يٍكبٍَكٍخ انزفبعم أكسذح يٕالسي 1أيٍُٕ داي فٍُم أيٍٍ( انًزاثخ فً يذهٕل دبيض انٍٓذسٔكهٕسٌك– 4يزغٍش ٔيزسهسم نًبدح ) ٌٌٕ انًٕجت انجزسي األثعًهٍخ ركبرف نجزيء ثُبئً ٌذعى ى يبدح داي اًٌٍٍ ٔانزً ثذٔسْب رًشدبدي انذبيم نجشٔرٌٕ انانجزيء األ انزي ًٌثم انخطٕح االسبسٍخ نعًهٍخ انجهًشح نهٕصٕل انى رذضٍش انجٕنًٍش انُٓبئً. نقذ رى دساسخ انصفبد انكٓشثبئٍخ ٔانزشكٍت انسطذً َزبئج انٕصف انفٍزٌبئً ٔانضٕئً ٍخ ٔانطشق انفٍزٌبئٍخ نزٕصٍف انسطٕح.نطجقخ انجٕنًٍش انشقٍقخ ثٕاسطخ انطشق انكٓشٔكًٍٍبئ . يُخفضخ( انًسؤٔنخ عٍ ركٌٍٕ انجٕنًٍش انزي ٔصف ثأَّ يٍ أَسجخ يُزظًخ ٔيزًبثهخ راد طبقخ رشزذ -N=أٔضذذ ٔجٕد انشاثطخ ) خزٍبسي نكم يٍ إٌَٔبد انشصبص ٔانكبديٍٕو زايٍ ٔاإلأٌ انقطت انكٓشثبئً انًعذل رى اسزخذايّ نهزطجٍقبد انجٍئٍخ انًزصهخ ثبنزقٍٍى انًز جزء يٍ انجهٌٍٕ نكم يٍ انشصبص ٔانكبديٍٕو عهى انزٕانً. 52ٔ 14فً عٍُبد انًٍبِ دٍث ٔصهذ دذٔد انزقٍٍى انى .أيٍُٕا داي فٍُم أيٍٍ، أقطبة دسبسخ، كبديٍٕو، سصبص – 4انجهًشح انكٓشٔكًٍٍبئٍخ، : يفتاح انكهًات 1. Introduction n recent years, electrochemical polymerization has received a great deal of attention as a unique method to construct and modify various electrode surfaces with certain polymeric films. The fabrication, characterization and application of polymer modified electrodes (PMEs) are important themes and a core area of research in chemistry. Electrochemical methods can effectively tailor the chemical and physical properties of the resulting polymer, including mechanical I EMAD KHUDAISH ET AL 44 resistance, electrical conductivity, stability and high electron affinity [1]. They can also exert control over the parameters of the film thickness and homogeneity [2]. These novel PMEs may potentially find application in a wide range of technologies including, energy storage systems [3], membrane gas separation [4], electrocatalysis [5], and sensors [6]. The polymeric films can be further incorporated by some modifiers such as enzymes [7], nanoparticles [8] and polymer composite structures [9] to facilitate certain applications. Since the pioneering work of Diaz and coworkers in the late 70s [10,11], the fabrication of modified electrodes with highly stable and conductive polymeric films (polypyrrol, polyaniline, and polythiophene) has been a further developmental step towards their effective application in corrosion inhibition [12], light emitting diodes [13], electro-photosensitization [14] and biosensors [15]. The electrochemical polymerization of aromatic amines such as aniline (Ani) has been studied widely [16], exploring the reaction mechanism and the kinetics of polyaniline (Pani) growth on conducting substrates. The initial step is the formation of the Ani cationic radical followed by dimerization reactions, and then chain growth via the linkage of radical ions or the connection of the radical with the neutral monomer. The major intermediate product was characterized as the dimer-aniline like constituent called 4-aminodiphenylamine (4-adpa) [17]. Recently, Planes et al. [18] have identified 4-adpa as the Ani-dimer intermediate produced via head-to-tail coupling of Ani cation radicals using a spectroscopic method. The conductivity and molecular mass of poly(4-aminodiphenylamine) prepared in aqueous HCl solution [19] were found to be significantly less than those of Pani due to the for mation of oligomeric products composed of four monomeric units. In another study, using in situ FTIR and UV-Vis methods, Zimmermann et al. [20] concluded that the main structure formed during the electrochemical polymerization of 4-adpa was the Ani- tetramer. A composite conducting film was also constructed by electrochemical polymerization of 4-adpa at pH = 5.0 in the presence of Ani [21]. The incorporation of Ani was featured for two reasons: (i) due to the lack of homo- polymerization reaction of 4-adpa where its electrochemical oxidation is believed to be slow and inefficient, and (ii) to enhance the propagation reactions of the oxidized 4-adpa species. The resulting film showed a good catalytic reactivity towards a number of redox couples in a weakly acidic buffer solution. Another novel work of Cotarelo et al. [22] was devoted to characterizing the polymeric film produced by electrochemical oxidation of 4-adpa in a strongly acidic medium using a number of microscopic and spectroscopic techniques. It was concluded that the resulting polymer displayed electrochemical, morphological and spectroscopic characters similar to those shown by Pani. Considerable attention has been given to environmental contamination with heavy metal ions for health and safety reasons. Therefore, a trace monitoring of these metal ions in the environment is an important but analytically challenging task. The maximum admissible limit for Pb 2+ and Cd 2+ ions for drinking water quality are 15 and 5 g L -1 , respectively, as reported by the United States Environmental Protection Agency (USEPA) in 2008. Electrochemical stripping analysis was recognized as an efficient tool for simultaneous monitoring of heavy metals [23]. The scope of sensing tools has been developed significantly for simultaneous and selective trace quantification of heavy metals via appropriate surface modifications, for example by the incorporation of bismuth film [24], boron-doped diamond [25], polypyrrole [26], poly(3,4-diaminoterthiophene) [27] and polyaniline [28]. The present work is devoted to studying the nature of resulting Padpa film deposited at glassy carbon electrode (Padpa/GCE) and its application for trace determination of cadmium (Cd 2+ ) and lead (Pb 2+ ) ions. Surface modification with Padpa was selected due to the structural limitations and involvement of different intermediates in producing Pani, while the formation of Padpa is known to proceed via a single specific intermediate, as illustrated in Scheme 1 given below. Therefore, producing a thin and smooth polymeric film at lower oxidative applied potential and avoiding the polymer over-oxidation is another important major theme of the present work. Moreover, the presence of a surface modifier, such as a conducting polymer, is likely to increase the electrode surface area and its adsorption capacity. 2. Experimental 2.1 Reagents Electrochemical measurements for metal analysis were carried out in an equimolar 0.1 M mixture of (KCl + HCl) solution (pH = 2.12) prepared in Millipore water. The electrolyte was degassed by purging oxygen-free nitrogen gas for 10 min, and blanketed throughout the experiment. A stock solution of the 4-adpa monomer (Aldrich) was prepared by dissolving a certain amount in 1.0 M HCl and sonicated for 5 min at 35 o C using (JAC Ultra Sonic, Korea). Standard solutions (1000 ppm, atomic absorption standard solutions) of Cd(II) and Pb(II) purchased from BDH Chemicals, UK, were diluted as required and used for simultaneous and selective determination. Also, Cu(II) and Hg(II) (BDH Chemicals, UK) were used for interference studies. All other chemicals were of analytical-reagent grade and used as received. 2.2 Electrochemical measurements The electrochemical measurements including cyclic voltammetry (CV) and differential pulse anodic stripping voltammetry (DPASV) experiments were conducted using a BAS 50W work station. The measurements were performed in a 20 mL electrochemical cell using a glassy carbon electrode (GCE) with a geometric area of 0.071 cm 2 as the working electrode, a platinum coil with a geometric area of 1.90 cm 2 as the counter electrode, and an Ag/ AgCl/ POLYMERIC FILM MODIFIED ELECTRODE 42 KCl(sat.) as the reference electrode. The potentiostat and electrodes were from Bioanalytical System, West Lafayette, IN, USA. Prior to each experiment, the working electrode was polished using a polishing cloth and alumina slurry (5.0 and 1.0m), washed with acetone, ultrasonicated for 5 min and finally rinsed thoroughly with distilled water. The electrode was then pre-treated electrochemically by scanning the potential repeatedly between -400 mV to +1000 mV for 25 cycles at a scan rate (v) of 100 mV s 1 and terminating at the anodic potential limit in the supporting electrolyte, in order to establish a reproducible electrode surface and avoid any previous fouling effect. Such a reversible potentiodynamic scan produces a surface composed of carbon-oxygen functional groups of phenol and quinol forms that increase the electrode reactivity and the grafting efficiency. The CV experiments were utilized mainly to study the progress of the electrochemical polymerization, and the stability and the sensitivity of the resulting polymeric film modified electrode. The typical parameters controlling the DPASV experiment were (i) deposition time = 120 s, (ii) deposition potential = 00 mV (with stirring mode), (iii) final potential = +200 mV at scan rate of 40 mV s 1 , (iv) pulse amplitude = 50 mV, (v) sample width = 25 ms, (vi) pulse width = 50 ms, (vii) pulse period = 100 ms and (viii) quiet time = 10 s. 2.3 Characterization techniques The structure and surface morphology of the polymer deposited at glassy carbon disks (5 mm  100 m) (from Hochtemperature-Werkstoffe, Gmbh, Germany) by repetitive potentiodynamic cycles were investigated by X-ray Photoelectron Spectroscopy (XPS) using an Omicron Nanotechnology XPS system, and by Atomic Force Microscopy (AFM) using a Nanoscope V Multimode microscope (Veeco Instrument, USA). The XPS spectra obtained were deconvoluted using CasaXPS program (Casa Software Ltd, UK), in which the background was simulated using Shirley function and the peaks were fitted using a Gaussian Lorentzian function. The AFM images were recorded ex situ using a tapping mode at a scan rate and imaging resolution of 0.5 Hz and 512 pixels, respectively. Electrochemical Impedance Spectro scopy (EIS) was employed to further investigate the interfacial structure due to surface modification and extract important information about the rate of electron transfer, the double-layer capacitance and the diffusion limited process. The EIS was carried out on EIS 300 (GAMRY, USA) connected to a three-electrode cell composed of Ag/AgCl, KCl(satd) and platinum coil as reference and counter electrodes, respectively. The working electrode was either the bare GCE or Padpa/GCE modified electrode. The EIS measurements were conducted at an open circuit potential of 5.0 mM [Fe(CN)6] 3/4 redox probe in the frequency range from 0.1 Hz to 100 kHz. 2.4 Treatment and preparation of the water sample A treated waste water sample used for agricultural irrigation was collected from the botanical garden located inside the Sultan Qaboos University. The sample was collected in 100 mL polyvinyl bottles, filtered and acidified with 1.0 mL of 1.0 M HCl. Prior to analysis, 5.0 mL of the sample was pipetted in a small vial and mixed with the required amounts of metal standard solutions. The standard addition method was applied to determine the concentration of both metal ions with reference to the metal-free water sample. 3. Results and discussion 3.1 Electrochemical polymerization of 4-adpa using CV method Figure 1 shows typical cyclic voltammograms (CVs) corresponding to the electrochemical polymerization of Padpa at GCE using 5.0 mM 4-adpa in 1.0 M HCl solution. The polymeric film was obtained by repetitive potential scans (25 cycles) between -200 mV and +800 mV vs. Ag/ AgCl at 50 mV s 1 . A pair of redox peak currents was developed (anodic) at +425 mV and (cathodic) +197 mV which increased constantly upon subsequent cycling. The reversible voltammetric waves describe the formation of reduced and oxidized oligomers called the leucoemeraldine and pernigraniline, respectively, which involves the transfer of two electrons and two protons [29]. The initiation step for the propagation of the polymer is the formation of a cationic intermediate called N-phenyl- quinonediimine (pqdi) [30] as shown in the mechanistic reaction presented in Scheme 1. This step is followed by a dimerization step of pqdi with the monomer to form the mono-charged radical intermediate responsible for the growth of the polymer. Petr et al. Have confirmed the formation of pqdi as the only product formed during the oxidation of 4- adpa by in situ UV-Vis electrochemical measurements [31]. Hence, in the reverse scan, the remaining surface amount of pqdi (not dimerized) may undergo a reduction reaction which gives rise to a smaller current response at 340 mV. It should be noted that the relative amount of both constituents (oxidized and reduced forms) depends on the acid concentration, the oxidative applied potential and the degree of polymerization (number of cycles). The experimental data presented in Figure 1 can be expressed in consecutive steps initiated by the formation of radical intermediates, dimerization, oligo-merization and the deposition of less soluble oligomers (tetramers and/or octamers) at the electrode surface [19,20]. The formation of an adhering polymeric film at the electrode surface was confirmed by Petr et al. [33] using electrochemical and Electron Spin Resonance (ESR) methods. The electrochemical EMAD KHUDAISH ET AL 44 behavior of the modified electrode was examined by stepping the electrode potential between 400 mV to +900 mV vs. Ag/AgCl in a monomer-free aqueous solution of 0.10 M HCl. Figure 1. Typical CVs (25 cycles) depicting the electrochemical polymerization of Padpa onto GCE using 5.0 mM 4-adpa monomer in 1.0 M HCl (the first segment is indicated by the dotted line). H N NH3 N NH2 + 2H+ + 2e- 4-aminodiphenylamine (4-adpa) N-phenylquinonediimine (pqdi) (4-adpa) + (pqdi) 2 Mono-charged radical intermediate H N NH2 Scheme 1: The initiation steps for the electrochemical polymerization of Padpa. Figure 2 depicts the electrode behavior as a function of scan rates in a monomer-free 0.10 M HCl solution. A redox surface type is developed that increased with increasing the scan rate from 25 to 300 mV s 1 . In the anodic scan, three peak currents arose at potentials +300, +350 and +440 mV, respectively (shown at the slowest potential scan rate). Apparently, a consecutive electron transfer process occurred due to a successive transition states of the surface material. In the reverse scan, the electron transfer also produces three cathodic peaks obtained at +435, +365 and +310 mV, respectively. Figure 2. The development of redox surface-type behavior as a function of scan rates in mV s 1 ; (a) 25, (b) 50, (c) 75, (d) 100, (e) 125, (f) 150, (g) 175, (h) 200, (i) 250 and (j) 300. POLYMERIC FILM MODIFIED ELECTRODE 44 The first two peaks are shifted to more positive potential and increased with subsequent increase in the scan rate consistent with increasing the rate of electron transfer process. Furthermore, these anodic peaks are found to merge at scan rates higher than 200 mV s -1 . A similar trend was apparent for the cathodic peaks that merged and shifted to a more negative potential. The peak separation (E) at the highest scan rate approached 216 mV suggesting the attachment of surface materials. The experimental data of the peak current as a function of scan rates (not shown) were further studied to calculate the surface coverage   of the deposited polymeric film in (mol cm2) applying Eq. (1) [34]. v RT AFn I 4 22 p         (1) The calculated surface concentration was 2.71  10 10 mol cm 2 , taking into consideration that n = 2 and A is the geometric area while other terms have their usual thermodynamic descriptions. 3.2 Surface morphological studies XPS and AFM methods were used to characterize the elemental structure of the electrode surface and confirm the deposition of the polymer. Figure 3 demonstrates the XPS short scan of C 1s which is deconvoluted into three peaks at 283.9, 285.1 and 287.3 eV corresponding to C-C, C-N and C=O bonds, as anticipated from the original structure of the monomer [22]. Similarly, the N 1s short scan gave rise to three peaks at 398.8, 400.1 and 402.3 eV corresponding to the tertiary amine (=N) bonding, neutral and protonated primary amines (NH2) and (NH3 + ) respectively. The presence of =N group is indicative of the fact that successive oxidation and deprotonation processes took place in the polymerization of the Padpa. AFM images reveal a uniform and symmetrical fiber structure with a lower energy dissipation factor. This could be attributed to reduction in the roughness factor of the film, having an average height of 35 nm and a cumulative surface area of 65 nm 2 . It also shows a low and uniform Young’s modulus (~15 GPa) pertinent to the deposition of a pristine Padpa substance. The surface roughness of the polymer is expected to become much coarser by increasing the number of potentiodynamic cycles in which a new route of polymerization process may control the progress of film formation. 3.3 Electrochemical impedance studies The AC impedance spectra presented by Nyquist plot in the presence of 0.5 M KNO3 solution containing 5.0 mM [Fe(CN)6] 3/4 are shown in Figure 4. Two characteristic parts are identified in the plot as a linear curve and a semi- circular shape, which occurred at low and high frequencies, respectively. The linear trend corresponds to the diffusion limited process while the arc shape represents the rate of electron transfer process. To understand the electrical properties of the electrode/solution interfaces, a modified Randle’s equivalent circuit (inset of Figure 4) was selected for fitting the impedance data [35]. The EIS data recorded at the bare GCE (inset) showed a charge transfer resistance (Rct) with a given diameter of 147 , compared to the Padpa/GCE modified electrode that revealed a larger value of 2670 . This trend evidently demonstrates that Padpa was successfully assembled at the GCE. 3.4 Applications 3.4.1 Simultaneous determination of cadmium and lead ions Figure 5 depicts the application of the modified electrode for simultaneous determination of Cd 2+ and Pb 2+ employing the DPASV method in which the anodic peak currents were recorded as a function of metal ion concentrations. The (I–E) curve illustrates the rising up of a couple of well-defined peaks at –825 mV and –535 mV, corresponding to the stripping of Cd 2+ and Pb 2+ , respectively. The peak separation (E = 290 mV) is significantly large, indicating an excellent selectivity and catalytic activity of the present system. Moreover, the anodic peak currents of both ions are increasing linearly with the concentration as illustrated by the calibration curve given in the inset of Figure 5. The sensitivity of the present system is evaluated by means of the slope difference of both ions obtained from the experimental data presented in Figure 5. The slope ratio of lead to cadmium ions   22 CdPb /SS is close to 2.75 indicating a higher sensitivity in determination of lead ions. The surface affinity of both ions was expected to be the same unless possible interaction forces occurred between them due to differences in their electronegativity values. Therefore, Pb 2+ ions of higher electronegativity were reduced and formed a micro-structure of particles or coated film at cathodic potential lower than that of Cd 2+ ions, which may have caused the formation of an intermetallic (Pb-Cd) structure [35]. The expected events occurred during deposition potential period when the preferential deposition of Pb was followed by a direct deposition of Cd at both the polymeric film and the Pb matrix already existing on the electrode surface. During the anodic stripping mode, Cd deposited at the polymeric film will first dissolute at – 825 mV and the remaining Cd deposited on to Pb will be stripped with Pb at more positive potential. It should be noted that the positive EMAD KHUDAISH ET AL 44 potential shift in the stripping of both ions shown in Figure 5 with increasing the concentration is an indication of such energetic interaction. Figure 3. Surface topographic analysis represented by XPS short scans of C 1s and N 1s with AFM images of dissipation and DMT Modulus of the Padpa/GCE surface film. Figure 4. EIS data for Padpa/GCE and bare GCE (insert) with the modified Randle’s equivalent circuit. Figure 5. DPASV curves recorded at Padpa/GCE in acidified 0.1 M KCl solution (pH = 2.12) for the simultaneous determination of Cd 2+ and Pb 2+ ions. The range of [Cd 2+ ] and [Pb 2+ ] are indicated by the calibration curve (Ip vs [M 2+ ]) given in the inset. POLYMERIC FILM MODIFIED ELECTRODE 44 Moreover, the limit of detection (LOD) was calculated using (3/S) where  is the standard deviation obtained from 5 replicates of the blank. The LODs were 25 and 14 g L 1 for Cd 2+ and Pb 2+ , respectively. The sensitivity of the present system given by the slope of the linear relationship of Ip vs [M 2+ ] was compared with other electrochemical systems [36-42] and presented in Table 1. The present work showed a good sensitivity for both metal ions suggesting the construction of a robust solid state sensor for environmental applications. It should be noted that the stripping analysis of each ion in the concentration range of 50 to 500 g L 1 was conducted separately to evaluate the surface catalytic efficiency and the rational scenario of binary concentrations. Such primary analysis along with controlling the method parameters, in particular the deposition potential and accumulation period, enhance the separation facility and minimize possible suppression of the cadmium peak [43]. Therefore, the linear concentration range of Cd 2+ ions presented in Figure 5 must have been relatively high to produce a significant change in the stripping peak current. Apparently, the binary solution of the above selected recipe allows a regular and steady deposition of both ions at the electrode surface, where only two symmetrical and well defined peaks arose regardless of the relative extent of surface capacitance due to the presence of the polymeric film. Table 1. The sensitivity of various electrochemical systems in (A/ g L 1 ) evaluated from the simultaneous determination data of both metal ions in their binary mixture. Surface Cadmium Lead Ref. Bi/Pani 0.73 0.074 [36] PEDOT 0.004 0.008 [37] Pani 0.021 0.059 [38] Bi/Nafion 0.027 0.019 [39] PPMA 0.007 0.098 [40] BDD 0.015 0.013 [41] Bi/Poly(p-ABSA) 0.031 0.019 [42] Padpa 0.038 0.104 this work However, the estimated base peaks for the stripping of Cd and Pb at their highest concentrations shown above were found to be 175 and 100 mV, respectively. The above important observations pertaining to analytical peak separation and low detection limits, suggest an excellent stability, sensitivity and adsorption capacity of the present electrocatalytic system. It is worthy to note that the above data were collected without intervening electrode conditioning between successive concentrations. The stability and the reproducibility of the modified electrode were examined by repeating the DPASV experiment 10 consecutive times in the presence of 250 g L 1 (Pb) and 500 g L 1 (Cd). The peak separation was successfully maintained, indicating a good stability of the modified electrode, while the current variation was 4.7% for Pb and 6.6% for Cd, suggesting that the electrode reactivity is not affected critically by the adsorption of analytes and can be used multiple times. 3.4.2 Selective determination of cadmium and lead ions The electrode selectivity and hence the interference trend was tested for each metal ion by sequentially changing the concentration of one metal ion in the presence of a high and constant concentration of the second one. Figure 6 depicts the effect of 1000 g L 1 of Pb 2+ in the determination of Cd 2+ ions using the DPASV method. The stripping peak of Cd is well separated and occurred at –820 mV vs (Ag/ AgCl) and increased linearly with increasing [Cd 2+ ] despite a possible interfering tendency that may be initiated by the presence of large [Pb 2+ ]. The calibration curve for the linear plot of Ip vs. [Cd 2+ ] is shown in the inset of Figure 6, and the calculated LOD (3σ/S) was 23 g L 1 . Nevertheless, the stripping peak of Pb (present in a large scale) obtained at –0 mV does not hinder or manipulate the stripping peak of Cd, indicating that Padpa active sites are capable of accommodating both metals during the accumulation period. In a similar fashion, the data presented in Figure 7 illustrates that the presence of 2000 g L 1 Cd does not alter the stripping peak position of Pb, which maintained its symmetrical shape and sharpness, and increased subsequently with increasing [Pb 2+ ]. The calibration curve for the linear plot of Ip vs. [Pb 2+ ] is shown in the inset of Figure 7, and the calculated LOD (3σ/S) was 13 g L 1 . Accordingly, it can be concluded that the surface based material did not deteriorate due to deposition of both metals and sustained its structure during the stripping mode in the positive scan. 3.4.3 Interference studies The presence of foreign metal ions in the water sample may change the nature and the morphology of the electrode surface and hence affect the electrochemical measurements of analytes under investigation. For this task, the simultaneous determination of 250 g L 1 (Pb) and 500 g L 1 (Cd) was investigated in the presence of 5000 g L 1 of EMAD KHUDAISH ET AL 25 the foreign ion. Foreign ions such as Na + , Mg 2+ , Ni 2+ , Co 2+ , Al 3+ , Fe 3+ , VO4 3 , MnO4  , Cl  , and NO3  had no interference on the present system. The effect of Cu 2+ and Hg 2+ on the stripping voltammetry of Pb and Cd ions is presented in Figures 8(A) and (B), respectively. The presence of 2500 g L 1 Cu 2+ (solid line) distorted the development of the Cd peak which appears very broad and unsymmetrical, while the peak potential of Pb was only shifted by +100 mV from its usual position (dotted line). The presence of 1000 g L 1 Hg 2+ (solid line) had a direct effect on the symmetry of the Cd peak current, which became much sharper and increased three fold the original value (dotted line), while it had no effect on the peak current of Pb. The above trend could be interpreted as due to the formation of a thin Hg layer that played a major r ole in the enhancement of the Cd voltammetric signal. 0 10 20 30 40 50 60 70 80 -1200 -1000 -800 -600 -400 -200 0 I/  A E / mV vs (Ag/AgCl) Cd Pb i a y = 47.401x R² = 0.9972 0 5 10 15 20 25 30 35 40 45 0 0.1 0.2 0.3 0.4 0.5 0.6 0.7 0.8 0.9 I p /  A [Cd2+]/ mg L1 Figure 6. DPASV curves recorded at Padpa/GCE in acidified 0.1 M KCl solution (pH = 2.12) for the selective determination of Cd 2+ in the presence of 1.0 mg L 1 Pb 2+ . The range of [Cd 2+ ] is (a) 0 increased by 0.1 mg L 1 each time to a final (i) 0.8 mg L 1 (inset is the calibration curve represented by Ip vs [Cd 2+ ]. Figure 7. DPASV curves recorded at Padpa/GCE in acidified 0.1 M KCl solution (pH = 2.12) for the selective determination of Pb 2+ in the presence of 2.0 mg L 1 Cd 2+ . The range of [Pb 2+ ] is (a) 0 increased by 0.05 mg L 1 each time to a final (i) 0.4 mg L 1 (inset is the calibration curve represented by Ip vs [Pb 2+ ]. 3.4.4 Analytical test to water sample The proposed system was tested for the determination of both metal ions in a water sample treated and prepared as described above in section 2.4. POLYMERIC FILM MODIFIED ELECTRODE 21 Figure 8. Interference study on the stripping peaks of 0.5 mg L 1 Cd 2+ and 0.25 mg L 1 Pb 2+ in the presence of (A) 2.5 mg L 1 of [Cu 2+ ] and (B) 1.0 mg L 1 of [Hg 2+ ] using acidified 0.1 M KCl solution (pH = 2.12). The analytical results including the recovery percentage are given in Table 2. The recoveries were more than 97% (the calculated relative standard deviation values were less than 10%), and demonstrate that the present system can offer a sensitive and accurate method for the monitoring of trace metal ions. Table 2. Analytical parameters and recovery percentage (n = 3) for Cd 2+ and Pb 2+ ions in water samples using standard addition method. The regression data obtained from Figure 5 were used to calculate their concentrations. Metal ions (I) (A) [Actual] (g L 1 ) [Found] (g L 1 ) Recovery (%) ) 2+ (Cd (1) 1.84 50 48.4 96.8 (2) 3.76 100 98.9 98.9 (3) 5.69 150 149.7 99.8 ) 2+ (Pb (1) 2.45 25 24.4 97.7 (2) 5.21 50 50.1 100.2 (3) 7.88 75 75.8 101.0 4. Conclusions A chemically modified electrode was fabricated via the electrochemical polymerization of Padpa at GCE in 1.0 M HCl solution. The surface coverage of the coated film was influenced by the applied anodic potential that initiated the progression of polymerization and defined the nature of the resulting polymer. The polymeric film modified electrode exhibited a reversible electrochemical behavior, demonstrated by the development of redox active sites. The estimated surface roughness and cumulative surface area of the modified electrode under the present working conditions is an index for possible doping process on the film matrix to improve its catalytic properties for certain analytical applications. The constructed modified electrode showed a potential capacity to be a reliable environmental sensor for the simultaneous determination of Cd 2+ and Pb 2+ ions. The incorporation of certain surface modifiers such as metal microfilms or metal nanoparticles on the Padpa moiety is another important area to investigate in developing solid-state sensors for environmental, biological and pharmaceutical applications. 5. Acknowledgement We acknowledge TRC and SQU for supporting the solid state sensor project; research grant number (RC/SCI/CHEM/11/01). References 1. Brito-Madurro, A.G., Ferreira, L.F., Vieira, S.N., Goulart, L.R. and Madurro, J.M. Immobilization of purine bases on a poly-4-aminophenol matrix. J. Mater. Sci., 2007, 42, 3238-3243. EMAD KHUDAISH ET AL 25 2. Dinh, H.N. and Birss, V.I. Effect of substrate on polyaniline film properties: a cyclic voltammetry and impedance study articles. J. Electrochem. Soc., 2000, 147, 3775-3784. 3. Murray, R.W. Polymer Modification of Electrodes. Ann. Res. Mater. Sci., 1984, 14, 145-169. 4. Dominique, N.D. and Fabienne, P.E. Polyaniline as a new sensitive layer for gas sensors. Anal. Chim. Acta, 2003, 475, 1-15. 5. Griese, S., Kampouris, D.K., Kadara, R.O. and Banks, C.E. Critical review of the electrocatalysis reported at C60 modified electrodes. Electroanalysis, 2008, 20, 1507-1512. 6. Tahir, Z.M., Alocilja, E.C. and Grooms, D.L. Polyaniline synthesis and its biosensor application. Biosens. Bioelectron., 2005, 20, 1690-1695. 7. Yang, H., Chung, T.D., Kim, Y.T., Choi, C.A., Jun, C.H. and Kim, H.C. Glucose sensor using a microfabricated electrode and electropolymerized bilayer films. Biosens. Bioelectron., 2002, 17, 251-259. 8. Liu, Y.C. and Chuang, T.C. Synthesis and characterization of gold/polypyrrole core-shell nanocomposites and elemental gold nanoparticles based on the gold-containing nanocomplexes prepared by electrochemical methods in aqueous solutions. J. Phys. Chem. B, 2003, 107, 12383-12386. 9. Levine, K. and Iroh, J.O. Electrochemical behavior of a composite of polyimide and polypyrrole. J. Mat. Chem., 2001, 11, 2248-2252. 10. Diaz, A.F., Kanazawa, K.K. and Gardini, G.P. Electrochemical polymerization of pyrrole. J. Chem. Soc. Chem. Commun., 1979, 14, 635-636. 11. Kanazawa, K.K., Diaz, A.F., Geiss, R.H., Gill, W.D., Kwak, J.F., Logan, J.A., Rabolt, J.F. and Street, G.B. Organic metals: polypyrrole, a stable synthetic “metallic” polymer. J. Chem. Soc. Chem. Commun., 1979, 19, 854-855. 12. Ahmad, N. and MacDiarmid, A.G. Inhibition of corrosion of steels with the exploitation of conducting polymers. Synth. Met., 1996, 78, 103-110. 13. Kraft, A., Grimsdale, A.C. and Holmes, A.B. Electroluminescent conjugated polymers - seeing polymers in a new light. Angew Chem. Int. Ed., 1998, 37, 402-428. 14. Sapp, S.A., Elliott, C.M., Contado, Caramori, C.S. and Bignozzi, C.A. Substituted polypyridine complexes of cobalt(II/III) as efficient electron-transfer mediators in dye-sensitized solar cells. J. Am. Chem. Soc., 2002, 124, 11215-11222. 15. Kim, J.H., Cho, J.H. and Cha, G.S. Conductimetric membrane strip immunosensor with polyaniline-bound gold colloids as signal generator. Biosens. Bioelectron., 2000, 14, 907-915. 16. Yang, H. and Bard, A.J. The application of fast scan cyclic voltammetry. Mechanistic study of the initial stage of electro-polymerization of aniline in aqueous solutions. J. Electroanal. Chem., 1992, 339, 423-449. 17. Ćirić-Marjanović, G., Trchová, M., Konyushenko, E.N., Holler, P. and Stejskal, J. Chemical oxidative polymerization of aminodiphenylamines. J. Phys. Chem. B, 2008, 112, 6976-6987. 18. Planes, G.A., Rodriguez, J.L., Miras, M.C., Garcia, G., Pastor, E. and Barbero, C.A. Spectroscopic evidence for intermediate species formed during aniline polymerization and polyaniline degradation, Phys. Chem. Chem. Phys., 2010, 12, 10584-10593. 19. Kitani, A., Yano, J., Kunai, A. And Sasaki, K. A conducting polymer derived from para-aminodiphenylamine. J. Electroanal. Chem. (Interfacial), 1987, 221, 69-82. 20. Zimmermann, A., Kunzelmann, U. and Dunsch, L. Initial states in the electropolymerization of aniline and p-aminodiphenylamine as studied by in situ FT-IR and UV-Vis spectro-electrochemistry. Synth. Met., 1998, 93, 17-25. 21. Cotarel, M.A., Huerta, F., Quijada, C., Cases, F. And Vazquez, J.L. The electrocatalytic behaviour of poly (aniline-co-4adpa) thin films in weakly acidic medium. Synth. Met., 2004, 144, 207-211. 22. Cotarelo, M.A., Huerta, F., QuiJada, C., Mallavia, R. and Vazquez, J.L. Synthesis and characterization of electroactive films deposited from aniline dimers electrochemical synthesis and engineering. J. Electrochem. Soc., 2006, 153, 114-122. 23. Wang, J., Lu, J., Hocevar, S.B., Farias, P.A.M. and Ogorevc, B. Bismuth-coated carbon electrodes for anodic stripping voltammetry. Anal. Chem., 2000, 72, 3218-3222. 24. Hutto, E.A., Hocevar, S.B., Ogorevc, B. and Smyth, M.R. Bismuth film electrode for simultaneous adsorptive stripping analysis of trace cobalt and nickel using constant current chronopotentiometric and voltammetric protocol. Electrochem. Commun., 2003, 5, 765-769. 25. Tsai, Y.C., Coles, B.A., Holt, K., Foord, J., Marken, F. and Compton, R.G. Microwave enhanced anodic stripping detection of lead in a river sediment sample. Mercury free procedure employing boron doped diamond electrode. Electroanalysis, 2001, 13, 831-835. 26. Heitzmann, M., Bucher, C., Moutet, J.C., Pereira, E., Rivas, B.L., Royal, G. and Saint-Aman, E. Complexation of poly(pyrrole-EDTA like) film modified electrodes: application to metal cations electroanalysis. Electrochim. Acta, 2007, 52, 3082-3087. 27. Rahman, M.A., Won, M.S. and Shim, Y.B. Characterization of an EDTA bonded conducting polymer modified electrode: its application for the simultaneous determination of heavy metal ions. Anal. Chem., 2003, 75, 1123-1129 http://www.sciencedirect.com/science/article/pii/S0003267002012291 http://www.sciencedirect.com/science/article/pii/S0956566304003732 http://www.sciencedirect.com/science/article/pii/S0956566301002664 http://www.sciencedirect.com/science/article/pii/S0956566301002664 http://pubs.acs.org/doi/abs/10.1021/jp035680h http://pubs.acs.org/doi/abs/10.1021/jp035680h http://pubs.acs.org/doi/abs/10.1021/jp035680h http://www.sciencedirect.com/science/article/pii/0379677996801093 http://www.sciencedirect.com/science/article/pii/0379677996801093 http://pubs.acs.org/doi/abs/10.1021/ja027355y http://pubs.acs.org/doi/abs/10.1021/ja027355y http://www.sciencedirect.com/science/article/pii/S0956566399000639 http://www.sciencedirect.com/science/article/pii/S0956566399000639 http://www.sciencedirect.com/science/article/pii/002207289280466H http://www.sciencedirect.com/science/article/pii/002207289280466H http://pubs.acs.org/doi/abs/10.1021/jp710963e http://pubs.acs.org/doi/abs/10.1021/jp710963e http://pubs.rsc.org/en/content/articlelanding/2010/cp/c002920c http://pubs.rsc.org/en/content/articlelanding/2010/cp/c002920c http://www.sciencedirect.com/science/article/pii/0022072887802462 http://www.sciencedirect.com/science/article/pii/S0379677998801276 http://www.sciencedirect.com/science/article/pii/S0379677998801276 http://www.sciencedirect.com/science/article/pii/S0379677904001237 http://www.sciencedirect.com/science/article/pii/S0379677904001237 http://www.sciencedirect.com/science/article/pii/S1388248103001772 http://www.sciencedirect.com/science/article/pii/S1388248103001772 http://www.sciencedirect.com/science/article/pii/S1388248103001772 http://www.sciencedirect.com/science/article/pii/S0013468606010486 http://www.sciencedirect.com/science/article/pii/S0013468606010486 POLYMERIC FILM MODIFIED ELECTRODE 25 28. Wagner, K., Strojek, J.W. and Kosiel, K. Electrochemical and quartz crystal microbalance studies of lead(II) deposition and stripping in the presence of copper on a gold electrode modified with 2,2′-bipyridyl in polyaniline. Anal. Chim. Acta, 2002, 455, 69-81. 29. Macdiarmid, A.G., Chiang, J.C., Richter, A.F. and Epstein, A.J. Polyaniline: a new concept in conducting polymers. Synth Met., 1987, 18, 285-290. 30. Uchiyama, S., Hasebe, Y., Maeda, Y. and Yoshida, Y. Highly sensitive cyclic voltammograms of 4-amino- diphenylamine obtained by a porous carbon felt electrode and estimation of the hydrolysis rate constant of its quinonediimine state at a neutral pH. Electroanal., 1997, 9, 822-826. 31. Petr, A. and Dunsch, L. Direct evidence of indamine cation radicals in the anodic oxidation of aniline by in situ ESR spectroscopy. J. Electroanal., Chem., 1996, 419, 55-59. 32. Petr, A. and Dunsch, L. Kinetics of the p-aminodiphenylamine radical in organic solution:  an electrochemical and electron spin resonance study. J. Phys. Chem., 1996, 100, 4867-4872. 33. Bard, A.J. and Faulkner, L.R. Electrochemical Methods: Fundamentals and Applications, (2 nd Edition), Wiley & Sons, New York, 2001. 34. Lisdat, F. and Schafer, D. The use of electrochemical impedance spectroscopy for biosensing. Anal. Bioanal. Chem., 2008, 391, 1555-1567. 35. Manivannan A., Kawasaki R., Tryk D.A. and Fujishima A. Interaction of Pb and Cd during anodic stripping voltammetric analysis at boron-doped diamond electrodes, Electrochim. Acta, 2004, 49, 3313-3318. 36. Zhu, W.W., Li, N.B. and Luo, H.Q. Anodic stripping voltammetry for the determination of Pb(II) and Cd(II) at a bismuth/poly(aniline) film electrode. Anal. Lett., 2006, 39, 2273-2284. 37. Vedhi, C., Selvanathan, G., Arumugam, P. and Manisankar, P. Electrochemical sensors of heavy metals using novel polymer-modified glassy carbon electrodes. Ionics, 2009, 15, 377-383. 38. Wang, Z., Liu, E. and Zhao, X. Glassy carbon electrode modified by conductive polyaniline coating for determination of trace lead and cadmium ions in acetate buffer solution. Thin Solid Films, 2011, 519, 5285- 5289. 39. Kefala, G. and Economou, A. Polymer-coated bismuth film electrodes for the determination of trace metals by sequential-injection analysis/ASV. Anal. Chim. Acta, 2006, 576, 283-289. 40. Heitzmann, M., Basaez, L., Brovelli, F., Bucher, C., Limosin, D., Pereira, E., Rivas, B.L., Royal, G., Saint- Aman, E. and Moutet, J-C. Voltammetric sensing of trace metals at a poly(pyrrole-malonic acid) film modified carbon electrode. Electroanal., 2005, 17, 1970-1976. 41. McGaw, E.A. and Swain, G.M. A comparison of boron-doped diamond thin-film and Hg-coated glassy carbon electrodes for anodic stripping voltammetric determination of heavy metal ions in aqueous media. Anal. Chim. Acta, 2006, 575, 180-189. 42. Wu Y., Li N.B. and Luo H.Q. Simultaneous measurements of Pb, Cd and Zn using differential pulse anodic stripping voltammetry at a bismuth/poly(p-aminobenzene sulfonic acid) film electrode. Sens. Actuat. B: Chemicals, 2008, 133, 677-681. 43. Oldham, K.B. and Myland, J.C. Fundamentals of Electrochemical Sciences, Academic Press, San Diego, 1994. Received 12 March 2014 Accepted 18 May 2014 http://www.sciencedirect.com/science/article/pii/S0003267001015768 http://www.sciencedirect.com/science/article/pii/S0003267001015768 http://www.sciencedirect.com/science/article/pii/S0003267001015768 http://www.sciencedirect.com/science/article/pii/0379677987908939 http://www.sciencedirect.com/science/article/pii/0379677987908939 http://www.sciencedirect.com/science/article/pii/S0022072896048619 http://www.sciencedirect.com/science/article/pii/S0022072896048619 http://pubs.acs.org/doi/abs/10.1021/jp952965o http://pubs.acs.org/doi/abs/10.1021/jp952965o http://link.springer.com/article/10.1007/s11581-008-0277-1 http://link.springer.com/article/10.1007/s11581-008-0277-1 http://www.sciencedirect.com/science/article/pii/S0040609011002264 http://www.sciencedirect.com/science/article/pii/S0040609011002264 http://www.sciencedirect.com/science/article/pii/S0003267006011809 http://www.sciencedirect.com/science/article/pii/S0003267006011809